CN111518438A - 一种可擦拭彩色塑料蜡笔材料及其应用 - Google Patents
一种可擦拭彩色塑料蜡笔材料及其应用 Download PDFInfo
- Publication number
- CN111518438A CN111518438A CN202010398336.3A CN202010398336A CN111518438A CN 111518438 A CN111518438 A CN 111518438A CN 202010398336 A CN202010398336 A CN 202010398336A CN 111518438 A CN111518438 A CN 111518438A
- Authority
- CN
- China
- Prior art keywords
- parts
- erasable
- colored plastic
- crayon
- plastic crayon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可擦拭彩色塑料蜡笔材料及其应用，所述可擦拭彩色塑料蜡笔材料包括如下重量份数的组分：石蜡30‑60份；硬脂酸5‑10份；聚丙烯3‑15份；聚烯烃弹性体1‑5份；可擦拭聚合物1‑5份；填料20‑40份；颜料3‑10份；颜料分散剂1‑5份。本发明通过聚丙烯、聚烯烃弹性体以及可擦拭聚合物复配，使得与硬脂酸、石蜡相结合后，整体材料不影响其他性能的情况下，赋予了材料优异的可擦拭性能；而且在上述树脂原料成分的添加不仅没有影响到蜡笔材料的书写性能以及上色性，反而还有助于蜡笔产品的描绘性能，使其书写时非常流畅、着色性能优异；同时避免了现有技术中色浆需要单独研磨分散好后才能与其余成分混合制造蜡笔的繁琐步骤，精简了制备工艺，降低了生产制造成本。
Description
技术领域
本发明涉及铅芯材料领域，尤其涉及一种可擦拭彩色塑料蜡笔材料及其应用。
背景技术
蜡笔作为一种绘画工具目前已被广泛使用，可有数十种颜色，蜡笔没有渗透性，是靠附着力固定在画面上，不适宜用过于光滑的纸、板，亦不能通过色彩的反复叠加求得复合色。它是儿童学习色彩画的理想工具，一些画家也用它进行写生和色彩记录。而目前普通蜡笔材料是由石蜡和色粉混合而成的，由于受到石蜡蜡笔的软化点较低，导致普通蜡笔的质地较软，伴有粘手感，使用时容易折断，并且伴有很多碎屑，不可以擦拭，绘画时不流畅，着色较差，且制备蜡笔材料时，须经过很多制备工序，该过程相当的复杂而且制作成本很高。
目前，现有的蜡笔的抗折断性、上色性，均难以满足日渐高标准的要求，同时在可擦拭性能方面也有待进一步提高，而且其制备方法较为繁琐，不利于大规模工业化的生产。
发明内容
本发明为解决现有蜡笔抗折断性、上色性均难以满足日渐高标准的要求，且可擦拭性能查的问题，提出一种可擦拭彩色塑料蜡笔材料及其应用。
为实现上述目的，本发明采用以下技术方案：
本发明的第一方面是提供一种可擦拭彩色塑料蜡笔材料，包括如下重量份数的组分：
进一步地，所述石蜡为半精炼石蜡、全精炼石蜡、微晶石蜡、液体石蜡和聚乙烯蜡中的一种或几种。
进一步地，所述硬脂酸为工业一级品，其含量为95-100％。
进一步地，所述聚烯烃弹性体为4556热塑性弹性体；所述可擦拭聚合物为氯化聚乙烯、聚氯乙烯、SBS、SEBS、SIS中的一种或几种。
进一步地，所述聚丙烯的平均分子量为80000-100000。
进一步地，所述可擦拭彩色塑料蜡笔材料还包括0.5-2份的助剂，所述助剂为润滑剂、增稠剂和香料中的一种或几种。
