CN1483873A - Multe-component hemp blended spinning products and textile technology thereof - Google Patents
Multe-component hemp blended spinning products and textile technology thereof Download PDFInfo
- Publication number
- CN1483873A CN1483873A CNA031388574A CN03138857A CN1483873A CN 1483873 A CN1483873 A CN 1483873A CN A031388574 A CNA031388574 A CN A031388574A CN 03138857 A CN03138857 A CN 03138857A CN 1483873 A CN1483873 A CN 1483873A
- Authority
- CN
- China
- Prior art keywords
- speed
- hemp
- roller
- multicomponent
- terylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a multicomposition hemp blended spinning products and its technology. It is made from four fibres of hemp, yak cashmere, polyester fiber and modal as raw material, and its linear density is 9.7-200 tex, and its total compactness is 30%-99.5%. Its spinning technology includes the following steps: hemp and yak cashmere, dressing (A1860), pre-drawing (A272F) model and polyester fibre, dressing (FA201A), pre-drawing (FA304) mixed drawing first pass, mixed drawing second pass, roving (FA401), spinning (P7501), coning, warping, sizing, weaving and fabric finishing.
Description
One, affiliated field:
The invention belongs to the flax spinning technical field, be specifically related to exploitation multicomponent hemp blended textile and textile technology thereof on cotton spinning apparatus.
Two, background technology:
At present China's hemp blending product is mainly hemp and cotton, hair, silk blend product, and its lining feel, drapability, wrinkle resistance are poor.
Three, summary of the invention
The present invention will solve that the lining feel of present China hemp blending product is poor, drapability is poor, the problem of wrinkle resistance difference, utilize the cotton spinning device fabrication to go out high-grade hemp blended textile at the deficiencies in the prior art.
The present invention can realize by following measure; A kind of multicomponent hemp blended textile, it is to be made by following materials of weight proportions:
40 parts of hemps
15 parts of yakwools
20 parts of terylene
25 parts of models (MODAL)
Wherein the raw material selected for use of hemp is a hemp tow, length 26mm ± 3mm, fineness 1500Nm; Yakwool fiber, length 30mm ± 3mm, fineness 1200Nm; The raw material that terylene is selected for use is a polyester staple fiber, length 38mm, fineness 1.25D; Modal fibre, length 38mm, fineness 1.25D.
A kind of textile technology of multicomponent hemp blended textile, technological process is:
Hemp, yakwool → comb and parallel cotton fibers prior to spinning (A186D) → in advance be (A272F) also
Model, terylene → comb and parallel cotton fibers prior to spinning (FA201A) → in advance be (FA304) also
Mix and one → mixed and two roads → rove (FA401) → spun yarn (F7501) → winder
(the sub-yarn clearer of distribution, air are twisted with the fingers knot) → warping → sizing → weave → fabric post-treatment
Four kinds of mixed with fibers of hemp, yakwool, terylene, model (MODAL) adopt two step mixing methods: two kinds of natural fabric hemps and yakwool, two kinds of chemical fibre models and terylene adopt bag to mix respectively blowing, utilization electronics distribute cotton equipment and many storehouses mixed cotton equipment; Two kinds of carded slivers mix also at drafting, adopt two roads to mix also;
1, combs procedure technology configuration (adopting two step mixing methods) clearly
A: hemp and yakwool, blowing main technique: comprehensive hired roughneck's speed 850-900r/min, lap roller speed 11-12r/min.Comb and parallel cotton fibers prior to spinning main technique: perverse roller speed 750-900r/min, cylinder speed 310-320r/min, perverse roller solder speed ratio is 1: 2.1, doffer speed 17.5r/min, and spacing between cylinder, cover plate is 0.3,0.28,0.25,0.25,0.28mm, spacing of cylinder, doffer is 0.13mm, the perverse roller feed plate 0.23mm that spaces.Carded sliver short fiber content remains in 10%.
B: model, terylene, blowing main technique: kirschner beater speed 700-800r/min, lap roller speed 11-12r/min.Comb and parallel cotton fibers prior to spinning main technique: perverse roller speed 600-700r/min, cylinder speed 285-310r/min, perverse roller solder speed ratio is 1: 2.1, doffer speed 19.5r/min, and spacing between cylinder, cover plate is 0.46,0.41,0.36,0.36,0.41mm, spacing of cylinder, doffer is 0.18mm, the perverse roller feed plate 0.41mm that spaces.Carded sliver short fiber content remains in 10%.
