CN1119596A - Method for making furniture relief and sculpture by using modified polyester - Google Patents
Method for making furniture relief and sculpture by using modified polyester Download PDFInfo
- Publication number
- CN1119596A CN1119596A CN 94108804 CN94108804A CN1119596A CN 1119596 A CN1119596 A CN 1119596A CN 94108804 CN94108804 CN 94108804 CN 94108804 A CN94108804 A CN 94108804A CN 1119596 A CN1119596 A CN 1119596A
- Authority
- CN
- China
- Prior art keywords
- modified polyester
- sculpture
- make
- relief
- furniture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a method for making furniture relief and sculpture by using modified polyester. Said method is divided into two portions of mould-making and casting and is different from existent technique in that it uses the uplifting method to make mould, uses modified polyester material to implement casting and various non-metallic mineral materials can be added in the modified polyester material to make them into various colourful furniture relief patterns and sculptures. The relief and sculpture patterns can be combined with existing furniture, and can be mounted on the faces of the furniture to make them more artistic.
Description
The present invention relates to a kind of production method of decorative effect, particularly a kind of method of making furniture relief, sculpture of modified polyester.
CN2045226U discloses a kind of Relief bedside, and in this technical scheme, embossing pattern is with the fiber glass resin cast molding and be bonded on the pasting board, and pasting board is fixed on the framework.Patternmaking process is at first to make pattern model with special loess, filler, auxiliary agent, the mud that is deployed into, makes soft mold with organic silicon rubber etc. according to pattern model again, makes die with cement, land plaster and waterglass etc. at last.The casting mold process is with fiber glass resin, and initator, promoter, filler, releasing agent, solvent, fiber and pigment dissolve the back with catching up with the cast molding of oxygen casting method by the proper proportion mixing, again through spontaneous curing in 1.5～2 hours, print embossing pattern.What the weak point that this technical scheme exists was that (1) fiber glass resin adopts when construction is to mount the brush method, and technology is cumbersome, and work efficiency is lower, and construction intensity is big; (2) can only operate in the plane, only can put down spray, flat brush, put down and water, put down, could realize catching up with the oxygen pouring operation preferably; (3) glass fiber reinforced plastics product fragility height, intensity and toughness are poor; (4) operation limitation is big, has greatly influenced the thin portion expressive force of model and pattern.
The purpose of this invention is to provide and a kind ofly do furniture relief with modified polyester, the method of sculpture, this method also comprises molding and casting two big processes, embossing pattern and the sculpture that can be made into are changeful, in conjunction with east, the various household goods of Western Culture characteristics, because foundry processing of the present invention is to have adopted the modified polyester material, overcome the weak point that prior art exists effectively, not only constructing operation is easy, the expressive force of embossing pattern is strong, the intensity height, good toughness, face and can plastotype construction under 45 degree drift angle degree half elevations or full facade situation can also use with multiple other combination of materials, produces multiple decorative effect, to satisfy all kinds of consumer demands, this is invented furniture relief, the sculpture series products, method or its improvement have proposed a kind of new technical scheme.
Can realize specifically constituting of above-mentioned purpose of the present invention: do the method for furniture relief, sculpture with modified polyester, be divided into molding and casting two partly, the outstanding difference of itself and prior art is:
1. make the mud embryo according to embossing pattern, the mud embryo immersed in the rice paper slurry, make its outer surface hang up paper pulp, coat mold glue after, heat to 45～85 ℃, the retention time is 15～20 minutes, and is extremely tack-free with hot blast drying, select non-ly to view and admire face or non-use face cracks, take out the mud embryo, print rubber moulding;
2. the peroxide cyclohexanone that in commercially available 918 resins, adds 10～50% (weight ratios), make the A material, in modification polyvinyl alcohol liquid, splash into the cobalt naphthenate solution of 2～15% (weight ratios), make the B material, A, B material are put into 25～45 ℃ constant temperature roaster respectively, heat after 5～40 minutes, pour into respectively cool off in two containers 1～2 hour stand-by;
3. with two kinds of materials of above-mentioned A, B in A: B=6: 4 ratio, add mixing in the composition of raw materials contain polyester material 30%, half-H 2 O calcium sulphate 43%, calcium carbonate 15.5%, magnesium silicate 6.5%, dibutyl phthalate 2%, cobalt naphthenate benzene second weak solution 2% and calcium sulfate 1%, print the modified polyester material;
4. the modified polyester material is molded in the rubber moulding, left standstill 2～3 hours, seal can obtain required embossment and sculpture pattern.
