CN1110727A - "Shushuangkang" linen fabric and production technology - Google Patents
"Shushuangkang" linen fabric and production technology Download PDFInfo
- Publication number
- CN1110727A CN1110727A CN 95110990 CN95110990A CN1110727A CN 1110727 A CN1110727 A CN 1110727A CN 95110990 CN95110990 CN 95110990 CN 95110990 A CN95110990 A CN 95110990A CN 1110727 A CN1110727 A CN 1110727A
- Authority
- CN
- China
- Prior art keywords
- shushuangkang
- linen
- production technology
- fibre
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a Shushuangkang flax fabric and manufacturing processing technology thereof. The product is a blending fabric of flax fiber and cotton fiber. The production technology comprises raw material pretreatment, yarn spinning, and weaving. The fabric surface is plumpy and uniform, breathable and comfortable, hence the application is extensive.
Description
The present invention relates to a kind of woven cloth and weaving method thereof.
Present textiles is the fabric of cotton and chemical fabrics basically, and cotton fiber is in short supply at the present source of goods, and chemical fibre textile has the defective of cost height, Application Areas limitation.
The object of the present invention is to provide and a kind ofly utilize flax to be main raw material, " Shushuangkang " linen fabric and production technology thereof that cost is low.
Technical solution of the present invention is:
A kind of " Shushuangkang " linen fabric, the difference of itself and prior art is: it is the BLENDED FABRIC of linen fibre and short-staple.
Wherein linen fibre mainly is the linen fibre that falls.Short-staple can be viscose or cotton etc.
A kind of production technology of " Shushuangkang " linen fabric, comprise spinning, weaving process, spinning process comprises opening picking, comb and parallel cotton fibers prior to spinning, drafting, rove, spun yarn, and weaving process comprises that network is put in order operation, sizing operation, weaved cotton cloth, arranging process, and the difference of itself and prior art is:
1) before spinning, at first linen fibre is carried out preliminary treatment.Be that the shredding combing is rejected staple fibre and fiber crops knot impurity and interrupted super over-length fibre, carry out humidification with antistatic additive, peregal again and add newborn the processing;
2) before the spinning, will carry out artificial mixed with little amount through pretreated linen fibre and short-staple;
3) slurries employing starch is that master, PVA are the mixed pulp of assisting in the sizing operation, also contains oil emulsion and hygroscopic agent glycerine in the slurries.
In the opening and cleaning step, big 10-15% when condenser wind speed ratio is handled the common cotton fiber.
In the mixing in doubling step, glue rod pressure needs than handling the big 7-15% of common cotton fiber.
In the spinning process, glue rod pressurization should be when handling the common cotton fiber big 10-15%.
Antistatic additive adopts SN or PM.
The concrete prescription of slurries is:
Starch 50-60%, bisnaphthol 0.2-0.5%,
PVA10-20%, waterglass 0.2-0.5%,
CMC3-4%, polyacrylamide 10-20%,
Glycerine 0.5-1%, oil emulsion 6.5-9%.
Also add caustic soda in the slurries to PH7-8.
Non-full neat and well spaced, the ventilative refreshing body, well-pressed rough of product cloth cover provided by the present invention, existing good taking has certain health care again; Both can make high-grade fabric, can be used as room decorating and medical and health cloth again, and cost be low.
Production technology of the present invention has solved that thick, hard, the crisp and rigidity of linen fibre is big, the problem of spinnability difference, and technology is simple, reliable.
The invention will be further described below in conjunction with embodiment:
Embodiment 1:
A kind of relax and the production technology of refreshing health sodolin comprises the following steps:
1, at first linen fibre is carried out preliminary treatment.
As raw material, utilize opening picking equipment that it is carried out preliminary shredding and combing flax noil or two tubbiness fiber crops,, interrupt the super over-length fibre of part to reject part staple fibre and fiber crops knot impurity in the raw material.The 2-5% that is equivalent to linen fibre weight again with antistatic additive SN() and peregal (1-3% that is equivalent to linen fibre weight) carry out dewing and add breast, heap is raised and was given birth to 24 hours, makes its infiltration evenly.
2, mix cotton type yarn:
Require to adopt proper proportion to mix according to fabric variety the raw material after the above-mentioned processing and short-staple (viscose or cotton or other short-staples), can adopt linen fibre: short-staple (routine viscose) is proper ratio such as 55: 45 or 70: 30 or 85: 15.Preferably adopt the method for artificial mixed with little amount during mixing.
