CN111778378A - 一种转炉溅渣护炉料及其使用方法 - Google Patents
一种转炉溅渣护炉料及其使用方法 Download PDFInfo
- Publication number
- CN111778378A CN111778378A CN202010666611.5A CN202010666611A CN111778378A CN 111778378 A CN111778378 A CN 111778378A CN 202010666611 A CN202010666611 A CN 202010666611A CN 111778378 A CN111778378 A CN 111778378A
- Authority
- CN
- China
- Prior art keywords
- converter
- calcium carbide
- magnesia
- slag splashing
- slag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种转炉溅渣护炉料及其使用方法,属于钢铁冶炼技术领域。技术方案是:其组分为镁砂和电石,镁砂和电石相互之间的质量比如下:对于转炉铁水炼钢,镁砂80‑90%、电石10‑20%;对于转炉半钢炼钢,镁砂60‑80%、电石20‑40%。本发明的有益效果是:加入电石可以大幅度降低渣中的氧化铁,提高溅渣护炉效果;选用再生塑料包装密封电石,再生塑料在冶炼高温状态下与沥青的作用相同,起到发热剂和粘结剂的作用,对溅渣护炉有益,本发明开辟了对再生塑料利用的新途径,特别是可以利用垃圾级的四级回收的再生塑料,变废为宝,节能环保。
Description
技术领域
本发明涉及一种转炉溅渣护炉料及其使用方法,属于钢铁冶炼技术领域。
背景技术
转炉是钢铁企业生产的主体设备,其寿命直接关系到转炉的生产成本。 为了提高转炉寿命,20世纪90年代中期,美国LTV公司首先开发并采用溅渣护炉技术,大幅提高了转炉炉龄。溅渣护炉料为炼钢生产的主要炉料,在炼钢生产中起熔渣和护炉作用。已有技术的转炉溅渣护炉料主要为镁砂和碳粉为主,存在的问题是:溅渣护炉效果差,达不到溅渣护炉的要求;由于溅渣护炉料以镁砂和碳粉为主,不能大幅度降低渣中的氧化铁,而渣中的氧化铁是溅渣护炉效果不佳的最重要因素。另外,再生塑料的合理使用也是一项节能环保的重要课题,再生塑料是指通过预处理、熔融造粒、改性等物理或化学的方法对废旧塑料进行加工处理后重新得到的塑料原料,是对塑料的再次利用。再生塑料也分等级,再生塑料产品可分为以下四级:一级回收:是指采用通常的加工方法把可回收的废旧塑料(边角料等)加工成与新料性能相同或相近的产品。二级回收:是指把废旧塑料(边角料等)经一种或多种加工方法加工成性能比新料稍差的产品。三级回收:是指回收废旧塑料中的化学成分,使之成为单体或燃料。四级回收:是指通过焚烧从废旧塑料中回收能量。对于利用价值极低的四级回收再生塑料,没有更好的利用途径,只能通过焚烧回收能量,污染环境。
发明内容
本发明目的是提供一种转炉溅渣护炉料及其使用方法,大幅度降低渣中的氧化铁,提高溅渣护炉效果,同时可以充分利用再生塑料,特别是四级回收的再生塑料,变废为宝,节能环保,解决背景技术中存在的上述问题。
本发明的技术方案是:
一种转炉溅渣护炉料,其组分为镁砂和电石,镁砂和电石相互之间的质量比如下:对于转炉铁水炼钢,镁砂80-90%、电石10-20%;对于转炉半钢炼钢,镁砂60-80%、电石20-40%。
上述比例是根据不同冶炼方式渣中的氧化铁不同而确定的;转炉铁水炼钢一般渣中氧化铁含量为17%,转炉半钢炼钢一般渣中氧化铁含量为23%。
所述电石装入用再生塑料制作的柱状罐体内,密封包装;所述镁砂压制成球团,柱状罐体与镁砂球团的粒径相同,粒径为30-60mm,按照上述比例混合在一起使用。
所述再生塑料为四级回收的再生塑料。