进一步优选地，所述所述润滑剂为脂肪酸酰胺、油酸中的一种或两种；所述增稠剂为有机膨润土、甲基纤维素、淀粉中的一种或几种；所述香料为樟脑香、花香、柑橘香、木香中的一种或几种。
进一步地，所述颜料为炭黑、耐晒黄、永固黄、氧化铁黄、联苯胺黄G、酒石黄、永固橙、氧化铁红、永固红、立索红、棕土、黄土、永固紫、群青、钻蓝、酞青蓝、酞青绿、二氧化钛和锦白中的一种或几种；所述颜料分散剂为乙撑双硬脂酸酰胺、武汉超支化HyperC100、德国瓦克AK-1000和科莱恩PE520中的一种或几种。
进一步地，所述填料为滑石粉、轻钙、重钙、硅酸铝、氢氧化铝、和高岭土中的一种或几种。
本发明的第二方面是提供了所述可擦拭彩色塑料蜡笔材料在制备彩色塑料蜡笔中的应用，制备所述彩色塑料蜡笔，包括如下步骤：按配比称取各原料，混合，在温度100-150℃条件下熔融，混匀，制成可擦拭彩色塑料蜡笔材料；然后将制备所得的可擦拭彩色塑料蜡笔材料在温度100-110℃下保温，再将其浇入模具中，冷却成型，即得所述彩色塑料蜡笔。
本发明采用上述技术方案，与现有技术相比，具有如下技术效果：
本发明的可擦拭彩色塑料蜡笔材料通过聚丙烯、聚烯烃弹性体以及可擦拭聚合物复配，使得与硬脂酸、石蜡相结合后，整体材料不影响其他性能的情况下，赋予了材料优异的可擦拭性能；而且在上述树脂原料成分的添加不仅没有影响到蜡笔材料的书写性能以及上色性，反而还有助于蜡笔产品的描绘性能，使其书写时非常流畅、着色性能优异；同时避免了现有技术中色浆需要单独研磨分散好后才能与其余成分混合制造蜡笔的繁琐步骤，精简了制备工艺，降低了生产制造成本，有利于大规模工业化的生产。
具体实施方式
下面通过具体实施例对本发明进行详细和具体的介绍，以使更好的理解本发明，但是下述实施例并不限制本发明范围。
实施例1
一种可擦拭彩色塑料蜡笔的制备：
可擦拭彩色塑料蜡笔材料，包括如下重量份数的组分：半精炼石蜡30份，硬脂酸8份，聚丙烯7份，4556 TPE 2份，SEBS 1份，滑石粉20份，轻钙20 份，永固黄5份，武汉超支化HyperC100 5份，润滑剂1份，香料1份。
可擦拭彩色塑料蜡笔的制备方法如下：将上述各原料加入反应釜中加热至 120℃，搅拌熔解5小时制得所述可擦拭彩色塑料蜡笔材料；保温在110℃温度条件下将可擦拭彩色塑料蜡笔材料浇入模具中，然后冷却成型，制得所述可擦拭彩色塑料蜡笔。
实施例2
一种可擦拭彩色塑料蜡笔的制备：
可擦拭彩色塑料蜡笔材料，包括如下重量份数的组分：全精炼石蜡30份，微晶石蜡15份，硬脂酸7份，聚丙烯10份，4556 TPE 5份，氯化聚乙烯2份，SBS 3份，高岭土20份，酞青蓝3份，乙撑双硬脂酸酰胺2份，德国瓦克AK-1000 1份，增稠剂1份，香料1份。
可擦拭彩色塑料蜡笔的制备方法如下：将上述各原料加入反应釜中加热至 150℃，搅拌熔解6小时制得所述可擦拭彩色塑料蜡笔材料；保温在120℃温度条件下将可擦拭彩色塑料蜡笔材料浇入模具中，然后冷却成型，制得所述可擦拭彩色塑料蜡笔。
实施例3
一种可擦拭彩色塑料蜡笔的制备：
可擦拭彩色塑料蜡笔材料，包括如下重量份数的组分：全精炼石蜡25份，微晶石蜡5份，液体石蜡5份，硬脂酸5份，聚丙烯13份，4556 TPE 2份，聚氯乙烯5份，硅酸铝20份，轻钙10份，炭黑1份，二氧化钛4份，颜料分散剂科莱恩PE520 3份，润滑剂1份，增稠剂1份。
可擦拭彩色塑料蜡笔的制备方法如下：将上述各原料加入反应釜中加热至 100℃，搅拌熔解4小时制得所述可擦拭彩色塑料蜡笔材料；保温在120℃温度条件下将可擦拭彩色塑料蜡笔材料浇入模具中，然后冷却成型，制得所述可擦拭彩色塑料蜡笔。
对比例1
一种彩色塑料蜡笔的制备：
