CN111849262A - 用于镜片的涂料、镜片和防红外线与紫外线的眼镜 - Google Patents
用于镜片的涂料、镜片和防红外线与紫外线的眼镜 Download PDFInfo
- Publication number
- CN111849262A CN111849262A CN201910320323.1A CN201910320323A CN111849262A CN 111849262 A CN111849262 A CN 111849262A CN 201910320323 A CN201910320323 A CN 201910320323A CN 111849262 A CN111849262 A CN 111849262A
- Authority
- CN
- China
- Prior art keywords
- lens
- coating
- parts
- glasses
- lens body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种用于镜片的涂料、镜片和防红外线与紫外线的眼镜。其中该用于镜片的涂料至少包括如下重量份的组分：氧化锡锑：1.5～2.5份、氟碳树脂乳液：50～75份、水性聚氨酯树脂：0.3～0.8份、聚丙烯酸钠：0.03～0.08份、聚乙烯醇：0.1～0.4份、水和/或醇类化合物：32～40份。本发明提供的涂料，能够在镜片本体上形成有效地阻隔红外辐射和紫外辐射的反射层，且该反射层能够使可见光顺利通过，因此该镜片和眼镜能够保护眼睛，免受红外辐射和紫外辐射的伤害，且不影响眼镜的正常功能。
Description
技术领域
本发明涉及一种用于镜片的涂料、镜片和防红外线与紫外线的眼镜，尤其涉及一种能够有效阻隔红外线和紫外线的涂料、镜片和眼镜。
背景技术
眼镜是目前较为普遍的视力矫正和视力保护工具，比如近视眼镜、远视眼镜、老花眼镜及散光眼镜。近年来的研究表明，红外线和紫外线会对人的眼睛带来伤害，比如红外线可造成眼底视网膜的伤害，人眼如果长期暴露于红外线可能引起白内障；而紫外线不仅会引发白内障，而且还会引起角膜炎、视网膜破坏，白内障、黄斑退化，雪盲等严重眼病。因此人们期待眼镜在具有视力保护和视力矫正的同时，还能够避免眼睛免受伤害。
实际上，目前大多数眼镜都或多或少具有阻隔红外线或阻隔紫外线的功能，一般多是在镜片本体上分别形成用于阻隔紫外线和红外线的薄膜而形成镜片。但是在阻隔红外线和红外线的同时，也降低了可见光的透过率，反而不利于视力矫正和视力保护。
墨镜(或称为太阳眼镜)可防止太阳光强烈刺激人眼，主要是通过在镜片加工过程中加入铁、铜、镍等金属粉末，以吸收紫外线，保护眼睛免受紫外线的伤害。但是在吸收紫外线的同时，可见光的透过率也受到了影响，目前一般墨镜对可见光的透射比(即可见光线的透光率或穿透率)较低，一般为40％～50％，有些墨镜甚至根本不适合在开车时佩戴，否则极易引发交通事故。此外，大多数墨镜对红外辐射几乎没有任何阻隔功能。
因此，如何开发出一款能够有效阻隔红外辐射和紫外辐射、且确保可见光顺利通过的涂料，使其能够用于眼镜而起到保护眼睛免受伤害，仍旧是目前有待解决的问题。
发明内容
针对现有技术中的上述缺陷，本发明提供一种用于镜片的涂料，其成膜后能够有效地阻碍红外线和紫外线并使可见光顺利通过，从而能够应用于眼镜中而起到保护眼睛的作用。
本发明提供一种镜片，其包括由上述用于镜片的涂料在镜片本体上形成的涂层，能够有效阻隔红外辐射和紫外辐射，且对可见光具有非常高的透射比，因此能够保护眼睛免受红外辐射和紫外辐射的伤害，且不影响视力矫正和保护。
本发明提供一种镜片的制备方法，该制备方法具有工艺简单、可行性高的特点。
