CN111569142A - 沸石尿不湿的配方与制备工艺 - Google Patents

沸石尿不湿的配方与制备工艺 Download PDF

Info

Publication number
CN111569142A
CN111569142A CN202010480970.1A CN202010480970A CN111569142A CN 111569142 A CN111569142 A CN 111569142A CN 202010480970 A CN202010480970 A CN 202010480970A CN 111569142 A CN111569142 A CN 111569142A
Authority
CN
China
Prior art keywords
zeolite
layer
finished product
semi
diaper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010480970.1A
Other languages
English (en)
Inventor
蔡稼平
虞磊磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Fuhuo Biological Environmental Protection Technology Co ltd
Original Assignee
Jiangsu Fuhuo Biological Environmental Protection Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Fuhuo Biological Environmental Protection Technology Co ltd filed Critical Jiangsu Fuhuo Biological Environmental Protection Technology Co ltd
Priority to CN202010480970.1A priority Critical patent/CN111569142A/zh
Publication of CN111569142A publication Critical patent/CN111569142A/zh
Pending legal-status Critical Current

Abstract

本发明公开了沸石尿不湿的配方与制备工艺，涉及尿不湿技术领域。沸石尿不湿的配方，所述沸石尿不湿包括表层、导流层、芯体、锁水层、底层和魔术贴，所述表层为棉布材质，所述导流层为聚丙烯无纺布材质，所述锁水层为聚乙烯膜材质，所述底层为聚丙烯无纺布材质，所述芯体由以下重量份的原料制成：40‑50wt%绒毛浆纤维、40‑50wt%超强高分子吸收树脂。本发明通过沸石粉的添加，能够使得尿不湿中含有的人类生长发育所需的全部常量元素和大部分微量元素，同时因为这些元素都是以离子的状态存在，因此其也极利于被婴儿所吸收和利用，从而能够促进婴儿发育，帮助婴儿健康成长。

Description

沸石尿不湿的配方与制备工艺
技术领域
本发明涉及尿不湿技术领域，具体为沸石尿不湿的配方与制备工艺。
背景技术
