CN111923175A - Method for making wooden handicraft - Google Patents
Method for making wooden handicraft Download PDFInfo
- Publication number
- CN111923175A CN111923175A CN202010801323.6A CN202010801323A CN111923175A CN 111923175 A CN111923175 A CN 111923175A CN 202010801323 A CN202010801323 A CN 202010801323A CN 111923175 A CN111923175 A CN 111923175A
- Authority
- CN
- China
- Prior art keywords
- rattan
- strips
- rattan wood
- wood strip
- hay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of rattan plaited processing, in particular to a method for manufacturing a wooden handicraft, which comprises the steps of selecting rattan strips; modifying the rattan wood strip; drying the rattan wood; and weaving rattan strips to form the handicraft. The invention has the beneficial effects that: cover the rattan wood strip through the plant ash, absorb the moisture on rattan wood strip surface, produce the heat through the hay burning and fumigate the rattan wood strip, further reduce the inside moisture of rattan wood strip, can reduce the inside bacterium of rattan wood strip simultaneously, the microorganism quantity, soak modification treatment to the rattan wood strip through the modified solution, the PH value is adjusted to rattan wood strip surface to the PH regulator, make rattan wood strip inside have toughness, prevent that the shrinkage cavity levelling agent is handled rattan wood strip surface, make rattan wood strip surface more smooth, handle the rattan wood strip through PH regulator and prevent the shrinkage cavity levelling agent, make the rattan wood strip difficult to produce and warp, rattan wood strip surface is more smooth simultaneously, be convenient for subsequent spray paint, make the lacquer painting and the difficult gassing of rattan wood strip surface.
Description
Technical Field
The invention relates to the technical field of rattan weaving processing, in particular to a manufacturing method of a wooden handicraft.
Background
The rattan plaited is a woven handicraft and a real article which take the skin and the core of the stem of the rattan plant as raw materials, the border of Tengchong and Burmese soil is in an original forest, and the rattan which is a tough rattan plant with extremely long body is produced. The Tengchong people uses the daily tools such as cane chairs and cane boxes which are woven by the method to have exquisite process, various varieties and durability, and is popular with consumers in ancient times and nowadays.
The reason that the air holes and the depressions are formed on the surface of the rattan woven handicraft article is that the rattan woven handicraft article is not treated in the manufacturing process, so that the rattan woven handicraft article is easy to deform, and after the rattan woven handicraft article is processed and the rattan woven surface is painted, air bubbles are formed on the painted surface and the rattan woven surface, and then the air holes and the depressions of the painted surface are formed, so that the appearance quality is affected.
Disclosure of Invention
The invention aims to overcome the problems in the prior art and provides a method for manufacturing a wooden handicraft, which can solve the problems in the prior art at least to a certain extent.
In order to achieve the technical purpose and achieve the technical effect, the invention is realized by the following technical scheme:
a method for manufacturing a wooden handicraft comprises the following steps:
step 1) selecting rattan strips with the diameter within 8-10mm, placing the selected rattan strips in plant ash to enable the plant ash to cover the surfaces of the rattan strips, paving hay on the surfaces of the plant ash, igniting the hay to enable the hay to burn for 20-25min, then cleaning the plant ash and the burnt hay ash out, and taking out the rattan strips;
step 2) placing the rattan wood strips treated in the step into a cleaning pool, adding a modification liquid into the cleaning pool to soak the rattan wood strips in the modification liquid, and performing modification treatment on the rattan wood strips, wherein the modification liquid comprises the following raw materials in parts by weight:
0.1-2 parts of pH regulator, 0.2-0.3 part of shrinkage-proof leveling agent, 0.5-3 parts of preservative and 20-30 parts of deionized water;
and 3) placing the rattan wood strips treated in the step into a drying device for drying, wherein the temperature of the drying device is set as follows:
the temperature of the first stage is 80-85 ℃, the drying time is 3 hours,
the temperature of the second stage is 90 ℃, the drying time is 1 hour,
the temperature of the third stage is 115-120 ℃, and the drying time is 10-17 minutes;
and 4) weaving the rattan wood strips processed in the step through a conventional process to form the artware.
As a further optimization of the technical scheme, in the step 2), the rattan strips are modified and then exposed for 3-5 hours.
As a further optimization of the above technical solution, the PH adjuster includes a mixed solution of potassium salt and sodium bicarbonate.
As a further optimization of the technical scheme, the preservative comprises a mixed solution consisting of silica powder, sodium benzoate, potassium sorbate and clear water.
