CN111151229A - Efficient self-cleaning air purifying agent for indoor decoration and preparation method thereof - Google Patents

Efficient self-cleaning air purifying agent for indoor decoration and preparation method thereof Download PDF

Info

Publication number
CN111151229A
CN111151229A CN201911374003.0A CN201911374003A CN111151229A CN 111151229 A CN111151229 A CN 111151229A CN 201911374003 A CN201911374003 A CN 201911374003A CN 111151229 A CN111151229 A CN 111151229A
Authority
CN
China
Prior art keywords
component
parts
purifying agent
air purifying
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201911374003.0A
Other languages
Chinese (zh)
Inventor
吴宪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Zhangrong Communication Technology Co Ltd
Original Assignee
Anhui Zhangrong Communication Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Zhangrong Communication Technology Co Ltd filed Critical Anhui Zhangrong Communication Technology Co Ltd
Priority to CN201911374003.0A priority Critical patent/CN111151229A/en
Publication of CN111151229A publication Critical patent/CN111151229A/en
Withdrawn legal-status Critical Current

Abstract

The invention provides a high-efficiency self-cleaning air purifying agent for indoor decoration and a preparation method thereof, wherein the high-efficiency self-cleaning air purifying agent comprises a component A and a component B in a mass ratio of 1:0.4-1, wherein the component A comprises the following raw materials in parts by weight: 5-8 parts of attapulgite, 6-10 parts of composite biomass, 0.5-1 part of ammonium carbonate, 0.3-0.7 part of composite microorganism and 53-5 parts of HZSM-53; the component B comprises the following raw materials in parts by weight: the composite material comprises, by compounding, 6-9 parts of porous alumina, 0.1-0.3 part of peel pulp, 0.1-0.5 part of sodium percarbonate, 0.3-1 part of plant extract and 1-4 parts of polyether polyol, and by adopting reasonable raw material proportion and process improvement, the utilization rate of active ingredients of raw materials is obviously improved, the carrying and embedding properties among the components are strong, the adsorption efficiency is obviously improved, and the composite material also has excellent antibacterial and insecticidal effects, purifies air, is pleasant in fragrance, good in overall airflow replacement effect, quick in purification effect, long in lasting effect, good in light-contact self-cleaning effect, obviously improved in comprehensive quality and strong in applicability.

Description

Efficient self-cleaning air purifying agent for indoor decoration and preparation method thereof
Technical Field
The invention relates to the technical field of air purifiers, in particular to a high-efficiency self-cleaning air purifier for indoor decoration and a preparation method thereof.
Background
The air purifying agent is a product which is formed by utilizing the adsorption and decomposition principles of natural substances and through modern scientific and technical treatment and has the functions of eliminating harmful gases in the air and removing various peculiar smells.
A plurality of air purifiers are available on the market at present, and the fish and the dragon are mixed. There are several types in general: adsorption type air purifying materials such as activated carbon and bamboo charcoal; masked odor removal products, such as gel cartridges, air fresheners; and decomposed odor removing products, such as an earth-like decomposed air purifying agent and a Fukanghenjia decomposed air purifying agent.
The adsorption type air purifying agent is a purifying product for removing pollutants by utilizing the performances of physical adsorption, chemical adsorption, oxidation, catalytic oxidation, reduction and the like of activated carbon. The covering type odor removal product covers various odors in the air by utilizing the fragrance of aromatic hydrocarbons, so that the odor removal effect is achieved. Many air fresheners do not actually remove odors from the vehicle interior, but merely mask them with a favorable odor type. The decomposition type air purification products are rare in the market, the products are natural ores which have oxidation-reduction reaction with odor molecules in the air under high temperature and negative pressure through a base decomposition complexing technology to directly generate harmless gases such as carbon dioxide, nitrogen, hydrogen and the like, the peculiar smell is thoroughly removed, and solid particles generated after the products are decomposed can be used as flower fertilizers without secondary pollution.
At present, air pollution is increasingly serious, not only outdoors, but also indoors, and air is polluted already, and the world health organization determines indoor air pollution as a dangerous factor which is arranged in the eighth place and threatens human health as early as 2005. With the continuous improvement of the environment protection degree and the living quality of the living room, most people are more and more aware of the importance of the environment protection of the living room. As toxic substances such as formaldehyde, benzene, amine, xylene, TVOC and the like are inevitably emitted in the process of decorating a new house, and the toxic and harmful gases are harmful to human bodies. If people live in the house for a long time or stay in the office of the house, the immunity of people is low, the people can have headache and fever if the people live in the house for a long time, the people can have cancer or induce cardiovascular diseases and other diseases if the people live in the house for a long time. Among the various groups, the injury is greatest, especially for children, the elderly and pregnant women. Therefore, the treatment of various indoor air pollution is rapidly becoming one of the important points of the research of the environmental protection industry.
For example, CN201810094371.9 "a cleaning agent for indoor air prepared from attapulgite", which is an invention disclosed in china, is an invention which is capable of obtaining a highly active cleaning agent for indoor air by selecting natural attapulgite ore and processing the same, then performing a chaos treatment on the processed attapulgite, and then performing a mixing reaction treatment on the processed attapulgite and the processed air cleaner by processing the cleaning agent. Compared with the traditional attapulgite treating agent, the purifying agent has stronger activity, but the adsorption and desorption effects of the purifying agent are still to be improved, and the comprehensive function and the effect are weaker, so that the multifunctional requirements of consumer groups on the purifying agent in various aspects, such as faint scent, nerve calming, antibiosis, disinsection, self-cleaning recycling and the like, are not facilitated, the application of the purifying agent is greatly limited, and the problems are further solved.
Disclosure of Invention
Aiming at the existing problems, the invention provides a high-efficiency self-cleaning air purifying agent for interior decoration and a preparation method thereof, wherein the high-efficiency self-cleaning air purifying agent is prepared by compounding components, adopting reasonable raw material proportion and process improvement, remarkably improving the utilization rate of active ingredients of raw materials, having strong carrying and embedding properties among the components, remarkably improving adsorption efficiency, having excellent antibacterial and insecticidal effects, purifying air, having pleasant fragrance, good overall airflow replacement effect, quick purification effect, long lasting effect, simultaneously having good light-touch self-cleaning effect, remarkably improving comprehensive quality and having strong applicability.
