CN109322022A - A kind of close SEILE textile strand and its production method and purposes - Google Patents
A kind of close SEILE textile strand and its production method and purposes Download PDFInfo
- Publication number
- CN109322022A CN109322022A CN201811346776.3A CN201811346776A CN109322022A CN 109322022 A CN109322022 A CN 109322022A CN 201811346776 A CN201811346776 A CN 201811346776A CN 109322022 A CN109322022 A CN 109322022A
- Authority
- CN
- China
- Prior art keywords
- cotton
- speed
- gauge
- roller
- dry weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to textile technology fields, and in particular to a kind of close SEILE textile strand and its production method and purposes.The production method obtains the close SEILE textile strand that number is 36 by cotton cleaning process, carding step, combing process, mixing in doubling step, Roving Frames, spinning process, winding procedure, folding process and twisting process using polyamide fibre double six fibers, combed long staple cottons as raw material.The parameter of each process is clearly limited in production method provided by the invention so that double six fibers of polyamide fibre and two kinds of fibers of combed long staple cotton can smoothly it is blended go out close SEILE textile strand of the number as 36；The fabric strength property produced using strand of the present invention is good, and wearability is good, moisture absorption is ventilative, can be used for making the army training clothes more demanding to wearability, tear resistance.
Description
Technical field
The invention belongs to textile technology fields, and in particular to a kind of close SEILE textile strand and its production method and purposes.
Background technique
The double most prominent advantages of six fibers of polyamide fibre are that the more other fibers of wearability are superior, are best in all textile fabrics
, under the conditions of, wearability is 10 times of cotton.In addition, double six fibers of polyamide fibre also have rotproofness, it is not afraid of and damages by worms, goes mouldy,
The advantages that strength is high, and elasticity is good, good hygroscopicity.
But double six fibers of above-mentioned polyamide fibre have the disadvantage that the double six fibrous fracture elongations of polyamide fibre are big, and resilience is strong, production
Frictional resistance is big in the process, is also easy to produce wrinkle strip.Because there are above-mentioned deficiencies, therefore in the prior art by double six fibers of polyamide fibre and combing
Long wool cotton blend cannot obtain yarn thinner and best in quality medium count yarn or high grade cotton yarn when being spinned.
Summary of the invention
In view of the deficiencies of the prior art, technical problem to be solved by the invention is to provide a kind of close SEILE textile strand and
Its production method and purposes, by this method can make double six fibers of polyamide fibre and combed long staple cotton it is blended obtain it is thinner and best in quality
Medium count yarn, which is that a kind of strength property is good, and wearability is good, moisture absorption breathable shell fabric single thread, can be used for make to wearability,
The more demanding army's training clothes single thread of tear resistance.
The technical scheme to solve the above technical problems is that a kind of production method of close SEILE textile strand, by
Double six fibers of polyamide fibre with combed long staple cotton is blended forms comprising following steps:
(1) cotton cleaning process: griping cotton machine hired roughneck's decrease speed each 3mm, revolving speed 960r/min, rotary machinery speed 2.8r/
Min, blade stretch out rib 3mm, Beater Speed 800r/min, fan speed 950r/min, the gauge of hired roughneck and pedal roller
12mm, lap roller speed 12r/min,
Double six fibers of polyamide fibre: the quantification of 361g/m of cotton roll dry weight, cotton roll length are 30.6m；
Long-staple cotton: the quantification of 350g/m of cotton roll dry weight, cotton roll length are 36.5m；
(2) carding step: cylinder and 7 mil of licker-in gauge, feed plate and 20 mil of licker-in gauge, cylinder and doffer's gauge
4 mils, mote knife height and machine frame are flat, knife spine with 90 ° of machine frame horizontal plane angle,
