CN111673374A - 一种铝电解槽摇篮架开裂修复方法 - Google Patents
一种铝电解槽摇篮架开裂修复方法 Download PDFInfo
- Publication number
- CN111673374A CN111673374A CN202010441218.6A CN202010441218A CN111673374A CN 111673374 A CN111673374 A CN 111673374A CN 202010441218 A CN202010441218 A CN 202010441218A CN 111673374 A CN111673374 A CN 111673374A
- Authority
- CN
- China
- Prior art keywords
- welding
- cradle
- cradle frame
- cracking
- repairing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的目的在于公开一种铝电解槽摇篮架开裂修复方法，与现有技术相比，能够保证在对电解槽摇篮架开裂处修复后，摇篮架仍可连续投入使用，有效延长电解槽摇篮架的使用寿命一倍以上，方便易行，在现有条件下容易实现，实现在线修复，节约时间，降低成本，不仅限于对电解槽摇篮架进行修复，而且还可以用于其他行业对重载支架进行修复，实现本发明的目的。
Description
技术领域
本发明涉及一种开裂修复方法，特别涉及一种铝电解槽摇篮架开裂修复方法。
背景技术
所谓摇篮架，实质上是用24组U型的约束架，也就是俗称的摇篮支架，紧密地卡住钢板焊成的壳体，壳体起容器作用。
摇篮架采用工字钢制造，具有较大的刚度和强度。摇篮架与壳体焊成一体，摇篮架除了对电解槽槽壳起到支撑固定作用外，更重要的是摇篮架要承受电解槽高温变形带来的巨大膨胀应力，使摇篮架悬臂产生巨大的侧向推力，造成摇篮架悬臂底部开裂(如图2所示)，存在极大的漏炉隐患。
传统的修复方法是停槽，将电解槽吊出去，更换一组新的摇篮架，需要30多天才能修复，耗费大量金钱。
因此，特别需要一种铝电解槽摇篮架开裂修复方法，以解决上述现有存在的问题。
发明内容
本发明的目的在于提供一种铝电解槽摇篮架开裂修复方法，针对现有技术的不足，采用在线修复的方法，方便易行，节约时间，节约成本。
本发明所解决的技术问题可以采用以下技术方案来实现：
一种铝电解槽摇篮架开裂修复方法，其特征在于，它包括如下步骤：
a、先将两片钢板打坡口，作为补强板，焊接在摇篮架开裂的裂口处，进行满焊；
b、再准备两块钢板，打坡口，作为加强板，焊接在摇篮架的两侧，进行满焊；
c、焊接完成后，做去应力处理，用气焊加热，使其自然冷却；
d、冷却后，摇篮架的裂口既修复。
在本发明的一个实施例中，在上述步骤中，气焊加热至300-400℃。
在本发明的一个实施例中，在上述步骤中，气焊加热后，用保温棉进行包裹，冷却后拆除保温棉。
本发明的铝电解槽摇篮架开裂修复方法，与现有技术相比，能够保证在对电解槽摇篮架开裂处修复后，摇篮架仍可连续投入使用，有效延长电解槽摇篮架的使用寿命一倍以上，方便易行，在现有条件下容易实现，实现在线修复，节约时间，降低成本，不仅限于对电解槽摇篮架进行修复，而且还可以用于其他行业对重载支架进行修复，实现本发明的目的。
本发明的特点可参阅本案图式及以下较好实施方式的详细说明而获得清楚地了解。
附图说明
图1为本发明的铝电解槽摇篮架开裂修复方法的示意图；
图2为本发明的铝电解槽摇篮架开裂的结构示意图。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体图示，进一步阐述本发明。
实施例
如图1和图2所示，本发明的铝电解槽摇篮架开裂修复方法，它包括如下步骤：
a、先将两片钢板打坡口，作为补强板20，然后焊接在摇篮架10的裂口11处，进行满焊；
b、再准备两块钢板，打坡口，作为加强板30，然后焊接在摇篮架10的两侧，进行满焊；
c、焊接完成后，做去应力处理，用气焊加热至300-400℃，然后用保温棉包裹，使其自然冷却；
d、冷却后，拆除保温棉，摇篮架10的裂口11既修复。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内，本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.一种铝电解槽摇篮架开裂修复方法，其特征在于，它包括如下步骤：
a、先将两片钢板打坡口，作为补强板，焊接在摇篮架开裂的裂口处，进行满焊；
b、再准备两块钢板，打坡口，作为加强板，焊接在摇篮架的两侧，进行满焊；
c、焊接完成后，做去应力处理，用气焊加热，使其自然冷却；
d、冷却后，摇篮架的裂口既修复。
2.如权利要求1所述的铝电解槽摇篮架开裂修复方法，其特征在于，在上述步骤中，气焊加热至300-400℃。
3.如权利要求1所述的铝电解槽摇篮架开裂修复方法，其特征在于，在上述步骤中，气焊加热后，用保温棉进行包裹，冷却后拆除保温棉。