As a further optimization of the technical scheme, the preservative comprises 40% of silica powder, 30% of sodium benzoate, 20% of potassium sorbate and the balance of clear water.
The invention has the beneficial effects that: covering the rattan wood strips with plant ash, absorbing water on the surfaces of the rattan wood strips, fumigating the rattan wood strips by heat generated by burning hay, further reducing the water inside the rattan wood strips, simultaneously reducing the number of bacteria and microorganisms inside the rattan wood strips, soaking the rattan wood strips in a modifying solution, modifying the surfaces of the rattan wood strips by a pH regulator, regulating the pH value of the surfaces of the rattan wood strips by a pH regulator to enable the interior of the rattan wood strips to have toughness, treating the surfaces of the rattan wood strips by a shrinkage-proof leveling agent to enable the surfaces of the rattan wood strips to be smoother, treating the rattan wood strips by a pH regulator and the shrinkage-proof leveling agent to enable the rattan wood strips to be difficult to deform, enabling the surfaces of the rattan wood strips to be smoother, facilitating subsequent paint spraying, enabling the surfaces of paint and the surfaces of the rattan wood strips to be difficult to generate bubbles, adding a preservative to enable the surfaces of the rattan wood strips to have corrosion resistance, and drying the rattan wood strips, the toughness of the rattan wood strip is improved.
Detailed Description
In order to make the technical means, the creation features, the achievement purposes and the effects of the invention easy to understand, the technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example 1
A method for manufacturing a wooden handicraft comprises the following steps:
step 1) selecting rattan strips with the diameter of 10mm, placing the selected rattan strips in plant ash to enable the plant ash to cover the surfaces of the rattan strips, paving hay on the surfaces of the plant ash, igniting the hay to enable the hay to burn for 20min, then cleaning the plant ash and the burnt hay ash, and taking out the rattan strips;
step 2) placing the rattan wood strips treated in the step into a cleaning pool, adding a modification liquid into the cleaning pool to soak the rattan wood strips in the modification liquid, and performing modification treatment on the rattan wood strips, wherein the modification liquid comprises the following raw materials in parts by weight:
1 part of pH regulator, 0.3 part of shrinkage-proof leveling agent, 0.5 part of preservative and 21 parts of deionized water, wherein the pH regulator comprises a mixed solution of potassium salt and sodium bicarbonate, the preservative comprises a mixed solution consisting of silica powder, sodium benzoate, potassium sorbate and clear water, the preservative comprises 40% of silica powder, 30% of sodium benzoate, 20% of potassium sorbate and the balance of clear water by weight, and the rattan wood strips are modified and then subjected to solarization for 3 hours;
and 3) placing the rattan wood strips treated in the step into a drying device for drying, wherein the temperature of the drying device is set as follows:
the temperature of the first stage is 85 ℃, the drying time is 3 hours,
the temperature of the second stage is 90 ℃, the drying time is 1 hour,
the temperature of the third stage is 115 ℃, and the drying time is 17 minutes;
and 4) weaving the rattan wood strips processed in the step through a conventional process to form the artware.
Example 2
A method for manufacturing a wooden handicraft comprises the following steps:
step 1) selecting rattan strips with the diameter of 9mm, placing the selected rattan strips in plant ash to enable the plant ash to cover the surfaces of the rattan strips, paving hay on the surfaces of the plant ash, igniting the hay to enable the hay to burn for 25min, then cleaning the plant ash and the burnt hay ash, and taking out the rattan strips;
step 2) placing the rattan wood strips treated in the step into a cleaning pool, adding a modification liquid into the cleaning pool to soak the rattan wood strips in the modification liquid, and performing modification treatment on the rattan wood strips, wherein the modification liquid comprises the following raw materials in parts by weight:
the preservative comprises, by weight, 40% of silica powder, 30% of sodium benzoate, 20% of potassium sorbate and the balance of clear water, and is prepared by modifying rattan wood strips, and then exposing the rattan wood strips to the sun for 3 hours;
and 3) placing the rattan wood strips treated in the step into a drying device for drying, wherein the temperature of the drying device is set as follows:
the temperature of the first stage is 85 ℃, the drying time is 3 hours,
the temperature of the second stage is 90 ℃, the drying time is 1 hour,
the temperature of the third stage is 120 ℃, and the drying time is 10 minutes;
and 4) weaving the rattan wood strips processed in the step through a conventional process to form the artware.