Double six fibers of polyamide fibre: cylinder speed 360r/min, licker-in speed 760r/min, doffer speed 16r/min, cover board speed
162mm/min is spent, the quantification of 19.6g/m of cotton carding dry weight, cylinder and 5 gauges of cover board are 10 mils × 9 mils × 8 mil × 8
Mil × 9 mils；
Long-staple cotton: cylinder speed 360r/min, licker-in speed 880r/min, doffer speed 15.5r/min, cover plate speed
251mm/min, the quantification of 14.05g/m of cotton carding dry weight, cylinder and 5 gauges of cover board are 8 mils × 7 mils × 7 mils × 7 English
Silk × 8 mils；
(3) combing process；
(4) mixing in doubling step: by one Yu Bing tri- and and, double six fibers of polyamide fibre are pre- and 7 and close, and dry weight is quantitative
20.47g/5m, roller gauge 12mm × 20mm, 6.7 times of mechanical commutation draft, 1.6 times of back area draft；It 6 and closes together, and closes distribution
For 3 combed long staple cotton items, double six ribbons of 3 polyamide fibres, dry weight quantifies 16.9g/5m, roller gauge 10mm × 18mm, mechanical
6.6 times of drawing-off, 1.6 times of back area draft；It two and 7 and closes, dry weight quantifies 16.6g/5m, roller gauge 10mm × 18mm, mechanical
7.1 times of drawing-off, 1.4 times of back area draft；It three and 7 and closes, dry weight quantifies 16.5g/5m, roller gauge 10mm × 18mm, mechanical
7.04 times of drawing-off, 1.3 times of back area draft；
(5) Roving Frames: 4.7 twirls of roving twist/10cm, roller gauge use 10mm × 24mm × 42mm, back area draft
1.2 times, nip gauge 7mm, the quantification of 3.84g/10m of rove dry weight, 8.59 times of mechanical commutation draft, front roller revolving speed 200r/min,
Weight in wet base 4g/10m, special number 400tex, twist factor 94, front roller diameter 28mm, pressing device winding number 2 enclose；
(6) spinning process；
(7) winding procedure；
(8) folding process；
(9) twisting process.
On the basis of aforementioned production method, the present invention, which can also be done, to be embodied further below or optimizes.
Specifically, the combing process: the long-staple cotton carded sliver combing preparation stage: silver lap combined roots are 20, dry weight
48g/m, roller gauge are 12 × 16mm, rouleau length 235m, lap roller linear speed 61.7m/min；And rolling up combined roots is 6
Root, dry weight 45g/m, roller gauge are 10 × 12mm, rouleau length 182m；Combing stage, dry weight 16.75g/5m, gauge are
7mm is fed for length 5.2mm, linters rate 10%；Back zone drafting multiple 1.36,2 indexing of cambered plate positioning, hairbrush revolving speed
1000r/min, cylinder revolving speed 225 clamp secondary/min.
Specifically, the spinning process: 49.8 times of mechanical commutation draft multiple, roller gauge 17mm × 38mm, back area draft times
Number is 1.18 times, nip gauge 2.5mm, front roller diameter 27mm, front roller revolving speed 162r/min, 96.5 twirls of the twist/10cm, twirl
Coefficient 391, rings model PG1-4254, wire loop model W321 36#；The winding procedure: electronic yarn clearer parameter: cotton knot N:
350% × 0.8cm, short and thick S:160% × 1.6cm, long thick L:35% × 35cm, details T:-35% × 30cm, produce N/J
The single thread that long 55/45 16.3tex is tightly matched；The folding process: producing on doubling machine, and two yarns are coiled into folding bobbin side by side,
Both sides uniform tension in order, tension pulley use 1g, 1460 turns/min of main motor revolving speed, front roller linear velocity 22.5m/min, and groove drum is straight
Diameter 86mm produces the doubling that 55/45 number of N/J long is 36；The twisting process: producing on two-for-one twister, and two are passed through
It crosses the single thread merged and is made strand, 73 twirls of the twist/10cm, twist factor 418, front roller linear velocity 11.1m/min produces N/
The strand that 55/45 number of J long is 36, the as described polyamide fibre and combed long staple cotton scribbled.
Specifically, double six fibers of polyamide fibre are at least up to following performance standard: than strong 5.62CN/dtex, elongation at break
55.29%, line density 1.67dtex, length 38mm, regain 1.63%.
Preferably, the needle cloth model in carding step are as follows: flat-clothing MCH32, Bearded-needle knitted cloth AC2030*01550, doffer
Needle cloth AD4030*01890, taker-in roller wire AT5610*06311.
