CN111893494A - 一种铝合金工件前处理药剂及其制备方法 - Google Patents
一种铝合金工件前处理药剂及其制备方法 Download PDFInfo
- Publication number
- CN111893494A CN111893494A CN202010771629.1A CN202010771629A CN111893494A CN 111893494 A CN111893494 A CN 111893494A CN 202010771629 A CN202010771629 A CN 202010771629A CN 111893494 A CN111893494 A CN 111893494A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- parts
- alloy workpiece
- pretreatment agent
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明针对现有技术中存在的技术问题，提供一种铝合金工件前处理药剂及其制备方法，其包括以下重量份数原料：酸性物质10‑30份、表面活性剂10‑20份、缓蚀剂0.01‑0.2份、钝化剂5‑20份；所述酸性物质为硫酸、磷酸柠檬酸、酒石酸中的一种或组合。提出了一种全新的铝合金前处理药剂及制备工艺，将除油、出光(表调)、钝化工艺融为一体，简化清洗工艺次数，减少清水的使用量，达到高效、环保、节能的目的。
Description
技术领域
本发明涉及铝合金前处理工艺技术领域，具体涉及一种铝合金工件前处理药剂及其制备方法。
背景技术
传统铝合金前处理工艺，用碱性除油剂通过加热来对工件进行脱脂、除油，进行二次水洗，再进行出光(表调)处理，又是二次水洗，再用铬酸盐进行钝化处理，又是二次水洗，然后烘干，最后进入涂装程序。
其明显缺点是碱性除油剂对铝合金在机加过程中形成的氧化霉斑不能去除，必须进行出光(表调)处理，同时除油需要加热，增加热能消耗，总计要进行6次水洗，造成水资源浪费。传统钝化剂是以铬酸盐为主，具有对人体较大毒性，对环境污染严重，已不能适应环保要求，不能适应社会、科技发展的需要。
现有碱性除油剂需要加热，才能够脱脂除油，同时要经过6次水洗，造成水资源浪费，要经过专门的出光(表调)程序才能够去掉铝合金产品在机加过程中形成的霉斑，降低生产效率，钝化剂采用以铬酸盐为主的体系，对操作人员和环境造成较大危害。
发明内容
本发明针对现有技术中存在的技术问题，提供一种铝合金工件前处理药剂及其制备方法，提出了一种全新的铝合金前处理药剂及制备工艺，将除油、出光(表调)、钝化工艺融为一体，简化清洗工艺次数，减少清水的使用量，达到高效、环保、节能的目的。
本发明解决上述技术问题的技术方案如下：一种铝合金工件前处理药剂，其包括以下重量份数原料：酸性物质10-30份、表面活性剂10-20份、缓蚀剂0.01-0.2份、钝化剂5-20份；所述酸性物质为硫酸、磷酸柠檬酸、酒石酸中的一种或组合。
作为优选的，所述缓蚀剂为咪唑啉、季铵盐、若丁、苯丙三氮唑中的一种或组合。
作为优选的，所述活性剂包括阴离子表面活性剂和非离子表面活性剂。
作为优选的，所述阴离子表面活性剂为磺酸盐、羧酸盐、硫酸盐中的一种或组合。
作为优选的，所述非离子表面活性剂为脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚中的一种或组合。
作为优选的，所述钝化剂为钼盐、钛盐、锆盐中的一种或组合。
一种铝合金工件前处理药剂的制备方法，其包括以下步骤：
步骤A：预先向反应釜中注入纯净水，并开启电机，使纯净水处于搅拌状态。
步骤B：制备混合液，先向反应釜内缓慢加入酸性物质，并让其充分溶解，所述酸性物质为硫酸、磷酸、柠檬酸、酒石酸中的一种或多种任意比组合。
步骤C：再向反应釜中依次加入表面活性剂和渗透剂，以让其充分溶解；
步骤D：再向反应釜中依次加入缓蚀剂和钝化剂，并分别搅拌30-60分钟。
步骤E：待反应釜内的物质充分溶解后，直至冷却后进行计量包装。
上述步骤中的混合液占药剂总质量的5％，纯净水占药剂总质量的95％。