In order to achieve the above object, the present invention adopts the following technical solutions:
an efficient self-cleaning air purifying agent for interior decoration comprises a component A and a component B in a mass ratio of 1:0.4-1, wherein the component A comprises the following raw materials in parts by weight: 5-8 parts of attapulgite, 6-10 parts of composite biomass, 0.5-1 part of ammonium carbonate, 0.3-0.7 part of composite microorganism and 53-5 parts of HZSM-53; the component B comprises the following raw materials in parts by weight: 6-9 parts of porous alumina, 0.1-0.3 part of peel pulp, 0.1-0.5 part of sodium percarbonate, 0.3-1 part of plant extract and 1-4 parts of polyether polyol.
Preferably, the composite biomass is selected from one or more of rice hulls, straws, corn stalks, corn bracts and pine wood chips; the preparation method of the prefabricated biomass comprises the steps of taking materials, crushing the materials into granules, spraying ethanol solution into the granules, carrying out heat treatment at 45-50 ℃ for 10-20min, and introducing NH into the granules3/N2Stirring the mixed gas at 75-95 deg.C for 40-60min, heat treating in superheated steam containing nitrogen for 30-60min, taking out, and granulating in a granulator.
Preferably, the ethanol solution is 45-50 wt% ethanol water solution, the spraying amount is 40 +/-2% of the mass of the granules, the spraying is carried out for 2-3 times, the spraying interval is 5-10min every time, and the uniform mixing is carried out after the spraying is finished each time; introduction of NH3/N2NH in the mixed gas3、N2The volume flow is 0.6-0.8L/h and 0.2-0.4L/h respectively; the content of nitrogen in the superheated steam containing nitrogen is 20 +/-5 vt percent, and the temperature of the superheated steam is 320-350 ℃.
Preferably, the composite microorganism comprises bacillus, candida lipolytica and pseudomonas, the number ratio of the bacillus to the candida lipolytica to the pseudomonas is 1:0.5-1:0-1, and the effective number of the composite microorganism is more than or equal to 1 multiplied by 109One per ml.
Preferably, the peel pulp is selected from one or more of orange, banana, apple, pear, peach and pomegranate, and is prepared by taking waste peel, adding mixed suspension of appropriate amount of nano titanium dioxide and hydroxypropyl β cyclodextrin, crushing, pulping, and aging for 8-12h to obtain peel pulp.
Preferably, the addition amount of the mixed suspension is 15-20% of the mass of the waste pericarp, wherein the mass ratio of the nano titanium dioxide, the hydroxypropyl β cyclodextrin and the water is 1:2-3: 10-15.
Preferably, the plant extract comprises peppermint essential oil, oleuropein and citric acid, and the mass ratio of the peppermint essential oil to the oleuropein to the citric acid is 5:0.3-0.7: 0.5-1.5.
Preferably, the preparation method of the high-efficiency self-cleaning air purifying agent for indoor decoration comprises the following steps:
1) preparation of component A
Taking materials according to parts by weight, adding a proper amount of distilled water into the attapulgite, heating and stirring at 45 ℃ to obtain pasty attapulgite for later use; blending the composite biomass with HZSM-5, firstly carrying out ultrasonic treatment for 10min at 12-15 ℃ and 40-50KHz in a nitrogen atmosphere, and then carrying out gradient temperature rise and ignition at 750 ℃ in the nitrogen atmosphere and 450-; adding prefabricated biomass into pasty attapulgite, stirring at high speed for 10-15min, dissolving ammonium carbonate in water, slowly adding ammonium carbonate under stirring, stirring at low speed for 20-40min, adding composite microorganism, and mixing to obtain component A;
2) preparation of component B
Taking materials according to parts by weight, firstly soaking porous alumina in 70 wt% ethanol solution for 10-15min, then washing with distilled water for drying, dissolving sodium percarbonate in water to prepare solution, then spraying the solution on the porous alumina, and then sending the porous alumina to a nitrogen atmosphere for heat treatment at 125-140 ℃ for 20-30min to obtain a pretreatment material for later use; sequentially adding the plant extract, polyether polyol and peel pulp into the pretreatment material, stirring and mixing at 30-45 ℃, taking out, and performing vacuum drying to obtain a component B for later use, wherein the total stirring time is not less than 30 min;
3) preparation of air purifying agent
Taking the component A and the component B according to the mass ratio, crushing the component B into particles with the particle size of less than 2mm, then uniformly blending the particles with the component A, feeding the particles into a granulator for granulation, drying until the water content is less than 15 wt%, and packaging and sealing.
Preferably, the viscosity of the pasty attapulgite in the step 1) is 900-1200 cP; the high speed stirring rate was 500rpm, and the low speed stirring rate was 60 rpm.
Preferably, the gradient temperature rise in the step 1) is that the temperature is raised to 450 ℃ within 5min, the temperature is preserved for 20-30min, then the temperature is raised to 540 ℃ at the speed of 3 ℃/min, the temperature is preserved for 10-20min, then the temperature is raised to 650 ℃ at the speed of 5 ℃/min, the temperature is preserved for 10-20min, finally the temperature is raised to 750 ℃ at the speed of 10 ℃/min, and the temperature is preserved for 30-60 min.
Due to the adoption of the technical scheme, the invention has the beneficial effects that: the invention obviously improves the utilization rate of the active ingredients of the raw materials by compounding the components and adopting reasonable raw material proportion and process improvement, has strong carrying and embedding performance among the components and obviously improved adsorption efficiency, has excellent antibacterial and insecticidal effects, purifies air, has pleasant fragrance, good whole airflow replacement effect, quick purification effect, long lasting effect, good light-touch self-cleaning effect, obviously improves the comprehensive quality and has strong applicability. After the product is used for a period of time, the product can be placed in a hot air flow at 32-38 ℃ for heat treatment for 3-5h and then is continuously used (the reduction of the harmful gas adsorption rate of the treated secondary product is less than 7%, and the reduction of the antibacterial rate is less than 12%, which is measured by products in examples).