Specifically, rings used in spinning process is PG1-4254, wire loop is W321 36#.
Preferably, mixing in doubling step by one Yu Bing tri- and and, double six fibers of polyamide fibre are pre- and 7 and close, and 6 simultaneously together
It closes, and closes and be assigned as 3 combed long staple cotton items, double six ribbons of 3 polyamide fibres.
Specifically, the equipment that production line uses includes: A002C type automatic plucker, A036B porcupine opener, A092A type
Tandem feeder, A076C type lapper, A186 carding machine, SXF1338 lap former, SXF1348 ribbon lap machine, FA266 combing
Machine, FA305 drawing frame, A454 fly frame, FA502 spinning frame, 21C~S bobbin-winding machine, TSB-36C doubling winder and TDN-128B are short
Fine two-for-one twister.
The present invention also provides a kind of close SEILE textile strands, are made by above-mentioned production method.
The present invention is also claimed a kind of above-mentioned close SEILE textile strand and wants for making to wearability, tear resistance
Seek the purposes of higher army's training clothes.
Compared with prior art, the beneficial effects of the present invention are:
(1) production method provided by the invention is successively sequentially through blowing, cotton carding, combing, drafting, rove, spun yarn, winder work
Sequence produces single thread, and each process in the production method has following features compared with prior art: cotton cleaning process using short route,
More combs are beaten less, thin feed falls less, increase degree of opening；Carding step protects fibre integrity to greatest extent and reduces the generation of cotton knot；
Mixing in doubling step ensures that two kinds of fibers are uniformly mixed, and guarantees the improvement of sliver weight unevenness, by one Yu Bing tri- and and；Slightly
Yarn process uses rolling density appropriate and pressing device winding number, reducing friction resistance；Spinning process is produced using Compact siro yarn.
According to process provided by the invention and specific process parameter can by double six fibers of polyamide fibre with combed long staple cotton is blended obtains number
For 36 close SEILE textile strands, and this appears to be in the prior art and cannot achieve.
(2) present invention is had using double six fibers of polyamide fibre and the blended close SEILE textile strand of production of combed long staple cotton, the yarn
Wearability is strong, is not afraid of mildew of damaging by worms, the advantages that elasticity is good, strength is high.
(3) the fabric product strength property made using single thread produced by the invention is good, and wearability is good, moisture absorption is ventilative, can
For making the army training clothes more demanding to wearability, tear resistance.
Specific embodiment
Principles and features of the present invention are described below in conjunction with specific embodiment, example is served only for explaining this hair
It is bright, it is not intended to limit the scope of the present invention.
To avoid repeating, raw material used in the following embodiment of the invention and specific production equipment are summarized as follows:
Double six fibers of polyamide fibre: than strong 5.62CN/dtex, elongation at break 55.29%, line density 1.67dtex, length
38mm, regain 1.63%；
The equipment that production line uses includes: A002C type automatic plucker, A036B porcupine opener, A092A type double hopper
Cotton feeder, A076C type lapper, A186 carding machine, SXF1338 lap former, SXF1348 ribbon lap machine, FA266 combing machine, FA305
Drawing frame, A454 fly frame, FA502 spinning frame, 21C~S bobbin-winding machine, TSB-36C doubling winder and TDN-128B chopped fiber two-for-one twisting machine.