2, drawing frame Process configuration, adopt two roads to mix also, head also installs evereven additional, adopts the overhead sliver of active type, and head back zone drafting multiple also is 1.6～1.8 times, adopt 8 and close, three model polyster fibre bars, five hemp yakwool bars are spaced, roller gauge 9-11mm, shaping linear velocity 110-130m/min.Two and back zone drafting multiple 1.06, and close radical 8, roller gauge 10-13mm, shaping linear velocity 115-130m/min.
3, Speed frames technology, drawing-off form Three Up Three Down double belt drafting.Roller gauge 23-32mm, back zone drafting multiple 1.05-1.20, twist factor 90-110, front roller speed 11-12r/min.
4, fine spining machine technology, drawing-off form Three Up Three Down length apron draft.Roller gauge 17-22mm, back zone drafting multiple 1.1-1.2, twist factor 320-380, front roller speed 130-180r/min.
5, bobbin winder Process configuration adopts Chang Ling, Xi'an DQSS-4A electronic yarn clearer, the empty twister of Italian Mei Sidan (MESDAN) 928B water-fog type.The clear parameter of electricity: short slub: 4.5cm 200%,, long slubbing: 40cm 90%,, long details :-70%60cm, material coefficient CX:7.5,600 meters/minute of winder linear velocities.
6, warping machines Process configuration, four districts, three floor are adopted in the tension force configuration, and warp yarn tension force is 67cn, and the speed of a motor vehicle is 200～380 meters/minute.
7, Sizing machines Process configuration, 30～80 meters/minute of the speed of a motor vehicle, the rate of sizing are 6～10%, regain 6～8%, percentage elongation≤0.7%, enhancing rate 〉=13%, subtract the rate of stretching≤12%, formula of size: converted starch: 70%PVA:15%LMA-98:8%LMA-96:4% glycerine: 3%.
8, weave the machine Process configuration, the speed of a motor vehicle: 340～480 rev/mins, moving and the grade of heald frame :+2, the shed opening of measuring in the reed place: 28/30mm, shed open is combined mean place (the loom number of degrees): 310/330, the upright position of the back rest: 0/+1/+2/+3, the horizontal level of the back rest: 8 pages of heald frames are following with the 2nd hole, surpass with the 3rd hole, the upright position of back beam spring: 1/2, the warp thread automatic stop arrangement is apart from the distance of last a slice heald frame: 350/450mm, the height of warp thread automatic stop arrangement elliptical rod: below, the height of stop over sheet pressure pin: 20/30mm
To carry out carbon black process for producing workshop temperature be 23～32 ℃ to all rollers in a kind of textile technology flow process of multicomponent hemp blended textile, and relative humidity is 75～82%.
Beneficial effect of the present invention: 1, utilize western resource hemp of China and yakwool; and be equipped with model (MODAL) and terylene; go out high-grade hemp blended textile in the cotton spinning device fabrication; not only produced favorable economic benefit, and China's enforcement strategy to develop western regions has been had very positive meaning.2, by the multicomponent hemp blended textile of this explained hereafter, function such as have that anti-mildew is antibacterial, moisture absorption ventilative, antiultraviolet, antistatic, drapability are good.
Four, the specific embodiment
A kind of multicomponent hemp blended textile, it is to be made by following materials of weight proportions:
40 parts of hemps
15 parts of yakwools
20 parts of terylene
25 parts of models (MODAL)
Wherein the raw material selected for use of hemp is a hemp tow, length 26mm, fineness 1500Nm; Yakwool fiber, length 30mm, fineness 1200Nm; The raw material that terylene is selected for use is a polyester staple fiber, length 38mm, fineness 1.25D; Modal fibre, length 38mm, fineness 1.25D.
A kind of textile technology of multicomponent hemp blended textile:
1, combs procedure technology configuration (adopting two step mixing methods) clearly
A: hemp and yakwool, blowing main technique: comprehensive hired roughneck's speed 870r/min, lap roller speed 12r/min.The comb and parallel cotton fibers prior to spinning main technique: perverse roller speed 890r/min, cylinder speed 320r/min, perverse roller solder speed ratio is 1: 2.1, doffer speed 18r/min, spacing between cylinder, cover plate is 0.3,0.28,0.25,0.25,0.28mm spacing of cylinder, doffer is 0.13mm, the perverse roller feed plate 0.23mm that spaces.Carded sliver short fiber content 7%.
