CN102733186B - Anti-bacterial and anti-wrinkling finishing method for cotton fabric - Google Patents
Anti-bacterial and anti-wrinkling finishing method for cotton fabric Download PDFInfo
- Publication number
- CN102733186B CN102733186B CN 201210251412 CN201210251412A CN102733186B CN 102733186 B CN102733186 B CN 102733186B CN 201210251412 CN201210251412 CN 201210251412 CN 201210251412 A CN201210251412 A CN 201210251412A CN 102733186 B CN102733186 B CN 102733186B
- Authority
- CN
- China
- Prior art keywords
- cotton fabric
- bacterial
- sodium
- body lotion
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides an anti-bacterial and anti-wrinkling finishing method for cotton fabric, comprising the following steps of: dissolving catalyst, and equimolar 2, 2, 6, 6-tetramethyl-4-pipradrol and butanetetracarboxylic acid in water, so that finishing bath foam can be formed; and soaking the cotton fabric in the finishing bath foam, treating the cotton fabric by the working procedures such as rolling and baking, soaping, washing by water, drying, halogenating and drying, wherein the catalyst is one of the sodium dihydrogen phosphate, disodium hydrogen phosphate, sodium polyphosphate and sodium hypophosphite, the halogenating treatment comprises the step of soaking the dried cotton fabric in active halogen-containing solution, and the drying temperature is 150-200DEG C. The cotton fabric which is finished by the method in an anti-bacterial and anti-wrinkling finishing way has the dual performances such as bacterial resistance and wrinkling resistance, is high in anti-bacterial efficiency, good in anti-wrinkling performance, and free from formaldehyde release.
Description
Technical field
The invention belongs to the weaving production technical field, be specifically related to the antibiotic of a kind of COTTON FABRIC and wrinkle proofing method.
Background technology
COTTON FABRIC enjoys people to favor because it has the multiple good wearability such as softness, comfortable, ventilative, good hygroscopicity.But COTTON FABRIC has inferior resistance to microorganism, can adsorb the hot humid medium that human body distributes when wearing, and for the breeding of microorganism provides good environment, thereby causes fabric to produce bad smell, even discolour, and mechanical strength reduces; In addition, COTTON FABRIC is subjected to External Force Acting in wearing process, relative displacement can occur in cellulose molecular chain or its fundamental structural unit, and original hydrogen bond is opened, and generates new hydrogen bond, after external force is eliminated, creep can occur, excessive in external force, in the action time long situation, permanent sex change and wrinkle just appear, the aesthetic property of impact dress.Therefore, COTTON FABRIC being carried out antibiotic and crease resistant functions arrangement is very important.
At present, prior art adopts traditional N-methylol amide resinoid as crease proofing agent usually, although the durable anti-wrinkle effect of this finishing agent is good, but the shortcomings such as the fabric of wherethrough reason exists, and strength loss is serious, yellowing and burst size of methanal are large, and deposit with wearing process in, also harmful formaldehyde be can constantly discharge, human skin and respiratory mucosa stimulated, in addition carcinogenic.Along with growth in the living standard, people more pay attention to the functional of clothes, only no longer possess competitive advantage through single textiles antibiotic or the crease resistant functions arrangement.Patent 200510123828 discloses a kind of wrinkle proofing method of color cotton fabric, adopts N-methylol amide resinoid as crease proofing agent; Although patent 200610119085 and patent 200810184879 adopt polybasic carboxylic acid class formaldehydeless finishing agent, only limit to single wrinkle proofing; Patent 00117001 discloses a kind of production method of antibiotic, crease resistant fabric, but the fabric of being processed by this method can discharge free formaldehyde; The 7th page to the 9th page of Shandong Textile science and technology the 5th phase of calendar year 2001 discloses a kind of polybasic carboxylic acid (citric acid and tartaric acid) and shitosan to the wrinkle resistant and antibiotic finish of COTTON FABRIC, but process COTTON FABRIC with shitosan as antiseptic, can affect Fabric Style, make the fabric face feel coarse, and this patent is not announced its anti-microbial property test effect data.
Summary of the invention
The defects that the applicant exists for Cotton Fabric method in the prior art, a kind of Anti-bacterial and Crease method of COTTON FABRIC is provided, and the COTTON FABRIC of putting in order by the method possesses antibiotic and wrinkle resistant dual property simultaneously, and antimicrobial efficiency is high, crease resistance is good, and formaldehydeless release.
