CN111087866A - 多彩水性涂料 - Google Patents

多彩水性涂料 Download PDF

Info

Publication number
CN111087866A
CN111087866A CN201811242234.1A CN201811242234A CN111087866A CN 111087866 A CN111087866 A CN 111087866A CN 201811242234 A CN201811242234 A CN 201811242234A CN 111087866 A CN111087866 A CN 111087866A
Authority
CN
China
Prior art keywords
agent
water
multicolor
percent
colorful
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811242234.1A
Other languages
English (en)
Inventor
陈潮佐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangmen Jinqiao New Material Co ltd
Original Assignee
Jiangmen Jinqiao New Material Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangmen Jinqiao New Material Co ltd filed Critical Jiangmen Jinqiao New Material Co ltd
Priority to CN201811242234.1A priority Critical patent/CN111087866A/zh
Publication of CN111087866A publication Critical patent/CN111087866A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种多彩水性涂料。其由如下质量百分比的组成分组成：19‑21％的硅丙乳液、4‑6％的聚苯并咪唑、64‑66％的多彩粒子组合物、0.1％的消泡剂、0.2％的多功能中和剂、1.0％的乙二醇、1.5％的成膜助剂、0.2％的增稠剂、0.1％的防腐剂和余量的离子水；其中，所述的多彩粒子组合物由保护胶液和基础漆混合造粒而成。本发明除具有现有多彩水性涂料的基本性能外，还进一步提高了产品的交联密度、粘结力、强度和耐候性能，以及增强了产品的耐老化性能。

Description

多彩水性涂料
技术领域
本发明属于建筑涂料技术领域，具体涉及一种多彩水性涂料。
背景技术
多彩水性涂料是一种仿花岗岩、美化墙体建筑的水性涂料，是由液态的水性树脂提炼包裹成胶状的水性彩色颗粒，并均匀地悬浮在特定的水性乳液中，最终形成了多姿多彩的、颗粒大小随意的高分子液态胶状的共聚物。是一种纯水性、无公害、富有花岗纹理、高分子元素结构的产品，目前被广泛应用于建筑外墙、园林雕塑、建筑廊柱、翻新改造等建筑项目上。但是，由于多彩水性涂料多用在室外，容易造成漆面开裂、脱落等现象，现有多彩水性涂料产品的耐候性和耐老化性能有待提高。
发明内容
本发明的目的在于提供一种多彩水性涂料，以有效解决现有技术的不足之处。
为达到上述目的，本发明采用如下技术方案：
多彩水性涂料，由如下质量百分比的组成分组成：19-21％的硅丙乳液、4-6％的聚苯并咪唑、64-66％的多彩粒子组合物、0.1％的消泡剂、0.2％的多功能中和剂、1.0％的乙二醇、1.5％的成膜助剂、0.2％的增稠剂、0.1％的防腐剂和余量的离子水；其中，所述的多彩粒子组合物由保护胶液和基础漆混合造粒而成。
进一步，所述多彩水性涂料由如下质量百分比的组成分组成：20％的硅丙乳液、5％的聚苯并咪唑、65％的多彩粒子组合物、0.1％的消泡剂、0.2％的多功能中和剂、1.0％的乙二醇、1.5％的成膜助剂、0.2％的增稠剂、0.1％的防腐剂和余量的离子水。
进一步，所述的保护胶液由如下质量百分比的组成分组成：5.5％的RT-1保护胶、0.5％的焦磷酸钠和94％的去离子水。
进一步，所述的基础漆由如下质量百分比的组成分组成：0.3％的分散剂、0.2％的亲油型润湿剂、0.5％的消泡剂、1％的金红石钛白粉、14％的煅烧高岭土、0.7％的多彩纤维素、0.2％的无机膨润土、0.1％的干膜防霉剂、0.8％的乙二醇、1％的成膜助剂、20％的弹性乳液、10％的硅丙乳液、16％的保护胶液、0.2％的多功能中和助剂、0.1％的防腐剂、0.3％的增稠剂和余量的去离子水。
作为优选，所述亲油型润湿剂为阴离子型或非离子型润湿剂。
作为优选，所述基础漆的粘度约为130KU。
作为优选，所述多彩水性涂料的粘度约为70KU。
本发明除具有现有多彩水性涂料的基本性能外，还进一步提高了产品的交联密度、粘结力、强度和耐候性能，以及增强了产品的耐老化性能。
具体实施方式
下面结合具体实施例对本发明进行详细说明。
一、组成分原料来源。
下述的组成分原料来源为：RT-1保护胶采购自上海裕竹公司；亲油型润湿剂为南通晗泰公司的PE-100型润湿剂；多彩纤维素为上海裕竹公司的HM-30/28型产品；消泡剂为上海裕竹公司的YZ-340型产品；干膜防腐剂为上海裕竹公司的YZ-750型产品；多功能中和助剂为上海裕竹公司的YZ-95型产品；增稠剂为上海裕竹公司的YZ-630型HASE增稠剂；防腐剂为上海裕竹公司的YZ-LXE型产品；成膜助剂为伊士曼公司的Texanol成膜助剂；弹性乳液为巴德富公司的RS-9389型弹性乳液；硅丙乳液是上海日出集团的TD-661型硅丙乳液。
二、多彩粒子组合物的组成及制备方法
1、保护胶液的组成和制备方法
保护胶液由质量百分比为5.5％的RT-1保护胶、0.5％的焦磷酸钠和94％的去离子水组成。制备方法为：在每分钟800转的转速下将焦磷酸钠分散到去离子水中，然后加入RT-1保护胶并逐步将转速提高到每分钟2000转至颗粒完全溶解。
2、基础漆的组成和制备方法
基础漆由质量百分比为0.3％的分散剂、0.2％的亲油型润湿剂、0.5％的消泡剂、1％的金红石钛白粉、14％的煅烧高岭土、0.7％的多彩纤维素、0.2％的无机膨润土、0.1％的干膜防霉剂、0.8％的乙二醇、1％的成膜助剂、20％的弹性乳液、10％的硅丙乳液、16％的保护胶液、0.2％的多功能中和助剂、0.1％的防腐剂、0.3％的增稠剂和余量的去离子水组成。其制备方法按现有基础漆制备方法，并需将基础漆粘度控制在130KU左右；基础漆制备完毕后，需静置不少于24小时。
3、多彩粒子组合物的制备方法
将基础漆和保护胶液按1:1的重量比例混合均匀，静置3-5分钟后用筛网或分散盘造粒，得到多彩粒子组合物。
三、多彩水性涂料
1、实施例1-3的多彩水性涂料配方如下表(组成分按质量百分比计算)
组成分 实施例1 实施例2 实施例3
硅丙乳液 19 20 21
聚苯并咪唑 6 5 4
消泡剂 0.1 0.1 0.1
多功能中和剂 0.2 0.2 0.2
乙二醇 1 1 1
成膜助剂 1.5 1.5 1.5
增稠剂 0.2 0.2 0.2
防腐剂 0.1 0.1 0.1
多彩粒子组合物 64 65 66
去离子水 余量 余量 余量
2、上述多彩水性涂料的制备方法为按现有常规方法将硅丙乳液、聚苯并咪唑、消泡剂、多功能中和剂、乙二醇、成膜助剂，防腐剂和离子水以搅拌方法混合均匀后，然后加入多彩粒子组合物并轻轻混合均匀，最后用增稠剂将粘度稳定在70KU左右。
四、性能测试结果
上述实施例1-3的多彩水性涂料符合行业使用要求，耐候性良好，具有良好的施工性。具体性能测试结果如下：
测试项目 测试结果
施工性 喷涂无困难，施工方便
低温储存稳定性，3次 无结块、凝聚及组成物的变化
96小时耐水性 涂层无起鼓、开裂和剥落现象
96小时耐碱性 涂层无起鼓、开裂和剥落现象
粘结强度MPa(标准状态) ≥1.45
粘结强度MPa(浸水后) ≥1.39
耐冲击力 涂层无裂纹、剥落以及明显变形现象