Example 3
A method for manufacturing a wooden handicraft comprises the following steps:
step 1) selecting rattan strips with the diameter of 8mm, placing the selected rattan strips in plant ash to enable the plant ash to cover the surfaces of the rattan strips, paving hay on the surfaces of the plant ash, igniting the hay to enable the hay to burn for 23min, then cleaning the plant ash and the burnt hay ash, and taking out the rattan strips;
step 2) placing the rattan wood strips treated in the step into a cleaning pool, adding a modification liquid into the cleaning pool to soak the rattan wood strips in the modification liquid, and performing modification treatment on the rattan wood strips, wherein the modification liquid comprises the following raw materials in parts by weight:
2 parts of a pH regulator, 0.22 part of a shrinkage-proof leveling agent, 3 parts of a preservative and 20 parts of deionized water, wherein the pH regulator comprises a mixed solution of potassium salt and sodium bicarbonate, the preservative comprises a mixed solution consisting of silica powder, sodium benzoate, potassium sorbate and clear water, the preservative comprises 40% of silica powder, 30% of sodium benzoate, 20% of potassium sorbate and the balance of clear water by weight, and the rattan wood strips are modified and then subjected to solarization for 5 hours;
and 3) placing the rattan wood strips treated in the step into a drying device for drying, wherein the temperature of the drying device is set as follows:
the temperature of the first stage is 83 ℃, the drying time is 3 hours,
the temperature of the second stage is 90 ℃, the drying time is 1 hour,
the temperature of the third stage is 120 ℃, and the drying time is 15 minutes;
and 4) weaving the rattan wood strips processed in the step through a conventional process to form the artware.
Example 4
A method for manufacturing a wooden handicraft comprises the following steps:
step 1) selecting rattan strips with the diameter within 9mm, placing the selected rattan strips in plant ash to enable the plant ash to cover the surfaces of the rattan strips, paving hay on the surfaces of the plant ash, igniting the hay to enable the hay to burn for 25min, then cleaning the plant ash and the burnt hay ash, and taking out the rattan strips;
step 2) placing the rattan wood strips treated in the step into a cleaning pool, adding a modification liquid into the cleaning pool to soak the rattan wood strips in the modification liquid, and performing modification treatment on the rattan wood strips, wherein the modification liquid comprises the following raw materials in parts by weight:
the preservative comprises, by weight, 40% of silica powder, 30% of sodium benzoate, 20% of potassium sorbate and the balance of clear water, and is prepared by modifying rattan wood strips, and then exposing the rattan wood strips to the sun for 3 hours;
and 3) placing the rattan wood strips treated in the step into a drying device for drying, wherein the temperature of the drying device is set as follows:
the temperature of the first stage is 85 ℃, the drying time is 3 hours,
the temperature of the second stage is 90 ℃, the drying time is 1 hour,
the temperature of the third stage is 118 ℃, and the drying time is 10 minutes;
and 4) weaving the rattan wood strips processed in the step through a conventional process to form the artware.
Example 5
A method for manufacturing a wooden handicraft comprises the following steps:
step 1) selecting rattan strips with the diameter of 0mm, placing the selected rattan strips in plant ash to enable the plant ash to cover the surfaces of the rattan strips, paving hay on the surfaces of the plant ash, igniting the hay to enable the hay to burn for 25min, then cleaning the plant ash and the burnt hay ash, and taking out the rattan strips;
step 2) placing the rattan wood strips treated in the step into a cleaning pool, adding a modification liquid into the cleaning pool to soak the rattan wood strips in the modification liquid, and performing modification treatment on the rattan wood strips, wherein the modification liquid comprises the following raw materials in parts by weight:
2 parts of a pH regulator, 0.2 part of a shrinkage-proof leveling agent, 0.5 part of a preservative and 30 parts of deionized water, wherein the pH regulator comprises a mixed solution of potassium salt and sodium bicarbonate, the preservative comprises a mixed solution consisting of silica powder, sodium benzoate, potassium sorbate and clear water, the preservative comprises 40% of the silica powder, 30% of the sodium benzoate, 20% of the potassium sorbate and the balance of the clear water by weight, and the rattan wood strips are modified and then subjected to solarization for 3 hours;
and 3) placing the rattan wood strips treated in the step into a drying device for drying, wherein the temperature of the drying device is set as follows:
the temperature of the first stage is 85 ℃, the drying time is 3 hours,
the temperature of the second stage is 90 ℃, the drying time is 1 hour,
the temperature of the third stage is 115 ℃, and the drying time is 12 minutes;
and 4) weaving the rattan wood strips processed in the step through a conventional process to form the artware.
