CN111333336A - 一种新型净化空气的负离子玻纤天花板制作工艺 - Google Patents
一种新型净化空气的负离子玻纤天花板制作工艺 Download PDFInfo
- Publication number
- CN111333336A CN111333336A CN202010142607.9A CN202010142607A CN111333336A CN 111333336 A CN111333336 A CN 111333336A CN 202010142607 A CN202010142607 A CN 202010142607A CN 111333336 A CN111333336 A CN 111333336A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- glass
- fiber cotton
- centrifugal
- photocatalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型净化空气的负离子玻纤天花板的制作工艺,所述净化空气的负离子天花板是由负离子光触乳液、玻璃纤维、粉填料、过氧水、过硫酸钾、乳化剂、纯丙烯酸树脂、助剂、羟基粒子粉末制成。本发明制备的净化空气的负离子天花板具有成本低、重量轻、绿色环保、循环利用、可降解以及使用范围广等优点,可用于住宅、展厅、办公等场地装修装潢等用途;本发明还提供其制备方法,成本低,性价比高,科学合理,简单易操作。
Description
技术领域
本发明涉及天花板制作技术领域,特别涉及一种新型负离子玻纤天花板制作工艺。
背景技术
随着社会发展,人们对于生活质量要求越来越高,尤其向往绿色健康的生活,特别对于房子的装修要求也越来越高,但是在豪华装修的背后,存在着严重的环境污染问题,现在装修与家具组装大多数采用到化学粘合剂,在使用过程当中会释放大量的甲醛等有毒气体,以及对以后长时间的居住期间,家具依然会不断释放出大量的有毒气体,将会对人体造成极大的危害。
发明内容
为了解决上述问题,本发明人进行了长时间研究,提供了一种负离子玻纤天花板制作工艺,从而完成了本发明。
一种负离子玻纤天花板制作方法,包括以下步骤:
(1)先将以重量份计25-45%的光触媒、0.05-0.3%的乳化剂和0.01-0.9%的过硫酸钾,再加上35-55%过氧水加入混合罐中搅拌,然后过虑,再将过滤得到的光触媒液体经过直流泵,进入光触媒液体计量罐,进而进入喷雾环;
(2)采用传统离心喷吹法生产玻璃纤维棉,当玻璃液进入旋转的离心盘,在离心作用下被拉伸成玻璃棉纤维时,先将纯丙烯酸树脂已雾化状态均匀喷射在玻璃棉纤维表面;
(3)将步骤(2)得到的表面均匀分布有光触媒液的离心玻纤棉板经集棉机集棉、压缩输送进入烘干炉固化,即得到玻纤棉板(3);
(4)再将步骤(1)中喷雾环内的光触媒液体按照预设流量以雾化状态均匀的喷射在玻纤棉板表面,即得到表面均匀分布有光触媒液体的玻纤棉板(3);
(5)将步骤(4)得到的表面均匀分布有光触媒液的离心玻纤棉板送进入烘干炉固化,即得到含有光触媒液的玻璃棉纤维板;
(6)对步骤(5)得到的玻璃纤维棉板进行将含羟自由基的玻璃毡涂层(1)涂抹在玻纤棉板表面,然后根据不同的装饰花纹进行压缩石膏涂料喷涂,即得到所述的玻璃纤维棉天花板。
其中,所述步骤(1)中,搅拌时间为2小时。
其中,所述在步骤(2)中,预设流量范围为5.0-15kg/分钟。
