CN111777978A - 一种不易老化且绿色环保的ms胶及其制备方法 - Google Patents
一种不易老化且绿色环保的ms胶及其制备方法 Download PDFInfo
- Publication number
- CN111777978A CN111777978A CN202010391084.1A CN202010391084A CN111777978A CN 111777978 A CN111777978 A CN 111777978A CN 202010391084 A CN202010391084 A CN 202010391084A CN 111777978 A CN111777978 A CN 111777978A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- friendly
- glue
- aging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种不易老化且绿色环保的MS胶，属于胶粘剂技术领域。不易老化且绿色环保的MS胶，按重量份计，其制备原料至少包含：硅烷改性聚醚预聚体93～105份、环保增塑剂60～100份、填料80～90份、催化剂2～4份、除水剂7～9份。本申请提供的一种不易老化且绿色环保的MS胶使用了环保无毒的增塑剂，在环保无毒的基础上，具有不易老化的特性，适用于多种基材，使用安全可靠。
Description
技术领域
本发明涉及胶粘剂技术领域，特别涉及一种不易老化且绿色环保的MS胶及其制备方法。
背景技术
MS胶，即硅烷改性聚醚胶的简称，对于环境合格人体亲和度高，适用于绝大多数建筑基材，具有良好的施工性、粘结性、耐久性以及耐候性，尤其具有可涂饰性，在建筑装饰上有着广泛的应用。
但是，现有技术中，由于MS胶的材质问题，导致其易老化，使用寿命偏低，亟待改善；且密封胶中的增塑剂一般为邻苯二甲酸酯类，但其是一种环境激素类物质并具有致癌性，人长期处于这种环境会严重影响健康，成年人会患生殖疾病、不孕不育，甚至患上癌症，而儿童会产生性早熟，不健康，不环保，亟待改善。
发明内容
本发明要解决的技术问题是提供一种不易老化且绿色环保的MS胶及其制备方法。
为了解决上述技术问题，本发明的第一方面提供了一种不易老化且绿色环保的MS胶，按重量份计，其制备原料至少包含：硅烷改性聚醚预聚体93～105份、环保增塑剂60～100 份、填料80～90份、催化剂2～4份、除水剂7～9份。
优选的，按重量份计，其制备原料至少包含：硅烷改性聚醚预聚体100份、环保增塑剂 80份、填料86份、催化剂3份、除水剂8份。
优选的，所述环保增塑剂为柠檬酸酯、环氧酸酯、脂肪酸酯中的一种或多种。
优选的，所述填料为纳米碳酸钙、气相白炭黑、重质碳酸钙、聚烯烃弹性体中的一种或多种。
优选的，所述聚烯烃弹性体粉为POE。
优选的，所述催化剂为辛酸亚锡、二乙酸二丁基锡、二辛酸二丁基锡、螯合锡中的一种或多种。
优选的，所述除水剂为乙烯基三甲氧基硅烷、乙烯基三乙氧基硅烷中的一种或多种。
优选的，按重量份计，所述制备原料还包含颜料3～5份、紫外吸收剂3～5份、光稳定剂3～5份。
优选的，所述颜料为钛白粉、锌白粉、炭黑、氧化铁黑、氧化铁红、氧化铁黄中的一种或多种。
本发明的第二方面提供了一种上述的不易老化且绿色环保的MS胶的制备方法，包括以下步骤：a.混料：称取环保增塑剂、填料、除水剂投入搅拌混合釜，搅拌混合0.5～1小时，加入硅烷改性聚醚预聚体继续搅拌至均匀，抽真空，在搅拌条件下升温至125～130℃，保持 2～4小时；b.反应：将釜内温度降至40～50℃，充入氮气，加入催化剂，重新抽真空，充分搅拌物料后，解除真空至常压，出料灌装，即得成品。
本申请提供的一种不易老化且绿色环保的MS胶使用了环保无毒的增塑剂，在环保无毒的基础上，具有不易老化的特性，适用于多种基材，使用安全可靠。
具体实施方式
下面对本发明的具体实施方式作进一步说明。在此需要说明的是，对于这些实施方式的说明用于帮助理解本发明，但并不构成对本发明的限定。此外，下面所描述的本发明各个实施方式中所涉及的技术特征只要彼此之间未构成冲突就可以相互组合。