The invention adopts two components for adsorption and purification, the component A takes attapulgite to be matched with composite biomass as a main adsorption main body and a framework, and the space porosity and stability are obviously improved by modifying the biomass and puffing and adjusting the space structure. Besides excellent adsorption and antibacterial effects, the attapulgite component also obviously improves the compatible connection effect with the component B, and has strong airflow transferability of a laminated structure as a filler capable of being connected with a porous framework, thereby being beneficial to the circulation of the whole air essence, and the antibacterial and essential oil components filled during the matching period have stronger purification effect. Meanwhile, the composite microorganism is added, the biochemical dual effects are achieved, the decomposition circulation is accelerated, the purification effect is fast, and the comprehensive efficiency durability is good; the component B takes porous alumina as a main adsorption medium, and then the peel pulp and the plant purification antibacterial component are filled, so that natural fragrance is provided on one hand, a proper breeding environment is provided on the other hand, and the component B and the component A are matched for use, so that the components compensate and promote each other, and the purification effect is stronger.
Detailed Description
In order to make the objects, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention. All other embodiments, which can be derived by a person skilled in the art from the embodiments of the present invention without any inventive step, are within the scope of the present invention.
Example 1:
an efficient self-cleaning air purifying agent for interior decoration comprises a component A and a component B in a mass ratio of 1:0.4, wherein the component A comprises the following raw materials in parts by weight: 8 parts of attapulgite, 6 parts of composite biomass, 0.5 part of ammonium carbonate, 0.5 part of composite microorganism and 53 parts of HZSM-53; the component B comprises the following raw materials in parts by weight: 6 parts of porous alumina, 0.2 part of peel pulp, 0.3 part of sodium percarbonate, 0.6 part of plant extract and 2 parts of polyether polyol.
The composite biomass is selected from one or more of rice hull, straw, corn stalk, corn bract and pine wood dust; the composite microorganism comprises Bacillus, Candida lipolytica, and Pseudomonas in a ratio of 1:0.5:0.5, and the effective number of the composite microorganism is not less than 1 × 109Per ml; the peel pulp is selected from any one or more of orange, banana, apple, pear, peach and pomegranate; the plant extract comprises peppermint essential oil, oleuropein and citric acid, and the mass ratio of the peppermint essential oil to the oleuropein to the citric acid is 5:0.5: 0.5.
The preparation method of the prefabricated biomass comprises the steps of taking materials, crushing the materials into granules, spraying 50 wt% of ethanol aqueous solution (the spraying amount of the ethanol aqueous solution is 40 +/-2% of the mass of the granules), spraying for 2-3 times at an interval of 5-10min every time, uniformly mixing after spraying every time), and carrying out heat treatment at 50 ℃ for 10 min; then NH is introduced into the solution3/N2Mixed gas, NH3、N2The volume flow rates are respectively 0.6L/h and 0.4L/h, stirring treatment is carried out for 60min at 75 ℃, finally heat treatment is carried out for 60min in 320 ℃ superheated water vapor containing 20 +/-5 vt% of nitrogen, and the mixture is taken out and sent into a granulator for granulation.
The preparation method of the peel pulp comprises the steps of firstly taking waste peel, then adding a proper amount of mixed suspension of nano titanium dioxide and hydroxypropyl β cyclodextrin into the waste peel, crushing the waste peel together for pulping, and aging for 8-12 hours to obtain the peel pulp for later use, wherein the addition amount of the mixed suspension is 20% of the mass of the waste peel, and the mass ratio of the nano titanium dioxide to the hydroxypropyl β cyclodextrin to the water is 1:2: 10.
The preparation method of the high-efficiency self-cleaning air purifying agent for interior decoration comprises the following steps:
1) preparation of component A
Taking materials according to parts by weight, adding a proper amount of distilled water into the attapulgite, heating and stirring at 45 ℃ to obtain pasty attapulgite, wherein the viscosity of the pasty attapulgite is 1000cP for later use; blending the composite biomass with HZSM-5, firstly carrying out ultrasonic treatment for 10min at 15 ℃ and 50KHz in a nitrogen atmosphere, and then carrying out gradient temperature rise and ignition at 750 ℃ in the nitrogen atmosphere and 450-; adding prefabricated biomass into pasty attapulgite, stirring at a high speed of 500rpm for 10min, dissolving ammonium carbonate in water, slowly adding the ammonium carbonate under stirring, stirring at a low speed of 60rpm for 40min, adding the compound microorganism, and uniformly mixing to obtain a component A for later use; wherein the gradient temperature rise is specifically that the temperature is raised to 450 ℃ within 5min, the temperature is preserved for 20-30min, then the temperature is raised to 540 ℃ at the speed of 3 ℃/min, the temperature is preserved for 10-20min, then the temperature is raised to 650 ℃ at the speed of 5 ℃/min, the temperature is preserved for 10-20min, finally the temperature is raised to 750 ℃ at the speed of 10 ℃/min, and the temperature is preserved for 30-60 min;
2) preparation of component B
Taking materials according to parts by weight, firstly soaking porous alumina in 70 wt% ethanol solution for 10-15min, then washing with distilled water for drying, dissolving sodium percarbonate in water to prepare solution, then spraying the solution on the porous alumina, and then sending the porous alumina to a nitrogen atmosphere for heat treatment at 140 ℃ for 20min to obtain a pretreatment material for later use; sequentially adding the plant extract, polyether polyol and peel pulp into the pretreatment material, stirring and mixing at 30-45 ℃, taking out, and performing vacuum drying to obtain a component B for later use, wherein the total stirring time is not less than 30 min;
3) preparation of air purifying agent
Taking the component A and the component B according to the mass ratio, crushing the component B into particles with the particle size of less than 2mm, then uniformly blending the particles with the component A, feeding the particles into a granulator for granulation, drying until the water content is less than 15 wt%, and packaging and sealing.