B: model, terylene, blowing main technique: kirschner beater speed 750-850r/min, lap roller speed 12.5r/min.Comb and parallel cotton fibers prior to spinning main technique: perverse roller speed 660r/min, cylinder speed 280r/min, perverse roller solder speed ratio is 1: 2.1, doffer speed 19.5r/min, and spacing between cylinder, cover plate is 0.46,0.41,0.36,0.36,0.41mm, spacing of cylinder, doffer is 0.18mm, the perverse roller feed plate 0.41mm that spaces.Carded sliver short fiber content 8%.
2, mixing in doubling step Process configuration, adopt two roads to mix also, head also installs evereven additional, adopts the overhead sliver of active type, and head back zone drafting multiple also is 1.6 times, adopt 8 and close, three model polyster fibre bars, five hemp yakwool bars are spaced, roller gauge 9-11mm, shaping linear velocity 125m/min.Two and back zone drafting multiple 1.08, and close radical 8, roller gauge 10-13mm, shaping linear velocity 130m/min.
3, rove procedure technology, drawing-off form Three Up Three Down double belt drafting.Roller gauge 23-32mm, back zone drafting multiple 1.09, twist factor 100, front roller speed 136r/min.
4, spinning process technology, drawing-off form Three Up Three Down length apron draft.Roller gauge 17-22mm, back zone drafting multiple 1.2, twist factor 355, front roller speed 160r/min.
5, winding procedure Process configuration adopts Chang Ling, Xi'an DQSS-4A electronic yarn clearer, the empty twister of Italian Mei Sidan (MESDAN) 928B water-fog type.The clear parameter of electricity: short slub: 4.5cm 200%,, long slubbing: 40cm 90%,, long details :-70%60cm, material coefficient CX:7.5,600 meters/minute of winder linear velocities.
6, warping process Process configuration, four districts, three floor are adopted in the tension force configuration, and warp yarn tension force is 67cn, and the speed of a motor vehicle is 360 meters/minute.
7, sizing procedure technology configuration, 38 meters parts of the speed of a motor vehicle, the rate of sizing is 8.5%, regain 6.5%, percentage elongation≤0.5%, enhancing rate 〉=14%, subtract the rate of stretching≤12%, formula of size: converted starch: 70%PVA:15%LMA-98:8%LMA-96:4% glycerine: 3%.
8, weaving process Process configuration, the speed of a motor vehicle: 450 rev/mins, moving and the grade of heald frame :+2, the shed opening of measuring in the reed place: 28mm, shed open combine mean place (the loom number of degrees): 320, the upright position of the back rest :+2, the horizontal level of the back rest: 7 pages of heald frames are with the 2nd hole, the upright position of back beam spring: 1/2, and the warp thread automatic stop arrangement is apart from the distance of last a slice heald frame: 390mm, the height of warp thread automatic stop arrangement elliptical rod: below, the height of stop over sheet pressure pin: 25mm
Wherein all rollers carry out the carbon black processing, and the workshop temperature is 28 ℃, and relative humidity is 82%
Claims (4)
1, a kind of multicomponent hemp blended textile, it is characterized in that: it is to be made by following materials of weight proportions:
40 parts of hemps
15 parts of yakwools
20 parts of terylene
25 parts of models
Wherein hemp to select raw material for use be hemp tow, length 26mm ± 3mm, fineness 1500Nm; Yakwool fiber, length 30mm ± 3mm, fineness 1200Nm; The raw material that terylene is selected for use is a polyester staple fiber, length 38mm, fineness 1.25D; Modal fibre, length 38mm, fineness 1.25D; The yarn of multicomponent hemp blended textile is the big linen blended yarn of multicomponent of line density 9.7～200tex, and the total tightness degree of multicomponent hemp blended textile is 30%～99.5%.