本发明提供一种防红外线与紫外线的眼镜，包括上述镜片，因此也同样能够保护眼睛免受红外辐射和紫外辐射的伤害。
为实现上述目的，本发明提供一种用于镜片的涂料，至少包括如下重量份的组分：氧化锡锑：1.5～2.5份、氟碳树脂乳液：50～75份、水性聚氨酯树脂：0.3～0.8份、聚丙烯酸钠：0.03～0.08份、聚乙烯醇：0.1～0.4份、水和/或醇类化合物：30～50份。
本发明提供的技术方案，通过将氧化锡锑、氟碳树脂乳液、水性聚氨酯树脂、聚丙烯酸钠、聚乙烯醇等组分进行合理组配，使该涂料在涂覆于镜片本体表面成膜后，能够有效阻碍红外线和紫外线通过，并确保可见光顺利通过，因此不仅能够保护眼睛免受红外辐射和紫外辐射的伤害，而且还不影响眼镜原本的视力矫正和视力保护功能。
氧化锡锑(Antimony Tin Oxide，ATO)又被称为纳米掺锑二氧化锡、锑锡氧化物，属于Sb掺杂SnO2的n型半导体材料。因氧化锡锑具有良好的导电性，目前氧化锡锑多用于制备抗静电涂料和抗静电纤维。
具体的，氧化锡锑的平均粒径最好不超过40nm。该氧化锡锑可按照常规手段自行制备，也可商购。在本发明具体实施过程中，所用氧化锡锑为商购氧化锡锑纳米粉末，粒度范围为20nm～40nm。
氟碳树脂乳液是特种丙烯酸酯类、特种氟树脂共聚物阴离子型乳液，具有优异的耐候性、耐水性、耐污染性和耐化学品性，一般作为涂料的成膜剂使用。可以理解，本发明中的涂料，由于采用水和/或醇类化合物作为溶剂，因此最好选择水性氟碳树脂乳液，可通过商购获得。
水性聚氨酯树脂又被称为水溶性聚氨酯树脂，属于环境友好的水性树脂，常用于作为粘合剂(或称为黏合剂)使用。水性聚氨酯树脂可分为阴离子型水性聚氨酯树脂、阳离子型水性聚氨酯树脂和非离子型水性聚氨酯树脂，均可通过商购获得。在本发明具体实施过程中，多选用非离子型水性聚氨酯树脂。
聚丙烯酸钠为水溶性直链高分子聚合物，可溶于水而形成粘稠状透明液体。聚丙烯酸钠具有亲水和疏水基团，常作为分散剂、增稠剂用于涂料中，使涂料保持体系稳定并使涂料整体具有适宜的粘度。本发明中，一般选择相对分子质量为1000～10000的聚丙烯酸钠，以使涂料具有较为适宜的粘性以及良好的稳定性。
聚乙烯醇为水溶性高分子聚合物，性能介于塑料和橡胶之间。聚乙烯醇水溶液有很好的粘接性和成膜性，能耐油类、润滑剂和烃类等大多数有机溶剂，可作为分散剂、乳液聚合、乳化稳定剂使用，常用于制造水溶性胶粘剂、制备感光胶和耐苯类溶剂的密封胶等。
本发明所提供的用于镜片的涂料中，水和/或醇类化合物作为溶剂，用于将其它各组分充分混合并可调整涂料的粘度。具体的，可以仅采用水或者仅采用醇类化合物作为溶剂，也可以采用水和醇类化合物共同作为溶剂。其中，醇类溶剂比如可以是乙醇、丙醇、丁醇等醇类化合物中的一种或多种。
在本发明优选的实施例中，是采用乙醇作为溶剂，或者使用乙醇水溶液作为溶剂。且当使用乙醇水溶液作为溶剂时，本发明对于乙醇水溶液的浓度不做特别限定。采用乙醇或者乙醇水溶液作为溶剂，不仅有利于涂覆在镜片本体表面的涂料迅速成膜，缩短加工时间，而且还具有安全、经济的优势。
溶剂的加入量可以根据实际涂覆工艺调整，以涂料的总重量为100份计，水和/或醇类化合物的用量一般为35～40份。
进一步的，本发明提供的用于镜片的涂料中，还可以包括碳纳米管0.001～0.005份，即该用于镜片的涂料包括如下重量份的组分：氧化锡锑：1.5～2.5份、氟碳树脂乳液：50～75份、水性聚氨酯树脂：0.3～0.8份、聚丙烯酸钠：0.03～0.08份、聚乙烯醇：0.1～0.4份、水和/或醇类化合物：32～40份、碳纳米管：0.001～0.005份。