为了解决上述问题，本发明的第一方面提供了一种不易老化且绿色环保的MS胶，按重量份计，其制备原料至少包含：硅烷改性聚醚预聚体93～105份、环保增塑剂60～100份、填料80～90份、催化剂2～4份、除水剂7～9份。本申请提供的一种不易老化且绿色环保的 MS胶使用了环保无毒的增塑剂，在环保无毒的基础上，具有不易老化的特性，适用于多种基材，使用安全可靠。
在一些优选的实施方式中，按重量份计，不易老化且绿色环保的MS胶的制备原料至少包含：硅烷改性聚醚预聚体100份、环保增塑剂80份、填料86份、催化剂3份、除水剂8份。
在一些实施方式中，所述环保增塑剂为柠檬酸酯、环氧酸酯、脂肪酸酯中的一种或多种。
在一些实施方式中，柠檬酸酯可列举为柠檬酸三乙酯、柠檬酸三丁酯、柠檬酸三辛酯、乙酰柠檬酸三丁酯、乙酰柠檬酸三辛酯等。
在一些实施方式中，环氧酸酯可列举为环氧大豆油、环氧化亚麻仁油、环氧硬脂酸辛酯、环氧油酸辛酯、环氧油酸丁酯、环氧油酸癸酯等。
在一些实施方式中，脂肪酸酯可列举为己二酸二辛酯、已二酸二异癸酯、壬二酸二辛酯、癸二酸二丁酸、癸二酸二辛酯、癸二酸二异辛酯等。
在一些实施方式中，所述填料为纳米碳酸钙、气相白炭黑、重质碳酸钙、聚烯烃弹性体中的一种或多种。
在一些实施方式中，所述聚烯烃弹性体粉为POE。
在一些实施方式中，所述增塑剂与填料的重量比为(1.5～4)：1；进一步优选的，所述增塑剂与填料的重量比为1.5：1。
在一些实施方式中，所述催化剂为辛酸亚锡、二乙酸二丁基锡、二辛酸二丁基锡、螯合锡中的一种或多种。
在一些实施方式中，所述除水剂为乙烯基三甲氧基硅烷、乙烯基三乙氧基硅烷中的一种或多种。
在一些实施方式中，所述填料与除水剂的重量比为8：1。
在一些实施方式中，按重量份计，所述制备原料还包含颜料3～5份、紫外吸收剂3～5 份、光稳定剂3～5份。
在一些实施方式中，按重量份计，所述制备原料还包含颜料4份、紫外吸收剂4份、光稳定剂4份。
在一些实施方式中，所述颜料为钛白粉、锌白粉、炭黑、氧化铁黑、氧化铁红、氧化铁黄中的一种或多种。
本发明的第二方面提供了一种不易老化且绿色环保的MS胶的制备方法，包括以下步骤：
a.混料：称取环保增塑剂、填料、除水剂投入搅拌混合釜，搅拌混合0.5～1小时，加入硅烷改性聚醚预聚体继续搅拌至均匀，抽真空，在搅拌条件下升温至125～130℃，保持2～ 4小时；
b.反应：将釜内温度降至40～50℃，充入氮气，加入催化剂，重新抽真空，充分搅拌物料后，解除真空至常压，出料灌装，即得成品。
在一些实施方式中，不易老化且绿色环保的MS胶的制备方法包括以下步骤：
a.混料：称取环保增塑剂、填料、除水剂投入搅拌混合釜，搅拌混合0.8小时，加入硅烷改性聚醚预聚体继续搅拌至均匀，抽真空，在搅拌条件下升温至130℃，保持3小时；
b.反应：将釜内温度降至45℃，充入氮气，加入催化剂，重新抽真空，充分搅拌物料后，
解除真空至常压，出料灌装，即得成品。
实施例1
实施例1提供了一种不易老化且绿色环保的MS胶，按重量份计，其制备原料至少包含：硅烷改性聚醚预聚体100份、环保增塑剂80份、填料86份、催化剂3份、除水剂8份；
所述环保增塑剂为柠檬酸酯，优选地为柠檬酸三丁酯；
所述填料为气相白炭黑与聚烯烃弹性体的混合物，气相白炭黑与聚烯烃弹性体的比例为 8:1；
所述催化剂为二乙酸二丁基锡；
所述除水剂为乙烯基三乙氧基硅烷。
本例还提供了上述不易老化且绿色环保的MS胶的制备方法，包括以下步骤：
a.混料：称取增塑剂、填料、除水剂投入搅拌混合釜，搅拌混合1小时，加入硅烷改性聚醚预聚体继续搅拌至均匀，抽真空，在搅拌条件下升温至130℃，保持3小时；
b.反应：将釜内温度降至40℃，充入氮气，加入催化剂，重新抽真空，充分搅拌物料后，解除真空至常压，出料灌装，即得成品。
实施例2
实施例2提供了一种不易老化且绿色环保的MS胶，其与实施例1的不同之处在于，所述制备原料还包含颜料4份、紫外吸收剂4份、光稳定剂4份；
所述颜料为炭黑；
所述紫外吸收剂为水杨酸苯酯；
所述光稳定剂为亚磷酸酯。
本例还提供了上述不易老化且绿色环保的MS胶的制备方法，包括以下步骤：
a.混料：称取增塑剂、填料、除水剂投入搅拌混合釜，搅拌混合1小时，加入硅烷改性聚醚预聚体继续搅拌至均匀，抽真空，在搅拌条件下升温至130℃，保持3小时；