彩色塑料蜡笔材料，包括如下重量份数的组分：全精炼石蜡25份，微晶石蜡5份，液体石蜡5份，硬脂酸5份，聚丙烯13份，硅酸铝20份，轻钙10份，炭黑1份，二氧化钛4份，颜料分散剂科莱恩PE520 3份，润滑剂1份，增稠剂1份。
彩色塑料蜡笔的制备方法如下：将上述各原料加入反应釜中加热至100℃，搅拌熔解4小时制得所述彩色塑料蜡笔材料；保温在120℃温度条件下将彩色塑料蜡笔材料浇入模具中，然后冷却成型，制得所述彩色塑料蜡笔。
对比例2
一种彩色塑料蜡笔的制备：
彩色塑料蜡笔材料，包括如下重量份数的组分：全精炼石蜡25份，微晶石蜡5份，硬脂酸5份，聚丙烯10份，硅酸铝20份，轻钙10份，炭黑1份，二氧化钛4份，颜料分散剂科莱恩PE520 3份，润滑剂1份，增稠剂1份。
彩色塑料蜡笔的制备方法如下：将上述各原料加入反应釜中加热至100℃，搅拌熔解4小时制得所述彩色塑料蜡笔材料；保温在120℃温度条件下将彩色塑料蜡笔材料浇入模具中，然后冷却成型，制得所述彩色塑料蜡笔。
将上述实施例1-3制备的可擦拭彩色塑料蜡笔材料与对比例1-2的彩色塑料蜡笔材料进行相关性能测试，结果如表1所示：
表1
以上对本发明的具体实施例进行了详细描述，但其只是作为范例，本发明并不限制于以上描述的具体实施例。对于本领域技术人员而言，任何对本发明进行的等同修改和替代也都在本发明的范畴之中。因此，在不脱离本发明的精神和范围下所作的均等变换和修改，都应涵盖在本发明的范围内。
Claims (10)
1.一种可擦拭彩色塑料蜡笔材料，其特征在于，包括如下重量份数的组分：
2.根据权利要求1所述的可擦拭彩色塑料蜡笔材料，其特征在于，所述石蜡为半精炼石蜡、全精炼石蜡、微晶石蜡、液体石蜡和聚乙烯蜡中的一种或几种。
3.根据权利要求1所述的可擦拭彩色塑料蜡笔材料，其特征在于，所述硬脂酸为工业一级品，其含量为95-100％。
4.根据权利要求1所述的可擦拭彩色塑料蜡笔材料，其特征在于，所述聚烯烃弹性体为4556热塑性弹性体；所述可擦拭聚合物为氯化聚乙烯、聚氯乙烯、SBS、SEBS、SIS中的一种或几种。
5.根据权利要求1所述的可擦拭彩色塑料蜡笔材料，其特征在于，所述聚丙烯的平均分子量为80000-100000。
6.根据权利要求1所述的可擦拭彩色塑料蜡笔材料，其特征在于，所述可擦拭彩色塑料蜡笔材料还包括0.5-2份的助剂，所述助剂为润滑剂、增稠剂和香料中的一种或几种。
7.根据权利要求6所述的可擦拭彩色塑料蜡笔材料，其特征在于，所述润滑剂为脂肪酸酰胺、油酸中的一种或两种；所述增稠剂为有机膨润土、甲基纤维素、淀粉中的一种或几种；所述香料为樟脑香、花香、柑橘香、木香中的一种或几种。
8.根据权利要求1所述的可擦拭彩色塑料蜡笔材料，其特征在于，所述颜料为炭黑、耐晒黄、永固黄、氧化铁黄、联苯胺黄G、酒石黄、永固橙、氧化铁红、永固红、立索红、棕土、黄土、永固紫、群青、钻蓝、酞青蓝、酞青绿、二氧化钛和锦白中的一种或几种；所述颜料分散剂为乙撑双硬脂酸酰胺、武汉超支化HyperC100、德国瓦克AK-1000和科莱恩PE520中的一种或几种。
9.根据权利要求1所述的可擦拭彩色塑料蜡笔材料，其特征在于，所述填料为滑石粉、轻钙、重钙、硅酸铝、氢氧化铝、和高岭土中的一种或几种。
10.根据权利要求1-9任一项所述的可擦拭彩色塑料蜡笔材料在制备彩色塑料蜡笔中的应用，其特征在于，制备所述彩色塑料蜡笔，包括如下步骤：按配比称取各原料，混合，在温度100-150℃条件下熔融，混匀，制成可擦拭彩色塑料蜡笔材料；使用注塑机在120℃温度条件下，注塑制得所述可擦拭蜡笔，冷却成型，即得所述彩色塑料蜡笔。