CN111100577A - 一种光固化胶带、制备工艺及其应用 - Google Patents

一种光固化胶带、制备工艺及其应用 Download PDF

Info

Publication number
CN111100577A
CN111100577A CN201911398749.5A CN201911398749A CN111100577A CN 111100577 A CN111100577 A CN 111100577A CN 201911398749 A CN201911398749 A CN 201911398749A CN 111100577 A CN111100577 A CN 111100577A
Authority
CN
China
Prior art keywords
adhesive tape
parts
tape
release film
vitamin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911398749.5A
Other languages
English (en)
Inventor
邵曼
光忠明
周晓南
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Ginnva New Material Technology Co ltd
Original Assignee
Jiangsu Ginnva New Material Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Ginnva New Material Technology Co ltd filed Critical Jiangsu Ginnva New Material Technology Co ltd
Priority to CN201911398749.5A priority Critical patent/CN111100577A/zh
Publication of CN111100577A publication Critical patent/CN111100577A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种光固化胶带及其制备方法，其中光固化胶带包括基材，离型膜，以及涂覆于基材和离型膜之间的胶粘剂层，所述胶粘剂层包括维生素0.2‑0.5份，UV丙烯酸树脂100份，引发剂0.5‑2份。本发明相比传统的热固化，采用更环保、更安全的紫外线固化，经固化后的胶带可产生维生素D，让胶带不仅有粘贴作用，还有助于指甲和皮肤对维生素D的吸收，起到医疗保健作用。