沸石粉是沸石岩经磨细后形成的一种粉状结晶性矿石材料，沸石岩是含水硅铝酸盐矿物，其架构含有许多孔隙，充满移动性自由度很高的大分子离子及水分子，在几百万年前，火山爆发喷出大量带硅酸铝的火山灰，经由风传递而沉积成浓厚的灰床，有些火山灰进入湖泊底部，有些灰床经过水的浸透，不管任何情况，火山灰和海水的化学反应结果产生天然沸石粉，沸石目前被开发应用于多种领域，主要是斜发沸石和丝光沸石，沸石岩经过磨细，或加入少量改性材料后一起磨细，就成为沸石粉，沸石粉中含有畜禽、水产动物和人类生长发育所需的全部常量元素和大部分微量元素这些元素都以离子状态存在，能被畜禽、水产动物以及人类所利用，此外沸石还具有独特的吸附性、催化性、离子交换性，离子的选择性、耐酸性、热稳定性、多成份性、及很高的生物活性和抗毒性等。
为了从尿不湿上为婴儿补充生长和发育所需要的微量元素，特此提出一种沸石尿不湿的配方与制备工艺。
发明内容
本发明的目的在于提供沸石尿不湿的配方与制备工艺，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：沸石尿不湿的配方，所述沸石尿不湿包括表层、导流层、芯体、锁水层、底层和魔术贴，所述表层为棉布材质，所述导流层为聚丙烯无纺布材质，所述锁水层为聚乙烯膜材质，所述底层为聚丙烯无纺布材质，所述芯体由以下重量份的原料制成：40-50wt%绒毛浆纤维、40-50wt%超强高分子吸收树脂、0.3-1.0wt%香精、1-10wt%沸石粉、0.3-0.5wt%热熔胶、0.3-0.5wt%卫生纸、0.3-1.0wt%棉布、0.3-1.0wt%聚乙烯膜、0.6-2.0wt%聚丙烯无纺布，所述沸石粉主要由二氧化硅、三氧化二铝、可溶性硅和可溶性铝组成。
更进一步地，所述绒毛浆纤维为抽出有机溶剂的木浆纤维和草浆纤维其中一种或者两种的混合物，所述香精为异戊酸异戊酯、异戊酸乙酯、丁酸异戊酯、香兰素、苯甲醛、柠檬醛、甲酸异戊酯、香叶油、乙酸烯丙酯、丁香油、甘油、醋酸乙酯、乙醇溶液和蒸馏水中的一种或者多种的混合物，所述乙醇溶液的浓度为95%。
更进一步地，所述超强高分子吸收树脂为淀粉-丙烯腈接枝聚合水解物、淀粉-丙烯酸共聚物、淀粉-丙烯酰胺接枝聚合物中的一种或者多种的混合物。
更进一步地，所述热熔胶为淀粉、糊精、聚乙烯醇、羧甲基纤维素和蒸馏水中的一种或者多种的混合物。
更进一步地，所述沸石尿不湿的芯体的制备工艺如下：
S1：首先采用粉碎机将绒毛浆纤维粉碎，得到粉碎物A；
S2：利用搅拌机将粉碎物A和超强高分子吸收树脂进行混合，混合温度为20-60摄氏度，混合时间为5-15分钟，得到混合物B；
S3：将香精和沸石粉添加到搅拌机当中，混合温度为20-60摄氏度，混合时间为15-25分钟得到混合物C；
S4：采用网轮吸附工艺将混合物C制作成棉芯D；
S5：将卫生纸喷涂上热熔胶，进一步的将卫生纸粘接在棉芯D的两面得到棉芯体E；
S6：将棉芯体E压实后在外部包覆上聚丙烯无纺布，然后进行网格压花得到成品芯体。
更进一步地，所述S3步骤中沸石粉和香精的添加顺序为先添加沸石粉再添加香精。
更进一步地，所述沸石尿不湿的制备工艺如下：
H1：将导流层喷涂热熔胶后粘贴在芯体的顶部，得到半成品F；
H2：将锁水层喷涂热熔胶后粘贴在半成品F的底部，得到半成品G；
H3：将表层喷涂热熔胶后粘贴在半成品G的顶部，得到半成品I；
H4：将底层喷涂热熔胶后粘贴在半成品H的底部，得到半成品J；
H5：将半成品J四角粘贴上魔术贴得到成品沸石尿不湿。
与现有技术相比，本发明的有益效果是：
（1）、沸石尿不湿的配方与制备工艺，通过沸石粉的添加，能够使得尿不湿中含有的人类生长发育所需的全部常量元素和大部分微量元素，同时因为这些元素都是以离子的状态存在，因此其也极利于被婴儿所吸收和利用，从而能够促进婴儿发育，帮助婴儿健康成长。