Example 2:
an efficient self-cleaning air purifying agent for interior decoration comprises a component A and a component B in a mass ratio of 1:0.8, wherein the component A comprises the following raw materials in parts by weight: 8 parts of attapulgite, 10 parts of composite biomass, 1 part of ammonium carbonate, 0.5 part of composite microorganism and 55 parts of HZSM-55; the component B comprises the following raw materials in parts by weight: 6 parts of porous alumina, 0.2 part of peel pulp, 0.4 part of sodium percarbonate, 0.5 part of plant extract and 3 parts of polyether polyol.
The composite biomass is selected from one or more of rice hull, straw, corn stalk, corn bract and pine wood dust; the composite microorganism comprises Bacillus, Candida lipolytica, and Pseudomonas in a ratio of 1:1:0.5, and the effective bacteria number of the composite microorganism is not less than 1 × 109Per ml; the peel pulp is selected from any one or more of orange, banana, apple, pear, peach and pomegranate; the plant extract comprises peppermint essential oil, oleuropein and citric acid, and the mass ratio of the peppermint essential oil to the oleuropein to the citric acid is 5:0.3: 1.5.
The preparation method of the prefabricated biomass comprises the steps of taking materials, crushing the materials into granules, spraying 50 wt% of ethanol aqueous solution (the spraying amount of the ethanol aqueous solution is 40 +/-2% of the mass of the granules), spraying for 2-3 times at an interval of 5-10min every time, uniformly mixing after spraying every time), and carrying out heat treatment at 450 ℃ for 20 min; then NH is introduced into the solution3/N2Mixed gas, NH3、N2The volume flow rates are respectively 0.8L/h and 0.2L/h, stirring treatment is carried out for 40min at 95 ℃, finally heat treatment is carried out for 60min in 320 ℃ superheated water vapor containing 20 +/-5 vt% of nitrogen, and the mixture is taken out and sent into a granulator for granulation.
The preparation method of the peel pulp comprises the steps of firstly taking waste peel, then adding a proper amount of mixed suspension of nano titanium dioxide and hydroxypropyl β cyclodextrin into the waste peel, crushing the waste peel together for pulping, and aging for 8-12 hours to obtain the peel pulp for later use, wherein the addition amount of the mixed suspension is 20% of the mass of the waste peel, and the mass ratio of the nano titanium dioxide to the hydroxypropyl β cyclodextrin to the water is 1:3: 15.
The preparation method of the high-efficiency self-cleaning air purifying agent for interior decoration comprises the following steps:
1) preparation of component A
Taking materials according to parts by weight, adding a proper amount of distilled water into the attapulgite, heating and stirring at 45 ℃ to obtain pasty attapulgite, wherein the viscosity of the pasty attapulgite is 1000cP for later use; blending the composite biomass with HZSM-5, firstly carrying out ultrasonic treatment for 10min at 15 ℃ and 40KHz in a nitrogen atmosphere, and then carrying out gradient temperature rise and ignition at 750 ℃ in the nitrogen atmosphere to obtain prefabricated biomass; adding prefabricated biomass into pasty attapulgite, stirring at a high speed of 500rpm for 15min, dissolving ammonium carbonate in water, slowly adding the ammonium carbonate under stirring, stirring at a low speed of 60rpm for 40min, adding the compound microorganism, and uniformly mixing to obtain a component A for later use; wherein the gradient temperature rise is specifically that the temperature is raised to 450 ℃ within 5min, the temperature is preserved for 20-30min, then the temperature is raised to 540 ℃ at the speed of 3 ℃/min, the temperature is preserved for 10-20min, then the temperature is raised to 650 ℃ at the speed of 5 ℃/min, the temperature is preserved for 10-20min, finally the temperature is raised to 750 ℃ at the speed of 10 ℃/min, and the temperature is preserved for 30-60 min;
2) preparation of component B
Taking materials according to parts by weight, firstly soaking porous alumina in 70 wt% ethanol solution for 10-15min, then washing with distilled water for drying, dissolving sodium percarbonate in water to prepare solution, then spraying the solution on the porous alumina, and then sending the porous alumina to a nitrogen atmosphere for heat treatment at 130 ℃ for 30min to obtain a pretreatment material for later use; sequentially adding the plant extract, polyether polyol and peel pulp into the pretreatment material, stirring and mixing at 30-45 ℃, taking out, and performing vacuum drying to obtain a component B for later use, wherein the total stirring time is not less than 30 min;
3) preparation of air purifying agent
Taking the component A and the component B according to the mass ratio, crushing the component B into particles with the particle size of less than 2mm, then uniformly blending the particles with the component A, feeding the particles into a granulator for granulation, drying until the water content is less than 15 wt%, and packaging and sealing.
Example 3:
an efficient self-cleaning air purifying agent for interior decoration comprises a component A and a component B in a mass ratio of 1:0.4, wherein the component A comprises the following raw materials in parts by weight: 6 parts of attapulgite, 6 parts of composite biomass, 0.8 part of ammonium carbonate, 0.7 part of composite microorganism and 53 parts of HZSM-53; the component B comprises the following raw materials in parts by weight: 6 parts of porous alumina, 0.3 part of peel pulp, 0.5 part of sodium percarbonate, 0.6 part of plant extract and 3 parts of polyether polyol.
The composite biomass is selected from one or more of rice hull, straw, corn stalk, corn bract and pine wood dust; the composite microorganism comprises Bacillus, Candida lipolytica, and Pseudomonas in a ratio of 1:0.5:0.5, and the effective number of the composite microorganism is not less than 1 × 109Per ml; the peel pulp is selected from any one or more of orange, banana, apple, pear, peach and pomegranate; the plant extract comprises mint essential oil, oleuropein and citric acid, and the mass ratio of the mint essential oil to the oleuropein to the citric acid is 5:0.7: 1.5.
