CN111454597A - Water-resistant paint - Google Patents
Water-resistant paint Download PDFInfo
- Publication number
- CN111454597A CN111454597A CN202010520905.7A CN202010520905A CN111454597A CN 111454597 A CN111454597 A CN 111454597A CN 202010520905 A CN202010520905 A CN 202010520905A CN 111454597 A CN111454597 A CN 111454597A
- Authority
- CN
- China
- Prior art keywords
- parts
- extracting solution
- water
- weight
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a waterproof paint which is prepared from methyl methacrylate, acrylonitrile, polyvinyl chloride resin, alumina, hydroxyethyl cellulose, epoxy resin, n-butyl acetate, dimethylbenzene, carbomer, talcum powder, an ultraviolet absorbent, a traditional Chinese medicine extracting solution, a waterproof agent and a skin care agent in parts by weight: 20-30 parts of methyl methacrylate; 25-40 parts of acrylonitrile; 5-15 parts of polyvinyl chloride resin; 3-7 parts of aluminum oxide; 2-6 parts of hydroxyethyl cellulose; 10-15 parts of epoxy resin; 10-15 parts of n-butyl acetate; 3-7 parts of dimethylbenzene; and 1-5 parts of carbomer. According to the invention, methyl methacrylate and acrylonitrile are taken as main raw materials, and a waterproof agent, epoxy resin, an ultraviolet absorbent, a traditional Chinese medicine extracting solution and a skin care agent are added, so that the waterproof, antistatic, ultraviolet-proof, antibacterial and skin-care properties of the paint can be effectively improved, the service life and the application range of the paint are effectively prolonged, the market competitiveness of the paint is expanded, and the paint conforms to the benefits of enterprises.
Description
Technical Field
The invention relates to the technical field of paint, in particular to waterproof paint.
Background
The paint is a chemical mixture coating which can firmly cover the surface of an object and has the functions of protection, decoration, marking and other special purposes, belongs to an organic chemical high polymer material, a formed coating film belongs to a high polymer compound type, and the paint belongs to a fine chemical product according to the classification of modern current chemical products, but the existing paint has poor waterproof performance and other performances, so that the service life and the use range of the existing paint are reduced, and the benefit of an enterprise is not facilitated, therefore, a waterproof paint is provided.
Disclosure of Invention
The invention aims to provide a waterproof paint to solve the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme: a waterproof paint is composed of methyl methacrylate, acrylonitrile, polyvinyl chloride resin, alumina, hydroxyethyl cellulose, epoxy resin, n-butyl acetate, dimethylbenzene, carbomer, talcum powder, an ultraviolet absorbent, a traditional Chinese medicine extracting solution, a waterproof agent and a skin care agent, and comprises the following components in parts by weight: 20-30 parts of methyl methacrylate; 25-40 parts of acrylonitrile; 5-15 parts of polyvinyl chloride resin; 3-7 parts of aluminum oxide; 2-6 parts of hydroxyethyl cellulose; 10-15 parts of epoxy resin; 10-15 parts of n-butyl acetate; 3-7 parts of dimethylbenzene; 1-5 parts of carbomer; 5-12 parts of talcum powder; 4-10 parts of an ultraviolet absorbent; 3-10 parts of a traditional Chinese medicine extracting solution; 6-12 parts of a waterproof agent; 2-8 parts of a skin care agent.
Preferably, the ultraviolet absorbent consists of ortho-tert-butyl-p-cresol, para-chloro-o-nitroaniline, sodium molybdate, organosilicon modified acrylic resin, bisphenol A diglycidyl ether, ethyl acetate and isopropanol, and comprises the following components in parts by weight: 50-80 parts of o-tert-butyl-p-cresol; 20-40 parts of p-chloro-o-nitroaniline; 10-20 parts of sodium molybdate; 3-7 parts of organic silicon modified acrylic resin; 2-5 parts of bisphenol A diglycidyl ether; 5-12 parts of ethyl acetate; 15-25 parts of isopropanol.
Preferably, the traditional Chinese medicine extracting solution consists of an abelmoschus manihot extracting solution, a mint extracting solution, a ginkgo leaf extracting solution, a clove extracting solution, a camellia extracting solution, a polygonatum extracting solution, a liquorice extracting solution and a folium artemisiae argyi extracting solution, and comprises the following components in parts by weight: 4-10 parts of an abelmoschus manihot flower extracting solution; 6-12 parts of mint extract; 4-8 parts of ginkgo leaf extract; 1-5 parts of clove extracting solution; 3-7 parts of camellia extract; 2-6 parts of polygonatum odoratum extract; 5-10 parts of liquorice extract; 7-15 parts of folium artemisiae argyi extract.
