CN111589370A - Dispersing agent for polyester fluorescent whitening agent - Google Patents
Dispersing agent for polyester fluorescent whitening agent Download PDFInfo
- Publication number
- CN111589370A CN111589370A CN202010459081.7A CN202010459081A CN111589370A CN 111589370 A CN111589370 A CN 111589370A CN 202010459081 A CN202010459081 A CN 202010459081A CN 111589370 A CN111589370 A CN 111589370A
- Authority
- CN
- China
- Prior art keywords
- dispersant
- terylene
- fluorescent whitening
- regulator
- dispersing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dispersant for a terylene fluorescent whitening agent, which relates to the textile chemical technology and aims to solve the problems that polyvinyl alcohol has poor water resistance when in use and is easy to be unstable after long use, and the technical scheme has the key points that: comprises 20-45% of fatty alcohol-polyoxyethylene ether, 20-31% of polyvinyl acetate, 3-6% of NaOH methanol solution, 10% of PVA-1799 aqueous solution, 5-13% of hydrochloric acid, 30-39% of formaldehyde solution, 5-12.4% of dispersant viscosity improver and the balance of deionized water. The dispersing agent for the polyester fluorescent whitening agent has good stability and strong dispersing ability.
Description
Technical Field
The invention relates to a textile chemical technology, in particular to a dispersant for a terylene fluorescent whitening agent.
Background
The dispersant is a surfactant which has two opposite properties of lipophilicity and hydrophilcity in a molecule. The amphiphilic agent is capable of uniformly dispersing solid and liquid particles of inorganic and organic pigments which are difficult to dissolve in liquids, and also preventing settling and agglomeration of the particles to form stable suspensions.
The dispersant is divided into: anionic type, cationic type, nonionic type, amphoteric type, electric neutral type, and high molecular type (including high, medium, and low molecular weight). Polyvinyl alcohol is a commonly used dispersant, and includes a hydroxyl group in its molecule, but it is poor in water resistance when used as a dispersant, and is liable to be unstable after a long period of use.
Therefore, a new solution is needed to solve this problem.
Disclosure of Invention
Aiming at the defects in the prior art, the invention aims to provide a dispersing agent for a polyester fluorescent whitening agent, which has better stability and stronger dispersing capacity.
The technical purpose of the invention is realized by the following technical scheme: a dispersing agent for a polyester fluorescent whitening agent comprises 20-45% of fatty alcohol-polyoxyethylene ether, 20-31% of polyvinyl acetate, 3-6% of NaOH methanol solution, 10% of PVA-1799 aqueous solution, 5-13% of hydrochloric acid, 30-39% of formaldehyde solution, 5-12.4% of a dispersing agent viscosity improver and the balance of deionized water.
Through adopting above-mentioned technical scheme, react through polyvinyl acetate, NaOH methanol solution, thereby take place partial hydrolysis, rethread hydrochloric acid and formaldehyde solution carry out acetalation reaction, then obtain acetalized polyvinyl alcohol, make it dissolve in water and have better water resistance, the difficult condition that decomposes that takes place, polyvinyl alcohol's molecular weight is lower in addition, thereby lead to the viscidity of dispersant to further descend, then further reduce the concentration of dispersant through deionized water, reduce the content of anion in the dispersant simultaneously, thereby further reduce the viscidity of dispersant, make this dispersant's stability better, and the difficult condition that takes place the cohesion, avoid appearing the flocculation group.
The invention is further configured to: also comprises 30-37% of ethanol.
Through adopting above-mentioned technical scheme, through setting up the ethanol to make it can dissolve polyvinyl alcohol as better medium, and further reduce dispersant viscosity, avoid the condition that the dispersant appears flocculating when using.
The invention is further configured to: the viscosity improver of the dispersing agent is a viscosity regulator.