Technical scheme of the present invention is as follows:
A kind of Anti-bacterial and Crease method of COTTON FABRIC, first with catalyst, equimolar 2,2,6,6-tetramethyl-4-piperidine alcohols and BTCA composition arrangement soluble in water body lotion, and COTTON FABRIC be impregnated in the described arrangement body lotion; Then through padding, preliminary drying and bake operation described COTTON FABRIC is processed, at last to soap through the described COTTON FABRIC that bakes processing, wash, oven dry, halogenation, again oven dry; Described catalyst is a kind of in sodium dihydrogen phosphate, sodium hydrogen phosphate, sodium polyphosphate, the sodium hypophosphite, and described halogenation treatment will be for impregnated in through the COTTON FABRIC of described drying and processing in sodium chlorate, calcium hypochlorite or the sodium hypobromite solution.
Its further technical scheme is:
In described arrangement body lotion, the mass percentage concentration of described catalyst is 0~10%.
In described arrangement body lotion, described 2,2,6, the mass percentage concentration of 6-tetramethyl-4-piperidine alcohols is 1~10%.
The described temperature that bakes processing is 150~200 ℃, and the time is 30~300s.
Described clorox, calcium hypochlorite, sodium hypobromite solution quality percentage concentration are respectively 0.01~1%.
Useful technique effect of the present invention is:
The present invention is first with catalyst, equimolar 2,2,6,6-tetramethyl-4-piperidine alcohols and BTCA composition arrangement soluble in water body lotion, and COTTON FABRIC be impregnated in the described arrangement body lotion; BTCA (BTCA) is in curing treatment process, dehydration forms cyclic acid anhydride under high temperature (150~200 ℃) condition, and further with 2,2, hydroxyl generation esterification on 6,6-tetramethyl-4-piperidine alcohols (TMP) and the large molecule of COTTON FABRIC fiber forms covalent cross-linking; In the halogenation operation, in 2,2,6 of the above-mentioned cross-linking reaction of process, the upper oxidisability halogen atom of introducing of 6-tetramethyl-4-piperidine alcohols (TMP) generates a kind of halogen amines with antibacterial functions at last.In addition and since BTCA (BTCA) this as a kind of good formaldehyde-free crease-proofing finishing agent, thereby make the COTTON FABRIC through arrangement possess simultaneously antibiotic and wrinkle resistant dual property, antimicrobial efficiency height, crease resistance is good, and formaldehydeless release.Anti-microbial property and crease recovery test show, the COTTON FABRIC of putting in order by the inventive method is with after inoculated bacteria contacts, sterilizing rate to staphylococcus aureus in 5min reaches 100%, in 10min to Escherichia coli O 157: the sterilizing rate of H7 reaches 83.25%, compare and be significantly increased before creasy recovery angle and the arrangement, be elevated to 251.6 by 111.7.
Description of drawings
Fig. 1 is the chemical principle figure (cross-linking reaction, halogenation) of the inventive method.
The specific embodiment
Below in conjunction with accompanying drawing, and by embodiment the present invention is specifically described.
As shown in Figure 1, under high temperature (150~200 ℃) condition, BTCA (BTCA) dehydration forms cyclic acid anhydride, further with 2,2,6, esterification occurs and forms covalent cross-linking in the hydroxyl (Cell-OH) on 6-tetramethyl-4-piperidine alcohols (TMP) and the large molecule of COTTON FABRIC fiber, at last by halogenation (take active chlorine as example), in 2,2 of the above-mentioned cross-linking reaction of process, 6, the upper oxidisability chlorine atom of introducing of 6-tetramethyl-4-piperidine alcohols (TMP), generation has the halogen amines of antibacterial functions, thereby makes COTTON FABRIC possess simultaneously antibiotic and wrinkle resistant dual property.
