CN111923506A - 一种铝箔吸管生产工艺 - Google Patents
一种铝箔吸管生产工艺 Download PDFInfo
- Publication number
- CN111923506A CN111923506A CN202010852669.9A CN202010852669A CN111923506A CN 111923506 A CN111923506 A CN 111923506A CN 202010852669 A CN202010852669 A CN 202010852669A CN 111923506 A CN111923506 A CN 111923506A
- Authority
- CN
- China
- Prior art keywords
- aluminum foil
- coating
- aluminum
- production process
- straw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铝箔吸管生产工艺，其生产工艺包括以下步骤：A、铝箔先清洗钝化再辊涂（或覆膜）加工，把整卷铝箔用食品级的水性涂料辊涂（或覆膜）在铝箔的正反面上，并可以按所需的颜色调色辊涂（或覆膜）及印刷图案；B、铝箔在双面辊涂（或覆膜）后再按实际需要的尺寸分条，本发明先对铝箔进行清洗钝化，然后再把食品级的水性涂料辊涂（或覆膜）在铝箔的正反面上，并可以按所需的颜色调色辊涂（或覆膜）及印刷图案，同时，在分条后的铝箔切口处继续涂设有保护涂层，最后根据吸管硬度和强度的不同需要将铝箔设置为单层或多层，同时，本申请中的铝箔吸管不限于圆型直吸管和弯曲吸管，其它异型的吸管也函括在内。
Description
技术领域
本发明涉及铝箔吸管技术领域，具体为一种铝箔吸管生产工艺。
背景技术
铝箔是一种用金属铝直接压延成薄片的烫印材料，其烫印效果与纯银箔烫印的效果相似，故又称假银箔，由于铝的质地柔软、延展性好，具有银白色的光泽，如果将压延后的薄片，用硅酸钠等物质裱在胶版纸上制成铝箔片，还可进行印刷，吸管又称饮管，是一条圆柱状，中空的制品，其主要功用是用来饮用杯子中饮料，也有用来吸食一些烹饪好的动物长骨的骨髓，一般直径在0.5cm左右，但是用来吸食酸奶、珍珠奶茶等饮品时，会用较粗的吸管，有的直径有1.2cm，是运用大气压强原理，使用时对着吸管吸走部分空气，将造成管内压强变小，而为了平衡气压，大气压强将会迫使管内液体上升，停止吸气时，管内液体下降，压强便回到平衡，由于现有的吸管大多为塑料制成，导致其不够节能环保，于是市场上出现了铝箔吸管，但现有的铝箔吸管其在使用过程中铝吸管铝的成份容易与空气接触，从而造成铝氧化或跟嘴巴接触被摄入人体，不利于产品的美观性和人们的身体健康，为此，我们提出一种铝箔吸管生产工艺。
发明内容
本发明的目的在于提供一种铝箔吸管生产工艺，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种铝箔吸管生产工艺，其生产工艺包括以下步骤：
A、铝箔先清洗钝化再辊涂（或覆膜）加工，把整卷铝箔用食品级的水性涂料辊涂（或覆膜）在铝箔的正反面上，并可以按所需的颜色调色辊涂（或覆膜）及印刷图案；
B、铝箔在双面辊涂（或覆膜）后再按实际需要的尺寸分条，分成宽度不一的窄铝卷，以备后面生产不同规格的铝吸管时使用；
C、分条好后的铝箔由于分条后会有切口产生，切口部分由于没有涂层保护，可以直接接触空气，还是会造成氧化的可能，必须对裸露的切口进行补涂烘干，保证所有切口都不能跟空气和饮料接触；
D、用专用的设备把已经做好前处理涂色印刷预分条后的铝箔按所需要形状、规格、直径大小，分单层或者多层缠绕，加食品级胶水或者食品级热熔胶缠绕烘干，让缠绕层粘合在一起；
