CN112026307A - 一种茂金属流滴春棚膜及其制备方法 - Google Patents

一种茂金属流滴春棚膜及其制备方法 Download PDF

Info

Publication number
CN112026307A
CN112026307A CN202010841951.7A CN202010841951A CN112026307A CN 112026307 A CN112026307 A CN 112026307A CN 202010841951 A CN202010841951 A CN 202010841951A CN 112026307 A CN112026307 A CN 112026307A
Authority
CN
China
Prior art keywords
dripping
metallocene
lldpe
ldpe
master batch
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN202010841951.7A
Other languages
English (en)
Other versions
CN112026307B (zh
Inventor
赵立功
柳波
王伟
胡云强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
North Huajin Chemical Industries Co Ltd
Original Assignee
North Huajin Chemical Industries Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by North Huajin Chemical Industries Co Ltd filed Critical North Huajin Chemical Industries Co Ltd
Priority to CN202010841951.7A priority Critical patent/CN112026307B/zh
Publication of CN112026307A publication Critical patent/CN112026307A/zh
Application granted granted Critical
Publication of CN112026307B publication Critical patent/CN112026307B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提出一种茂金属流滴春棚膜及其制备方法，该茂金属流滴春棚膜通过不同树脂(LDPE、LLDPE、mLLDPE对流滴剂相容性不同的特点，以及不同流滴剂(长效、短效)在树脂中析出速度的不同，进行不同比例的复配，实现在7～10℃的棚温下流滴剂能够均匀析出，流滴期可以达到30～45天，满足春棚的对流滴功能的需求，有效提高地温，促进作物生长，营造良好种植环境。本发明适用于春季的温室棚面覆盖，产品具有流滴性，以及透光率高、增温效果好、物理性能强等特点，白天升温速度快，可减缓夜间棚温下降速度，提高棚内温度，促进作物早熟，大大提高种植经济效益。