The manufacture craft of mold glue is that modification polyvinyl alcohol liquid is that Kunming Metallurgy Inst produces with a rubber of 78%, 10% natural emulsion and 12% carbolic acid mixing, and the concentration of used this liquid of this law is for 10～45 droplets/second in dropper instrument.
Add weight ratio in the modified polyester material described in 3. and be 1.5～3% white carbon or/and 10% barium sulfate.
Add weight ratio in the modified polyester material described in 3. and be 30～50% mica sheet or malachite green or malachite indigo plant.
Below in conjunction with embodiment in detail the present invention is described in detail:
Embodiment 1:
Make the mud embryo according to embossing pattern, the mud embryo immersed in the rice paper slurry, make its outer surface hang up paper pulp, coat mold glue after, heat to 45 ℃, the retention time is 20 minutes, and is extremely tack-free with hot blast drying, select non-ly to view and admire face or non-use face cracks, take out the mud embryo, promptly make rubber moulding;
The peroxide cyclohexanone that in commercially available 918 resins, adds 20% (weight ratio), make the A material, in modification polyvinyl alcohol liquid, splash into the cobalt naphthenate solution of 10% (weight ratio), make the B material, A, B material are put into 45 ℃ constant temperature roaster respectively, heat after 20 minutes, it is stand-by to pour in two containers cooling 2 hours respectively into;
With two kinds of materials of above-mentioned A, B in A: B=6: 4 ratio, add mixing in the composition of raw materials contain polyester material 30%, half-H 2 O calcium sulphate 43%, calcium carbonate 15.5%, magnesium silicate 6.5%, dibutyl phthalate 2%, cobalt naphthenate benzene second weak solution 2% and calcium sulfate 1%, print the modified polyester material;
The manufacture craft of mold glue is that modification polyvinyl alcohol liquid is that Kunming Metallurgy Inst produces with a rubber of 78%, 10% natural emulsion and 12% carbolic acid mixing, and the concentration of used this liquid of this law is for 45 droplets/second in dropper instrument.
Add weight ratio and be 2% white carbon in above-mentioned modified polyester material or/and 10% barium sulfate is molded into the modified polyester material in the rubber moulding, left standstill 3 hours, seal can obtain required embossment and sculpture pattern.
Embodiment 2:
Make the mud embryo according to embossing pattern, the mud embryo immersed in the rice paper slurry, make its outer surface hang up paper pulp, coat mold glue after, add and put to 60 ℃, the retention time is 15 minutes, and is extremely tack-free with hot blast drying, select non-ly to view and admire face or non-use face cracks, take out the mud embryo, print rubber moulding;
The peroxide cyclohexanone that in commercially available 918 resins, adds 30% (weight ratio), make the A material, in modification polyvinyl alcohol liquid, splash into the cobalt naphthenate solution of 8% (weight ratio), make the B material, A, B material are put into 30 ℃ constant temperature roaster respectively, heat after 10 minutes, it is stand-by to pour in two containers cooling 1 hour respectively into;
All the other operating procedures and prescription are with embodiment 1;
In above-mentioned modified polyester material, add weight ratio and be 10% barium sulfate and weight ratio and be 30～50% mica sheet, the modified polyester material is molded in the rubber moulding, left standstill 2 hours, can obtain required embossing pattern.The embossing pattern that this embossing pattern is made has laser effect under illumination, seal has colourama and scattering arranged and refraction effect.