E、按长度要求分段切断，切断后再把切口处补涂食品级的涂料并烘干；
F、然后再把一头或者两头做卷边处理，又或者一头做成有角度的切口，也可以做成平口的管。
G、检验合格后包装入库。
优选的，所述步骤A中的铝箔厚度为0.02-0.2mm，且辊涂（或覆膜）的涂层厚度为2-60μm，同时，辊涂（或覆膜）及图案印刷之后还需要使用烘干机构对其进行烘干处理，且烘干机构为多排等距设置的热风机，同时，热风机通过支架固定连接在加工台的顶部，加工台的顶部还等距分布有多个内部通过轴承活动连接加热棒的空心结构的金属材质输送辊。
优选的，所述步骤D中一般有3层，里箔不上胶，中间的箔双面上胶，外箔一面上胶一面不上胶，如需要不同的吸管硬度和强度，可以通过增减铝箔的厚度或硬度来调整，也可以增加缠绕的层数来调整，同时，单层、多层均为铝箔或最外面一层是铝箔、中间层是纸皮、最里面是铝箔或铝箔与纸皮的任意分层组合。
优选的，所述步骤E中的切口有平切口和斜切口，这样就可以保证整支铝吸管铝的成份100％没有跟空气接触，造成铝氧化或跟嘴巴接触被摄入人体。
优选的，所述步骤A中调色所用的涂料以及印刷图案所需的油墨均按达到有关国家食品包材标准的材料制作，且辊涂（或覆膜）的目的是为了使铝箔不能够和空气接触而产生氧化，也能保证消费者在使用铝吸管时不会接触到裸露铝的成份，铝成份不会被摄入人体内。
与现有技术相比，本发明的有益效果如下：
本发明先对铝箔进行清洗钝化，然后再把食品级的水性涂料辊涂（或覆膜）在铝箔的正反面上，可有效提高铝箔的涂胶效率，并可以按所需的颜色调色辊涂（或覆膜）及印刷图案，可有效提高本铝箔吸管样式的多样性，同时，在分条后的铝箔切口处继续涂设有保护涂层，可使铝箔的任何部位都不能跟空气和饮料接触，这样就可以保证整支铝吸管铝的成份100％没有跟空气接触，造成铝氧化或跟嘴巴接触被摄入人体，最后根据吸管硬度和强度的不同需要将铝箔设置为单层或多层，同时，本申请中的铝箔吸管不限于圆型直吸管和弯曲吸管，其它异型的吸管也函括在内。
具体实施方式
下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
一种铝箔吸管生产工艺，其生产工艺包括以下步骤：
A、铝箔先清洗钝化再辊涂（或覆膜）加工，把整卷铝箔用食品级的水性涂料辊涂（或覆膜）在铝箔的正反面上，并可以按所需的颜色调色辊涂（或覆膜）及印刷图案；
B、铝箔在双面辊涂（或覆膜）后再按实际需要的尺寸分条，分成宽度不一的窄铝卷，以备后面生产不同规格的铝吸管时使用；
C、分条好后的铝箔由于分条后会有切口产生，切口部分由于没有涂层保护，可以直接接触空气，还是会造成氧化的可能，必须对裸露的切口进行补涂烘干，保证所有切口都不能跟空气和饮料接触；
D、用专用的设备把已经做好前处理涂色印刷预分条后的铝箔按所需要形状、规格、直径大小，分单层或者多层缠绕，加食品级胶水或者食品级热熔胶缠绕加热烘干，让缠绕层粘合在一起；
E、按长度要求分段切断，切断后再把切口处补涂食品级的涂料并烘干；
F、然后再把一头或者两头做卷边处理，又或者一头做成有角度的切口，也可以做成平口的管；
G、检验合格后包装入库。
先对铝箔进行清洗钝化，然后再把食品级的水性涂料辊涂（或覆膜）在铝箔的正反面上，可有效提高铝箔的涂胶效率，并可以按所需的颜色调色辊涂（或覆膜）及印刷图案，可有效提高本铝箔吸管样式的多样性，同时，在分条后的铝箔切口处继续涂设有保护涂层，可使铝箔的任何部位都不能跟空气和饮料接触，这样就可以保证整支铝吸管铝的成份100％没有跟空气接触，造成铝氧化或跟嘴巴接触被摄入人体，最后根据吸管硬度和强度的不同需要将铝箔设置为单层或多层，同时，本申请中的铝箔吸管不限于圆型直吸管和弯曲吸管，其它异型的吸管也函括在内。
