CN111730291A - 一种镀锌钢管内衬不锈钢复合管材的生产工艺 - Google Patents
一种镀锌钢管内衬不锈钢复合管材的生产工艺 Download PDFInfo
- Publication number
- CN111730291A CN111730291A CN202010607453.6A CN202010607453A CN111730291A CN 111730291 A CN111730291 A CN 111730291A CN 202010607453 A CN202010607453 A CN 202010607453A CN 111730291 A CN111730291 A CN 111730291A
- Authority
- CN
- China
- Prior art keywords
- steel pipe
- stainless steel
- pipe
- galvanized steel
- production process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种镀锌钢管内衬不锈钢复合管材的生产工艺,具体步骤如下:步骤a、将镀锌钢管选取一定的长度进行切割,随后将切割的边缘处进行打磨;步骤b、将打磨后的镀锌钢管内壁进行修整;步骤c、将不锈钢管的外壁进行修整,并对其外壁进行抛光处理。本发明提供的一种镀锌钢管内衬不锈钢复合管材的生产工艺,利用此方法可以快速的对复合管材进行制备,并且通过快速冷却成型,和高温定时成型使得其耐压性能较强,使用寿命较长。
Description
技术领域
本发明涉及一种镀锌钢管内衬不锈钢复合管材的生产工艺,属于复合管材生产技术领域。
背景技术
复合管材是以金属与热塑性塑料复合结构为基础的管材,内衬塑聚丙烯、聚乙烯或外焊接交联聚乙烯等非金属材料成型,具有金属管材和非金属管材的优点,不锈钢复合管由不锈钢和碳素结构钢两种金属材料采用无损压力同步复合成的新材料,兼具不锈钢抗腐蚀耐磨和卓越外表,以及碳素钢良好的抗弯强度及抗冲击性。但是现有的不锈钢复合管材在制备时工序较为繁琐,其管材耐压性不强。
发明内容
本发明的目的在于提供一种镀锌钢管内衬不锈钢复合管材的生产工艺,以解决上述背景技术中提出的现有的不锈钢复合管材在制备时工序较为繁琐,其管材耐压性不强的问题。
为实现上述目的,本发明提供如下技术方案:一种镀锌钢管内衬不锈钢复合管材的生产工艺,具体步骤如下:
步骤a、将镀锌钢管选取一定的长度进行切割,随后将切割的边缘处进行打磨;
步骤b、将打磨后的镀锌钢管内壁进行修整;
步骤c、将不锈钢管的外壁进行修整,并对其外壁进行抛光处理;
步骤d、将处理后的不锈钢管推入镀锌钢管内侧进行套合;
步骤e、套合后将其两端封闭处理,并进行内部高温成型;
步骤f、成型后进行速干处理,并进行冷却。
优选的,所述步骤a的打磨时间为5-10min。
优选的,所述步骤e成型温度设置在150-180℃,时间为30-40min。
优选的,所述步骤f的冷却时间为15-20min。
与现有技术相比,本发明的有益效果如下:
本发明提供的一种镀锌钢管内衬不锈钢复合管材的生产工艺,利用此方法可以快速的对复合管材进行制备,并且通过快速冷却成型,和高温定时成型使得其耐压性能较强,使用寿命较长。
具体实施方式
为使本领域技术人员更加清楚和明确本发明的技术方案,下面结合实施例对本发明作进一步详细的描述,但本发明的实施方式不限于此。
本实施例提供的一种镀锌钢管内衬不锈钢复合管材的生产工艺,具体步骤如下:
步骤a、将镀锌钢管选取一定的长度进行切割,随后将切割的边缘处进行打磨,打磨时间为5-10min;
步骤b、将打磨后的镀锌钢管内壁进行修整;
步骤c、将不锈钢管的外壁进行修整,并对其外壁进行抛光处理;
步骤d、将处理后的不锈钢管推入镀锌钢管内侧进行套合;
步骤e、套合后将其两端封闭处理,并进行内部高温成型,成型温度设置在150-180℃,时间为30-40min;
步骤f、成型后进行速干处理,并进行冷却,冷却时间为15-20min。
以上所述,仅为本发明进一步的实施例,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明所公开的范围内,根据本发明的技术方案及其构思加以等同替换或改变,都属于本发明的保护范围。
Claims (4)
1.一种镀锌钢管内衬不锈钢复合管材的生产工艺,其特征在于:具体步骤如下:
步骤a、将镀锌钢管选取一定的长度进行切割,随后将切割的边缘处进行打磨;
步骤b、将打磨后的镀锌钢管内壁进行修整;
步骤c、将不锈钢管的外壁进行修整,并对其外壁进行抛光处理;
步骤d、将处理后的不锈钢管推入镀锌钢管内侧进行套合;
步骤e、套合后将其两端封闭处理,并进行内部高温成型;
步骤f、成型后进行速干处理,并进行冷却。
2.根据权利要求1所述的一种镀锌钢管内衬不锈钢复合管材的生产工艺,其特征在于:所述步骤a的打磨时间为5-10min。
3.根据权利要求1所述的一种镀锌钢管内衬不锈钢复合管材的生产工艺,其特征在于:所述步骤e成型温度设置在150-180℃,时间为30-40min。
4.根据权利要求1所述的一种镀锌钢管内衬不锈钢复合管材的生产工艺,其特征在于:所述步骤f的冷却时间为15-20min。