（2）、沸石尿不湿的配方与制备工艺，通过沸石粉的添加，间接的增强了尿不湿的吸附性能，使得尿不湿能够吸附尿液和人体当中的有毒物质，从而使得尿不湿具有一定的抗毒性能，同时因为沸石粉为弱碱性，因此所生产的尿不湿具有一定的杀菌功能。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一：
沸石尿不湿的配方，沸石尿不湿包括表层、导流层、芯体、锁水层、底层和魔术贴，表层为棉布材质，导流层为聚丙烯无纺布材质，锁水层为聚乙烯膜材质，底层为聚丙烯无纺布材质，芯体由以下重量份的原料制成：45wt%绒毛浆纤维、45wt%超强高分子吸收树脂、0.3wt%香精、1wt%沸石粉、0.4wt%热熔胶、0.4wt%卫生纸、0.8wt%棉布、0.7wt%聚乙烯膜、1.4wt%聚丙烯无纺布，沸石粉为80%的二氧化硅、10%的三氧化二铝、5%的可溶性硅和5%的可溶性铝组成。
绒毛浆纤维为抽出有机溶剂的50%的木浆纤维和50%的草浆纤维的混合物，香精为0.5%的异戊酸异戊酯、0.5%的异戊酸乙酯、0.5%的丁酸异戊酯、1%的香兰素、1%的苯甲醛、1%的柠檬醛、1%的甲酸异戊酯、1%的香叶油、0.5%的乙酸烯丙酯、0.5%的丁香油、0.5%的甘油、0.5%的醋酸乙酯、41.5%的乙醇溶液和50%的蒸馏水的混合物，其中乙醇溶液的浓度为95%。
超强高分子吸收树脂为40%的淀粉-丙烯腈接枝聚合水解物、30%的淀粉-丙烯酸共聚物和30%的淀粉-丙烯酰胺接枝聚合物的混合物。
热熔胶为60%的淀粉、5%的糊精、3%的聚乙烯醇、4%的羧甲基纤维素和28%的蒸馏水的混合物。
沸石尿不湿的芯体的制备工艺如下：
S1：首先采用粉碎机将绒毛浆纤维粉碎，得到粉碎物A；
S2：利用搅拌机将粉碎物A和超强高分子吸收树脂进行混合，混合温度为25摄氏度，混合时间为10分钟，得到混合物B；
S3：将香精和沸石粉添加到搅拌机当中，混合温度为25摄氏度，混合时间为20分钟得到混合物C；
S4：采用网轮吸附工艺将混合物C制作成棉芯D；
S5：将卫生纸喷涂上热熔胶，进一步的将卫生纸粘接在棉芯D的两面得到棉芯体E；
S6：将棉芯体E压实后在外部包覆上聚丙烯无纺布，然后进行网格压花得到成品芯体。
S3步骤中沸石粉和香精的添加顺序为先添加沸石粉再添加香精。
沸石尿不湿的制备工艺如下：
H1：将导流层喷涂热熔胶后粘贴在芯体的顶部，得到半成品F；
H2：将锁水层喷涂热熔胶后粘贴在半成品F的底部，得到半成品G；
H3：将表层喷涂热熔胶后粘贴在半成品G的顶部，得到半成品I；
H4：将底层喷涂热熔胶后粘贴在半成品H的底部，得到半成品J；
H5：将半成品J四角粘贴上魔术贴得到成品沸石尿不湿。
实施例二：
沸石尿不湿的配方，沸石尿不湿包括表层、导流层、芯体、锁水层、底层和魔术贴，表层为棉布材质，导流层为聚丙烯无纺布材质，锁水层为聚乙烯膜材质，底层为聚丙烯无纺布材质，芯体由以下重量份的原料制成：45wt%绒毛浆纤维、45wt%超强高分子吸收树脂、0.3wt%香精、5wt%沸石粉、0.4wt%热熔胶、0.4wt%卫生纸、0.8wt%棉布、0.7wt%聚乙烯膜、1.4wt%聚丙烯无纺布，沸石粉为80%的二氧化硅、10%的三氧化二铝、5%的可溶性硅和5%的可溶性铝组成。
绒毛浆纤维为抽出有机溶剂的50%的木浆纤维和50%的草浆纤维的混合物，香精为0.5%的异戊酸异戊酯、0.5%的异戊酸乙酯、0.5%的丁酸异戊酯、1%的香兰素、1%的苯甲醛、1%的柠檬醛、1%的甲酸异戊酯、1%的香叶油、0.5%的乙酸烯丙酯、0.5%的丁香油、0.5%的甘油、0.5%的醋酸乙酯、41.5%的乙醇溶液和50%的蒸馏水的混合物，其中乙醇溶液的浓度为95%。
超强高分子吸收树脂为40%的淀粉-丙烯腈接枝聚合水解物、30%的淀粉-丙烯酸共聚物和30%的淀粉-丙烯酰胺接枝聚合物的混合物。