一种转炉溅渣护炉料及其使用方法,包含如下步骤:
制备转炉溅渣护炉料,其组分为镁砂和电石,镁砂和电石相互之间的质量比如下:对于转炉铁水炼钢,镁砂80-90%、电石10-20%;对于转炉半钢炼钢,镁砂60-80%、电石20-40%;所述电石装入用再生塑料制作的柱状罐体内,密封包装;所述镁砂压制成球团,柱状罐体与镁砂球团的粒径相同,粒径为30-60mm,按照上述比例混合在一起使用;
在转炉冶炼结束、留渣后,向转炉内加入转炉溅渣护炉料,吨钢加入3-6公斤。
本发明的有益效果是:加入电石可以大幅度降低渣中的氧化铁,提高溅渣护炉效果;选用再生塑料包装密封电石,再生塑料在冶炼高温状态下与沥青的作用相同,起到发热剂和粘结剂的作用,对溅渣护炉有益,本发明开辟了对再生塑料利用的新途径,特别是可以利用垃圾级的四级回收的再生塑料,变废为宝,节能环保。
具体实施方式
以下通过实施例对本发明作进一步说明。
一种转炉溅渣护炉料,其组分为镁砂和电石,镁砂和电石相互之间的质量比如下:对于转炉铁水炼钢,镁砂80-90%、电石10-20%;对于转炉半钢炼钢,镁砂60-80%、电石20-40%。
上述比例是根据不同冶炼方式渣中的氧化铁不同而确定的;转炉铁水炼钢一般渣中氧化铁含量为17%,转炉半钢炼钢一般渣中氧化铁含量为23%。
所述电石装入用再生塑料制作的柱状罐体内,密封包装;所述镁砂压制成球团,柱状罐体与镁砂球团的粒径相同,粒径为30-60mm,按照上述比例混合在一起使用。
所述再生塑料为四级回收的再生塑料。
一种转炉溅渣护炉料及其使用方法,包含如下步骤:
制备转炉溅渣护炉料,其组分为镁砂和电石,镁砂和电石相互之间的质量比如下:对于转炉铁水炼钢,镁砂80-90%、电石10-20%;对于转炉半钢炼钢,镁砂60-80%、电石20-40%;所述电石装入用再生塑料制作的柱状罐体内,密封包装;所述镁砂压制成球团,柱状罐体与镁砂球团的粒径相同,粒径为30-60mm,按照上述比例混合在一起使用;
在转炉冶炼结束、留渣后,向转炉内加入转炉溅渣护炉料,吨钢加入3-6公斤。
本发明与已有技术使用效果对比实验:
1、在某钢厂两座100吨转炉铁水炼钢,进行对比实验,相同的冶炼条件下,分别加入已有技术的溅渣护炉料(镁砂和碳粉为主)和本发明转炉溅渣护炉料,结果如下:使用已有技术溅渣护炉,炉龄为14300次;使用本发明溅渣护炉,炉龄为21750次。同时,利用了再生塑料包装密封电石,变废为宝。
2、在某钢厂两座150吨转炉半钢炼钢,进行对比实验,相同的冶炼条件下,分别加入已有技术的溅渣护炉料(镁砂和碳粉为主)和本发明转炉溅渣护炉料,结果如下:使用已有技术溅渣护炉,炉龄为67410次;使用本发明溅渣护炉,炉龄为9135次。同时,利用了四级回收的再生塑料包装密封电石,变废为宝。
Claims (4)
1.一种转炉溅渣护炉料,其特征在于:其组分为镁砂和电石,镁砂和电石相互之间的质量比如下:对于转炉铁水炼钢,镁砂80-90%、电石10-20%;对于转炉半钢炼钢,镁砂60-80%、电石20-40%。
2.根据权利要求1所述的一种转炉溅渣护炉料,其特征在于:所述电石装入用再生塑料制作的柱状罐体内,密封包装;所述镁砂压制成球团,柱状罐体与镁砂球团的粒径相同,粒径为30-60mm,按照上述比例混合在一起使用。
3.根据权利要求1或2所述的一种转炉溅渣护炉料,其特征在于:所述再生塑料为四级回收的再生塑料。
4.一种转炉溅渣护炉料的使用方法,其特征在于包含如下步骤:
制备转炉溅渣护炉料,其组分为镁砂和电石,镁砂和电石相互之间的质量比如下:对于转炉铁水炼钢,镁砂80-90%、电石10-20%;对于转炉半钢炼钢,镁砂60-80%、电石20-40%;所述电石装入用再生塑料制作的柱状罐体内,密封包装;所述镁砂压制成球团,柱状罐体与镁砂球团的粒径相同,粒径为30-60mm,按照上述比例混合在一起使用;
在转炉冶炼结束、留渣后,向转炉内加入转炉溅渣护炉料,吨钢加入3-6公斤。