Embodiment 3:
According to embossment and sculpture design producing mud embryo, the mud embryo is immersed in the rice paper slurry, make its outer surface hang up paper pulp, coat mold glue after, heat to 50 ℃, the retention time is 18 minutes, and is extremely tack-free with hot blast drying, select non-ly to view and admire face or non-use face cracks, take out the mud embryo, print rubber moulding;
The peroxide cyclohexanone that in commercially available 918 resins, adds 25% (weight ratio), make the A material, in modification polyvinyl alcohol liquid, splash into the cobalt naphthenate solution of 15% (weight ratio), make the B material, A, B material are put into 35 ℃ constant temperature roaster respectively, heat after 30 minutes, pour 2 hours special using of cooling in two containers respectively into;
All the other operating procedures and fill a prescription the same;
The manufacture craft of mold glue is that modification polyvinyl alcohol liquid is that Kunming Metallurgy Inst produces with a rubber of 78%, 10% natural emulsion and 12% carbolic acid mixing, and the concentration of used this liquid of this law is for 20 droplets/second in dropper instrument.
In above-mentioned modified polyester material, add weight ratio and be 2% white carbon or/and 10% barium sulfate, add weight ratio again and be 30% Yunnan real estate malachite green or the blue ore particles of malachite, the modified polyester material is molded in the rubber moulding, left standstill 3 hours, seal can obtain required embossment and sculpture pattern.This embossment and sculpture pattern article have the effect of bornite handicraft.
In sum, embossment that will make with the method for the invention and sculpture pattern and existing furniture make up, seal is installed on the various of furniture and views and admires on face and the use face, can make existing article of furniture upgrading, improve retaining, make daily living article have more artistry and ornamental value, certainly, technical scheme of the present invention can apply to sculpture fully and make, and it has opened up new approach for equally the making of sculptures art work.
Claims (4)
1, make the method for furniture relief, sculpture of modified polyester, be divided into molding and casting mold two partly, it is characterized in that:
1. make the mud embryo according to embossing pattern, the mud embryo immersed in the rice paper slurry, make its outer surface hang up paper pulp, coat mold glue after, heat to 45～85 ℃, the retention time is 15～20 minutes, and is extremely tack-free with hot blast drying, select non-ly to view and admire face or non-use face cracks, take out the mud embryo, print rubber moulding;
2. the peroxide cyclohexanone that in commercially available 918 resins, adds 10～50% (weight ratios), make the A material, in modification polyvinyl alcohol liquid, splash into the cobalt naphthenate solution of 2～15% (weight ratios), make the B material, A, B material are put into 25～45 ℃ constant temperature roaster respectively, heat after 5～40 minutes, pour into respectively cool off in two containers 1～2 hour stand-by;
3. with two kinds of materials of above-mentioned A, B in A: B=6: 4 ratio, add mixing in the composition of raw materials contain polyester material 30%, half-H 2 O calcium sulphate 43%, calcium carbonate 15.5%, magnesium silicate 6.5%, dibutyl phthalate 2%, cobalt naphthenate benzene second weak solution 2% and calcium sulfate 1%, print the modified polyester material;
4. the modified polyester material is molded in the rubber moulding, left standstill 2～3 hours, seal can obtain required embossment and sculpture pattern.
2, according to the described method of making furniture relief, sculpture of modified polyester of claim 1, it is characterized in that: the manufacture craft of mold glue is with a rubber of 78%, 10% natural emulsion and 12% carbolic acid mixing, modification polyvinyl alcohol liquid is that Kunming Metallurgy Inst produces, and the concentration of used this liquid of this law is for using 10～45 droplets/second in dropper instrument.
3, describedly do the method for furniture relief, sculpture according to claim 1 or 2, it is characterized in that with modified polyester: add weight ratio in the modified polyester material 3. and be 1.5～3% from carbon black or/and 10% barium sulfate.
4, describedly do the method for furniture relief, sculpture according to claim 1 or 2, it is characterized in that: add weight ratio in the modified polyester material 3. and be 30～50% mica sheet or malachite green or malachite indigo plant with modified polyester.