CN111074574A - Multifunctional after-finishing process for cotton and linen fabric - Google Patents
Multifunctional after-finishing process for cotton and linen fabric Download PDFInfo
- Publication number
- CN111074574A CN111074574A CN201811212103.9A CN201811212103A CN111074574A CN 111074574 A CN111074574 A CN 111074574A CN 201811212103 A CN201811212103 A CN 201811212103A CN 111074574 A CN111074574 A CN 111074574A
- Authority
- CN
- China
- Prior art keywords
- agent
- finishing
- fabric
- cotton
- multifunctional
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a multifunctional after-finishing process of a cotton-linen fabric, which comprises the following process steps: soaking the fabric in finishing agent at 10-18 deg.C for 15-25min, performing warm treatment at 35-45 deg.C for 35-50min, padding at mangle rate of 80-90%, and drying at 30-35 deg.C to 7-8% to dry; putting the fabric dried to 7-8 degrees into a baking machine for baking treatment, wherein the baking temperature is 105 ℃ and 115 ℃, and the machine speed is 40-45 m/min; putting the baked fabric into a setting machine for setting treatment; and (5) rolling the fabric after the sizing is finished. The finishing agent comprises flame-retardant finishing agent MCH-50465-75 g/L, penetrating agent OT 1.5-2.5g/L, cross-linking agent 2-3g/L, softening agent GS-55018-25g/L, three-proofing finishing agent 3M-363325-30 g/L, and chitosan antibacterial agent 4-10g/L and uvioresistant agent C8125-45 g/L. The invention can simultaneously carry out antibacterial, uvioresistant, flame retardant and three-proofing finishing on the fabric, simplifies the production process, reduces the production cost, improves the production efficiency and has good market popularization value.
Description
Technical Field
The invention relates to the field of after-finishing of textile technology, in particular to a multifunctional after-finishing process of cotton and linen fabrics.
Background
With the development of society and economy, the living standard of people is improved, the single-function textile can not meet the requirements of people, and the multifunctional finished textile is more and more accepted and used by people due to the excellent performance.
The multifunctional after-finishing of the fabric is a technological process for improving the appearance and the hand feeling of the fabric, enhancing the wearability or endowing special functions (such as antibiosis, ultraviolet resistance, crease resistance, static resistance, water resistance, oil resistance, stain resistance, flame retardance and the like) by a chemical or physical method, and is a processing process for adding flowers to the fabric.
At present, the multifunctional finishing of the fabric is often a finishing process with a single function, and to endow the fabric with multiple functions, the fabric needs to be finished in sequence through multiple finishing processes, so that the finishing process is complicated, the cost is high, and the efficiency is low.
Disclosure of Invention
The invention aims to overcome the defects and provide a multifunctional after-finishing process for cotton and linen fabrics, which can simultaneously carry out antibacterial, ultraviolet-resistant, flame-retardant and three-proofing finishing on the fabrics, simplify the production process, reduce the production cost and improve the production efficiency.
The invention relates to a multifunctional after-finishing process of a cotton and linen fabric, which comprises the following steps: soaking the fabric in finishing agent at 10-18 deg.C for 15-25min, performing warm treatment at 35-45 deg.C for 35-50min, padding at mangle rate of 80-90%, and drying at 30-35 deg.C to 7-8% to dry; putting the fabric dried to 7-8 degrees into a baking machine for baking treatment, wherein the baking temperature is 105 ℃ and 115 ℃, and the machine speed is 40-45 m/min; setting the baked fabric in setting machine at setting temperature of 105-; winding the fabric after finishing the shaping;
the finishing agent comprises MCH-50465-75 g/L of flame-retardant finishing agent suitable for Chengqiao chemical company, 1.5-2.5g/L of penetrant OT of Zibojie chemical company, 2-3g/L of cross-linking agent, GS-55018-25g/L of softener of Jian national chemical auxiliary factory in Ningbo city, 3M-363325-30 g/L of finishing agent of 3M company, 4-10g/L of chitosan antibacterial agent and 25-45g/L of uvioresistant agent C8125 of Basff company.
Preferably, the finishing agent comprises MCH-50470g/L of flame-retardant finishing agent suitable for Chengqiaojie chemical company, 2g/L of penetrant OT 2g/L of Zibojie chemical company, 2.5g/L of cross-linking agent, GS-55023g/L of softener of national auxiliary chemical factories of Ningbo city, 3M-363327 g/L of three-proof finishing agent, 7g/L of chitosan antibacterial agent and 8135 g/L of uvioresistant agent C8135 of Basff company.
Preferably, the cross-linking agent is polymaleic acid.
Preferably, the padding mode is two-padding and two-rolling.
Preferably, the baking temperature is 110 ℃, and the machine speed is 43 m/min.
Preferably, the setting temperature is 110 ℃, and the machine speed is 52 m/min.
The invention has the beneficial effects that: the invention can simultaneously carry out antibacterial, uvioresistant, flame retardant and three-proofing finishing on the fabric, simplifies the production process, reduces the production cost, improves the production efficiency and has good market popularization value.