通过在用于镜片的涂料中加入微量的碳纳米管，不仅有利于用于镜片的涂料涂覆在镜片上所形成的涂层散热，避免眼镜在高温下佩戴时温度过高而对眼镜以及人体眼部以及眼部周围造成伤害，而且还可以提高眼镜的力学性能，比如提高镜片的耐磨性能，此外还基本不影响镜片对光线的选择透过性。
该碳纳米管尤其可以是单壁碳纳米管，其平均粒径最好不超过5nm。在本发明具体实施过程中，所用碳纳米管选用单壁2～5nm规格商品粉体碳纳米管。
本发明提供一种镜片，包括镜片本体以及反射层，其中该反射层是将前述用于镜片的涂料涂覆在镜片本体表面形成的膜层。
本发明对于上述镜片本体的材质不做特别限定，包括但不限于树脂镜片、玻璃镜片、PC镜片等。
发明人研究发现，将上述配方的涂料涂覆在镜片本体上所形成的膜层对于镜片本体具有良好的附着力，尤其对于目前用于制作普通近视眼镜、远视眼镜、老花眼镜及散光眼镜的镜片本体，均具有良好的粘附力。
本发明还提供上述镜片的制备方法，包括将用于镜片的涂料涂覆在镜片本体表面，再经干燥，在镜片本体表面形成反射层，得到镜片；或者，将镜片本体浸没在用于镜片的涂料中，取出后干燥，在镜片本体表面形成反射层，得到镜片。
在本发明具体实施过程中，可首先将镜片本体固定，然后将配制好的涂料通过喷涂、淋涂、辊涂、挂涂等手段涂覆在镜片本体上，经常温(25℃)下静置或者在30～80℃下适当加热，待涂料中的溶剂充分挥发，涂料在镜片本体表面固化并形成粘附牢固的薄膜，即为反射层，从而得到能够有效阻隔红外辐射和紫外辐射的镜片。
或者，也可将镜片本体先浸没在预先配制好的涂料中，再取出后于常温下静置或者在30～80℃下适当加热，待其中的溶剂充分挥发，涂料在镜片本体表面固化并形成粘附牢固的薄膜，从而在镜片本体两个表面上均形成了反射层，得到能够有效阻隔红外辐射和紫外辐射的镜片。
可以理解，在涂覆之前，镜片本体应保持清洁，比如可首先采用去离子水和乙醇等对镜片本体进行清洗。
本发明中，如前所述，可以在镜片本体的一个表面上涂覆上述涂料并形成反射层，也可以在镜片本体两个表面上都形成反射层，具体可以根据对于镜片的实际功能需求合理选择，本发明在此不做特别限定。当然，若在镜片本体的单面上形成反射层，可以在镜片本体远离眼镜的一面上涂覆涂料并形成反射层，也可以在镜片本体朝向眼镜的一面上涂覆涂料并形成反射层，本发明在此也不做特别限定。
本发明还提供一种防红外线与紫外线的眼镜，包括镜架以及前述的镜片。
本发明对于镜片与镜架之间的连接方式和安装方式不做特别限定，可采用目前常规的手段，将镜片以镶嵌等方式固定在镜架上即可。
可以理解，由于镜片上具有能够有效阻碍紫外辐射和红外辐射的反射层，而且该反射层具有较高的可见光透射比，因此，若该眼镜作为近视眼镜、远视眼镜、老花眼镜或散光眼镜，不仅能够具有矫正和保护视力的功能，而且能够有效避免红外光和紫外光辐射对眼睛造成的伤害。若该眼镜作为墨镜，由于该反射层对可见光具有极高的透过率，因此能够在开车时佩戴，提高驾驶员的行驶安全。
本发明提供的用于镜片的涂料，通过各组分之间的合理组配，使该用于镜片的涂料所形成的涂层能够对红外辐射和紫外辐射具有很好的阻隔效果，并且可以是可见光顺利通过，以将该涂料用于玻璃镜片本体(紫外线阻隔率为34.5％、红外线阻隔率为5.0％、可见光透过率为93.1％)为例，所得到的镜片对于紫外线的阻隔率达到了50％以上，对红外线的阻隔率达到了80％以上，可见光透过率可达到80％以上。因此，将该涂料用于镜片，能够有效避免红外线和紫外线对眼睛所造成的伤害，并且不影响眼镜本身的视力矫正等功能。
此外，该用于镜片的涂料的成分简单，所需原料均为常规材料，均可通过商购获得，因此还具有原料易得、成本低廉的优势。
本发明提供的镜片，其包括由上述用于镜片的涂料所制成的反射层，由于该反射层能够有效地阻隔红外线和紫外线，且确保可见光顺利通过，因此该镜片能够起到保护眼睛的作用，并且不影响镜片的正常功能。