The preparation method of the prefabricated biomass comprises the steps of taking materials, crushing the materials into granules, spraying 50 wt% of ethanol aqueous solution (the spraying amount of the ethanol aqueous solution is 40 +/-2% of the mass of the granules), spraying for 2-3 times at an interval of 5-10min every time, uniformly mixing after spraying every time), and carrying out heat treatment at 45 ℃ for 20 min; then NH is introduced into the solution3/N2Mixed gas, NH3、N2The volume flow rates are respectively 0.8L/h and 0.2L/h, stirring treatment is carried out for 60min at 85 ℃, finally heat treatment is carried out for 60min in 350 ℃ superheated water vapor containing 20 +/-5 vt% of nitrogen, and the mixture is taken out and sent into a granulator for granulation.
The preparation method of the peel pulp comprises the steps of firstly taking waste peel, then adding a proper amount of mixed suspension of nano titanium dioxide and hydroxypropyl β cyclodextrin into the waste peel, crushing the waste peel together for pulping, and aging for 8-12 hours to obtain the peel pulp for later use, wherein the adding amount of the mixed suspension is 15% of the mass of the waste peel, and the mass ratio of the nano titanium dioxide to the hydroxypropyl β cyclodextrin to the water is 1:3: 10.
The preparation method of the high-efficiency self-cleaning air purifying agent for interior decoration comprises the following steps:
1) preparation of component A
Taking materials according to parts by weight, adding a proper amount of distilled water into the attapulgite, heating and stirring at 45 ℃ to obtain pasty attapulgite, wherein the viscosity of the pasty attapulgite is 1200cP for later use; blending the composite biomass with HZSM-5, firstly carrying out ultrasonic treatment for 10min at 12 ℃ and 50KHz in a nitrogen atmosphere, and then carrying out gradient temperature rise and ignition at 750 ℃ in the nitrogen atmosphere to obtain prefabricated biomass; adding prefabricated biomass into pasty attapulgite, stirring at a high speed of 500rpm for 15min, dissolving ammonium carbonate in water, slowly adding the ammonium carbonate under stirring, stirring at a low speed of 60rpm for 40min, adding the compound microorganism, and uniformly mixing to obtain a component A for later use; wherein the gradient temperature rise is specifically that the temperature is raised to 450 ℃ within 5min, the temperature is preserved for 20-30min, then the temperature is raised to 540 ℃ at the speed of 3 ℃/min, the temperature is preserved for 10-20min, then the temperature is raised to 650 ℃ at the speed of 5 ℃/min, the temperature is preserved for 10-20min, finally the temperature is raised to 750 ℃ at the speed of 10 ℃/min, and the temperature is preserved for 30-60 min;
2) preparation of component B
Taking materials according to parts by weight, firstly soaking porous alumina in 70 wt% ethanol solution for 10-15min, then washing with distilled water for drying, dissolving sodium percarbonate in water to prepare solution, then spraying the solution on the porous alumina, and then sending the porous alumina to a nitrogen atmosphere for heat treatment at 125 ℃ for 30min to obtain a pretreatment material for later use; sequentially adding the plant extract, polyether polyol and peel pulp into the pretreatment material, stirring and mixing at 30-45 ℃, taking out, and performing vacuum drying to obtain a component B for later use, wherein the total stirring time is not less than 30 min;
3) preparation of air purifying agent
Taking the component A and the component B according to the mass ratio, crushing the component B into particles with the particle size of less than 2mm, then uniformly blending the particles with the component A, feeding the particles into a granulator for granulation, drying until the water content is less than 15 wt%, and packaging and sealing.
Example 4:
the efficient self-cleaning air purifying agent for interior decoration comprises a component A and a component B in a mass ratio of 1:1, wherein the component A comprises the following raw materials in parts by weight: 6 parts of attapulgite, 10 parts of composite biomass, 1 part of ammonium carbonate, 0.6 part of composite microorganism and HZSM-55 parts; the component B comprises the following raw materials in parts by weight: 9 parts of porous alumina, 0.3 part of peel pulp, 0.2 part of sodium percarbonate, 1 part of plant extract and 4 parts of polyether polyol.
The composite biomass is selected from one or more of rice hull, straw, corn stalk, corn bract and pine wood dust; the composite microorganism comprises bacillus, candida lipolytica and pseudomonas, and the number of the bacillus, the candida lipolytica and the pseudomonas isThe ratio is 1:1:1, the effective bacteria number of the compound microorganism is more than or equal to 1 multiplied by 109Per ml; the peel pulp is selected from any one or more of orange, banana, apple, pear, peach and pomegranate; the plant extract comprises mint essential oil, oleuropein and citric acid, and the mass ratio of the mint essential oil to the oleuropein to the citric acid is 5:0.5: 1.5.
the preparation method of the prefabricated biomass comprises the steps of taking materials, crushing the materials into granules, spraying 50 wt% of ethanol aqueous solution (the spraying amount of the ethanol aqueous solution is 40 +/-2% of the mass of the granules), spraying for 2-3 times at an interval of 5-10min every time, uniformly mixing after spraying every time), and carrying out heat treatment at 50 ℃ for 10 min; then NH is introduced into the solution3/N2Mixed gas, NH3、N2The volume flow rates are respectively 0.7L/h and 0.3L/h, stirring treatment is carried out for 40min at 95 ℃, finally heat treatment is carried out for 50min in 350 ℃ superheated water vapor containing 20 +/-5 vt% of nitrogen, and the mixture is taken out and sent into a granulator for granulation.
The preparation method of the peel pulp comprises the steps of firstly taking waste peel, then adding a proper amount of mixed suspension of nano titanium dioxide and hydroxypropyl β cyclodextrin into the waste peel, crushing the waste peel together for pulping, and aging for 8-12 hours to obtain the peel pulp for later use, wherein the addition amount of the mixed suspension is 20% of the mass of the waste peel, and the mass ratio of the nano titanium dioxide to the hydroxypropyl β cyclodextrin to the water is 1:2: 10.