Detailed Description
Example 1
A multifunctional after-finishing process for cotton and linen fabrics adopts the following process steps: soaking the fabric in finishing agent at 10 deg.C for 25min, performing warm treatment at 35 deg.C for 50min, performing two-soaking and two-rolling treatment at mangle rate of 80%, and drying at 30 deg.C to 7% dryness; putting the fabric dried to 7 mm into a baking machine for baking treatment, wherein the baking temperature is 105 ℃, and the machine speed is 40 m/min; putting the baked fabric into a setting machine for setting treatment, wherein the setting temperature is 105 ℃, and the locomotive speed is 45 m/min; winding the fabric after finishing the shaping; the finishing agent comprises MCH-50465g/L flame-retardant finishing agent of Chengqiao chemical company, penetrating agent OT 1.5/L of Zibohaijie chemical company, polymaleic acid cross-linking agent 2g/L, softening agent GS-55018 g/L of State national auxiliary chemical factories of Ningbo city, 3M-363325 g/L three-proofing finishing agent, chitosan antibacterial agent 4g/L and uvioresistant agent C8125 g/L of Basff company.
Example 2
A multifunctional after-finishing process for cotton and linen fabrics adopts the following process steps: soaking the fabric in finishing agent at 15 deg.C for 20min, performing heat treatment at 40 deg.C for 40min, performing two-soaking and two-rolling treatment at mangle rate of 85%, and drying at 32 deg.C to 8% dry; putting the fabric dried to 8 degrees into a baking machine for baking treatment, wherein the baking temperature is 110 ℃, and the machine speed is 43 m/min; putting the baked fabric into a setting machine for setting treatment, wherein the setting temperature is 110 ℃, and the machine speed is 52 m/min; winding the fabric after finishing the shaping; the finishing agent comprises MCH-50470g/L of flame-retardant finishing agent suitable for Chengqian chemical company, OT 2g/L of penetrant OT 2g/L of Zibohaijie chemical company, polymaleic acid cross-linking agent 2.5g/L, softener GS-55023g/L of State Jian national auxiliary chemical plant of Ningbo city, 3M-363327 g/L of three-proof finishing agent 3M-363327 g/L of chitosan antibacterial agent 7g/L and uvioresistant agent C8135 g/L of Basff company.
Example 3
A multifunctional after-finishing process for cotton and linen fabrics adopts the following process steps: soaking the fabric in finishing agent at 18 deg.C for 15min, performing heat treatment at 45 deg.C for 35min, performing two-soaking and two-rolling treatment at mangle rate of 90%, and drying at 35 deg.C to 8% dry; putting the fabric dried to 8 degrees into a baking machine for baking treatment, wherein the baking temperature is 115 ℃ and the locomotive speed is 45 m/min; putting the baked fabric into a setting machine for setting treatment, wherein the setting temperature is 115 ℃, and the machine speed is 60 m/min; winding the fabric after finishing the shaping; the finishing agent comprises MCH-50475g/L of flame-retardant finishing agent suitable for Chengqian chemical company, 2.5g/L of penetrating agent OT of Zibohaijie chemical company, 3g/L of polymaleic acid cross-linking agent, GS-55025 g/L of softener of State Jian national auxiliary chemical plant in Ningbo city, 3M-363330 g/L of three-proof finishing agent of Shang 3M company, 10g/L of chitosan antibacterial agent and C8145 g/L of uvioresistant agent of Basff company.
While the preferred embodiments of the present invention have been described in detail, it will be understood by those skilled in the art that the invention is not limited thereto, and that various changes and modifications may be made without departing from the spirit of the invention, and the scope of the appended claims is to be accorded the full range of equivalents.
Claims (6)
1. A multifunctional after-finishing process for cotton and linen fabrics is characterized by comprising the following steps: soaking the fabric in finishing agent at 10-18 deg.C for 15-25min, performing warm treatment at 35-45 deg.C for 35-50min, padding at mangle rate of 80-90%, and drying at 30-35 deg.C to 7-8% to dry; putting the fabric dried to 7-8 degrees into a baking machine for baking treatment, wherein the baking temperature is 105 ℃ and 115 ℃, and the machine speed is 40-45 m/min; setting the baked fabric in setting machine at setting temperature of 105-; winding the fabric after finishing the shaping;
the finishing agent comprises MCH-50465-75 g/L of flame-retardant finishing agent suitable for Chengqiao chemical company, 1.5-2.5g/L of penetrant OT of Zibojie chemical company, 2-3g/L of cross-linking agent, GS-55018-25g/L of softener of Jian national chemical auxiliary factory in Ningbo city, 3M-363325-30 g/L of finishing agent of 3M company, 4-10g/L of chitosan antibacterial agent and 25-45g/L of uvioresistant agent C8125 of Basff company.
2. A multifunctional post-finishing process for ramie cotton fabric as claimed in claim 1, wherein the finishing agent includes MCH-50470g/L, penetration agent OT 2g/L, cross-linking agent 2.5g/L, softening agent GS-55023g/L of domestic chemical auxiliary factory, Ningbo city , three-proofing finishing agent 3M-363327 g/L, chitosan antibacterial agent 7g/L, and uvioresistant agent C8135 g/L.
3. The multifunctional post-finishing process for cotton and linen fabrics as claimed in claims 1 and 2, characterized in that the cross-linking agent is polymaleic acid.
4. The multifunctional post-finishing process of cotton and linen fabrics as claimed in claims 1-3, wherein the padding mode is two-padding and two-rolling.
5. The multifunctional post-finishing process of cotton and linen fabrics as claimed in claims 1-4, wherein the baking temperature is 110 ℃ and the machine speed is 43 m/min.
6. The multifunctional post-finishing process of cotton and linen fabrics as claimed in claims 1-5, wherein the setting temperature is 110 ℃, and the machine speed is 52 m/min.