Embodiment 1
With sodium dihydrogen phosphate, equimolar 2,2,6,6-tetramethyl-4-piperidine alcohols (TMP) and BTCA (BTCA) composition arrangement soluble in water body lotion, wherein, the mass percentage concentration of sodium dihydrogen phosphate is 10%, 2, the mass percentage concentration of 2,6,6-tetramethyl-4-piperidine alcohols (TMP) is 1%; Untrimmed COTTON FABRIC sample (available from Zhejiang Guandong Dyeing and Garment Co., Ltd.) be impregnated in the described arrangement body lotion, and adopt two two modes of rolling of soaking on padding machine, it to be carried out pressure rolling, time 10min, pick-up rate 100%, take out COTTON FABRIC, in 80 ℃ of preliminary drying 10min in dryer, then in baker, bake 300s in 150 ℃; To soap through the above-mentioned COTTON FABRIC that bakes processing (COTTON FABRIC that will put in order is washed 15min in commercially available cleaning solution), then wash and dry, it is (pH12) among 0.01% the liquor natrii hypochloritis that COTTON FABRIC after will drying at last impregnated in mass percentage concentration, take out COTTON FABRIC behind the 1h, in dryer, dry 2h in 45 ℃.
Embodiment 2
With sodium hydrogen phosphate, equimolar 2,2,6,6-tetramethyl-4-piperidine alcohols (TMP) and BTCA (BTCA) composition arrangement soluble in water body lotion, wherein, the mass percentage concentration of sodium hydrogen phosphate is 5%, 2, the mass percentage concentration of 2,6,6-tetramethyl-4-piperidine alcohols (TMP) is 5%; Untrimmed COTTON FABRIC sample (the same) be impregnated in the described arrangement body lotion, and adopt two two modes of rolling of soaking on padding machine, it to be carried out pressure rolling, time 10min, pick-up rate 100%, take out COTTON FABRIC, in 90 ℃ of preliminary drying 6min in dryer, then in baker, bake 210s in 180 ℃; To soap through the above-mentioned COTTON FABRIC that bakes processing (COTTON FABRIC that will put in order is washed 15min in commercially available cleaning solution), then wash and dry, it is (pH7.0) among 0.5% the liquor natrii hypochloritis that COTTON FABRIC after will drying at last impregnated in mass percentage concentration, take out COTTON FABRIC behind the 1h, in dryer, dry 2h in 45 ℃.
Embodiment 3
With sodium polyphosphate, equimolar 2,2,6,6-tetramethyl-4-piperidine alcohols (TMP) and BTCA (BTCA) composition arrangement soluble in water body lotion, wherein, the mass percentage concentration of sodium polyphosphate is 5%, 2, the mass percentage concentration of 2,6,6-tetramethyl-4-piperidine alcohols (TMP) is 5%; Untrimmed COTTON FABRIC sample (the same) be impregnated in the described arrangement body lotion, and adopt two two modes of rolling of soaking on padding machine, it to be carried out pressure rolling, time 10min, pick-up rate 100%, take out COTTON FABRIC, in 100 ℃ of preliminary drying 5min in dryer, then in baker, bake 120s in 180 ℃; To soap through the above-mentioned COTTON FABRIC that bakes processing (COTTON FABRIC that will put in order is washed 15min in commercially available cleaning solution), then wash and dry, it is (pH7) in 0.5% the calcium hypochlorite solution that COTTON FABRIC after will drying at last impregnated in mass percentage concentration, take out COTTON FABRIC behind the 1h, in dryer, dry 2h in 45 ℃.
Embodiment 4
With sodium hypophosphite, equimolar 2,2,6,6-tetramethyl-4-piperidine alcohols (TMP) and BTCA (BTCA) composition arrangement soluble in water body lotion, wherein, the mass percentage concentration of sodium hypophosphite is 1%, 2, the mass percentage concentration of 2,6,6-tetramethyl-4-piperidine alcohols (TMP) is 10%; Untrimmed COTTON FABRIC sample (the same) be impregnated in the described arrangement body lotion, and adopt two two modes of rolling of soaking on padding machine, it to be carried out pressure rolling, time 10min, pick-up rate 100%, take out COTTON FABRIC, in 120 ℃ of preliminary drying 1min in dryer, then in baker, bake 30s in 200 ℃; To soap through the above-mentioned COTTON FABRIC that bakes processing (COTTON FABRIC that will put in order is washed 15min in commercially available cleaning solution), then wash and dry, it is (pH12) in 1% the sodium hypobromite solution that COTTON FABRIC after will drying at last impregnated in mass percentage concentration, take out COTTON FABRIC behind the 1h, in dryer, dry 2h in 45 ℃.
Antibiotic and the crease resistance test of COTTON FABRIC:
Anti-microbial property test: test according to revising the described method of AATCC100-1999 anti-microbial property testing standard;
Crease recovery property testing: test according to the described method of GB/T3819-1997 " the restorative mensuration of textile fabric folding line is replied horn cupping ".
