CN111533575A - 一种混凝土密封固化剂及其施工工艺 - Google Patents
一种混凝土密封固化剂及其施工工艺 Download PDFInfo
- Publication number
- CN111533575A CN111533575A CN202010367530.5A CN202010367530A CN111533575A CN 111533575 A CN111533575 A CN 111533575A CN 202010367530 A CN202010367530 A CN 202010367530A CN 111533575 A CN111533575 A CN 111533575A
- Authority
- CN
- China
- Prior art keywords
- concrete
- ground
- curing agent
- sealing curing
- construction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种混凝土密封固化剂，由50～70wt％的活性硅酸盐、10～20wt％的氟硅酸镁与氟硅酸锌的混合物、1～3wt％的氢氟酸、1～3wt％的聚和胍盐、1～3wt％的微膨胀剂、其余为水和其他助剂组成。该混凝土渗透密封固化剂是一种无色、无味、无毒、无害的新型抗菌建筑材料，以活性硅酸盐为主要成分的聚合溶液，可应用在新浇筑混凝土地面或旧地面翻新，通过充分渗透，其有效成份能迅速地与混凝土中的游离钙发生化学反应，生成结晶胶体来填充结构空隙，增加结构的致密性，使得混凝土表层形成一个坚如岩石的密封实体，极大地提高混凝土结构表层的强度和耐磨性，从而使地面永久防尘、防滑、耐磨、坚硬、抗压、抗渗、抗风化、耐化学性、光亮、环保等，延长了地面的使用寿命。
Description
技术领域
本发明涉及水泥地面改善涂料技术领域，尤其涉及一种混凝土密封固化剂及其施工工艺。
背景技术
混凝土，简称为砼，是指由胶凝材料将集料胶结成整体的工程复合材料的统称，通常讲的混凝土一词是指用水泥作胶凝材料，砂、石作集料；与水(可含外加剂和掺合料)按一定比例配合，经搅拌而得的水泥混凝土，也称普通混凝土，具有经济、耐久、耐火、高抗压性能等优点，它广泛应用于土木工程。
由于混凝土硬化过程中，表层和内部结构含有大量相互贯穿的细孔，导致混凝土结构物在服役过程中，时常因为表面质量不良或密实度不够而难以抵挡环境中腐蚀物质的侵蚀，造成混凝土结构性能的加速劣化，降低混凝土结构物的耐久性和服役寿命。针对混凝土存在的缺陷，现有技术普遍采用混凝土密封固化剂来对混凝土结构物进行处理。
混凝土密封固化剂，又名液体硬化剂或混凝土密封剂。目前市场上的无机类混凝土地面硬化剂主要由三类产品：第一类是以硅酸钠为主要成分的钠基盐类产品，其可以优先提高混凝土强度和耐磨性，但耐久性差，易于泛碱影响后期地坪效果；第二类是以硅酸钾为主要成分的钾基盐产品，其性能与钠基盐相比无明显提高；第三类是以硅酸锂为主要成分的锂基盐产品，从国外引进的产品大多是此类产品，其密封硬化效果较为显著，但由于是进口产品，其价格比较昂贵。
发明内容
有鉴于此，本发明的目的在于提供一种混凝土密封固化剂，本发明提供的混凝土密封固化剂涂装在混凝土结构物表面后，能明显提高混凝土结构物的强度和疏水性，同时具有一定的抗菌防腐的功能。
本发明提供了一种混凝土密封固化剂，所述混凝土密封固化剂由50～70wt％的活性硅酸盐、10～20wt％的氟硅酸镁与氟硅酸锌的混合物、1～3wt％的氢氟酸、1～3wt％的聚和胍盐、1～3wt％的微膨胀剂、其余为水和其他助剂组成。
所述活性硅酸盐为硅酸钠、硅酸钾或硅酸锂中的一种或多种。
所述氟硅酸镁与氟硅酸锌的混合物比例为1～5：1。
所述聚和胍盐为聚合单胍盐，尤其是六甲基聚合单胍盐。