Preferably, the waterproof agent consists of ethylene propylene diene monomer, core-shell structure polymer emulsion, PVC, phenolic resin, quartz sand, talcum powder, Portland cement and water-soluble resin, and the water-soluble resin comprises the following ingredients in percentage by weight: 60-80 parts of nitrile rubber; 3-7 parts of core-shell structure polymer emulsion; 8-15 parts of PVC; 15-25 parts of phenolic resin; 5-10 parts of quartz sand; 2-8 parts of talcum powder; 10-25 parts of Portland cement; 7-12 parts of water-soluble resin.
Preferably, the skin care agent consists of glycerin, saponin essence, a surfactant, essence, collagen, hydroxyethyl cellulose, dibutyl phthalate and deionized water, and the skin care agent comprises the following ingredients in percentage by weight: 15-25 parts of glycerol; 10-20 parts of saponin essence; 13-20 parts of a surfactant; 2-6 parts of essence; 1-5 parts of collagen; 3-10 parts of hydroxyethyl cellulose; 3-8 parts of dibutyl phthalate; 20-50 parts of deionized water.
Preferably, it also includes a preparation method, and the preparation method conveniently comprises the following steps:
A. removing impurities: separately putting polyvinyl chloride resin, alumina, hydroxyethyl cellulose, epoxy resin, carbomer and talcum powder into an impurity removal box for impurity removal treatment;
B. crushing: respectively putting the raw materials after impurity removal into a crusher for crushing treatment;
C. mixing: adding the pulverized raw materials into a mixer according to weight parts, mixing, and adding methyl methacrylate, acrylonitrile, n-butyl acetate, xylene, ultraviolet absorbent, Chinese medicinal extractive solution, water repellent and skin care agent according to weight parts after mixing for 3-8 min;
D. and (3) filtering: putting the mixed solution into a filter box for filtering treatment;
E. filling: putting the filtered solution into a filling machine for filling treatment;
F. and packaging and warehousing after the inspection is qualified.
Preferably, a heater is further arranged in the step C in a matched manner, the heater is a microwave heater, an electromagnetic induction heating heater and a water resistance heater, and meanwhile, the heating temperature is 30-50 ℃.
Preferably, three filter screens are arranged in the filter box in the step D, and the three filter screens are respectively a sponge filter layer, an activated carbon filter layer and a KDF filter layer.
Compared with the prior art, the invention has the following beneficial effects:
according to the invention, methyl methacrylate and acrylonitrile are taken as main raw materials, and a waterproof agent, epoxy resin, an ultraviolet absorbent, a traditional Chinese medicine extracting solution and a skin care agent are added, so that the waterproof, antistatic, ultraviolet-proof, antibacterial and skin-care properties of the paint can be effectively improved, the service life and the application range of the paint are effectively prolonged, the market competitiveness of the paint is expanded, and the paint conforms to the benefits of enterprises.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
A waterproof paint is composed of methyl methacrylate, acrylonitrile, polyvinyl chloride resin, alumina, hydroxyethyl cellulose, epoxy resin, n-butyl acetate, dimethylbenzene, carbomer, talcum powder, an ultraviolet absorbent, a traditional Chinese medicine extracting solution, a waterproof agent and a skin care agent, and comprises the following components in parts by weight: 20-30 parts of methyl methacrylate; 25-40 parts of acrylonitrile; 5-15 parts of polyvinyl chloride resin; 3-7 parts of aluminum oxide; 2-6 parts of hydroxyethyl cellulose; 10-15 parts of epoxy resin; 10-15 parts of n-butyl acetate; 3-7 parts of dimethylbenzene; 1-5 parts of carbomer; 5-12 parts of talcum powder; 4-10 parts of an ultraviolet absorbent; 3-10 parts of a traditional Chinese medicine extracting solution; 6-12 parts of a waterproof agent; 2-8 parts of a skin care agent.
Methyl methacrylate and acrylonitrile are used as main raw materials, and a waterproof agent, epoxy resin, an ultraviolet absorbent, a traditional Chinese medicine extracting solution and a skin care agent are added, so that the waterproof, antistatic, ultraviolet-proof, antibacterial and skin-care properties of the paint can be effectively improved, the service life and the application range of the paint are effectively prolonged, the market competitiveness of the paint is expanded, and the paint accords with the benefits of enterprises.