其中,所述在步骤(2)中,采用传统离心喷吹法生产玻璃棉纤维时,将以重量份计20-30%石英粉、10.6-10.8%长石、9.5-10.5%硼砂、2.0-3.0%方解石、3-6%白云石、9-13%纯碱、20-50%平板玻璃的混合料加入窑炉的熔化池中进行熔化处理,制得玻璃液,玻璃液依次流过漏板、离心机,进入旋转的离心盘。
其中,所述在步骤(3)中,烘干温度范围控制为240-260℃。
其中,所述在步骤(4)中,中预设流量为25-35g每平方。
其中,所述在步骤(4)中,在所述玻纤棉板上进行涂抹光触媒乳液时,保证在无菌的环境进行操作。
其中,所述在步骤(5)中,烘干温度范围控制为185-200℃。其中,所述在步骤(6)中,含羟自由基的玻璃毡涂层是以重量计份42-48%水,与粉填料35-45%,以及助剂1.3-1.6%,和羟基粒子粉末5-7%,纯丙烯酸树脂10-13%的配比制得涂层玻纤毡浆料。
下面对本发明作进一步详细阐述:
一种玻璃棉天花板,它包括玻璃棉板层、玻纤毡层、光触媒液层、石膏涂料层,所述玻璃棉板层由表面均匀分布有环保树脂粘结剂的离心玻璃棉纤维制得,所述的离心玻璃棉纤维与环保树脂粘结剂的质量比为:88-91:9-13,所述的环保树脂粘结剂由环保树脂与添加剂组成并且它们的质量比为420-450:220-280,所述的环保树脂为普通的纯丙烯酸树脂,所述的添加剂的组成成分为硅油、硅烷与过氧水并且它们的质量比为4-5:0.5-1:550-600。
一种如上所述的玻璃棉天花板的制备方法,它包括以下步骤:
(1)先将以重量份计25-45%的光触媒、0.05-0.3%的乳化剂和0.01-0.9%的过硫酸钾,再加上35-55%过氧水加入混合罐中搅拌2小时,然后过虑,再将过滤得到的光触媒液体经过直流泵,进入光触媒液体计量罐,进而进入喷雾环;
(2)再将以重量份计400-480份的环保树脂与200-300份的添加剂加入混合罐中搅拌1小时,然后过滤,再将过滤得到的环保树脂粘结剂经过螺杆泵,进入管道混合器和管道稳压器,进入粘结剂计量罐,进而进入喷雾环;
(3)采用传统离心喷吹法生产玻璃棉纤维,将以重量份计20-30%石英粉、10.6-10.8%长石、9.5-10.5%硼砂、2.0-3.0%方解石、3-6%白云石、9-13%纯碱、20-50%平板玻璃的混合料加入窑炉的熔化池中进行熔化处理,制得玻璃液,玻璃液依次流过漏板、离心机,进入旋转的离心盘,当玻璃液进入旋转的离心盘,在离心作用下被拉伸成玻璃棉纤维时,将步骤(2)中喷雾环内的环保树脂粘结剂按照5.0-15kg/分钟的预设流量以雾化状态均匀的喷射在离心玻璃棉纤维表面,即得到表面均匀分布有环保树脂粘结剂的离心玻璃棉纤维;
(4)将步骤(3)得到的表面均匀分布有光触媒液的离心玻纤棉板经集棉机集棉、压缩输送进入烘干炉固化,即得到玻纤棉板(3);
(5)再将步骤(1)中喷雾环内的光触媒液体按照预设流量以雾化状态均匀的喷射在玻纤棉板表面,即得到表面均匀分布有光触媒液体的玻纤棉板(3);
(6)将步骤(5)得到的表面均匀分布有光触媒液的离心玻纤棉板送进入烘干炉固化,然后根据不同的装饰花纹进行压缩石膏涂料喷涂,即得到含有光触媒液的玻璃棉纤维板;
(7)对步骤(6)得到的玻璃纤维棉板进行将含羟自由基的玻璃毡涂层(1)涂抹在玻纤棉板表面,然后根据不同的装饰花纹进行压缩石膏涂料喷涂,即得到所述的玻璃纤维棉天花板。
其中,所述本发明中的环保树脂为不会释放甲醛等有害物质的树脂。