The preparation method of the high-efficiency self-cleaning air purifying agent for interior decoration comprises the following steps:
1) preparation of component A
Taking materials according to parts by weight, adding a proper amount of distilled water into the attapulgite, heating and stirring at 45 ℃ to obtain pasty attapulgite, wherein the viscosity of the pasty attapulgite is 1200cP for later use; blending the composite biomass with HZSM-5, firstly carrying out ultrasonic treatment for 10min at 15 ℃ and 50KHz in a nitrogen atmosphere, and then carrying out gradient temperature rise and ignition at 750 ℃ in the nitrogen atmosphere and 450-; adding prefabricated biomass into pasty attapulgite, stirring at a high speed of 500rpm for 15min, dissolving ammonium carbonate in water, slowly adding the ammonium carbonate under stirring, stirring at a low speed of 60rpm for 40min, adding the compound microorganism, and uniformly mixing to obtain a component A for later use; wherein the gradient temperature rise is specifically that the temperature is raised to 450 ℃ within 5min, the temperature is preserved for 20-30min, then the temperature is raised to 540 ℃ at the speed of 3 ℃/min, the temperature is preserved for 10-20min, then the temperature is raised to 650 ℃ at the speed of 5 ℃/min, the temperature is preserved for 10-20min, finally the temperature is raised to 750 ℃ at the speed of 10 ℃/min, and the temperature is preserved for 30-60 min;
2) preparation of component B
Taking materials according to parts by weight, firstly soaking porous alumina in 70 wt% ethanol solution for 10-15min, then washing with distilled water for drying, dissolving sodium percarbonate in water to prepare solution, then spraying the solution on the porous alumina, and then sending the porous alumina to a nitrogen atmosphere for heat treatment at 130 ℃ for 30min to obtain a pretreatment material for later use; sequentially adding the plant extract, polyether polyol and peel pulp into the pretreatment material, stirring and mixing at 30-45 ℃, taking out, and performing vacuum drying to obtain a component B for later use, wherein the total stirring time is not less than 30 min;
3) preparation of air purifying agent
Taking the component A and the component B according to the mass ratio, crushing the component B into particles with the particle size of less than 2mm, then uniformly blending the particles with the component A, feeding the particles into a granulator for granulation, drying until the water content is less than 15 wt%, and packaging and sealing.
Example 5:
an efficient self-cleaning air purifying agent for interior decoration comprises a component A and a component B in a mass ratio of 1:0.7, wherein the component A comprises the following raw materials in parts by weight: 6 parts of attapulgite, 8 parts of composite biomass, 0.8 part of ammonium carbonate, 0.6 part of composite microorganism and 54 parts of HZSM-54; the component B comprises the following raw materials in parts by weight: 7 parts of porous alumina, 0.3 part of peel pulp, 0.4 part of sodium percarbonate, 0.6 part of plant extract and 1 part of polyether polyol.
The composite biomass is selected from one or more of rice hull, straw, corn stalk, corn bract and pine wood dust; the composite microorganism comprises Bacillus, Candida lipolytica, and Pseudomonas in a quantity ratio of 1:0.5:0.2, and the effective bacteria number of the composite microorganism is not less than 1 × 109Per ml; the peel pulp is selected from any one or more of orange, banana, apple, pear, peach and pomegranate; the plant extract comprises peppermint essential oil, oleuropein and citric acid, and the mass ratio of the peppermint essential oil to the oleuropein to the citric acid is 5:0.3: 0.5.
The preparation method of the prefabricated biomass comprises the steps of taking materials, crushing the materials into particlesSpraying 50 wt% ethanol water solution (the spraying amount of the ethanol water solution is 40 + -2% of the mass of the granule, spraying 2-3 times at an interval of 5-10min every time, and uniformly mixing after spraying every time), and heat treating at 50 deg.C for 10 min; then NH is introduced into the solution3/N2Mixed gas, NH3、N2The volume flow rates are respectively 0.7L/h and 0.3L/h, stirring at 75 ℃ for 60min, finally performing heat treatment in 350 ℃ superheated water vapor containing 20 +/-5 vt% of nitrogen for 30min, taking out and feeding into a granulator for granulation.
The preparation method of the peel pulp comprises the steps of firstly taking waste peel, then adding a proper amount of mixed suspension of nano titanium dioxide and hydroxypropyl β cyclodextrin into the waste peel, crushing the waste peel together for pulping, and aging for 8-12 hours to obtain the peel pulp for later use, wherein the adding amount of the mixed suspension is 15% of the mass of the waste peel, and the mass ratio of the nano titanium dioxide to the hydroxypropyl β cyclodextrin to the water is 1:3: 10.
The preparation method of the high-efficiency self-cleaning air purifying agent for interior decoration comprises the following steps:
1) preparation of component A
Taking materials according to parts by weight, adding a proper amount of distilled water into the attapulgite, heating and stirring at 45 ℃ to obtain pasty attapulgite, wherein the viscosity of the pasty attapulgite is 900cP for later use; blending the composite biomass with HZSM-5, firstly carrying out ultrasonic treatment for 10min at 12 ℃ and 50KHz in a nitrogen atmosphere, and then carrying out gradient temperature rise and ignition at 750 ℃ in the nitrogen atmosphere to obtain prefabricated biomass; adding prefabricated biomass into pasty attapulgite, stirring at a high speed of 500rpm for 10min, dissolving ammonium carbonate in water, slowly adding the ammonium carbonate under stirring, stirring at a low speed of 60rpm for 40min, adding the compound microorganism, and uniformly mixing to obtain a component A for later use; wherein the gradient temperature rise is specifically that the temperature is raised to 450 ℃ within 5min, the temperature is preserved for 20-30min, then the temperature is raised to 540 ℃ at the speed of 3 ℃/min, the temperature is preserved for 10-20min, then the temperature is raised to 650 ℃ at the speed of 5 ℃/min, the temperature is preserved for 10-20min, finally the temperature is raised to 750 ℃ at the speed of 10 ℃/min, and the temperature is preserved for 30-60 min;
2) preparation of component B
Taking materials according to parts by weight, firstly soaking porous alumina in 70 wt% ethanol solution for 10-15min, then washing with distilled water for drying, dissolving sodium percarbonate in water to prepare solution, then spraying the solution on the porous alumina, and then sending the porous alumina to a nitrogen atmosphere for heat treatment at 140 ℃ for 30min to obtain a pretreatment material for later use; sequentially adding the plant extract, polyether polyol and peel pulp into the pretreatment material, stirring and mixing at 30-45 ℃, taking out, and performing vacuum drying to obtain a component B for later use, wherein the total stirring time is not less than 30 min;
3) preparation of air purifying agent
Taking the component A and the component B according to the mass ratio, crushing the component B into particles with the particle size of less than 2mm, then uniformly blending the particles with the component A, feeding the particles into a granulator for granulation, drying until the water content is less than 15 wt%, and packaging and sealing.