Description

一种茂金属流滴春棚膜及其制备方法
技术领域
本发明属于农用薄膜制造技术领域，具体涉及一种茂金属流滴春棚膜及其制备方法。
背景技术
随着设施农业的发展，通过扣大棚膜种植蔬菜、瓜果等农作物已经不仅局限于越冬暖棚(秋季扣棚冬季成熟)，在春季也开始进行扣棚种植蔬菜、瓜果，同比大地同类作物早1～2个月上市。另一方面，春棚还可有效防止鸟类、昆虫对作物果实的伤害，更能给农户带来可观的经济效益。
春棚通常使用没有流滴性能的普通聚乙烯耐老化棚膜，缺点是在扣棚初期的3、4月份为保温需要没有放风膜面水滴多(白水滴)影响透光，从而导致地温升温慢，影响作物初期生长。有的地区也采用越冬暖棚使用的流滴膜，但因春棚保温差，春棚温度低于10～13℃以下时流滴剂不析出，同样也产生影响透光的白水滴，同样也导致地温低。
发明内容
(一)要解决的技术问题
本发明提出一种茂金属流滴春棚膜及其制备方法，以解决流滴膜低温不析出或析出慢，实现春棚初期流滴、高保温、高透光，有效提高地温、促进作物生长，实现早熟高产的的技术问题。
(二)技术方案
为了解决上述技术问题，本发明提出一种茂金属流滴春棚膜，该春棚膜经三层共挤工艺吹塑成型，各层所用树脂按如下要求选用：
作为抗紫外线耐老化层的外层，质量百分比组成为：LDPE与LLDPE树脂合计77～79％，其中LDPE:LLDPE＝1:1；mLLDPE树脂13～15％；耐老化功能母料1.9～2.1％，流滴保温耐老化功能母料5.9～6.1％；
作为流滴保温层的中层，质量百分比组成为：LDPE、LLDPE与mLLDPE树脂合计84～86％，其中LDPE:LLDPE:mLLDPE＝1:1:1；流滴保温耐老化功能母料14～16％；
作为减雾流滴保温层的内层，质量百分比组成为：LDPE与LLDPE树脂合计84～85％，其中LDPE:LLDPE＝2:1；流滴保温耐老化功能母料14～15％。
进一步地，耐老化功能母料的质量百分比组成为：LLDPE87～89％，受阻胺光稳定剂7.5～8.5％，复合抗氧剂3.5～4.5％。
进一步地，流滴保温耐老化功能母料的质量百分比组成为：LLDPE26％，LDPE25％，EVA树脂23.4％，受阻胺光稳定剂2.7％，复合抗氧剂0.9～1.1％，长效流滴剂5.6％，短效流滴剂8.4％，复合保温剂7.9～8.1％。
进一步地，流滴保温耐老化功能母料中，LLDPE的熔融指数为0.7～1.1g/10min，LDPE的熔融指数为1.5～2.0g/10min。
此外，本发明还提出一种茂金属流滴春棚膜的制备方法，该制备方法包括如下步骤：
制备耐老化功能母料：按照配方称量各种原料和助剂，每100kg一批；投入高速混合机搅拌均匀，经双螺杆挤出机拉条、水冷、风干、切粒、旋风除湿，包装备用；
制备流滴保温耐老化功能母料：按照配方称量各种原料和助剂，每75kg一批；投入密炼机搅拌、捏合，经单螺杆挤出机造粒后备用；
制备茂金属流滴春棚膜：将各种聚乙烯树脂及功能母料加入混料器中搅拌均匀，分别送入三台挤出机中，物料分别经三台挤出机的熔融、塑化、挤出到三层共挤模头经螺旋体继续塑化，经过圆形口模共同挤出；从圆形口模挤出复合筒状膜管，膜管在模心吹进的压缩空气吹胀作用下横向拉伸，同时经过圆形风口的冷却和上牵引夹辊的纵向牵伸，最后经插板插叠和收卷制得茂金属流滴春棚膜。
进一步地，挤出机的长径比为30:1，模头为三层复合中心进料型。
(三)有益效果
本发明提出一种茂金属流滴春棚膜及其制备方法，该茂金属流滴春棚膜通过不同树脂(LDPE、LLDPE、mLLDPE对流滴剂相容性不同的特点，以及不同流滴剂(长效、短效)在树脂中析出速度的不同，进行不同比例的复配，实现在7～10℃的棚温下流滴剂能够均匀析出，流滴期可以达到30～45天，满足春棚的对流滴功能的需求，有效提高地温，促进作物生长，营造良好种植环境。本发明适用于春季的温室棚面覆盖，产品具有流滴性，以及透光率高、增温效果好、物理性能强等特点，白天升温速度快，可减缓夜间棚温下降速度，提高棚内温度，促进作物早熟，大大提高种植经济效益。
附图说明
图1为本发明的流滴保温耐老化功能母料制备工艺流程图；
图2为本发明的茂金属流滴春棚膜生产工艺流程图。
具体实施方式
为使本发明的目的、内容和优点更加清楚，下面结合附图和实施例，对本发明的具体实施方式作进一步详细描述。