b.反应：将釜内温度降至40℃，充入氮气，加入催化剂、颜料、紫外吸收剂、光稳定剂，重新抽真空，充分搅拌物料后，解除真空至常压，出料灌装，即得成品。
实施例3
实施例3提供了一种不易老化且绿色环保的MS胶，其与实施例1的不同之处在于，所述增塑剂为环氧大豆油。
本例还提供了上述不易老化且绿色环保的MS胶的制备方法，其步骤与实施例1类似。
实施例4
实施例4提供了一种不易老化且绿色环保的MS胶，其与实施例1的不同之处在于，所述填料为气相白炭黑。
本例还提供了上述不易老化且绿色环保的MS胶的制备方法，其步骤与实施例1类似。
实施例5
实施例5提供了一种不易老化且绿色环保的MS胶，其与实施例1的不同之处在于，所述填料为为纳米碳酸钙。
本例还提供了上述不易老化且绿色环保的MS胶的制备方法，其步骤与实施例1类似。
实施例6
实施例6提供了一种不易老化且绿色环保的MS胶，其与实施例2的不同之处在于，所述颜料为为钛白粉。
本例还提供了上述不易老化且绿色环保的MS胶的制备方法，其步骤与实施例2类似。
性能评估
1、抗老化性能
根据GB/T7122-1996对实施例1-6制备所得MS胶的剥离强度进行测试，记录户外暴晒 1000个小时后其剥离强度的保持率，以剥离强度的保持率来衡量MS胶的抗老化性能。
2、粘结性能
根据GB/T7122-1996对实施例1-6制备所得MS胶的剥离强度进行测试，记录水中作业 1000个小时后其剥离强度的保持率，以剥离强度的保持率来衡量MS胶的粘结性能。
| 粘结性能(％) | 抗老化性能(％) | |
| 实施例1 | 98 | 97 |
| 实施例2 | 99 | 98 |
| 实施例3 | 96 | 95 |
| 实施例4 | 93 | 95 |
| 实施例5 | 95 | 97 |
| 实施例6 | 96 | 97 |
由以上结果可知，本发明制备所得MS胶无毒无味、环保，可在水中作业，施工方便简单，粘结性能优异，粘结牢固，并且具有优异的抗老化性能，使用寿命长。
以上对本发明的实施方式作了详细说明，但本发明不限于所描述的实施方式。对于本领域的技术人员而言，在不脱离本发明原理和精神的情况下，对这些实施方式进行多种变化、修改、替换和变型，仍落入本发明的保护范围内。
Claims (10)
1.一种不易老化且绿色环保的MS胶，其特征在于，按重量份计，其制备原料至少包含：硅烷改性聚醚预聚体93～105份、环保增塑剂60～100份、填料80～90份、催化剂2～4份、除水剂7～9份。
2.根据权利要求1所述的不易老化且绿色环保的MS胶，其特征在于，按重量份计，其制备原料至少包含：硅烷改性聚醚预聚体100份、环保增塑剂80份、填料86份、催化剂3份、除水剂8份。
3.根据权利要求1所述的不易老化且绿色环保的MS胶，其特征在于，所述环保增塑剂为柠檬酸酯、环氧酸酯、脂肪酸酯中的一种或多种。
4.根据权利要求1所述的不易老化且绿色环保的MS胶，其特征在于，所述填料为纳米碳酸钙、气相白炭黑、重质碳酸钙、聚烯烃弹性体中的一种或多种。
5.根据权利要求4所述的不易老化且绿色环保的MS胶，其特征在于，所述聚烯烃弹性体粉为POE。
6.根据权利要求1所述的不易老化且绿色环保的MS胶，其特征在于，所述催化剂为辛酸亚锡、二乙酸二丁基锡、二辛酸二丁基锡、螯合锡中的一种或多种。
7.根据权利要求1所述的不易老化且绿色环保的MS胶，其特征在于，所述除水剂为乙烯基三甲氧基硅烷、乙烯基三乙氧基硅烷中的一种或多种。
8.根据权利要求1所述的不易老化且绿色环保的MS胶，其特征在于，按重量份计，所述制备原料还包含颜料3～5份、紫外吸收剂3～5份、光稳定剂3～5份。
9.根据权利要求8所述的不易老化且绿色环保的MS胶，其特征在于，所述颜料为钛白粉、锌白粉、炭黑、氧化铁黑、氧化铁红、氧化铁黄中的一种或多种。
10.一种根据权利要求1-9任一项所述的不易老化且绿色环保的MS胶的制备方法，其特征在于，包括以下步骤：a.混料：称取环保增塑剂、填料、除水剂投入搅拌混合釜，搅拌混合0.5～1小时，加入硅烷改性聚醚预聚体继续搅拌至均匀，抽真空，在搅拌条件下升温至125～130℃，保持2～4小时；b.反应：将釜内温度降至40～50℃，充入氮气，加入催化剂，重新抽真空，充分搅拌物料后，解除真空至常压，出料灌装，即得成品。