Example 6:
an efficient self-cleaning air purifying agent for interior decoration comprises a component A and a component B in a mass ratio of 1:0.5, wherein the component A comprises the following raw materials in parts by weight: 6 parts of attapulgite, 7 parts of composite biomass, 0.6 part of ammonium carbonate, 0.5 part of composite microorganism and 54 parts of HZSM-54; the component B comprises the following raw materials in parts by weight: 7 parts of porous alumina, 0.2 part of peel pulp, 0.2 part of sodium percarbonate, 0.8 part of plant extract and 2 parts of polyether polyol.
The composite biomass is selected from one or more of rice hull, straw, corn stalk, corn bract and pine wood dust; the composite microorganism comprises Bacillus, Candida lipolytica, and Pseudomonas in a ratio of 1:0.5:0.5, and the effective number of the composite microorganism is not less than 1 × 109Per ml; the peel pulp is selected from any one or more of orange, banana, apple, pear, peach and pomegranate; the plant extract comprises mint essential oil, oleuropein and citric acid, and the mass ratio of the mint essential oil to the oleuropein to the citric acid is 5:0.3:1.
The preparation method of the prefabricated biomass comprises the steps of taking materials, crushing the materials into granules, spraying 50 wt% of ethanol aqueous solution (the spraying amount of the ethanol aqueous solution is 40 +/-2% of the mass of the granules), spraying for 2-3 times at an interval of 5-10min every time, uniformly mixing after spraying every time), and carrying out heat treatment at 50 ℃ for 20 min; then NH is introduced into the solution3/N2Mixed gas, NH3、N2The volume flow rates are respectively 0.8L/h and 0.2L/h, and the mixture is stirred at 80 ℃ for 60min, and finallyHeat-treating in 320 deg.C superheated steam containing 20 + -5 vt% nitrogen gas for 60min, taking out, and granulating in a granulator.
The preparation method of the peel pulp comprises the steps of firstly taking waste peel, then adding a proper amount of mixed suspension of nano titanium dioxide and hydroxypropyl β cyclodextrin into the waste peel, crushing the waste peel together for pulping, and aging for 8-12 hours to obtain the peel pulp for later use, wherein the addition amount of the mixed suspension is 20% of the mass of the waste peel, and the mass ratio of the nano titanium dioxide to the hydroxypropyl β cyclodextrin to the water is 1:3: 15.
The preparation method of the high-efficiency self-cleaning air purifying agent for interior decoration comprises the following steps:
1) preparation of component A
Taking materials according to parts by weight, adding a proper amount of distilled water into the attapulgite, heating and stirring at 45 ℃ to obtain pasty attapulgite, wherein the viscosity of the pasty attapulgite is 900cP for later use; blending the composite biomass with HZSM-5, firstly carrying out ultrasonic treatment for 10min at 15 ℃ and 50KHz in a nitrogen atmosphere, and then carrying out gradient temperature rise and ignition at 750 ℃ in the nitrogen atmosphere and 450-; adding prefabricated biomass into pasty attapulgite, stirring at a high speed of 500rpm for 15min, dissolving ammonium carbonate in water, slowly adding the ammonium carbonate under stirring, stirring at a low speed of 60rpm for 40min, adding the compound microorganism, and uniformly mixing to obtain a component A for later use; wherein the gradient temperature rise is specifically that the temperature is raised to 450 ℃ within 5min, the temperature is preserved for 20-30min, then the temperature is raised to 540 ℃ at the speed of 3 ℃/min, the temperature is preserved for 10-20min, then the temperature is raised to 650 ℃ at the speed of 5 ℃/min, the temperature is preserved for 10-20min, finally the temperature is raised to 750 ℃ at the speed of 10 ℃/min, and the temperature is preserved for 30-60 min;
2) preparation of component B
Taking materials according to parts by weight, firstly soaking porous alumina in 70 wt% ethanol solution for 10-15min, then washing with distilled water for drying, dissolving sodium percarbonate in water to prepare solution, then spraying the solution on the porous alumina, and then sending the porous alumina to a nitrogen atmosphere for heat treatment at 140 ℃ for 30min to obtain a pretreatment material for later use; sequentially adding the plant extract, polyether polyol and peel pulp into the pretreatment material, stirring and mixing at 30-45 ℃, taking out, and performing vacuum drying to obtain a component B for later use, wherein the total stirring time is not less than 30 min;
3) preparation of air purifying agent
Taking the component A and the component B according to the mass ratio, crushing the component B into particles with the particle size of less than 2mm, then uniformly blending the particles with the component A, feeding the particles into a granulator for granulation, drying until the water content is less than 15 wt%, and packaging and sealing.
The product prepared by the embodiment of the invention is subjected to performance test, and the data is as follows:
wherein, comparative example 1 is based on example 1, using component A alone;
comparative example 2 based on example 1, component B alone;
comparative example 3 is based on example 1, without complex microorganisms and pericarp pulp;
comparative example 4 is based on example 1, without composite biomass and HZSM-5;
Figure BDA0002340432320000161
the above examples are only intended to illustrate the technical solution of the present invention, but not to limit it; although the present invention has been described in detail with reference to the foregoing embodiments, it will be understood by those of ordinary skill in the art that: the technical solutions described in the foregoing embodiments may still be modified, or some technical features may be equivalently replaced; and such modifications or substitutions do not depart from the spirit and scope of the corresponding technical solutions of the embodiments of the present invention.