本发明的有益效果是：本发明提供了一种铝合金前处理药剂及其制备方法，将脱脂除油剂，由碱性配方改成酸性配方，在除油剂里引入缓蚀剂、出光(表调)和钝化剂，在去掉工件表面的油脂污垢的同时除掉工件表面因机械加工形成的氧化霉斑，同时在工件表面形成一层致密的耐蚀性、附着力俱佳的钝化膜。设备简单易制，合成工艺简单，常温生产，条件容易控制，生产稳定。以钝化剂成分淘汰掉毒性强的铬酸盐，改用对环境相对友好的钼盐、钛盐、锆盐，具有较高的环保价值。本发明的药剂在前处理生产过程中脱脂除油，出光(表调)，钝化，在一个工序里完成，之后只进行一次自来水清洗，再进行一次纯净水清洗，减少工艺环节，提高生产效率，大大减少清洗水使用量，减少排污成本，提高生产效益。
具体实施方式
实施例一
本实施例公开了一种铝合金工件前处理药剂，其包括以下重量份数原料：硫酸10份、阴离子表面活性剂5份、非离子表面活性剂5份、咪唑啉0.01份、钼盐5份；所述阴离子表面活性剂为磺酸盐；所述非离子表面活性剂为脂肪醇聚氧乙烯醚。
实施例二
本实施例公开了一种铝合金工件前处理药剂，其包括以下重量份数原料：酸性物质20份、表面活性剂15份、缓蚀剂0.1份、钝化剂15份；所述酸性物质为硫酸、磷酸柠檬酸、酒石酸中的一种或任意比组合，本实施例采用酒石酸。所述表面活性剂中阴离子表面活性剂5份，非离子表面活性剂10份，所述钝化剂为钛盐，所述缓蚀剂为苯丙三氮唑。
实施例三
本实施例公开了一种铝合金工件前处理药剂，其包括以下重量份数原料：酸性物质30份、表面活性剂20份、缓蚀剂0.2份、钝化剂20份；所述酸性物质为硫酸、磷酸柠檬酸、酒石酸中的一种或组合，本实施例采用酒石酸。所述表面活性剂包括10份阴离子表面活性剂和10份非离子表面活性剂，所述缓蚀剂为若丁，所述钝化剂为锆盐。
实施例四
本实施例公开了一种铝合金工件前处理药剂的制备方法，其包括以下步骤：
步骤A：预先向反应釜中注入纯净水，并开启电机，使纯净水处于搅拌状态。
步骤B：制备混合液，先向反应釜内缓慢加入酸性物质，并让其充分溶解，所述酸性物质为硫酸、磷酸、柠檬酸、酒石酸中的一种或多种任意比组合。
步骤C：再向反应釜中依次加入表面活性剂和渗透剂，以让其充分溶解；
步骤D：再向反应釜中依次加入缓蚀剂和钝化剂，并分别搅拌30-60分钟。
步骤E：待反应釜内的物质充分溶解后，直至冷却后进行计量包装。
上述步骤中的混合液占工作液总质量的5％，自来水占工作液总质量的95％。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (7)
1.一种铝合金工件前处理药剂，其特征在于，其包括以下重量份数原料：酸性物质10-30份、表面活性剂10-20份、缓蚀剂0.01-0.2份、钝化剂5-20份；所述酸性物质为硫酸、磷酸柠檬酸、酒石酸中的一种或组合。
2.根据权利要求1所述的一种铝合金工件前处理药剂，其特征在于，所述缓蚀剂为咪唑啉、季铵盐、若丁、苯丙三氮唑中的一种或组合。
3.根据权利要求1所述的一种铝合金工件前处理药剂，其特征在于，所述活性剂包括阴离子表面活性剂和非离子表面活性剂。
4.根据权利要求3所述的一种铝合金工件前处理药剂，其特征在于，所述阴离子表面活性剂为磺酸盐、羧酸盐、硫酸盐中的一种或组合。
5.根据权利要求3所述的一种铝合金工件前处理药剂，其特征在于，所述非离子表面活性剂为脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚中的一种或组合。
6.根据权利要求1所述的一种铝合金工件前处理药剂，其特征在于，所述钝化剂为钼盐、钛盐、锆盐中的一种或组合。
7.一种铝合金工件前处理药剂的制备方法，其特征在于，其包括以下步骤：
步骤A：预先向反应釜中注入纯净水，并开启电机，使纯净水处于搅拌状态；
步骤B：制备混合液，先向反应釜内缓慢加入酸性物质，并让其充分溶解，所述酸性物质为硫酸、磷酸、柠檬酸、酒石酸中的一种或多种任意比组合；
步骤C：再向反应釜中依次加入表面活性剂和渗透剂，以让其充分溶解；
步骤D：再向反应釜中依次加入缓蚀剂和钝化剂，并分别搅拌30-60分钟；
步骤E：待反应釜内的物质充分溶解后，直至冷却后进行计量包装；
上述步骤中的混合液占工作液药总质量的5％，自来水占工作液总质量的95％。