其中,所述本发明中环保树脂粘结剂(4)采用纯丙烯酸树脂配合相应的添加剂使用,不仅可以使环保树脂粘结剂分布更加均匀,水解效果更好,而且固化后强度更好、耐侯性更强,不会因久置而发软,更适合用于本产品。
通过本发明的一种负离子玻纤天花板制作方法,可以达到以下技术效果:
1.本发明通过天花板自带负氧离子能有效激活空气中的氧气分子,更容易使人体吸收,可以有效预防空调病;
2.本发明中采用的植物负氧离子原液降尘杀菌,减轻二手烟危害的功效,能够有效的去除和中合装修带来的甲醛、苯、甲苯、一氧化碳等有毒气体,保护人类身体健康.;
3.本发明中的天花板质量轻,能减少对建筑物的载荷要求,便于运载和安装,降低安全隐患;
4.本发明可以中和电器带来的高压静电,在其前面形成一层负离子保护层,有效减轻电器产生的高压静电对人体的伤害,同时减少灰尘对电器的损害。
附图说明
图1示出本发明中正面示意图;
图2示出本发明中侧面剖视图。
附图标号说明:
1-含羟自由基的玻璃毡涂层;
2-光触媒乳液层;
3-玻纤棉板;
4-环保树脂粘结剂。
具体实施方式
为了能更好的对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。以下少一个示例性实施例的描述实际上仅仅是说明性的,决不作为对至对本发明及其应用或使用的任何限制。基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
需要注意的是,这里所使用的术语仅是为了描述具体实施方式,而非意图限制根据本申请的示例性实施方式。如在这里所使用的,除非上下文另外明确指出,否则单数形式也意图包括复数形式,此外,还应当理解的是,当在本说明书中使用术语“包含”和/或“包括”时,其指明存在特征、步骤、操作、器件、组件和/或它们的组合。
除非另外具体说明,否则在这些实施例中阐述的部件和步骤的相对布置、数字表达式和数值不限制本发明的范围。同时,应当明白,为了便于描述,附图中所示出的各个部分的尺寸并不是按照实际的比例关系绘制的。对于相关领域普通技术人员已知的技术、方法和设备可能不作详细讨论,但在适当情况下,所述技术、方法和设备应当被视为授权说明书的一部分。在这里示出和讨论的所有示例中,任何具体值应被解释为仅仅是示例性的,而不是作为限制。因此,示例性实施例的其它示例可以具有不同的值。应注意到:相似的标号和字母在下面的附图中表示类似项,因此,一旦某一项在一个附图中被定义,则在随后的附图中不需要对其进行进一步讨论。
在本发明的描述中,需要理解的是,方位词如“前、后、上、下、左、右”、“横向、竖向、垂直、水平”和“顶、底”等所指示的方位或位置关系通常是基于附图所示的方位或位置关系,仅是为了便于描述本发明和简化描述,在未作相反说明的情况下,这些方位词并不指示和暗示所指的装置或元件必须具有特定的方位或者以特定的方位构造和操作,因此不能理解为对本发明保护范围的限制;方位词“内、外”是指相对于各部件本身的轮廓的内外。
为了便于描述,在这里可以使用空间相对术语,如“在……之上”、“在……上方”、“在……上表面”、“上面的”等,用来描述如在图中所示的一个器件或特征与其他器件或特征的空间位置关系。应当理解的是,空间相对术语旨在包含除了器件在图中所描述的方位之外的在使用或操作中的不同方位。例如,如果附图中的器件被倒置,则描述为“在其他器件或构造上方”或“在其他器件或构造之上”的器件之后将被定位为“在其他器件或构造下方”或“在其他器件或构造之下”。因而,示例性术语“在……上方”可以包括“在……上方”和“在……下方”两种方位。该器件也可以其他不同方式定位(旋转90度或处于其他方位),并且对这里所使用的空间相对描述作出相应解释。