Claims (10)

1. The efficient self-cleaning air purifying agent for indoor decoration is characterized by comprising a component A and a component B in a mass ratio of 1:0.4-1, wherein the component A comprises the following raw materials in parts by weight: 5-8 parts of attapulgite, 6-10 parts of composite biomass, 0.5-1 part of ammonium carbonate, 0.3-0.7 part of composite microorganism and 53-5 parts of HZSM-53; the component B comprises the following raw materials in parts by weight: 6-9 parts of porous alumina, 0.1-0.3 part of peel pulp, 0.1-0.5 part of sodium percarbonate, 0.3-1 part of plant extract and 1-4 parts of polyether polyol.
2. Indoor according to claim 1The high-efficiency self-cleaning air purifying agent for decoration is characterized in that: the composite biomass is selected from one or more of rice hulls, straws, corn stalks, corn bracts and pine wood chips; the preparation method of the prefabricated biomass comprises the steps of taking materials, crushing the materials into granules, spraying ethanol solution into the granules, carrying out heat treatment at 45-50 ℃ for 10-20min, and then introducing NH into the granules3/N2Stirring the mixed gas at 75-95 deg.C for 40-60min, heat treating in superheated steam containing nitrogen for 30-60min, taking out, and granulating in a granulator.
3. The efficient self-cleaning air purifying agent for interior decoration according to claim 2, which is characterized in that: the ethanol solution is 45-50 wt% ethanol water solution, the spraying amount is 40 +/-2% of the mass of the granules, the spraying is carried out for 2-3 times, the spraying interval is 5-10min every time, and the uniform mixing is carried out after the spraying is finished every time; introduction of said NH3/N2NH in the mixed gas3、N2The volume flow is 0.6-0.8L/h and 0.2-0.4L/h respectively; the content of nitrogen in the superheated steam containing nitrogen is 20 +/-5 vt percent, and the temperature of the superheated steam is 320-350 ℃.
4. The efficient self-cleaning air purifying agent for interior decoration according to claim 1, which is characterized in that: the composite microorganism comprises bacillus, candida lipolytica and pseudomonas, the number ratio of the bacillus to the candida lipolytica to the pseudomonas is 1:0.5-1:0-1, and the effective number of the composite microorganism is more than or equal to 1 multiplied by 109One per ml.
5. The efficient self-cleaning air purifying agent for indoor decoration as claimed in claim 1, wherein the peel pulp is selected from any one or more of, but not limited to, orange, banana, apple, pear, peach and pomegranate, and is prepared by taking waste peel, adding a mixed suspension of a proper amount of nano titanium dioxide and hydroxypropyl β cyclodextrin, crushing and pulping together, and aging for 8-12h to obtain the peel pulp for later use.
6. The efficient self-cleaning air purifying agent for indoor decoration as claimed in claim 5, wherein the addition amount of the mixed suspension is 15-20% of the mass of the waste pericarp, and the mass ratio of the nano titanium dioxide, the hydroxypropyl β cyclodextrin and the water is 1:2-3: 10-15.
7. The efficient self-cleaning air purifying agent for interior decoration according to claim 1, which is characterized in that: the plant extract comprises mint essential oil, oleuropein and citric acid, and the mass ratio of the mint essential oil to the oleuropein to the citric acid is 5:0.3-0.7: 0.5-1.5.
8. The efficient self-cleaning air purifying agent for interior decoration according to any one of claims 1 to 7, which is prepared by the following steps:
1) preparation of component A
Taking materials according to parts by weight, adding a proper amount of distilled water into the attapulgite, heating and stirring at 45 ℃ to obtain pasty attapulgite for later use; blending the composite biomass with HZSM-5, firstly carrying out ultrasonic treatment for 10min at 12-15 ℃ and 40-50KHz in a nitrogen atmosphere, and then carrying out gradient temperature rise and ignition at 750 ℃ in the nitrogen atmosphere and 450-; adding prefabricated biomass into pasty attapulgite, stirring at high speed for 10-15min, dissolving ammonium carbonate in water, slowly adding ammonium carbonate under stirring, stirring at low speed for 20-40min, adding composite microorganism, and mixing to obtain component A;
2) preparation of component B
Taking materials according to parts by weight, firstly soaking porous alumina in 70 wt% ethanol solution for 10-15min, then washing with distilled water for drying, dissolving sodium percarbonate in water to prepare solution, then spraying the solution on the porous alumina, and then sending the porous alumina to a nitrogen atmosphere for heat treatment at 125-140 ℃ for 20-30min to obtain a pretreatment material for later use; sequentially adding the plant extract, polyether polyol and peel pulp into the pretreatment material, stirring and mixing at 30-45 ℃, taking out, and performing vacuum drying to obtain a component B for later use, wherein the total stirring time is not less than 30 min;
3) preparation of air purifying agent
Taking the component A and the component B according to the mass ratio, crushing the component B into particles with the particle size of less than 2mm, then uniformly blending the particles with the component A, feeding the particles into a granulator for granulation, drying until the water content is less than 15 wt%, and packaging and sealing.
9. The efficient self-cleaning air purifying agent for interior decoration according to claim 8, wherein: the viscosity of the pasty attapulgite in the step 1) is 900-1200 cP; the high speed stirring rate was 500rpm, and the low speed stirring rate was 60 rpm.
10. The efficient self-cleaning air purifying agent for interior decoration according to claim 8, wherein: the gradient temperature rise in the step 1) is specifically that the temperature is raised to 450 ℃ within 5min, the temperature is preserved for 20-30min, then the temperature is raised to 540 ℃ at the speed of 3 ℃/min, the temperature is preserved for 10-20min, then the temperature is raised to 600 ℃ and 650 ℃ at the speed of 5 ℃/min, the temperature is preserved for 10-20min, finally the temperature is raised to 750 ℃ at the speed of 10 ℃/min, and the temperature is preserved for 30-60 min.
CN201911374003.0A 2019-12-27 2019-12-27 Efficient self-cleaning air purifying agent for indoor decoration and preparation method thereof Withdrawn CN111151229A (en)