Embodiment 1
A kind of close SEILE textile strand, by double six fibers of polyamide fibre with combed long staple cotton is blended forms, include the following steps:
(1) cotton cleaning process
It is damaged less as far as possible for double six fibers of protection polyamide fibre, to shorten process as far as possible and use strike mode less, reduce hitting power
Degree increases degree of opening.Griping cotton machine hired roughneck's decrease speed each 3mm, revolving speed 960r/min, rotary machinery speed 2.8r/min, knife
Piece stretches out rib 3mm, Beater Speed 800r/min, fan speed 950r/min, the gauge 12mm of hired roughneck and pedal roller, cotton roll
Roller speed 12r/min,
Double six fibers of polyamide fibre: the quantification of 361g/m of cotton roll dry weight, cotton roll length are 30.6m；
Long-staple cotton: the quantification of 350g/m of cotton roll dry weight, cotton roll length are 36.5m；
(2) carding step
Cotton carding produces on A186 carding machine,
Cylinder and 7 mil of licker-in gauge, feed plate and 20 mil of licker-in gauge, cylinder and 4 mil of doffer's gauge, dedusting
Knife up degree and machine frame are flat, knife spine with 90 ° of machine frame horizontal plane angle,
Double six fibers of polyamide fibre: cylinder speed 360r/min, licker-in speed 760r/min, doffer speed 16r/min, cover board speed
162mm/min is spent, the quantification of 19.6g/m of cotton carding dry weight, cylinder and 5 gauges of cover board are 10 mils × 9 mils × 8 mil × 8
Mil × 9 mils；
Long-staple cotton: cylinder speed 360r/min, licker-in speed 880r/min, doffer speed 15.5r/min, cover plate speed
251mm/min, the quantification of 14.05g/m of cotton carding dry weight, cylinder and 5 gauges of cover board are 8 mils × 7 mils × 7 mils × 7 English
Silk × 8 mils；
(3) combing process
Long-staple cotton crosses combing process, excludes the short flannel in the carded sliver, improves the uniformity of fiber, obtain fiber further
It stretches, parallel and separation, the item for improving yarn is dry, strength and gloss, and item is made and does uniform combing sliver, so as to next procedure
Processing.The long-staple cotton carded sliver combing preparation stage: silver lap combined roots be 20, dry weight 48g/m, roller gauge be 12 ×
16mm, rouleau length 235m, lap roller linear speed 61.7m/min；And roll up combined roots be 6, dry weight 45g/m, roller every
Away from for 10 × 12mm, rouleau length 182m；
Combing stage, dry weight 16.75g/5m, gauge 7mm are fed for (retrogressing) length 5.2mm, linters rate 10%；Afterwards
Area's drafting multiple 1.36,2 indexing of cambered plate positioning, hairbrush revolving speed 1000r/min, cylinder revolving speed 225 clamp secondary/min；
(4) mixing in doubling step
Drafting on FA305 drawing frame through producing, to ensure that two kinds of fibers are uniformly mixed and improvement sliver weight is irregular, by one
Road Yu Bing tri- and and, double six fiber rebounds of polyamide fibre are strong, and elongation is big, and strip easily contracts together, and drafting multiple will design as far as possible
Dot, and can not be too small.
Double six fibers of polyamide fibre are pre- and 7 and close, and dry weight quantifies 20.47g/5m, roller gauge 12mm × 20mm, mechanical commutation draft
6.7 times, 1.6 times of back area draft；It 6 and closes together, and closes and be assigned as 3 combed long staple cotton items, double six ribbons of 3 polyamide fibres,
Dry weight quantifies 16.9g/5m, roller gauge 10mm × 18mm, and 6.6 times of mechanical commutation draft, 1.6 times of back area draft；It two and 7 and closes,
Dry weight quantifies 16.6g/5m, roller gauge 10mm × 18mm, and 7.1 times of mechanical commutation draft, 1.4 times of back area draft；It three and 7 and closes,
Dry weight quantifies 16.5g/5m, roller gauge 10mm × 18mm, and 7.04 times of mechanical commutation draft, 1.3 times of back area draft；
(5) Roving Frames
Rove produces on FA454 fly frame, and double six fiber rebounds of polyamide fibre are strong, is fed into winding part friction in rove
Resistance is big, and easily broken end rolls up to form a pseudohardness head.For reducing friction resistance, using pressing device winding number appropriate and winding tension.