Claims (7)

1.多彩水性涂料，其特征在于，由如下质量百分比的组成分组成：19-21％的硅丙乳液、4-6％的聚苯并咪唑、64-66％的多彩粒子组合物、0.1％的消泡剂、0.2％的多功能中和剂、1.0％的乙二醇、1.5％的成膜助剂、0.2％的增稠剂、0.1％的防腐剂和余量的离子水；其中，所述的多彩粒子组合物由保护胶液和基础漆混合造粒而成。
2.根据权利要求1所述的多彩水性涂料，其特征在于，由如下质量百分比的组成分组成：20％的硅丙乳液、5％的聚苯并咪唑、65％的多彩粒子组合物、0.1％的消泡剂、0.2％的多功能中和剂、1.0％的乙二醇、1.5％的成膜助剂、0.2％的增稠剂、0.1％的防腐剂和余量的离子水。
3.根据权利要求1或2所述的多彩水性涂料，其特征在于，所述的保护胶液由如下质量百分比的组成分组成：5.5％的RT-1保护胶、0.5％的焦磷酸钠和94％的去离子水。
4.根据权利要求3所述的多彩水性涂料，其特征在于，所述的基础漆由如下质量百分比的组成分组成：0.3％的分散剂、0.2％的亲油型润湿剂、0.5％的消泡剂、1％的金红石钛白粉、14％的煅烧高岭土、0.7％的多彩纤维素、0.2％的无机膨润土、0.1％的干膜防霉剂、0.8％的乙二醇、1％的成膜助剂、20％的弹性乳液、10％的硅丙乳液、16％的保护胶液、0.2％的多功能中和助剂、0.1％的防腐剂、0.3％的增稠剂和余量的去离子水。
5.根据权利要求4所述的多彩水性涂料，其特征在于，所述亲油型润湿剂为阴离子型或非离子型润湿剂。
6.根据权利要求5所述的多彩水性涂料，其特征在于，所述基础漆的粘度约为130KU。
7.根据权利要求6所述的多彩水性涂料，其特征在于，所述多彩水性涂料的粘度约为70KU。
CN201811242234.1A 2018-10-24 2018-10-24 多彩水性涂料 Pending CN111087866A (zh)