本实施例提出一种茂金属流滴春棚膜及其制备方法，该茂金属流滴春棚膜在配方设计上选用优质的低密度聚乙烯树脂(LDPE)、线性低密度聚乙烯树脂(LLDPE)、茂金属聚乙烯树脂(mLLDPE，以茂金属锆为催化剂聚合的线性聚乙烯)、EVA树脂以及复合保温剂、流滴剂(长效型和短效型)和光稳定剂为原料生产。
在上述聚烯烃树脂中，与流滴剂相容性较好的树脂排序为：EVA＞LDPE＞LLDPE＞mLLDPE；同一类树脂中，不同的熔融指数的品种(牌号)对流滴剂的分散和迁移具有影响；在低温情况下，流滴剂析出情况是短效流滴剂好于长效流滴剂。
综合上述聚烯烃树脂和流滴剂的特性，结合母料生产工艺及棚膜生产工艺特点，进行不同原料的复配和筛选，本实施例最终确定茂金属流滴春棚膜的配方。
本实施例的茂金属流滴春棚膜及其制备方法包括如下步骤：
(1)制备耐老化功能母料：
线性低密度聚乙烯粉料(LLDPE)：84.5kg；
受阻胺光稳定剂(
Figure BDA0002641752660000041
HS-362)：11.5kg；
复合抗氧剂(B215)：4kg；
各组份合计100kg为一批。
以上各组分准确称量，投入高速混合机中搅拌均匀，时间40～50秒；经双螺杆挤出机拉条、水冷、风干、切粒、旋风除湿，包装备用。
(2)制备流滴保温耐老化功能母料：
线性低密度聚乙烯粉料(LLDPE，熔融指数0.7～1.1g/10min)：19.5kg；
低密度聚乙烯粉料(LDPE，熔融指数1.5～2.0g/10min)：18.75kg；
EVA树脂：17.55kg；
受阻胺光稳定剂(
Figure BDA0002641752660000042
HS-362)：2.025kg；
复合抗氧剂(B215)：0.675kg；
流滴剂(长效，LY-6)：4.2kg；
流滴剂(短效，HP-Ⅲ)：6.3kg；
复合保温剂：6kg；
各组份合计75kg为一批。
以上各组分准确称量，投入密炼机中搅拌、捏合，经单螺杆挤出机造粒后备用，具体工艺流程如图1所示，包括投放到密炼机加料口中，降下加压盖，混炼、捏合20～30分钟。混炼完成后经斗提将料团送入单螺杆挤出机中，依靠螺杆旋转产生的压力及剪切力，使得物料可以充分进行塑化以及均匀混合，通过口模成型，经切粒机切粒成型，旋风分离器除湿，产出成品。
(3)制备茂金属流滴春棚膜
采用三层共挤吹膜工艺，在各层原料中按比例加入功能母料，经三层共挤工艺吹塑成型。各层所用树脂按如下要求选用。
①外层(抗紫外线耐老化层)：
低密度聚乙烯(LDPE)：39.4％；
线型低密度聚乙烯(LLDPE)：39.4％；
茂金属线性低密度聚乙烯(mLLDPE)：13.1％；
耐老化功能母料：2.1％；
流滴保温耐老化功能母料：6.0％。
②中层(流滴保温层)：
低密度聚乙烯(LDPE)：28.3％；
线型低密度聚乙烯(LLDPE)：28.3％；
茂金属线性低密度聚乙烯(mLLDPE)：28.3％；
流滴保温耐老化功能母料：15.0％。
③内层(减雾流滴保温层)：
低密度聚乙烯(LDPE)：43％；
线型低密度聚乙烯(LLDPE)：43％；
流滴保温耐老化功能母料：14.0％。
棚膜的生产具体工艺流程如图2所示。将称量好的物料用混料器搅拌15min，使物料混合均匀，分别送入三台挤出机中。挤出机长径比为30:1，模头为三层复合中心进料型。物料分别经三台挤出机的熔融、塑化、挤出到三层共挤模头经螺旋体继续塑化，经过圆形口模共同挤出。其中，内层由中心进料，中层和外层由侧面进料，原料混炼后经机头流道进一步均化，从圆形口模挤出三层不同原料组成的结合紧密、分层明显的复合筒状膜管；通过控制内冷风机进、排风量，把管状料胚吹胀到所需要的直径，同时由内、外风环送出的空气冷却定型，其中，膜管在模心吹进的压缩空气吹胀作用下横向拉伸，同时经过圆形风口的冷却和上牵引夹辊的纵向牵伸；定型的膜泡经过人字板和插板进入第一牵引装置，插板机构将薄膜制品在进入牵引装置压辊之前进行折叠；最后经收卷制得茂金属流滴春棚膜，由此可减少收卷装置的体积以及成品膜卷的尺寸，方便产品的储存和运输。
通过对本实施例的茂金属流滴春棚进行水浴测试，水温60℃出白滴时间同比普通流滴膜早1.5天，具备提前析出功能，流滴失效时间(白滴面积30％)为7～8天，可有效达到流滴持效期要求。经过在多地的实际扣棚，能够达到预期流滴效果，产品流滴性能良好，符合设计预期，满足西瓜、辣椒、豆角等作物春季扣棚的环境需求。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和变形，这些改进和变形也应视为本发明的保护范围。