4.7 twirls of roving twist/10cm, roller gauge use 10mm × 24mm × 42mm, 1.2 times of back area draft, nip gauge 7mm, slightly
The quantification of 3.84g/10m of yarn dry weight, 8.59 times of mechanical commutation draft, front roller revolving speed 200r/min, weight in wet base 4g/10m, special number
400tex, twist factor 94, front roller diameter 28mm, pressing device winding number 2 enclose；
(6) spinning process
The advantages of spun yarn is produced on FA502 type spinning frame using close SEILE textile, and spinning and SEILE textile are tightly combined, structure
Closely, filoplume is less.49.8 times of mechanical commutation draft multiple, roller gauge is 17mm × 38mm, and back zone drafting multiple is 1.18 times, pincers
Mouth gauge 2.5mm, front roller diameter 27mm, front roller revolving speed 162r/min, 96.5 twirls of the twist/10cm, twist factor 391, rings
With model PG1-4254, wire loop model W321 36#；
(7) winding procedure
Single thread winder produces on the automatic winder in Japanese village field.Using Wu Site electronic yarn clearer and empty twirl nothing
Knot technology guarantees that yarn defect is effectively removed.Cotton knot N:350% × 0.8cm, short and thick S:160% × 1.6cm, long thick L:35% ×
35cm, details T:-35% × 30cm produce the single thread that N/J long 55/4516.3tex is tightly matched.
(8) folding process: producing on doubling machine, and two yarns are coiled into folding bobbin, both sides uniform tension in order, tension pulley side by side
N/J long is produced using 1g, 1460 turns/min of main motor revolving speed, front roller linear velocity 22.5m/min, groove drum diameter 86mm
The doubling that 55/45 number is 36；
(9) twisting process: producing on two-for-one twister, is made strand by combineds single thread for two, and the twirl of the twist 73/
10cm, twist factor 418, front roller linear velocity 11.1m/min produce the strand that 55/45 number of N/J long is 36, as
The polyamide fibre and combed long staple cotton scribbled.
Embodiment 2
With in the production method of embodiment 1 each process and relevant parameter it is all the same, difference be mixed cotton process in use
Combing medium staple cotton and nylon fibre progress are blended, and the weight ratio of nylon fibre and combing medium staple cotton is 55:45, work of finally twisting thread
The number of strand obtained in sequence is 36.
Performance test
The close SEILE textile stock that embodiment 1, embodiment 2 are produced according to the conventional method of field of textiles or national standard
Line carries out the test of correlated performance, and test result is as follows shown in table:
By the data of upper table it is found that double six fibers of the polyamide fibre prepared of above-described embodiment 1 and the blended production of combed long staple cotton
The quality of close SEILE textile strand is preferable, while the fabric strength property of strand production is good, and wearability is good, moisture absorption is ventilative, can
For making the army training clothes more demanding to wearability, tear resistance.
In conclusion the present invention produces close SEILE textile strand line using six fibers of polyamide fibre pair and combed long staple cotton are blended,
The fabric strength property of strand production is good, and wearability is good, moisture absorption is ventilative, can be used for making and want to wearability, tear resistance
Seek higher army's training clothes.
The foregoing is merely presently preferred embodiments of the present invention, is not intended to limit the invention, it is all in spirit of the invention and
Within principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of production method of close SEILE textile strand, which is characterized in that blended by double six fibers of polyamide fibre and combed long staple cotton
It forms, includes the following steps:
(1) cotton cleaning process: griping cotton machine hired roughneck's decrease speed each 3mm, revolving speed 960r/min, rotary machinery speed 2.8r/min,
Blade stretches out rib 3mm, Beater Speed 800r/min, fan speed 950r/min, the gauge 12mm of hired roughneck and pedal roller, cotton
Roller speed 12r/min is rolled up,
Double six fibers of polyamide fibre: the quantification of 361g/m of cotton roll dry weight, cotton roll length are 30.6m；
Long-staple cotton: the quantification of 350g/m of cotton roll dry weight, cotton roll length are 36.5m；