Description

一种光固化胶带、制备工艺及其应用
技术领域
本发明涉及一种光固化胶带，尤其涉及一种光固化胶带及其制备工艺 和应用。
背景技术
目前使用在人体上的运动胶带或者女性常用的指甲贴等，在使用过程中对 人体没有任何的好处，有时候仅仅是为了美观而已。但如果将这些胶带中加入 维生素D，在使用的过程中即可以起到现有的使用效果，还能有助于人体对维 生素D的吸收，促进指甲和骨骼的生长，调节免疫功能。
维生素D(简称VD)是一种脂溶性维生素，乃环戊烷多氢菲类化合物，一 组结构上与固醇有关，功能上可防止佝偻病的维生素，最主要的是维生素D3与 D2。前者由人皮下的7-脱氢胆固醇经紫外线照射而成。后者由植物或酵母中含 有的麦角固醇经紫外线照射而成。维生素D的主要功用是促进小肠粘膜细胞对 钙和磷的吸收。肠中钙离子吸收需要一种钙结合蛋白，1，25-二羟基维生素D3 可诱导此蛋白合成，促进Ca2+吸收，又可促进钙盐的更新及新骨生成，也促进 磷吸收与肾小管细胞对钙、磷的重吸收，故可提高血钙、血磷浓度，有利于新 骨生成和钙化。
目前市场上还未出现将胶带结合维生素D一起应用的产品。
发明内容
本发明的目的在于提供一种光固化胶带及其制备方法，以及具体应用。
为实现前述目的，本发明一种紫外光固化胶带，包括基材，离型膜，以及 涂覆于基材和离型膜之间的胶粘剂层，所述胶粘剂层包括
维生素0.2-0.5份，
UV丙烯酸树脂100份，
引发剂0.5-2份，
以上份数按质量份数配比。
作为本发明的进一步改进，所述维生素包括7-脱氢胆固醇、麦角钙化甾醇 中的一种或两种。
作为本发明的进一步改进，所述引发剂包括1-羟基环己基苯基甲酮，2-羟基 -2-甲基-1-苯基-1-丙酮中的一种或两种。
作为本发明的进一步改进，所述基材为印刷版PVC材质。
作为本发明的进一步改进，所述离型膜为单面离型的PET薄膜。
作为本发明的进一步改进，所述离型膜的离型力为10-15g/25mm。
本发明还提供了一种光固化胶带的制备方法，包括以下步骤：
a、称取UV丙烯酸树脂100份，引发剂0.5-2份，维生素0.2-0.5份置于真 空搅拌器中，搅拌3～5min，待充分搅拌混合均匀后，制得混合胶水；
b、采用辊式手涂法，在基材和离型膜之间倒入混合胶水，调整基材和离型 膜之间的间距至25-50μm，匀速拉动一端，制得未固化的胶带；
c、将所述未固化的胶带放入紫外线固化器中，将能量调节至 2000-2300mJ/cm2，固化时间0.5～1min，然后取出制得光固化胶带。
作为本发明的进一步改进，步骤b中匀速拉动的速度为6～10m/min。
本发明还提供了一种所述的光固化胶带的用途，将光固化胶带贴合于指甲 上，有助于指甲的生长和美容。
本发明还提供了一种所述的光固化胶带的用途，将光固化胶带贴合于皮肤 上，有助于皮肤对维生素D的吸收。
本发明有益效果：
本发明提供了一种光固化胶带及其制备方法，以及具体应用，本发明相比 传统的热固化，采用更环保、更安全的紫外线固化，经固化后的胶带可产生维 生素D，让胶带不仅有粘贴作用，还有助于指甲和皮肤对维生素D的吸收，起 到医疗保健作用。
具体实施方式
以下将结合具体实施例对本发明进行详细描述。
本实施方式提供了一种紫外光固化胶带，包括基材，离型膜，以及涂覆于 基材和离型膜之间的胶粘剂层，所述胶粘剂层包括
维生素0.2-0.5份，
UV丙烯酸树脂100份，
引发剂0.5-2份，
以上份数按质量份数配比。
其中，所述维生素包括7-脱氢胆固醇、麦角钙化甾醇中的一种或两种。所 述引发剂包括1-羟基环己基苯基甲酮，2-羟基-2-甲基-1-苯基-1-丙酮中的一种或 两种。
其中，所述基材为印刷版PVC材质，所述离型膜为单面离型的PET薄膜， 所述离型膜的离型力为10-15g/25mm。
本实施方式还提供了一种光固化胶带的制备方法，包括以下步骤：
a、称取UV丙烯酸树脂100份，引发剂0.5-2份，维生素0.2-0.5份置于真 空搅拌器中，搅拌3～5min，待充分搅拌混合均匀后，制得混合胶水；
b、采用辊式手涂法，在基材和离型膜之间倒入混合胶水，调整基材和离型 膜之间的间距至25-50μm，匀速拉动一端，制得未固化的胶带；
c、将所述未固化的胶带放入紫外线固化器中，将能量调节至 2000-2300mJ/cm2，固化时间0.5～1min，然后取出制得光固化胶带。
其中，步骤b中匀速拉动的速度为6～10m/min。
具体的，下面提供几组制备方法的实施方式，
实施例1
称取7-脱氢胆固醇0.2份，UV丙烯酸树脂100份，1-羟基环己基苯基甲酮 0.5份置于真空搅拌器中，搅拌3min，充分搅拌混合均匀后，制得混合胶水。 采用辊式手涂法，在PVC基材和25μm PET离型膜之间倒入上述混合胶水，调 整基材与离型膜之间的间距至50μm，匀速拉动一端，制得未固化的指甲胶带。 将未固化的指甲胶带放入紫外线固化器中，能量调至2000mJ/cm2，固化0.5min 后得到指甲胶带。
实施例2
称取麦角钙化甾醇0.3份，UV丙烯酸树脂100份，2-羟基-2-甲基-1-苯基-1- 丙酮1份置于真空搅拌器中，搅拌4min，充分搅拌混合均匀后，制得混合胶水。 采用辊式手涂法，在PVC基材和25μm PET离型膜之间倒入上述混合胶水，调 整基材与离型膜之间的间距至25μm，匀速拉动一端，制得未固化的指甲胶带。 将未固化的指甲胶带放入紫外线固化器中，能量调至2200mJ/cm2，固化0.8min 后得到指甲胶带。
实施例3
称取7-脱氢胆固醇0.2份，麦角钙化甾醇0.3份，UV丙烯酸树脂100份， 1-羟基环己基苯基甲酮2份置于真空搅拌器中，搅拌5min，充分搅拌混合均匀 后，制得混合胶水。采用辊式手涂法，在PVC基材和25μm PET离型膜之间倒 入上述混合胶水，调整基材与离型膜之间的间距至25μm，匀速拉动一端，制 得未固化的指甲胶带。将未固化的指甲胶带放入紫外线固化器中，能量调至 2300mJ/cm2，固化1min后得到指甲胶带。
实施例4
称取7-脱氢胆固醇0.5份，UV丙烯酸树脂100份，1-羟基环己基苯基甲酮 1份，2-羟基-2-甲基-1-苯基-1-丙酮1份置于真空搅拌器中，搅拌5min，充分搅 拌混合均匀后，制得混合胶水。采用辊式手涂法，在PVC基材和25μm PET离 型膜之间倒入上述混合胶水，调整基材与离型膜之间的间距至45μm，匀速拉 动一端，制得未固化的指甲胶带。将未固化的指甲胶带放入紫外线固化器中， 能量调至2300mJ/cm2，固化1min后得到指甲胶带。
将通过上述实施例制得的光固化胶带贴合于指甲或者皮肤上，在实现胶带 自身贴合功能的前提下，还能有助于指甲和皮肤对维生素D的吸收，起到医疗 保健的作用。此外将该光固化胶带配合有各种图案的印刷纸，赋予指甲或皮肤 更多的美观。而且本发明采用的主要制作技术是紫外线光固化，相比较传统热 固化更环保、更安全，不会伤害指甲。
应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方 式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见， 本领域技术人员应当将说明书作为一个整体，各实施方式中的技术方案也可 以经适当组合，形成本领域技术人员可以理解的其他实施方式。
上文所列出的一系列的详细说明仅仅是针对本发明的可行性实施方式 的具体说明，它们并非用以限制本发明的保护范围，凡未脱离本发明技艺精 神所作的等效实施方式或变更均应包含在本发明的保护范围。