Claims (6)

1.一种茂金属流滴春棚膜，其特征在于，所述春棚膜经三层共挤工艺吹塑成型，各层所用树脂按如下要求选用：
作为抗紫外线耐老化层的外层，质量百分比组成为：LDPE与LLDPE树脂合计77～79％，其中LDPE:LLDPE＝1:1；mLLDPE树脂13～15％；耐老化功能母料1.9～2.1％，流滴保温耐老化功能母料5.9～6.1％；
作为流滴保温层的中层，质量百分比组成为：LDPE、LLDPE与mLLDPE树脂合计84～86％，其中LDPE:LLDPE:mLLDPE＝1:1:1；流滴保温耐老化功能母料14～16％；
作为减雾流滴保温层的内层，质量百分比组成为：LDPE与LLDPE树脂合计84～85％，其中LDPE:LLDPE＝2:1；流滴保温耐老化功能母料14～15％。
2.如权利要求1所述的茂金属流滴春棚膜，其特征在于，所述耐老化功能母料的质量百分比组成为：LLDPE87～89％，受阻胺光稳定剂7.5～8.5％，复合抗氧剂3.5～4.5％。
3.如权利要求1所述的茂金属流滴春棚膜，其特征在于，所述流滴保温耐老化功能母料的质量百分比组成为：LLDPE26％，LDPE25％，EVA树脂23.4％，受阻胺光稳定剂2.7％，复合抗氧剂0.9～1.1％，长效流滴剂5.6％，短效流滴剂8.4％，复合保温剂7.9～8.1％。
4.如权利要求1所述的茂金属流滴春棚膜，其特征在于，所述流滴保温耐老化功能母料中，LLDPE的熔融指数为0.7～1.1g/10min，LDPE的熔融指数为1.5～2.0g/10min。
5.一种如权利要求1～4任一项所述的茂金属流滴春棚膜的制备方法，其特征在于，所述制备方法包括如下步骤：
制备耐老化功能母料：按照配方称量各种原料和助剂，每100kg一批；投入高速混合机搅拌均匀，经双螺杆挤出机拉条、水冷、风干、切粒、旋风除湿，包装备用；
制备流滴保温耐老化功能母料：按照配方称量各种原料和助剂，每75kg一批；投入密炼机搅拌、捏合，经单螺杆挤出机造粒后备用；
制备茂金属流滴春棚膜：将各种聚乙烯树脂及功能母料加入混料器中搅拌均匀，分别送入三台挤出机中，物料分别经三台挤出机的熔融、塑化、挤出到三层共挤模头经螺旋体继续塑化，经过圆形口模共同挤出；从圆形口模挤出复合筒状膜管，膜管在模心吹进的压缩空气吹胀作用下横向拉伸，同时经过圆形风口的冷却和上牵引夹辊的纵向牵伸，最后经插板插叠和收卷制得茂金属流滴春棚膜。
6.如权利要求6所述的制备方法，其特征在于，所述挤出机的长径比为30:1，模头为三层复合中心进料型。
CN202010841951.7A 2020-08-20 2020-08-20 一种茂金属流滴春棚膜及其制备方法 Active CN112026307B (zh)