Example 6
A method for manufacturing a wooden handicraft comprises the following steps:
step 1) selecting rattan strips with the diameter of 8.5mm, placing the selected rattan strips in plant ash, covering the plant ash on the surfaces of the rattan strips, paving hay on the surfaces of the plant ash, igniting the hay, burning the hay for 25min, cleaning the plant ash and the burnt hay ash, and taking out the rattan strips;
step 2) placing the rattan wood strips treated in the step into a cleaning pool, adding a modification liquid into the cleaning pool to soak the rattan wood strips in the modification liquid, and performing modification treatment on the rattan wood strips, wherein the modification liquid comprises the following raw materials in parts by weight:
the preservative comprises, by weight, 40% of silica powder, 30% of sodium benzoate, 20% of potassium sorbate and the balance of clear water, and is characterized by comprising 0.11 parts of a pH regulator, 0.23 parts of a shrinkage-proof leveling agent, 3 parts of a preservative and 23 parts of deionized water, wherein the pH regulator comprises a mixed solution of potassium salt and sodium bicarbonate, the preservative comprises a mixed solution of silica powder, sodium benzoate, potassium sorbate and clear water, and the preservative comprises the following raw materials, by weight, 40% of silica powder, 30% of sodium benzoate, 20% of potassium sorbate and the balance of clear water;
and 3) placing the rattan wood strips treated in the step into a drying device for drying, wherein the temperature of the drying device is set as follows:
the temperature of the first stage is 82 ℃, the drying time is 3 hours,
the temperature of the second stage is 90 ℃, the drying time is 1 hour,
the temperature of the third stage is 118 ℃, and the drying time is 17 minutes;
and 4) weaving the rattan wood strips processed in the step through a conventional process to form the artware.
It is noted that, herein, relational terms such as first and second, and the like may be used solely to distinguish one entity or action from another entity or action without necessarily requiring or implying any actual such relationship or order between such entities or actions. Also, the terms "comprises," "comprising," or any other variation thereof, are intended to cover a non-exclusive inclusion, such that a process, method, article, or apparatus that comprises a list of elements does not include only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus. Without further limitation, an element defined by the phrase "comprising an … …" does not exclude the presence of other identical elements in a process, method, article, or apparatus that comprises the element.
The preferred embodiments of the invention disclosed above are intended to be illustrative only. The preferred embodiments are not intended to be exhaustive or to limit the invention to the precise embodiments disclosed. Obviously, many modifications and variations are possible in light of the above teaching. The embodiments were chosen and described in order to best explain the principles of the invention and the practical application, to thereby enable others skilled in the art to best utilize the invention. The invention is limited only by the claims and their full scope and equivalents.
Claims (5)
1. The manufacturing method of the wooden handicraft is characterized by comprising the following steps:
step 1) selecting rattan strips with the diameter within 8-10mm, placing the selected rattan strips in plant ash to enable the plant ash to cover the surfaces of the rattan strips, paving hay on the surfaces of the plant ash, igniting the hay to enable the hay to burn for 20-25min, then cleaning the plant ash and the burnt hay ash out, and taking out the rattan strips;
step 2) placing the rattan wood strips treated in the step into a cleaning pool, adding a modification liquid into the cleaning pool to soak the rattan wood strips in the modification liquid, and performing modification treatment on the rattan wood strips, wherein the modification liquid comprises the following raw materials in parts by weight:
0.1-2 parts of pH regulator, 0.2-0.3 part of shrinkage-proof leveling agent, 0.5-3 parts of preservative and 20-30 parts of deionized water;
and 3) placing the rattan wood strips treated in the step into a drying device for drying, wherein the temperature of the drying device is set as follows:
the temperature of the first stage is 80-85 ℃, the drying time is 3 hours,
the temperature of the second stage is 90 ℃, the drying time is 1 hour,
the temperature of the third stage is 115-120 ℃, and the drying time is 10-17 minutes;
and 4) weaving the rattan wood strips processed in the step through a conventional process to form the artware.
2. The method for manufacturing a wooden craft as claimed in claim 1, wherein in the step 2), the rattan strips are exposed for 3-5 hours after being modified.
3. The method of manufacturing a wooden craft as claimed in claim 1, wherein the PH adjuster includes a mixed solution of potassium salt and sodium bicarbonate.
4. The method for manufacturing a wooden craft as claimed in claim 1, wherein the preservative includes a mixed solution consisting of silica powder, sodium benzoate, potassium sorbate and clear water.
5. The method for manufacturing the wooden crafts as claimed in claim 4, wherein the preservative comprises 40% of silica powder, 30% of sodium benzoate, 20% of potassium sorbate and the balance of clear water.