热熔胶为60%的淀粉、5%的糊精、3%的聚乙烯醇、4%的羧甲基纤维素和28%的蒸馏水的混合物。
沸石尿不湿的芯体的制备工艺如下：
S1：首先采用粉碎机将绒毛浆纤维粉碎，得到粉碎物A；
S2：利用搅拌机将粉碎物A和超强高分子吸收树脂进行混合，混合温度为25摄氏度，混合时间为10分钟，得到混合物B；
S3：将香精和沸石粉添加到搅拌机当中，混合温度为25摄氏度，混合时间为20分钟得到混合物C；
S4：采用网轮吸附工艺将混合物C制作成棉芯D；
S5：将卫生纸喷涂上热熔胶，进一步的将卫生纸粘接在棉芯D的两面得到棉芯体E；
S6：将棉芯体E压实后在外部包覆上聚丙烯无纺布，然后进行网格压花得到成品芯体。
S3步骤中沸石粉和香精的添加顺序为先添加沸石粉再添加香精。
沸石尿不湿的制备工艺如下：
H1：将导流层喷涂热熔胶后粘贴在芯体的顶部，得到半成品F；
H2：将锁水层喷涂热熔胶后粘贴在半成品F的底部，得到半成品G；
H3：将表层喷涂热熔胶后粘贴在半成品G的顶部，得到半成品I；
H4：将底层喷涂热熔胶后粘贴在半成品H的底部，得到半成品J；
H5：将半成品J四角粘贴上魔术贴得到成品沸石尿不湿。
实施例三：
沸石尿不湿的配方，沸石尿不湿包括表层、导流层、芯体、锁水层、底层和魔术贴，表层为棉布材质，导流层为聚丙烯无纺布材质，锁水层为聚乙烯膜材质，底层为聚丙烯无纺布材质，芯体由以下重量份的原料制成：45wt%绒毛浆纤维、45wt%超强高分子吸收树脂、0.3wt%香精、10wt%沸石粉、0.4wt%热熔胶、0.4wt%卫生纸、0.8wt%棉布、0.7wt%聚乙烯膜、1.4wt%聚丙烯无纺布，沸石粉为80%的二氧化硅、10%的三氧化二铝、5%的可溶性硅和5%的可溶性铝组成。
绒毛浆纤维为抽出有机溶剂的50%的木浆纤维和50%的草浆纤维的混合物，香精为0.5%的异戊酸异戊酯、0.5%的异戊酸乙酯、0.5%的丁酸异戊酯、1%的香兰素、1%的苯甲醛、1%的柠檬醛、1%的甲酸异戊酯、1%的香叶油、0.5%的乙酸烯丙酯、0.5%的丁香油、0.5%的甘油、0.5%的醋酸乙酯、41.5%的乙醇溶液和50%的蒸馏水的混合物，其中乙醇溶液的浓度为95%。
超强高分子吸收树脂为40%的淀粉-丙烯腈接枝聚合水解物、30%的淀粉-丙烯酸共聚物和30%的淀粉-丙烯酰胺接枝聚合物的混合物。
热熔胶为60%的淀粉、5%的糊精、3%的聚乙烯醇、4%的羧甲基纤维素和28%的蒸馏水的混合物。
沸石尿不湿的芯体的制备工艺如下：
S1：首先采用粉碎机将绒毛浆纤维粉碎，得到粉碎物A；
S2：利用搅拌机将粉碎物A和超强高分子吸收树脂进行混合，混合温度为25摄氏度，混合时间为10分钟，得到混合物B；
S3：将香精和沸石粉添加到搅拌机当中，混合温度为25摄氏度，混合时间为20分钟得到混合物C；
S4：采用网轮吸附工艺将混合物C制作成棉芯D；
S5：将卫生纸喷涂上热熔胶，进一步的将卫生纸粘接在棉芯D的两面得到棉芯体E；
S6：将棉芯体E压实后在外部包覆上聚丙烯无纺布，然后进行网格压花得到成品芯体。
S3步骤中沸石粉和香精的添加顺序为先添加沸石粉再添加香精。
沸石尿不湿的制备工艺如下：
H1：将导流层喷涂热熔胶后粘贴在芯体的顶部，得到半成品F；
H2：将锁水层喷涂热熔胶后粘贴在半成品F的底部，得到半成品G；
H3：将表层喷涂热熔胶后粘贴在半成品G的顶部，得到半成品I；
H4：将底层喷涂热熔胶后粘贴在半成品H的底部，得到半成品J；
H5：将半成品J四角粘贴上魔术贴得到成品沸石尿不湿。
对比例一：
去除沸石粉，其余成分和制备方法同实施例一。
表1 性能检测表
检测项目 单位 标准 实施例一 实施例二 实施例三 对比例一
