CN111303710A - 一种反射隔热弹性真石漆及其制备方法 - Google Patents
一种反射隔热弹性真石漆及其制备方法 Download PDFInfo
- Publication number
- CN111303710A CN111303710A CN202010256709.3A CN202010256709A CN111303710A CN 111303710 A CN111303710 A CN 111303710A CN 202010256709 A CN202010256709 A CN 202010256709A CN 111303710 A CN111303710 A CN 111303710A
- Authority
- CN
- China
- Prior art keywords
- parts
- stone
- reflective
- paint
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及真石漆技术领域，公开了一种反射隔热弹性真石漆及其制备方法，包括以下重量份的原料：去离子水120‑135份，疏水纤维素2‑4份，分散剂1‑3份，消泡剂0.2‑1.2份，润湿剂0.1‑0.6份，AMP‑95 1‑2份，成膜助剂10‑15份，防腐剂1‑3份，反射隔热颜料50‑60份，纳米空心陶瓷微珠65‑70份，纯丙乳液48‑56份，纯丙弹性乳液48‑56份，天然大理石碎石100‑110份，天然云母片510‑520份，碱溶胀增稠剂3‑6份。该真石漆仿石材效果逼真的同时，具有优异的耐老化性能，抗开裂性好，附着力强、耐水透气，而且反射隔热性能显著，尤其适用于高温日照强烈的地区。
Description
技术领域
本发明涉及真石漆技术领域，特别涉及一种反射隔热弹性真石漆及其制备方法。
背景技术
真石漆是一种装饰效果酷似大理石、花岗岩的厚浆型涂料，主要采用各种颜色的天然石粉配制而成，应用于建筑外墙的仿石材效果。真石漆装饰性强，自然色泽，具有天然石材的质感，各种线格设计，能提供各种立体形状的花纹结构，能从视觉上彰显整个建筑的高雅与庄重之美，是外墙干挂石材最佳替代品。
但是，传统的真石漆抗开裂性能，耐老化性能、附着力、耐水透气性能差，使用寿命低，不具备反射隔热性能，尤其是针对高温日照强烈的地区，例如在我国中部和南方地区，不能达到当下建筑节能发展的要求，限制了其应用发展。
发明内容
本发明要解决的技术问题是提供一种反射隔热弹性真石漆及其制备方法，该真石漆仿石材效果逼真的同时，具有优异的耐老化性能，抗开裂性好，附着力强、耐水透气，而且反射隔热性能显著，尤其适用于高温日照强烈的地区。
为了解决上述技术问题，本发明的技术方案为：
一种反射隔热弹性真石漆，包括以下重量份的原料：去离子水120-135份，疏水纤维素2-4份，分散剂1-3份，消泡剂0.2-1.2份，润湿剂0.1-0.6份，AMP-95 1-2份，成膜助剂10-15份，防腐剂1-3份，反射隔热颜料50-60份，纳米空心陶瓷微珠65-70份，纯丙乳液48-56份，纯丙弹性乳液48-56份，天然大理石碎石100-110份，天然云母片510-520份，碱溶胀增稠剂3-6份。
作为一优选的实施方式，所述的反射隔热弹性真石漆，包括以下重量份的原料：去离子水125.5份，疏水纤维素2.5份，分散剂1.5份，消泡剂0.8份，润湿剂0.5份，AMP-95 1.2份，成膜助剂11份，防腐剂1.5份，反射隔热颜料54份，纳米空心陶瓷微珠69份，纯丙乳液50份，纯丙弹性乳液50份，天然大理石碎石103份，天然云母片515份，碱溶胀增稠剂4.5份。