本发明还提供了所述混凝土密封固化剂应用于新地坪的施工方法，该方法包括如下步骤：
用专业洗地机加清水清洗地面脏物；
待地面干透后，喷洒混凝土渗透密封固化剂于混凝土表面，使其充分湿润；
用毛刷、橡胶扫帚或排拖不断轻刷地面，需保持20～30分钟的渗透；
待渗透60分钟后，材料逐步变粘稠时，喷水雾使其充分溶解再次反应；
根据地面情况及使用要求，照前面施工步骤重新施工一次，固化效果更强；
最后用橡胶扫帚或真空吸尘器去除所有表面的污渍及残留固化剂，然后让地面自然变干即可。
本发明还提供了所述混凝土密封固化剂应用于旧地坪的施工方法，该方法包括如下步骤：
原地面施工有地坪漆，需采用磨削加金钢头机进行打磨施工，露出原基础面；
原地面为水泥、水磨石、金钢砂、地面翻砂，则采用翻新机加磨片进行表面打磨处理；
根据地面实际情况选用磨片，使地表面毛孔打开有利于材料的充分渗透；
其它施工步骤与新地坪一样，根据地面的基础及使用要求进行特殊处理。
本发明具有如下优点和有益的效果：
本发明提供的混凝土密封固化剂由50～70wt％的活性硅酸盐、10～20wt％的氟硅酸镁与氟硅酸锌的混合物、1～3wt％的氢氟酸、1～3wt％的聚和胍盐、1～3wt％的微膨胀剂、其余为水和其他助剂组成，该固化剂涂装在混凝土结构物表面后，其中的硅酸盐和微膨胀剂成分可迅速渗入混凝土内部并与游离钙反应，生成不可溶解的非晶态水化硅酸钙，从而实现对混凝土结构物细孔的封堵，提高混凝土结构物的硬度。同时，固化剂中的氟硅酸镁与氟硅酸锌的混合物、氢氟酸、聚和胍盐通过协同作用可以在混凝结构物表面形成疏水性抗菌膜层，增加混凝土结构物表面的疏水性以及抗菌性。实验结果表明，混凝土结构物表面涂装了本发明提供的混凝土密封固化剂之后，其表面莫式硬度高于7，吸水率低于0.6％，液滴接触角大于95°。
本发明的混凝土渗透密封固化剂是一种无色、无味、无毒、无害、阻燃环保节能型的新型建筑材料，以活性硅酸盐为主要成分的聚合溶液，该混凝土渗透密封固化剂可应用在新浇筑混凝土地面或旧地面翻新，通过充分渗透，该混凝土渗透密封固化剂的有效成份能迅速地与混凝土中的游离钙发生化学反应，生成结晶胶体来填充结构空隙，增加结构的致密性，使得混凝土表层形成一个坚如岩石的密封实体，极大地提高混凝土结构表层的强度和耐磨性，从而得到地面永久防尘、防滑、耐磨、坚硬、抗压、抗渗、抗风化、耐化学性、光亮、环保等，大大延长地面的使用寿命。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供了一种混凝土密封固化剂组成：
50～70wt％的活性硅酸盐
10～20wt％的氟硅酸镁与氟硅酸锌的混合物
1～3wt％的氢氟酸
1～3wt％的聚和胍盐
1～3wt％的微膨胀剂
其余为水和其他助剂组成。
所述活性硅酸盐为硅酸钠、硅酸钾或硅酸锂中的一种或多种。
所述氟硅酸镁与氟硅酸锌的混合物比例为1～5：1。
所述聚和胍盐为聚合单胍盐，尤其是六甲基聚合单胍盐。
本发明还提供了所述混凝土密封固化剂应用于新地坪的施工方法，该方法包括如下步骤：
用专业洗地机加清水清洗地面脏物；
待地面干透后，喷洒混凝土渗透密封固化剂于混凝土表面，使其充分湿润；
用毛刷、橡胶扫帚或排拖不断轻刷地面，需保持20～30分钟的渗透；
待渗透60分钟后，材料逐步变粘稠时，喷水雾使其充分溶解再次反应；
根据地面情况及使用要求，照前面施工步骤重新施工一次，固化效果更强；
最后用橡胶扫帚或真空吸尘器去除所有表面的污渍及残留固化剂，然后让地面自然变干即可。
新制地面上施工最早可以紧跟在粉光作业后，当人可在上面行走而不会产生脚印时，即可使用；但一般情况下要求对新制混凝土地面进行28天的常规养护后再施工，同时地面需机械压光，高标号的混凝土施工后的效果会更佳。
本发明还提供了所述混凝土密封固化剂应用于旧地坪的施工方法，该方法包括如下步骤：