滑渗量 ml ≦20.0 3.2 5.0 8.3 3.0
回渗量 g ≦10.0 1.1 2.3 3.1 1.0
渗漏量 g ≦0.5 0 0.1 0.1 0
大肠菌群 / 不得检出 未检出 未检出 未检出 未检出
绿脓杆菌 / 不得检出 未检出 未检出 未检出 未检出
金黄色葡萄球菌 / 不得检出 未检出 未检出 未检出 未检出
溶血性链球菌 / 不得检出 未检出 未检出 未检出 未检出
从表1可以得出，相对于未添加沸石粉的尿不湿，添加1wt%、5wt%和10wt%的沸石粉的尿不湿，其滑渗量、回渗量和渗透量虽然有所减弱，但是其性能仍然符合尿不湿检测标准。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (7)

1.沸石尿不湿的配方，所述沸石尿不湿包括表层、导流层、芯体、锁水层、底层和魔术贴，所述表层为棉布材质，所述导流层为聚丙烯无纺布材质，所述锁水层为聚乙烯膜材质，所述底层为聚丙烯无纺布材质，其特征在于：所述芯体由以下重量份的原料制成：40-50wt%绒毛浆纤维、40-50wt%超强高分子吸收树脂、0.3-1.0wt%香精、1-10wt%沸石粉、0.3-0.5wt%热熔胶、0.3-0.5wt%卫生纸、0.3-1.0wt%棉布、0.3-1.0wt%聚乙烯膜、0.6-2.0wt%聚丙烯无纺布，所述沸石粉主要由二氧化硅、三氧化二铝、可溶性硅和可溶性铝组成。
2.根据权利要求1所述的沸石尿不湿的配方，其特征在于：所述绒毛浆纤维为抽出有机溶剂的木浆纤维和草浆纤维其中一种或者两种的混合物，所述香精为异戊酸异戊酯、异戊酸乙酯、丁酸异戊酯、香兰素、苯甲醛、柠檬醛、甲酸异戊酯、香叶油、乙酸烯丙酯、丁香油、甘油、醋酸乙酯、乙醇溶液和蒸馏水中的一种或者多种的混合物，所述乙醇溶液的浓度为95%。
3.根据权利要求1所述的沸石尿不湿的配方，其特征在于：所述超强高分子吸收树脂为淀粉-丙烯腈接枝聚合水解物、淀粉-丙烯酸共聚物、淀粉-丙烯酰胺接枝聚合物中的一种或者多种的混合物。
4.根据权利要求1所述的沸石尿不湿的配方，其特征在于：所述热熔胶为淀粉、糊精、聚乙烯醇、羧甲基纤维素和蒸馏水中的一种或者多种的混合物。
5.沸石尿不湿的芯体的制备工艺，其特征在于：所述沸石尿不湿的芯体的制备工艺如下：
S1：首先采用粉碎机将绒毛浆纤维粉碎，得到粉碎物A；
S2：利用搅拌机将粉碎物A和超强高分子吸收树脂进行混合，混合温度为20-60摄氏度，混合时间为5-15分钟，得到混合物B；
S3：将香精和沸石粉添加到搅拌机当中，混合温度为20-60摄氏度，混合时间为15-25分钟得到混合物C；
S4：采用网轮吸附工艺将混合物C制作成棉芯D；
S5：将卫生纸喷涂上热熔胶，进一步的将卫生纸粘接在棉芯D的两面得到棉芯体E；
S6：将棉芯体E压实后在外部包覆上聚丙烯无纺布，然后进行网格压花得到成品芯体。
6.根据权利要求5所述的沸石尿不湿的芯体的制备工艺，其特征在于：所述S3步骤中沸石粉和香精的添加顺序为先添加沸石粉再添加香精。
7.沸石尿不湿的制备工艺，其特征在于：所述沸石尿不湿的制备工艺如下：
H1：将导流层喷涂热熔胶后粘贴在芯体的顶部，得到半成品F；
H2：将锁水层喷涂热熔胶后粘贴在半成品F的底部，得到半成品G；
H3：将表层喷涂热熔胶后粘贴在半成品G的顶部，得到半成品I；
H4：将底层喷涂热熔胶后粘贴在半成品H的底部，得到半成品J；
H5：将半成品J四角粘贴上魔术贴得到成品沸石尿不湿。
CN202010480970.1A 2020-05-30 2020-05-30 沸石尿不湿的配方与制备工艺 Pending CN111569142A (zh)