2, a kind of textile technology of multicomponent hemp blended textile, it is characterized in that: technological process is:
Hemp, yakwool → comb and parallel cotton fibers prior to spinning → in advance also
Model, terylene → comb and parallel cotton fibers prior to spinning → in advance also
Mixed also one → mixed also two roads → rove → spun yarn → winder → warping → sizing → weave → fabric post-treatment
Four kinds of mixed with fibers of hemp, yakwool, terylene, model adopt two step mixing methods: two kinds of natural fabric hemps and yakwool, and two kinds of chemical fibre models and terylene adopt bag to mix respectively blowing, utilization electronics distribute cotton equipment and many storehouses mixed cotton equipment; Two kinds of carded slivers mix also at drafting, adopt two roads to mix also;
A, comb procedure technology configuration clearly, adopt two step mixing methods
Hemp and yakwool, blowing main technique: comprehensive hired roughneck's speed 850-900r/min, lap roller speed 11-12r/min; Comb and parallel cotton fibers prior to spinning main technique: perverse roller speed 800-900r/min, cylinder speed 310-330r/min, perverse roller solder speed ratio is 1: 2.1, doffer speed 17-19r/min, and spacing between cylinder, cover plate is 0.3,0.28,0.25,0.25,0.28mm, spacing of cylinder, doffer is 0.13mm, the perverse roller feed plate 0.23mm that spaces; Carded sliver short fiber content remains in 10%;
Model, terylene, blowing main technique: kirschner beater speed 750-850r/min, lap roller speed 12-13r/min; Comb and parallel cotton fibers prior to spinning main technique: perverse roller speed 600-700r/min, cylinder speed 270-290r/min, perverse roller solder speed ratio is 1: 2.1, doffer speed 19-20r/min, and spacing between cylinder, cover plate is 0.46,0.41,0.36,0.36,0.41mm, spacing of cylinder, doffer is 0.18mm, the perverse roller feed plate 0.41mm that spaces; Carded sliver short fiber content remains in 10%;
B, drawing frame Process configuration, adopt two roads to mix also, head also installs evereven additional, adopts the overhead sliver of active type, and head back zone drafting multiple also is 1.6～1.8 times, adopt 8 and close, three model polyster fibre bars, five hemp yakwool bars are spaced, roller gauge 9-11mm, shaping linear velocity 125m/min; Two and back zone drafting multiple 1.06-1.00, and close radical 8, roller gauge 10-13mm, shaping linear velocity 130m/min;
C, Speed frames technology, drawing-off form Three Up Three Down double belt drafting, roller gauge 23-32mm, back zone drafting multiple 1.05-1.20, twist factor 90-110, front roller speed 125-150r/min;
D, fine spining machine technology, drawing-off form Three Up Three Down length apron draft, roller gauge 17-22mm, back zone drafting multiple 1.1-1.2, twist factor 320-380, front roller speed 130-180r/min;
E, bobbin winder Process configuration, the clear parameter of electricity: short slub: 4.5cm 200%,, long slubbing: 40cm 90%,, long details: 60cm-70%,, material coefficient CX:7.5,600 meters/minute of winder linear velocities;
F, warping machines Process configuration, four districts, three floor are adopted in the tension force configuration, and warp yarn tension force is 67cn, and the speed of a motor vehicle is 200～380 meters/minute;
G, Sizing machines Process configuration, 30～80 meters/minute of the speed of a motor vehicle, the rate of sizing are 6～10%, regain 6～8%, percentage elongation≤0.7%, enhancing rate 〉=13%, subtract the rate of stretching≤12%, formula of size: converted starch: 70%PVA:15%LMA-98:8%LMA-96:4% glycerine: 3%;
H, weave the machine Process configuration, the speed of a motor vehicle: 340～480 rev/mins, moving and the grade of heald frame :+2, the shed opening of measuring in the reed place: 28/30mm, shed open is combined mean place, the loom number of degrees: 310/330, the upright position of the back rest: 0/+1/+2/+3, the horizontal level of the back rest: 8 pages of heald frames are following with the 2nd hole, surpass with the 3rd hole the upright position of back beam spring: 1/2, the warp thread automatic stop arrangement is apart from the distance of last a slice heald frame: 350/450mm, the height of warp thread automatic stop arrangement elliptical rod: below, the height of stop over sheet pressure pin: 20/30mm.
3, the textile technology of a kind of multicomponent hemp blended textile according to claim 2 is characterized in that: all rollers carry out carbon black to be handled.
4, the textile technology of a kind of multicomponent hemp blended textile according to claim 2 is characterized in that: the workshop temperature is 23～32 ℃, and relative humidity is 75～82%.