The ultraviolet absorbent consists of ortho-tert-butyl-p-cresol, p-chloro-o-nitroaniline, sodium molybdate, organic silicon modified acrylic resin, bisphenol A diglycidyl ether, ethyl acetate and isopropanol, and comprises the following components in parts by weight: 50-80 parts of o-tert-butyl-p-cresol; 20-40 parts of p-chloro-o-nitroaniline; 10-20 parts of sodium molybdate; 3-7 parts of organic silicon modified acrylic resin; 2-5 parts of bisphenol A diglycidyl ether; 5-12 parts of ethyl acetate; 15-25 parts of isopropanol.
The traditional Chinese medicine extracting solution consists of an abelmoschus manihot extracting solution, a mint extracting solution, a ginkgo leaf extracting solution, a clove extracting solution, a camellia extracting solution, a polygonatum extracting solution, a liquorice extracting solution and a folium artemisiae argyi extracting solution, and comprises the following components in parts by weight: 4-10 parts of an abelmoschus manihot flower extracting solution; 6-12 parts of mint extract; 4-8 parts of ginkgo leaf extract; 1-5 parts of clove extracting solution; 3-7 parts of camellia extract; 2-6 parts of polygonatum odoratum extract; 5-10 parts of liquorice extract; 7-15 parts of folium artemisiae argyi extract.
The waterproof agent consists of ethylene propylene diene monomer, core-shell structure polymer emulsion, PVC, phenolic resin, quartz sand, talcum powder, Portland cement and water-soluble resin, and the waterproof agent comprises the following ingredients in percentage by weight: 60-80 parts of nitrile rubber; 3-7 parts of core-shell structure polymer emulsion; 8-15 parts of PVC; 15-25 parts of phenolic resin; 5-10 parts of quartz sand; 2-8 parts of talcum powder; 10-25 parts of Portland cement; 7-12 parts of water-soluble resin.
The skin care agent consists of glycerin, saponin essence, surfactant, essence, collagen, hydroxyethyl cellulose, dibutyl phthalate and deionized water, and the skin care agent comprises the following ingredients in percentage by weight: 15-25 parts of glycerol; 10-20 parts of saponin essence; 13-20 parts of a surfactant; 2-6 parts of essence; 1-5 parts of collagen; 3-10 parts of hydroxyethyl cellulose; 3-8 parts of dibutyl phthalate; 20-50 parts of deionized water.
The preparation method is also included, and the preparation method comprises the following steps:
A. removing impurities: separately putting polyvinyl chloride resin, alumina, hydroxyethyl cellulose, epoxy resin, carbomer and talcum powder into an impurity removal box for impurity removal treatment;
B. crushing: respectively putting the raw materials after impurity removal into a crusher for crushing treatment;
C. mixing: adding the pulverized raw materials into a mixer according to weight parts, mixing, and adding methyl methacrylate, acrylonitrile, n-butyl acetate, xylene, ultraviolet absorbent, Chinese medicinal extractive solution, water repellent and skin care agent according to weight parts after mixing for 3-8 min;
D. and (3) filtering: putting the mixed solution into a filter box for filtering treatment;
E. filling: putting the filtered solution into a filling machine for filling treatment;
F. and packaging and warehousing after the inspection is qualified.
And C, a heater is also matched and arranged in the step C, the heater is a microwave heater, an electromagnetic induction heater and a water resistance heater, and meanwhile, the heating temperature is 30-50 ℃.
And D, arranging three filter screens in the filter box in the step D, wherein the three filter screens are respectively a sponge filter layer, an active carbon filter layer and a KDF filter layer.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (8)
1. A water-resistant paint characterized by: the waterproof paint consists of methyl methacrylate, acrylonitrile, polyvinyl chloride resin, alumina, hydroxyethyl cellulose, epoxy resin, n-butyl acetate, xylene, carbomer, talcum powder, an ultraviolet absorbent, a traditional Chinese medicine extracting solution, a waterproof agent and a skin-care agent, and comprises the following components in parts by weight: 20-30 parts of methyl methacrylate; 25-40 parts of acrylonitrile; 5-15 parts of polyvinyl chloride resin; 3-7 parts of aluminum oxide; 2-6 parts of hydroxyethyl cellulose; 10-15 parts of epoxy resin; 10-15 parts of n-butyl acetate; 3-7 parts of dimethylbenzene; 1-5 parts of carbomer; 5-12 parts of talcum powder; 4-10 parts of an ultraviolet absorbent; 3-10 parts of a traditional Chinese medicine extracting solution; 6-12 parts of a waterproof agent; 2-8 parts of a skin care agent.