Claims (10)

1.一种紫外光固化胶带，包括基材，离型膜，以及涂覆于基材和离型膜之间的胶粘剂层，其特征在于：所述胶粘剂层包括
维生素0.2-0.5份，
UV丙烯酸树脂100份，
引发剂0.5-2份，
以上份数按质量份数配比。
2.根据权利要求1所述的光固化胶带，其特征在于：所述维生素包括7-脱氢胆固醇、麦角钙化甾醇中的一种或两种。
3.根据权利要求1所述的光固化胶带，其特征在于：所述引发剂包括1-羟基环己基苯基甲酮，2-羟基-2-甲基-1-苯基-1-丙酮中的一种或两种。
4.根据权利要求1所述的光固化胶带，其特征在于：所述基材为印刷版PVC材质。
5.根据权利要求1所述的光固化胶带，其特征在于：所述离型膜为单面离型的PET薄膜。
6.根据权利要求1所述的光固化胶带，其特征在于：所述离型膜的离型力为10-15g/25mm。
7.一种如权利要求1所述的光固化胶带的制备方法，其特征在于包括以下步骤：
a、称取UV丙烯酸树脂100份，引发剂0.5-2份，维生素0.2-0.5份置于真空搅拌器中，搅拌3～5min，待充分搅拌混合均匀后，制得混合胶水；
b、采用辊式手涂法，在基材和离型膜之间倒入混合胶水，调整基材和离型膜之间的间距至25-50μm，匀速拉动一端，制得未固化的胶带；
c、将所述未固化的胶带放入紫外线固化器中，将能量调节至2000-2300mJ/cm2，固化时间0.5～1min，然后取出制得光固化胶带。
8.根据权利要求7所述的光固化胶带的制备方法，其特征在于：步骤b中匀速拉动的速度为6～10m/min。
9.一种如权利要求1-6中任意一项所述的光固化胶带的用途，其特征在于：将光固化胶带贴合于指甲上，有助于指甲的生长和美容。
10.一种如权利要求1-6中任意一项所述的光固化胶带的用途，其特征在于：将光固化胶带贴合于皮肤上，有助于皮肤对维生素D的吸收。
CN201911398749.5A 2019-12-30 2019-12-30 一种光固化胶带、制备工艺及其应用 Pending CN111100577A (zh)