3, spinning process
Comprise common process steps such as opening picking, comb and parallel cotton fibers prior to spinning, drafting, rove, spun yarn.But during opening picking, poor because of the linen fibre bulkiness, than great, density is high, so the wind speed of condenser needs to strengthen about 10-15% when handling the common cotton fiber.When comb and parallel cotton fibers prior to spinning, can suitably increase the weight of weight of card sliver (21-24g/5m) and install bar-guiding device additional.When drafting, be the gripping of reinforcing fibre, rubber roll pressure should strengthen about 10% when handling the common cotton fiber.When spun yarn, rubber roll pressurization also should strengthen about 10-15% when handling the common cotton fiber, and can strengthen the spun yarn twist, and twist factor can be controlled in 420-500.
4, weaving process
Comprise that network puts in order operation, sizing operation and common process steps such as the operation of weaving cotton cloth, arranging process.But slurry formula (weight proportion) is selected for use when the sizing operation:
Starch 52%, bisnaphthol 0.5%,
PVA15%, waterglass 0.4%,
CMC3.2%, polyacrylamide 20%,
Oil emulsion 8%, glycerine 0.9%.
Add caustic soda again to PH7-8.
In arranging process, preferably dry by the fire cloth before the member and handle, go mouldy preventing.
In the spinning process, the Temperature and Humidity Control in workshop, general winter temperature should be greater than 20 ℃, and relative humidity should be at 63-70%; Summer temp should be less than 32 ℃, and relative humidity should be at 65-75%.
In the weaving process, the Temperature and Humidity Control in workshop, general winter temperature is about 22-24 ℃, about relative humidity 68-78%; Summer temp is about 28-30 ℃, about relative humidity 70-80%.
Promptly make " Shushuangkang " linen fabric through above-mentioned steps, it is the BLENDED FABRIC of linen fibre and short-staple.Product after tested, equal accord with Q/320621MAB06-92 of every index and the requirement of Q/320621MAB07-93 product standard Grade A.
Embodiment 2:
In the sizing operation, slurries adopt the prescription of following percentage by weight:
Starch 59%, bisnaphthol 0.3%,
PVA18%, waterglass 0.3%,
CMC3.9%, polyacrylamide 11.3%,
Glycerine 0.7%, oil emulsion 6.5%.
Add caustic soda again and be neutralized to PH7-8.All the other are all with embodiment 1.
Embodiment 3:
In the slashing technique, slurries adopt the prescription of following percentage by weight:
Starch 53%, bisnaphthol 0.4%,
PVA19.7%, waterglass 0.5%,
CMC3.0%, polyacrylamide 15%,
Glycerine 0.6%, oil emulsion 7.8%.
Add caustic soda again and be neutralized to PH7-8, all the other are with embodiment 1.
Claims (10)
1, a kind of " Shushuangkang " linen fabric is characterized in that: the BLENDED FABRIC that is linen fibre and short-staple.
2, " Shushuangkang " linen fabric according to claim 1 is characterized in that: linen fibre is the linen fibre that falls.
3, " Shushuangkang " linen fabric according to claim 1 is characterized in that: short-staple is a viscose.
4, the production technology of the described " Shushuangkang " linen fabric of a kind of claim 1, comprise spinning, weaving process, spinning process comprises opening picking, comb and parallel cotton fibers prior to spinning, drafting, rove, spun yarn, weaving process comprises that network is put in order operation, sizing operation, weaved cotton cloth, arranging process, it is characterized in that: 1) before spinning, at first linen fibre is carried out preliminary treatment, be that the shredding combing is rejected staple fibre and fiber crops knot impurity and interrupted super over-length fibre, carry out humidification with antistatic additive, peregal again and add newborn the processing;
2) before the spinning, will carry out artificial mixed with little amount through pretreated linen fibre and short-staple;
3) slurries employing starch is that master, PVA are the mixed pulp of assisting in the sizing operation, also contains oil emulsion and hygroscopic agent glycerine in the slurries.
5, the production technology of " Shushuangkang " linen fabric according to claim 4 is characterized in that: in the opening and cleaning step, and big 10-15% when condenser wind speed ratio is handled the common cotton fiber.
6, the production technology of " Shushuangkang " linen fabric according to claim 4 is characterized in that: in the mixing in doubling step, glue rod pressure needs than handling the big 7-15% of common cotton fiber.
7, the production technology of " Shushuangkang " linen fabric according to claim 4 is characterized in that: in the spinning process, glue rod pressurization should be when handling the common cotton fiber big 10-15%.
8, the production technology of " Shushuangkang " linen fabric according to claim 4 is characterized in that: antistatic additive adopts SN.
9, according to the production technology of the described " Shushuangkang " linen fabric of claim 4, it is characterized in that: the concrete prescription of slurries is (percentage by weights):
Starch 50-60%, bisnaphthol 0.2-0.5%,
PVA10-15%, waterglass 0.2-0.5%,
CMC3-4%, polyacrylamide 10-20%,
Glycerine 0.5-1%, oil emulsion 6.5-9%.
10, the production technology of " Shushuangkang " linen fabric according to claim 9 is characterized in that: also add caustic soda in the slurries to PH7-8.