本发明提供的镜片的制备方法，工艺简单可行，非常利于实际的生产和推广。
本发明提供的防红外线与紫外线的眼镜，其镜片上设有上述反射层，由于该反射层能够有效地阻隔红外线和紫外线，且具有较高的可见光透射比，因此该眼镜能够起到保护眼睛的作用，防止红外线和紫外线对眼睛造成的伤害，并且还不影响眼镜的正常功能。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
本实施例提供一种用于镜片的涂料，该用于镜片的涂料的配方如下表1所示。按照表1所示配方，将各组分经砂磨机充分研磨，得到涂料。
表1
| 组分名称 | 性质 | 质量分数/％ |
| 氧化锡锑(ATO) | 粒度为20～40nm | 2.0 |
| 氟碳树脂乳液 | 60.0 | |
| 水性聚氨酯 | 0.5 | |
| 聚丙烯酸钠 | 相对分子质量为1000～10000 | 0.05 |
| 聚乙烯醇 | 0.2 | |
| 工业乙醇 | 37.25 |
将该用于镜片的涂料喷涂在玻璃材质的镜片本体上，经室温下静置，待涂料固化成膜，得到镜片。
采用光栅分光光度计和傅里叶变换红外光谱仪对该幕帘以及聚酰亚胺薄膜的透光性进行测试测试该镜片与镜片本体的透光性，测试结果如表2所示。
表2
| 紫外线阻隔率 | 红外线阻隔率 | 可见光透过率 | |
| 镜片本体 | 34.5％ | 5.0％ | 93.1％ |
| 镜片 | 52.1％ | 84.7％ | 80.0％ |
由表2的测试结果对比可知，当将本实施例中的用于镜片的涂料用于镜片本体时，所得到的镜片对于紫外线和红外线的阻隔率均显著高于镜片本体，尤其是对红外线阻隔率达到了84.7％，此外对可见光的透过率也达到了80.0％，因此能够显著降低红外线和紫外线对于眼睛的伤害，且不影响镜片的视物功能。
对比例1
测试从市场上购买的墨镜进行透光性测试，其紫外线阻隔率几乎达到了100％，但是，该墨镜对红外线的阻隔率约为9.0％，由此可知，该墨镜对于红外线几乎无阻隔能力；该墨镜对可见光的透过率仅为43.6％，不推荐司机使用，否则极易引发交通事故。
实施例2
本实施例提供一种用于镜片的涂料，该用于镜片的涂料的配方如下表3所示。将该用于镜片的涂料喷涂在玻璃材质的镜片本体(与实施例1一致)上，经室温下静置，待涂料固化成膜，得到镜片。
采用与实施例1中一致的测试手段，测试该镜片的透光性，测试结果如表4所示。
表3
| 组分名称 | 性质 | 质量分数/％ |
| 氧化锡锑(ATO) | 粒度为20～40nm | 2.0 |
| 氟碳树脂乳液 | 60.0 | |
| 水性聚氨酯 | 0.499 | |
| 聚丙烯酸钠 | 相对分子质量为1000～10000 | 0.05 |
| 聚乙烯醇 | 0.2 | |
| 单壁碳纳米管 | 规格为2～5nm | 0.001 |
| 乙醇水溶液 | 等体积的工业乙醇与去离子水 | 37.25 |
表4
| 紫外线阻隔率 | 红外线阻隔率 | 可见光透过率 | |
| 镜片本体 | 34.5％ | 5.0％ | 93.1％ |
| 镜片 | 51.3％ | 82.5％ | 81.7％ |
由表4的测试结果对比可知，当将本实施例中的用于镜片的涂料用于镜片本体时，所得到的镜片对于紫外线和红外线的阻隔率均显著高于镜片本体，尤其是对红外线阻隔率达到了82.5％，此外对可见光的透过率也达到了81.7％，因此能够显著降低红外线和紫外线对于眼睛的伤害，且不影响镜片的视物功能。