The invention is further configured to: the viscosity regulator comprises one or more of paraffin, microcrystalline wax, polyethylene wax, oxidized polyethylene wax, polypropylene wax, saso wax, hyperbranched polymer, APAO, ethylene bis stearamide, EVA, urea, hydroxylamine hydrochloride, hydroxylamine sulfate and cyclohexanol.
The invention is further configured to: also comprises a pH regulator.
By adopting the technical scheme, the pH regulator is arranged, so that the pH value of the dispersing agent can be regulated.
The invention is further configured to: the pH regulator is sodium hydroxide or potassium hydroxide or a mixture of the sodium hydroxide and the potassium hydroxide.
The invention is further configured to: comprises 26-40% of fatty alcohol-polyoxyethylene ether, 25-28% of polyvinyl acetate, 3.6-4.9% of NaOH methanol solution, 10% of PVA-1799 aqueous solution, 7-11% of hydrochloric acid, 36-38% of formaldehyde solution, 8-11% of dispersant viscosity improver and the balance of deionized water.
In conclusion, the invention has the following beneficial effects:
through polyvinyl acetate, NaOH methanol solution reacts, thereby take place partial hydrolysis, rethread hydrochloric acid and formaldehyde solution carry out acetalation reaction, then obtain acetalized polyvinyl alcohol, make it dissolve in aqueous and have better water resistance, the difficult condition that decomposes that takes place, polyvinyl alcohol's molecular weight is lower in addition, thereby lead to the viscidity of dispersant to further descend, then further reduce the concentration of dispersant through the deionized water, reduce the content of anion in the dispersant simultaneously, thereby further reduce the viscidity of dispersant, make the stability of this dispersant better, and be difficult to take place the condition of cohesion, avoid appearing the flocculation.
Detailed Description
The present invention will be described in detail with reference to examples.
The first embodiment is as follows:
a dispersing agent for a terylene fluorescent whitening agent comprises 26% of fatty alcohol-polyoxyethylene ether, 26% of polyvinyl acetate, 3.9% of NaOH methanol solution, 10% of PVA-1799 aqueous solution, 9.6% of hydrochloric acid, 36% of formaldehyde solution, 8.5% of a dispersing agent viscosity improver, 3.95% of aluminum hydroxide, 8.9% of ferrous chloride, 33% of ethanol, a pH regulator, 8.5% of sodium chloride and the balance of deionized water.
The viscosity modifier of the dispersing agent is a viscosity regulator, and the viscosity regulator comprises one or more of paraffin, microcrystalline wax, polyethylene wax, oxidized polyethylene wax, polypropylene wax, saso wax, hyperbranched polymer, APAO, ethylene bis stearamide, EVA, urea, hydroxylamine hydrochloride, hydroxylamine sulfate and cyclohexanol.
The pH regulator is sodium hydroxide or potassium hydroxide or a mixture of the two.
Example two:
a dispersing agent for a terylene fluorescent whitening agent comprises 30% of fatty alcohol-polyoxyethylene ether, 27% of polyvinyl acetate, 4.2% of NaOH methanol solution, 10% of PVA-1799 aqueous solution, 9.95% of hydrochloric acid, 37% of formaldehyde solution, 9.3% of a dispersing agent viscosity improver, 4.1% of aluminum hydroxide, 9.2% of ferrous chloride, 35% of ethanol, a pH regulator, 8.9% of sodium chloride and the balance of deionized water.
The viscosity modifier of the dispersing agent is a viscosity regulator, and the viscosity regulator comprises one or more of paraffin, microcrystalline wax, polyethylene wax, oxidized polyethylene wax, polypropylene wax, saso wax, hyperbranched polymer, APAO, ethylene bis stearamide, EVA, urea, hydroxylamine hydrochloride, hydroxylamine sulfate and cyclohexanol.
The pH regulator is sodium hydroxide or potassium hydroxide or a mixture of the two.