2. A water-resistant paint according to claim 1, wherein: the ultraviolet absorbent consists of ortho-tert-butyl-p-cresol, p-chloro-o-nitroaniline, sodium molybdate, organic silicon modified acrylic resin, bisphenol A diglycidyl ether, ethyl acetate and isopropanol, and comprises the following components in parts by weight: 50-80 parts of o-tert-butyl-p-cresol; 20-40 parts of p-chloro-o-nitroaniline; 10-20 parts of sodium molybdate; 3-7 parts of organic silicon modified acrylic resin; 2-5 parts of bisphenol A diglycidyl ether; 5-12 parts of ethyl acetate; 15-25 parts of isopropanol.
3. A water-resistant paint according to claim 1, wherein: the traditional Chinese medicine extracting solution is composed of an abelmoschus manihot extracting solution, a mint extracting solution, a ginkgo leaf extracting solution, a clove extracting solution, a camellia extracting solution, a polygonatum extracting solution, a liquorice extracting solution and a folium artemisiae argyi extracting solution, and comprises the following components in parts by weight: 4-10 parts of an abelmoschus manihot flower extracting solution; 6-12 parts of mint extract; 4-8 parts of ginkgo leaf extract; 1-5 parts of clove extracting solution; 3-7 parts of camellia extract; 2-6 parts of polygonatum odoratum extract; 5-10 parts of liquorice extract; 7-15 parts of folium artemisiae argyi extract.
4. A water-resistant paint according to claim 1, wherein: the waterproof agent consists of ethylene propylene diene monomer, core-shell structure polymer emulsion, PVC, phenolic resin, quartz sand, talcum powder, Portland cement and water-soluble resin, and the waterproof agent comprises the following ingredients in percentage by weight: 60-80 parts of nitrile rubber; 3-7 parts of core-shell structure polymer emulsion; 8-15 parts of PVC; 15-25 parts of phenolic resin; 5-10 parts of quartz sand; 2-8 parts of talcum powder; 10-25 parts of Portland cement; 7-12 parts of water-soluble resin.
5. A water-resistant paint according to claim 1, wherein: the skin care agent consists of glycerin, saponin essence, a surfactant, essence, collagen, hydroxyethyl cellulose, dibutyl phthalate and deionized water, and the skin care agent comprises the following ingredients in percentage by weight: 15-25 parts of glycerol; 10-20 parts of saponin essence; 13-20 parts of a surfactant; 2-6 parts of essence; 1-5 parts of collagen; 3-10 parts of hydroxyethyl cellulose; 3-8 parts of dibutyl phthalate; 20-50 parts of deionized water.
6. A water-resistant paint according to claim 1, wherein: the preparation method is also included, and the preparation method comprises the following steps:
A. removing impurities: separately putting polyvinyl chloride resin, alumina, hydroxyethyl cellulose, epoxy resin, carbomer and talcum powder into an impurity removal box for impurity removal treatment;
B. crushing: respectively putting the raw materials after impurity removal into a crusher for crushing treatment;
C. mixing: adding the pulverized raw materials into a mixer according to weight parts, mixing, and adding methyl methacrylate, acrylonitrile, n-butyl acetate, xylene, ultraviolet absorbent, Chinese medicinal extractive solution, water repellent and skin care agent according to weight parts after mixing for 3-8 min;
D. and (3) filtering: putting the mixed solution into a filter box for filtering treatment;
E. filling: putting the filtered solution into a filling machine for filling treatment;
F. and packaging and warehousing after the inspection is qualified.
7. A water-resistant paint according to claim 6, wherein: and C, a heater is also matched and arranged in the step C, the heater is a microwave heater, an electromagnetic induction heating heater and a water resistance heater, and meanwhile, the heating temperature is 30-50 ℃.
8. A water-resistant paint according to claim 6, wherein: and D, arranging three filter screens in the filter box in the step D, wherein the three filter screens are respectively a sponge filter layer, an activated carbon filter layer and a KDF filter layer.