此外，由于碳纳米管具有良好的力学性能，尤其具有良好的硬度和柔韧性，因此还能改善反射层的力学性能，比如可使镜片具有良好的耐磨性能；并且由于碳纳米管具有良好的传热性能，所以能够使镜片本体的热导率得到很大的改善，当在炎热的天气下佩戴眼镜时，由于镜片具有良好的传热性能，能够避免高温对眼镜以及人体眼睛所造成的伤害。
并且，进一步对比实施例1和实施例2的测试结果可知，在用于镜片的涂料中加入适量的碳纳米管，对镜片的透光性影响不大。大致而言，在用于镜片的涂料中加入碳纳米管之后，镜片对红外线和紫外线的阻隔率略有下降，而对可见光的透过率则略有提高，因此可根据实际需求，选择在涂料中加入碳纳米管。
对比例2
本对比例提供一种涂料，该涂料的配方与实施例1中涂料的配方基本一致，区别在于涂料的配方，具体本对比例中所用涂料的配方如表5所示。
表5
| 组分名称 | 性质 | 质量分数/％ |
| 氧化锡锑(ATO) | 粒度为20～40nm | 1.0 |
| 氟碳树脂乳液 | 60.0 | |
| 水性聚氨酯 | 0.5 | |
| 聚丙烯酸钠 | 相对分子质量为1000～10000 | 0.05 |
| 聚乙烯醇 | 0.2 | |
| 工业乙醇 | 38.25 |
按照与实施例1相同的方法制备镜片，并对得到的镜片进行透光性测试，测试结果如表6所示。
表6
| 紫外线阻隔率 | 红外线阻隔率 | 可见光透过率 | |
| 镜片本体 | 34.5％ | 5.0％ | 93.1％ |
| 镜片 | 42.2％ | 70.6％ | 88.4％ |
由表6的测试结果对比可知，当将本对比例的涂料用于镜片本体时，所得到的镜片对于紫外线和红外线的阻隔率均显著高于镜片本体，但是紫外线阻隔率的增幅并不明显。进一步比较实施例1和对比例2的结果可知，当氧化锡锑的用量较少时，镜片对红外线和紫外线的阻隔率均明显降低。
最后应说明的是：以上各实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述各实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分或者全部技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的范围。
Claims (10)
1.一种用于镜片的涂料，其特征在于，至少包括如下重量份的组分：氧化锡锑：1.5～2.5份、氟碳树脂乳液：50～75份、水性聚氨酯树脂：0.3～0.8份、聚丙烯酸钠：0.03～0.08份、聚乙烯醇：0.1～0.4份、水和/或醇类化合物：32～40份。
2.根据权利要求1所述的用于镜片的涂料，其特征在于，所述氧化锡锑的平均粒度不超过40nm。
3.根据权利要求1所述的用于镜片的涂料，其特征在于，所述聚丙烯酸钠的相对分子质量为1000～10000。
4.根据权利要求1所述的用于镜片的涂料，其特征在于，所述醇类化合物选自乙醇、丙醇和丁醇中的至少一种。
5.根据权利要求1-4任一项所述的用于镜片的涂料，其特征在于，还包括碳纳米管0.001～0.005份。
6.根据权利要求5所述的用于镜片的涂料，其特征在于，所述碳纳米管为单壁碳纳米管。
7.一种镜片，其特征在于，包括镜片本体以及反射层，其中所述反射层是将权利要求1-6任一项所述的用于镜片的涂料涂覆在镜片本体表面形成的膜层。
8.根据权利要求7所述的镜片，其特征在于，所述镜片本体的材质为树脂或玻璃。
9.一种权利要求7或8所述镜片的制备方法，其特征在于，包括：将所述用于镜片的涂料涂覆在镜片本体表面，再经干燥，在镜片本体表面形成反射层，得到镜片；
或者，将所述镜片本体浸没在所述用于镜片的涂料中，取出后干燥，在镜片本体表面形成反射层，得到镜片。
10.一种防红外线与紫外线的眼镜，其特征在于，包括镜架以及权利要求7或8所述的镜片。