Get with above-described embodiment 1~embodiment 4 in identical COTTON FABRIC sample, according to embodiment 2 described methods this COTTON FABRIC sample is carried out Anti-bacterial and Crease, but without halogenation treatment.This COTTON FABRIC and embodiment 2 gained COTTON FABRIC without halogenation treatment are carried out the anti-microbial property test, and test result sees Table 1.
The test of table 1 anti-microbial property
aThe inoculated bacteria total amount is 1.27 * 10
7CFU,
bThe inoculated bacteria total amount is 2.00 * 10
7CFU, COTTON FABRIC-TMP-BTCA are the COTTON FABRIC without halogenation treatment, and COTTON FABRIC-TMP-BTCA-Cl is embodiment 2 gained COTTON FABRIC.
The test data of table 1 shows, the COTTON FABRIC of carrying out Anti-bacterial and Crease according to the method for the invention is with after inoculated bacteria contacts, and in 5min the sterilizing rate of staphylococcus aureus being reached 100%(is that the reduction of staphylococcus aureus is 1.27 * 10
7CFU), in 10min to Escherichia coli O 157: it is Escherichia coli O 157 that the sterilizing rate of H7 reaches 83.25%(: the reduction of H7 is 1.67 * 10
7CFU), anti-microbial property is good.
Get three parts in COTTON FABRIC sample identical among above-described embodiment 1~embodiment 4.First part without any processing; Process according to embodiment 2 described methods for second part, different is not add catalyst in the described arrangement body lotion; Process according to embodiment 2 described methods for the 3rd part.Above-mentioned three parts of COTTON FABRIC samples are carried out the crease recovery property testing, and test result sees Table 2.
Table 2 finishing technique is on the impact of wrinkle recovery angle of woven fabrics using viscoelasticity theory
The test data of table 2 shows, compares with the COTTON FABRIC without any processing, and the COTTON FABRIC creasy recovery angle that carries out Anti-bacterial and Crease according to the method for the invention is significantly increased.When not adding catalyst in the arrangement body lotion, creasy recovery angle is elevated to 222.9 by 111.7, and behind the interpolation catalyst, creasy recovery angle is elevated to 251.6 by 111.7 in the arrangement body lotion, and crease resistance is good.
The related raw material of above embodiment and reagent are the commercially available prod, and the machinery equipment of using is the conventional machinery equipment in this area.
Above-described only is preferred embodiment of the present invention, the invention is not restricted to above embodiment.Be appreciated that other improvement and variation that those skilled in the art directly derive or associate under the prerequisite that does not break away from spirit of the present invention and design, all should think to be included within protection scope of the present invention.
Claims (5)
1. the Anti-bacterial and Crease method of a COTTON FABRIC is characterized in that: first with catalyst, equimolar 2,2,6, and 6-tetramethyl-4-piperidine alcohols and BTCA composition arrangement soluble in water body lotion, and COTTON FABRIC be impregnated in the described arrangement body lotion; Then through padding, preliminary drying and bake operation described COTTON FABRIC is processed, at last to soap through the described COTTON FABRIC that bakes processing, wash, oven dry, halogenation, again oven dry; Described catalyst is a kind of in sodium dihydrogen phosphate, sodium hydrogen phosphate, sodium polyphosphate, the sodium hypophosphite, and described halogenation treatment will be for impregnated in through the COTTON FABRIC of described drying and processing in clorox, calcium hypochlorite or the sodium hypobromite solution.
2. the Anti-bacterial and Crease method of described COTTON FABRIC according to claim 1, it is characterized in that: in described arrangement body lotion, the mass percentage concentration of described catalyst is 1~10%.
3. the Anti-bacterial and Crease method of described COTTON FABRIC according to claim 1 is characterized in that: described 2,2,6 in described arrangement body lotion, the mass percentage concentration of 6-tetramethyl-4-piperidine alcohols is 1~10%.
4. the Anti-bacterial and Crease method of described COTTON FABRIC according to claim 1, it is characterized in that: the described temperature that bakes processing is 150~200 ℃, and the time is 30~300s.
5. the Anti-bacterial and Crease method of described COTTON FABRIC according to claim 1, it is characterized in that: described clorox, calcium hypochlorite, sodium hypobromite solution quality percentage concentration are respectively 0.01~1%.