步骤A中的铝箔厚度为0.02-0.2mm，且辊涂（或覆膜）的涂层厚度为2-60μm，同时，辊涂（或覆膜）及图案印刷之后还需要使用烘干机构对其进行烘干处理，且烘干机构为多排等距设置的热风机，同时，热风机通过支架固定连接在加工台的顶部，加工台的顶部还等距分布有多个内部通过轴承活动连接加热棒的空心结构的金属材质输送辊。
步骤D中一般有3层，里箔不上胶，中间的箔双面上胶，外箔一面上胶一面不上胶，如需要不同的吸管硬度和强度，可以通过增减铝箔的厚度或硬度来调整，也可以增加缠绕的层数来调整，同时，单层、多层均为铝箔或最外面一层是铝箔、中间层是纸皮、最里面是铝箔或铝箔与纸皮的任意分层组合。
步骤E中的切口有平切口和斜切口，这样就可以保证整支铝吸管铝的成份100％没有跟空气接触，造成铝氧化或跟嘴巴接触被摄入人体。
步骤A中调色所用的涂料以及印刷图案所需的油墨均按达到有关国家食品包材标准的材料制作，且辊涂（或覆膜）的目的是为了使铝箔不能够和空气接触而产生氧化，也能保证消费者在使用铝吸管时不会接触到裸露铝的成份，铝成份不会被摄入人体内。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (5)
1.一种铝箔吸管生产工艺，其特征在于：其生产工艺包括以下步骤：
A、铝箔先清洗钝化再辊涂（或覆膜）加工，把整卷铝箔用食品级的水性涂料辊涂（或覆膜）在铝箔的正反面上，并可以按所需的颜色调色辊涂（或覆膜）及印刷图案；
B、铝箔在双面辊涂（或覆膜）后再按实际需要的尺寸分条，分成宽度不一的窄铝卷，以备后面生产不同规格的铝吸管时使用；
C、分条好后的铝箔由于分条后会有切口产生，切口部分由于没有涂层保护，可以直接接触空气，还是会造成氧化的可能，必须对裸露的切口进行补涂烘干，保证所有切口都不能跟空气和饮料接触；
D、用专用的设备把已经做好前处理涂色印刷预分条后的铝箔按所需要形状、规格、直径大小，分单层或者多层缠绕，加食品级胶水或者食品级热熔胶缠绕烘干，加热让缠绕层粘合在一起；
E、按长度要求分段切断，切断后再把切口处补涂食品级的涂料并烘干；
F、然后再把一头或者两头做卷边处理，又或者一头做成有角度的切口，也可以做成平口的管；
G、检验合格后包装入库。
2.根据权利要求1所述的一种铝箔吸管生产工艺，其特征在于：所述步骤A中的铝箔厚度为0.02-0.2mm，且辊涂（或覆膜）的涂层厚度为2-60μm，同时，辊涂（或覆膜）及图案印刷之后还需要使用烘干机构对其进行烘干处理，且烘干机构为多排等距设置的热风机，同时，热风机通过支架固定连接在加工台的顶部，加工台的顶部还等距分布有多个内部通过轴承活动连接加热棒的空心结构的金属材质输送辊。
3.根据权利要求1所述的一种铝箔吸管生产工艺，其特征在于：所述步骤D中一般有3层，里箔不上胶，中间的箔双面上胶，外箔一面上胶一面不上胶，如需要不同的吸管硬度和强度，可以通过增减铝箔的厚度或硬度来调整，也可以增加缠绕的层数来调整，同时，单层、多层均为铝箔或最外面一层是铝箔、中间层是纸皮、最里面是铝箔或铝箔与纸皮的任意分层组合。
4.根据权利要求1所述的一种铝箔吸管生产工艺，其特征在于：所述步骤E中的切口有平切口和斜切口，这样就可以保证整支铝吸管铝的成份100％没有跟空气接触，造成铝氧化或跟嘴巴接触被摄入人体。
5.根据权利要求1所述的一种铝箔吸管生产工艺，其特征在于：所述步骤A中调色所用的涂料以及印刷图案所需的油墨均按达到有关国家食品包材标准的材料制作，且辊涂（或覆膜）的目的是为了使铝箔不能够和空气接触而产生氧化，也能保证消费者在使用铝吸管时不会接触到裸露铝的成份，铝成份不会被摄入人体内。