原地面施工有地坪漆，需采用磨削加金钢头机进行打磨施工，露出原基础面；
原地面为水泥、水磨石、金钢砂、地面翻砂，则采用翻新机加磨片进行表面打磨处理；
根据地面实际情况选用磨片，使地表面毛孔打开有利于材料的充分渗透；
其它施工步骤与新地坪一样，根据地面的基础及使用要求进行特殊处理。
本发明的混凝土渗透密封固化剂的优点如下:
坚硬耐磨。经混凝土渗透密封固化剂处理后的地面，莫氏硬度将达到8，莫氏硬度提高45.3％；混凝土渗透密封固化剂能够将混凝土中的各种成分固化成一个坚硬的实体，增加硬度和密实度，经使用混凝土渗透密封固化剂的地面熟化后，耐磨度将提高到3倍以上，并随着时间的增长而持续增加地面的强度。
防尘防滑。经混凝土渗透密封固化剂中的有效成分与混凝土中的硅酸盐发生化学反应后，在混凝土表面形成一个无尘，致密的整体，从而达到永久的控制由表面空隙释出的混凝土微粒，起到防尘的效果；普通混凝土地面的盐碱成份会从表面析出，导致打滑，但混凝土渗透密封固化剂地面则不同，它在混凝土表面形成一个坚固、致密的整体，盐碱成份不会从表面析出，达到防滑的效果。
抗压抗渗。经混凝土渗透密封固化剂处理后的试样比未处理试样增强27.3％，抗折强度提高3倍以上；混凝土渗透密封固化剂中的有效成分能有效渗入到混凝土内，并与其发生化学反应，锁住里面的毛孔，对混凝土表面起到永久的密封效果，能有效抑制水、油和其它的表面污物进入到混凝土内。
抗化学性。经混凝土渗透密封处理后的地面不受电池酸、漂白剂、盐酸液、紫外线损伤，同时能有效阻止氯离子的通过，防酸、防碱，防风化可经受各种恶劣气候考验。
光亮环保。经混凝土渗透密封固化剂处理后的地面会出现大理石般光泽，使用越久光泽度越好；无色、无臭、无毒、阻燃的新型环保绿色产品。可边生产边施工，可快速投入使用。
另外，施工后地面无需打蜡，仅需清水或偶然用肥皂水拖地，将节约大量维修及保养成本；同时施工过混凝土渗透密封固化剂的地坪可提高(延长)使用寿命长达30年以上。由于消除表面不利结合之混凝土盐类，处理好的表面更有利于上漆、防水材料、结合削及地板材料的使用，与任何种类的涂装材料的结合及相容。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (6)
1.一种混凝土密封固化剂，其特征在于，所述混凝土密封固化剂由50～70wt％的活性硅酸盐、10～20wt％的氟硅酸镁与氟硅酸锌的混合物、1～3wt％的氢氟酸、1～3wt％的聚和胍盐、1～3wt％的微膨胀剂、其余为水和其他助剂组成。
2.根据权利要求1所述一种混凝土密封固化剂，其特征在于，所述活性硅酸盐为硅酸钠、硅酸钾或硅酸锂中的一种或多种。
3.根据权利要求1所述一种混凝土密封固化剂，其特征在于，氟硅酸镁与氟硅酸锌的混合物比例为1～5：1。
4.根据权利要求1所述一种混凝土密封固化剂，其特征在于，所述聚和胍盐为聚合单胍盐。
5.权利要求1～4所述的混凝土密封固化剂的施工工艺,其特征在于，新地坪施工包括如下步骤：
用专业洗地机加清水清洗地面脏物；
待地面干透后，喷洒混凝土渗透密封固化剂于混凝土表面，使其充分湿润；
用毛刷、橡胶扫帚或排拖不断轻刷地面，需保持20～30分钟的渗透；
待渗透60分钟后，材料逐步变粘稠时，喷水雾使其充分溶解再次反应；
根据地面情况及使用要求，照前面施工步骤重新施工一次，固化效果更强；
最后用橡胶扫帚或真空吸尘器去除所有表面的污渍及残留固化剂，然后让地面自然变干即可。
6.权利要求1～4所述的混凝土密封固化剂的施工工艺,其特征在于，旧地坪施工包括如下步骤：
原地面施工有地坪漆，需采用磨削加金钢头机进行打磨施工，露出原基础面；
原地面为水泥、水磨石、金钢砂、地面翻砂，则采用翻新机加磨片进行表面打磨处理；
根据地面实际情况选用磨片，使地表面毛孔打开有利于材料的充分渗透；
其它施工步骤与新地坪一样，根据地面的基础及使用要求进行特殊处理。