作为一优选的实施方式，所述疏水纤维素为羟乙基改性疏水纤维素。
作为一优选的实施方式，所述反射隔热颜料采用亨斯迈500反射隔热颜料。
一种所述的反射隔热弹性真石漆的制备方法，包括以下步骤：
步骤1)：将去离子水、疏水纤维素加入分散设备，调整转速为580-650r/s，搅拌时间8-12min；
步骤2)：将转速调整为980-1100r/s，并依次加入分散剂、消泡剂、润湿剂、AMP-95、成膜助剂、防腐剂、反射隔热颜料，搅拌时间28-35min；
步骤3)：将转速调整为280-350r/s，加入纳米空心陶瓷微珠，搅拌时间12-18min；
步骤4)：将转速调整为120-160r/min，依次加入纯丙乳液、纯丙弹性乳液，搅拌时间8-12min；
步骤5)：将转速调整为90-110r/min，依次加入天然大理石碎石、天然云母片、去离子水、碱溶胀增稠剂，搅拌时间18-25min；
步骤6)：经检验、包装，即得成品。
作为一优选的实施方式，制备生产过程中，温度控制不超过60℃。
作为一优选的实施方式，步骤1)与步骤5)中两次去离子水添加用量比为10:1-15:1。
作为一优选的实施方式，所述分散设备采用调速变频分散机和热感不锈钢物料分散缸。
采用上述技术方案，以自交联型丙烯酸共聚乳液为粘结料，通过加入纳米空心陶瓷微珠，红外反射隔热颜料，加工助剂，并利用天然彩砂，优化配伍，并通过相应的加工工艺，调配加料顺序，控制分散过程，制备得到该真石漆；该产品反射隔热性能显著，解决了传统真石漆所不具备的隔热抗裂性能的问题，极大的提高了真石漆的使用寿命，可延长使用年限40％，尤其适用于高温日照强烈的地区，例如我国中部、南方地区，符合建筑节能的要求，可为建筑降低室温5-12℃；综合性能优异，仿石材效果逼真的同时，具有优异的耐老化性能，抗开裂性好，附着力强、耐水透气，满足JG/T 24-2000和JG/235-2014的质量标准。
具体实施方式
下面对本发明的具体实施方式作进一步说明。在此需要说明的是，对于这些实施方式的说明用于帮助理解本发明，但并不构成对本发明的限定。此外，下面所描述的本发明各个实施方式中所涉及的技术特征只要彼此之间未构成冲突就可以相互组合。
对本发明进一步说明，使所属技术领域的技术人员更好的实施本发明。
实施例1
一种反射隔热弹性真石漆，包括以下重量份的原料：去离子水120份，疏水纤维素2份，分散剂1份，消泡剂0.2份，润湿剂0.1份，AMP-95 1份，成膜助剂10份，防腐剂1份，反射隔热颜料50份，纳米空心陶瓷微珠65份，纯丙乳液48份，纯丙弹性乳液48份，天然大理石碎石100份，天然云母片510份，碱溶胀增稠剂3份。
疏水纤维素为羟乙基改性疏水纤维素。
反射隔热颜料采用亨斯迈500反射隔热颜料。
纯丙乳液为自交联型丙烯酸共聚乳液，纯丙弹性乳液为自交联弹性丙烯酸乳液。
一种反射隔热弹性真石漆的制备方法，包括以下步骤：
步骤1)：将去离子水、疏水纤维素加入分散设备，调整转速为580r/min，搅拌时间12min；
步骤2)：将转速调整为980r/min，并依次加入分散剂、消泡剂、润湿剂、AMP-95、成膜助剂、防腐剂、反射隔热颜料，搅拌时间35min；
步骤3)：将转速调整为280r/min，加入纳米空心陶瓷微珠，搅拌时间18min；
步骤4)：将转速调整为120r/min，依次加入纯丙乳液、纯丙弹性乳液，搅拌时间12min；
步骤5)：将转速调整为90r/min，依次加入天然大理石碎石、天然云母片、去离子水、碱溶胀增稠剂，搅拌时间25min；