此外,需要说明的是,使用“第一”、“第二”等词语来限定零部件,仅仅是为了便于对相应零部件进行区别,如没有另行声明,上述词语并没有特殊含义,因此不能理解为对本发明保护范围的限制。
根据发明的一种新型负离子玻纤天花板制作工艺
在一种优选实施方式中,所述制作工艺包括以下步骤:
(1)先将以重量份计25-45%的光触媒、0.05-0.3%的乳化剂和0.01-0.9%的过硫酸钾,再加上35-55%过氧水加入混合罐中搅拌,然后过虑,再将过滤得到的光触媒液体经过直流泵,进入管道混合器和管道稳压器,进入光触媒液体计量罐,进而进入喷雾环;
(2)采用传统离心喷吹法生产玻璃纤维棉,当玻璃液进入旋转的离心盘,在离心作用下被拉伸成玻璃棉纤维时,先将纯丙烯酸树脂已雾化状态均匀喷射在玻璃棉纤维表面;
(3)将步骤(2)得到的表面均匀分布有光触媒液的离心玻纤棉板经集棉机集棉、压缩输送进入烘干炉固化,即得到玻纤棉板(3);
(4)再将步骤(1)中喷雾环内的光触媒液体按照预设流量以雾化状态均匀的喷射在玻纤棉板表面,即得到表面均匀分布有光触媒液体的玻纤棉板(3);
(5)将步骤(4)得到的表面均匀分布有光触媒液的离心玻纤棉板送进入烘干炉固化,即得到含有光触媒液的玻璃棉纤维板;
(6)对步骤(5)得到的玻璃纤维棉板进行将含羟自由基的玻璃毡涂层(1)涂抹在玻纤棉板表面,然后根据不同的装饰花纹进行压缩石膏涂料喷涂,即得到所述的玻璃纤维棉天花板。
在一种优选实施方式中,所述制作方法还包括以下步骤:一种玻璃棉天花板,它包括玻璃棉板层、玻纤毡层、光触媒液层、石膏涂料层,所述玻璃棉板层由表面均匀分布有环保树脂粘结剂的离心玻璃棉纤维制得,所述的离心玻璃棉纤维与环保树脂粘结剂的质量比为:88-91:9-13,所述的环保树脂粘结剂由环保树脂与添加剂组成并且它们的质量比为420-450:220-280,所述的环保树脂为普通的纯丙烯酸树脂,所述的添加剂的组成成分为硅油、硅烷与过氧水并且它们的质量比为4-5:0.5-1:550-600。
一种如上所述的玻璃棉天花板的制备方法,它包括以下步骤:
(1)先将以重量份计25-45%的光触媒、0.05-0.3%的乳化剂和0.01-0.9%的过硫酸钾,再加上35-55%过氧水加入混合罐中搅拌2小时,然后过虑,再将过滤得到的光触媒液体经过直流泵,进入光触媒液体计量罐,进而进入喷雾环;
(2)再将以重量份计400-480份的环保树脂与200-300份的添加剂加入混合罐中搅拌1小时,然后过滤,再将过滤得到的环保树脂粘结剂经过螺杆泵,进入管道混合器和管道稳压器,进入粘结剂计量罐,进而进入喷雾环;
(3)采用传统离心喷吹法生产玻璃棉纤维,将以重量份计20-30%石英粉、10.6-10.8%长石、9.5-10.5%硼砂、2.0-3.0%方解石、3-6%白云石、9-13%纯碱、20-50%平板玻璃的混合料加入窑炉的熔化池中进行熔化处理,制得玻璃液,玻璃液依次流过漏板、离心机,进入旋转的离心盘,当玻璃液进入旋转的离心盘,在离心作用下被拉伸成玻璃棉纤维时,将步骤(2)中喷雾环内的环保树脂粘结剂按照5.0-15kg/分钟的预设流量以雾化状态均匀的喷射在离心玻璃棉纤维表面,即得到表面均匀分布有环保树脂粘结剂的离心玻璃棉纤维;