Example three:
a dispersing agent for a polyester fluorescent whitening agent comprises 40% of fatty alcohol-polyoxyethylene ether, 28% of polyvinyl acetate, 4.9% of NaOH methanol solution, 10% of PVA-1799 aqueous solution, 11% of hydrochloric acid, 38% of formaldehyde solution, 11% of a dispersing agent viscosity improver, 4.85% of aluminum hydroxide, 9.76% of ferrous chloride, 37% of ethanol, a pH regulator, 9.3% of sodium chloride and the balance of deionized water.
The viscosity modifier of the dispersing agent is a viscosity regulator, and the viscosity regulator comprises one or more of paraffin, microcrystalline wax, polyethylene wax, oxidized polyethylene wax, polypropylene wax, saso wax, hyperbranched polymer, APAO, ethylene bis stearamide, EVA, urea, hydroxylamine hydrochloride, hydroxylamine sulfate and cyclohexanol.
The pH regulator is sodium hydroxide or potassium hydroxide or a mixture of the two.
Comparative example: a dispersant for a fluorescent whitening agent produced by Technological Ltd.
The dispersant for the fluorescent brightener for terylene obtained in examples 1 to 3 and a comparative product are subjected to performance detection, and the specific detection method is as follows:
measured using a rheometer type AG-2000 at a measurement temperature of 18 ℃ and a shear rate of 100S-1The apparent viscosity and the detection results are shown in table 1; the stability of the dispersant can be represented by the influence of the standing time of the dispersant after the dispersant is incorporated into the terylene fluorescent whitening agent on the water precipitation rate of the terylene fluorescent whitening agent, and the detection results are shown in table 2.
TABLE 1
TABLE 2
As can be seen from the results detected in tables 1 and 2, the dispersant for the fluorescent brightener for terylene has better stability and stronger dispersing ability.
The above description is only a preferred embodiment of the present invention, and the protection scope of the present invention is not limited to the above embodiments, and all technical solutions belonging to the idea of the present invention belong to the protection scope of the present invention. It should be noted that modifications and embellishments within the scope of the invention may occur to those skilled in the art without departing from the principle of the invention, and are considered to be within the scope of the invention.
Claims (7)
1. A dispersant for a terylene fluorescent whitening agent is characterized in that: comprises 20-45% of fatty alcohol-polyoxyethylene ether, 20-31% of polyvinyl acetate, 3-6% of NaOH methanol solution, 10% of PVA-1799 aqueous solution, 5-13% of hydrochloric acid, 30-39% of formaldehyde solution, 5-12.4% of dispersant viscosity improver and the balance of deionized water.
2. The dispersant for the fluorescent brightener for terylene according to claim 1, is characterized in that: also comprises 30-37% of ethanol.
3. The dispersant for the fluorescent brightener for terylene according to claim 1, is characterized in that: the viscosity improver of the dispersing agent is a viscosity regulator.
4. The dispersing agent for the terylene fluorescent whitening agent according to claim 3, characterized in that: the viscosity regulator comprises one or more of paraffin, microcrystalline wax, polyethylene wax, oxidized polyethylene wax, polypropylene wax, saso wax, hyperbranched polymer, APAO, ethylene bis stearamide, EVA, urea, hydroxylamine hydrochloride, hydroxylamine sulfate and cyclohexanol.
5. The dispersant for the fluorescent brightener for terylene according to claim 1, is characterized in that: also comprises a pH regulator.
6. The dispersing agent for the terylene fluorescent whitening agent according to claim 5, characterized in that: the pH regulator is sodium hydroxide or potassium hydroxide or a mixture of the sodium hydroxide and the potassium hydroxide.
7. The dispersant for the fluorescent brightener for terylene according to claim 1, is characterized in that: comprises 26-40% of fatty alcohol-polyoxyethylene ether, 25-28% of polyvinyl acetate, 3.6-4.9% of NaOH methanol solution, 10% of PVA-1799 aqueous solution, 7-11% of hydrochloric acid, 36-38% of formaldehyde solution, 8-11% of dispersant viscosity improver and the balance of deionized water.