步骤6)：经检验、包装，即得成品。
制备生产过程中，温度控制不超过60℃。
步骤1)与步骤5)中两次去离子水添加用量比为10:1。
分散设备采用调速变频分散机和热感不锈钢物料分散缸。
实施例2
一种反射隔热弹性真石漆，包括以下重量份的原料：去离子水135份，疏水纤维素4份，分散剂3份，消泡剂1.2份，润湿剂0.6份，AMP-95 2份，成膜助剂15份，防腐剂3份，反射隔热颜料60份，纳米空心陶瓷微珠70份，纯丙乳液56份，纯丙弹性乳液56份，天然大理石碎石110份，天然云母片520份，碱溶胀增稠剂6份。
疏水纤维素为羟乙基改性疏水纤维素。
反射隔热颜料采用亨斯迈500反射隔热颜料。
一种反射隔热弹性真石漆的制备方法，包括以下步骤：
步骤1)：将去离子水、疏水纤维素加入分散设备，调整转速为650r/s，搅拌时间12min；
步骤2)：将转速调整为1100r/s，并依次加入分散剂、消泡剂、润湿剂、AMP-95、成膜助剂、防腐剂、反射隔热颜料，搅拌时间28min；
步骤3)：将转速调整为350r/s，加入纳米空心陶瓷微珠，搅拌时间12min；
步骤4)：将转速调整为160r/min，依次加入纯丙乳液、纯丙弹性乳液，搅拌时间8min；
步骤5)：将转速调整为110r/min，依次加入天然大理石碎石、天然云母片、去离子水、碱溶胀增稠剂，搅拌时间18min；
步骤6)：经检验、包装，即得成品。
制备生产过程中，温度控制不超过60℃。
步骤1)与步骤5)中两次去离子水添加用量比为15:1。
分散设备采用调速变频分散机和热感不锈钢物料分散缸。
实施例3
一种反射隔热弹性真石漆，包括以下重量份的原料：去离子水128份，疏水纤维素3份，分散剂2份，消泡剂0.7份，润湿剂0.4份，AMP-95 1.5份，成膜助剂13份，防腐剂2份，反射隔热颜料55份，纳米空心陶瓷微珠68份，纯丙乳液52份，纯丙弹性乳液52份，天然大理石碎石105份，天然云母片515份，碱溶胀增稠剂4份。
疏水纤维素为羟乙基改性疏水纤维素。
反射隔热颜料采用亨斯迈500反射隔热颜料。
一种反射隔热弹性真石漆的制备方法，包括以下步骤：
步骤1)：将去离子水、疏水纤维素加入分散设备，调整转速为610r/s，搅拌时间9min；
步骤2)：将转速调整为1000r/s，并依次加入分散剂、消泡剂、润湿剂、AMP-95、成膜助剂、防腐剂、反射隔热颜料，搅拌时间30min；
步骤3)：将转速调整为310r/min，加入纳米空心陶瓷微珠，搅拌时间14min；
步骤4)：将转速调整为140r/min，依次加入纯丙乳液、纯丙弹性乳液，搅拌时间11min；
步骤5)：将转速调整为100r/min，依次加入天然大理石碎石、天然云母片、去离子水、碱溶胀增稠剂，搅拌时间20min；
步骤6)：经检验、包装，即得成品。
制备生产过程中，温度控制不超过60℃。
步骤1)与步骤5)中两次去离子水添加用量比为13:1。
分散设备采用调速变频分散机和热感不锈钢物料分散缸。
实施例4
一种反射隔热弹性真石漆，包括以下重量份的原料：去离子水125.5份，疏水纤维素2.5份，分散剂1.5份，消泡剂0.8份，润湿剂0.5份，AMP-95 1.2份，成膜助剂11份，防腐剂1.5份，反射隔热颜料54份，纳米空心陶瓷微珠69份，纯丙乳液50份，纯丙弹性乳液50份，天然大理石碎石103份，天然云母片515份，碱溶胀增稠剂4.5份。
疏水纤维素为羟乙基改性疏水纤维素。
反射隔热颜料采用亨斯迈500反射隔热颜料。
纯丙乳液为自交联型丙烯酸共聚乳液，纯丙弹性乳液为自交联弹性丙烯酸乳液。