(4)将步骤(3)得到的表面均匀分布有光触媒液的离心玻纤棉板经集棉机集棉、压缩输送进入烘干炉固化,即得到玻纤棉板;
(5)再将步骤(1)中喷雾环内的光触媒液体按照预设流量以雾化状态均匀的喷射在玻纤棉板表面,即得到表面均匀分布有光触媒液体的玻纤棉板;
(6)将步骤(5)得到的表面均匀分布有光触媒液的离心玻纤棉板送进入烘干炉固化,然后根据不同的装饰花纹进行压缩石膏涂料喷涂,即得到含有光触媒液的玻璃棉纤维板(3);
(7)对步骤(6)得到的玻璃纤维棉板进行将含羟自由基的玻璃毡涂层(1)涂抹在玻纤棉板表面,然后根据不同的装饰花纹进行压缩石膏涂料喷涂,即得到所述的玻璃纤维棉天花板;
其中,所述本发明中的环保树脂为不会释放甲醛等有害物质的树脂。
其中,所述本发明中环保树脂粘结剂采用纯丙烯酸树脂配合相应的添加剂使用,不仅可以使环保树脂粘结剂分布更加均匀,水解效果更好,而且固化后强度更好、耐侯性更强,不会因久置而发软,更适合用于本产品。
以上结合具体实施方式和范例性实例对本发明进行了详细说明,不过这些说明并不能理解为对本发明的限制。本领域技术人员理解,在不偏离本发明精神和范围的情况下,可以对本发明技术方案及其实施方式进行多种等价替换、修饰或改进,这些均落入本发明的范围内。本发明的保护范围以所附权利要求为准。
Claims (7)
1.一种新型净化空气的负离子玻纤天花板制作工艺,其特征在于,它包括以下步骤:
(1)先将以重量份计25-45%的光触媒、0.05-0.3%的乳化剂和0.01-0.9%的过硫酸钾,再加上35-55%过氧水加入混合罐中搅拌,然后过虑,再将过滤得到的光触媒液体经过直流泵,进入光触媒液体计量罐,进而进入喷雾环;
(2)采用传统离心喷吹法生产玻璃纤维棉,当玻璃液进入旋转的离心盘,在离心作用下被拉伸成玻璃棉纤维时,先将纯丙烯酸树脂已雾化状态均匀喷射在玻璃棉纤维表面;
(3)将步骤(2)得到的表面均匀分布有光触媒液的离心玻纤棉板经集棉机集棉、压缩输送进入烘干炉固化,即得到玻纤棉板(3);
(4)再将步骤(1)中喷雾环内的光触媒液体按照预设流量以雾化状态均匀的喷射在玻纤棉板表面,即得到表面均匀分布有光触媒液体的玻纤棉板(3);
(5)将步骤(4)得到的表面均匀分布有光触媒液的离心玻纤棉板送进入烘干炉固化,即得到含有光触媒液的玻璃棉纤维板;
(6)对步骤(5)得到的玻璃纤维棉板进行将含羟自由基的玻璃毡涂层(1)涂抹在玻纤棉板表面,然后根据不同的装饰花纹进行压缩石膏涂料喷涂,即得到所述的玻璃纤维棉天花板。
2.根据权利要求1所述的制备工艺,其特征在于步骤(1)中,搅拌时间为2小时。
3.根据权利要求1所述的制备工艺,其特征在于步骤(2)中,预设流量范围为5.0-15kg/分钟。
4.根据权利要求1所述的制备工艺,其特征在于步骤(2)中,采用高速离心喷吹法生产玻璃棉纤维棉时,将以重量份计20-30%石英粉、10.6-10.8%长石、9.5-10.5%硼砂、2.0-3.0%方解石、3-6%白云石、9-13%纯碱、20-50%平板玻璃的混合料加入窑炉的熔化池中进行熔化处理,制得玻璃液,玻璃液依次流过漏板、离心机,进入旋转的离心盘。
5.根据权利要求1所述的制备工艺,其特征在于在步骤(3)中,烘干温度范围控制为240-260℃。
6.根据权利要求1所述的制备工艺,其特征在于在步骤(4)中预设流量为25-35g每平方。
7.根据权利要求1所述的制备工艺,其特征在于在步骤(5)中,烘干温度范围控制为185-200℃。