一种反射隔热弹性真石漆的制备方法，包括以下步骤：
步骤1)：将去离子水、疏水纤维素加入分散设备，调整转速为600r/s，搅拌时间10min；
步骤2)：将转速调整为1000r/s，并依次加入分散剂、消泡剂、润湿剂、AMP-95、成膜助剂、防腐剂、反射隔热颜料，搅拌时间30min；
步骤3)：将转速调整为300r/s，加入纳米空心陶瓷微珠，搅拌时间15min；
步骤4)：将转速调整为150r/min，依次加入纯丙乳液、纯丙弹性乳液，搅拌时间10min；
步骤5)：将转速调整为100r/min，依次加入天然大理石碎石、天然云母片、去离子水、碱溶胀增稠剂，搅拌时间20min；
步骤6)：经检验、包装，即得成品。
制备生产过程中，温度控制不超过60℃。
步骤1)与步骤5)中两次去离子水添加用量比为10:1-15:1。
分散设备采用调速变频分散机和热感不锈钢物料分散缸。
以上对本发明的实施方式作了详细说明，但本发明不限于所描述的实施方式。对于本领域的技术人员而言，在不脱离本发明原理和精神的情况下，对这些实施方式进行多种变化、修改、替换和变型，仍落入本发明的保护范围内。
Claims (8)
1.一种反射隔热弹性真石漆，其特征在于，包括以下重量份的原料：
去离子水120-135份，疏水纤维素2-4份，分散剂1-3份，消泡剂0.2-1.2份，润湿剂0.1-0.6份，AMP-95 1-2份，成膜助剂10-15份，防腐剂1-3份，反射隔热颜料50-60份，纳米空心陶瓷微珠65-70份，纯丙乳液48-56份，纯丙弹性乳液48-56份，天然大理石碎石100-110份，天然云母片510-520份，碱溶胀增稠剂3-6份。
2.根据权利要求1所述的反射隔热弹性真石漆，其特征在于，包括以下重量份的原料：
去离子水125.5份，疏水纤维素2.5份，分散剂1.5份，消泡剂0.8份，润湿剂0.5份，AMP-95 1.2份，成膜助剂11份，防腐剂1.5份，反射隔热颜料54份，纳米空心陶瓷微珠69份，纯丙乳液50份，纯丙弹性乳液50份，天然大理石碎石103份，天然云母片515份，碱溶胀增稠剂4.5份。
3.根据权利要求1所述的反射隔热弹性真石漆，其特征在于：所述疏水纤维素为羟乙基改性疏水纤维素。
4.根据权利要求1所述的反射隔热弹性真石漆，其特征在于：所述反射隔热颜料采用亨斯迈500反射隔热颜料。
5.一种如权利要求1-4任一项所述的反射隔热弹性真石漆的制备方法，其特征在于，包括以下步骤：
步骤1)：将去离子水、疏水纤维素加入分散设备，调整转速为580-650r/s，搅拌时间8-12min；
步骤2)：将转速调整为980-1100r/s，并依次加入分散剂、消泡剂、润湿剂、AMP-95、成膜助剂、防腐剂、反射隔热颜料，搅拌时间28-35min；
步骤3)：将转速调整为280-350r/s，加入纳米空心陶瓷微珠，搅拌时间12-18min；
步骤4)：将转速调整为120-160r/min，依次加入纯丙乳液、纯丙弹性乳液，搅拌时间8-12min；
步骤5)：将转速调整为90-110r/min，依次加入天然大理石碎石、天然云母片、去离子水、碱溶胀增稠剂，搅拌时间18-25min；
步骤6)：经检验、包装，即得成品。
6.根据权利要求5所述的反射隔热弹性真石漆的制备方法，其特征在于：制备生产过程中，温度控制不超过60℃。
7.根据权利要求5所述的反射隔热弹性真石漆的制备方法，其特征在于：步骤1)与步骤5)中两次去离子水添加用量比为10:1-15:1。
8.根据权利要求5所述的反射隔热弹性真石漆的制备方法，其特征在于：所述分散设备采用调速变频分散机和热感不锈钢物料分散缸。