(2) carding step: cylinder and 7 mil of licker-in gauge, feed plate and 20 mil of licker-in gauge, cylinder and 4 English of doffer's gauge
Silk, mote knife height and machine frame are flat, knife spine with 90 ° of machine frame horizontal plane angle,
Double six fibers of polyamide fibre: cylinder speed 360r/min, licker-in speed 760r/min, doffer speed 16r/min, cover plate speed
162mm/min, the quantification of 19.6g/m of cotton carding dry weight, cylinder and 5 gauges of cover board are 10 mils × 9 mils × 8 mils × 8 English
Silk × 9 mils；
Long-staple cotton: cylinder speed 360r/min, licker-in speed 880r/min, doffer speed 15.5r/min, cover plate speed 251mm/
Min, the quantification of 14.05g/m of cotton carding dry weight, cylinder and 5 gauges of cover board are 8 mils × 7 mils × 7 mils × 7 mils × 8 English
Silk；
(3) combing process；
(4) mixing in doubling step: by one Yu Bing tri- and and, double six fibers of polyamide fibre are pre- and 7 and close, and dry weight quantifies 20.47g/
5m, roller gauge 12mm × 20mm, 6.7 times of mechanical commutation draft, 1.6 times of back area draft；It 6 and closes together, and closes and be assigned as 3 essences
Long wool sliver, double six ribbons of 3 polyamide fibres are combed, dry weight quantifies 16.9g/5m, roller gauge 10mm × 18mm, mechanical commutation draft 6.6
Times, 1.6 times of back area draft；It two and 7 and closes, dry weight quantifies 16.6g/5m, roller gauge 10mm × 18mm, mechanical commutation draft 7.1
Times, 1.4 times of back area draft；It three and 7 and closes, dry weight quantifies 16.5g/5m, roller gauge 10mm × 18mm, mechanical commutation draft 7.04
Times, 1.3 times of back area draft；
(5) Roving Frames: 4.7 twirls of roving twist/10cm, roller gauge use 10mm × 24mm × 42mm, back area draft 1.2
Times, nip gauge 7mm, the quantification of 3.84g/10m of rove dry weight, 8.59 times of mechanical commutation draft, front roller revolving speed 200r/min, weight in wet base
4g/10m, special number 400tex, twist factor 94, front roller diameter 28mm, pressing device winding number 2 enclose；
(6) spinning process；
(7) winding procedure；
(8) folding process；
(9) twisting process.
2. the production method of close SEILE textile strand according to claim 1, which is characterized in that the combing process: long
The suede cotton carded sliver combing preparation stage: silver lap combined roots are 20, dry weight 48g/m, and roller gauge is 12 × 16mm, and rouleau is long
Spend 235m, lap roller linear speed 61.7m/min；And roll up combined roots be 6, dry weight 45g/m, roller gauge be 10 ×
12mm, rouleau length 182m；Combing stage, dry weight 16.75g/5m, gauge 7mm are fed for length 5.2mm, and linters rate is
10%；Back zone drafting multiple 1.36,2 indexing of cambered plate positioning, hairbrush revolving speed 1000r/min, cylinder revolving speed 225 clamp secondary/min.
3. according to claim 1 to the production method of 2 described in any item close SEILE textile strands, which is characterized in that described thin
Yarn process: 49.8 times of mechanical commutation draft multiple, roller gauge is 17mm × 38mm, and back zone drafting multiple is 1.18 times, nip gauge
2.5mm, front roller diameter 27mm, front roller revolving speed 162r/min, 96.5 twirls of the twist/10cm, twist factor 391, rings model
PG1-4254, wire loop model W321 36#；The winding procedure: electronic yarn clearer parameter: cotton knot N:350% × 0.8cm, short and thick S:
160% × 1.6cm, long thick L:35% × 35cm, details T:-35% × 30cm, produce 55/45 16.3tex of N/J long and tightly match
Single thread；The folding process: producing on doubling machine, and two yarns are coiled into folding bobbin, both sides uniform tension in order, tension pulley side by side
N/J long is produced using 1g, 1460 turns/min of main motor revolving speed, front roller linear velocity 22.5m/min, groove drum diameter 86mm
The doubling that 55/45 number is 36；The twisting process: producing on two-for-one twister, and stock is made by combined single thread by two
Line, 73 twirls of the twist/10cm, twist factor 418, front roller linear velocity 11.1m/min, producing 55/45 number of N/J long is 36
Strand, the as described polyamide fibre and combed long staple cotton scribbled.
4. the production method of close SEILE textile strand according to claim 1, which is characterized in that double six fibers of polyamide fibre are at least
Reach following performance standard: than strong 5.62CN/dtex, elongation at break 55.29%, line density 1.67dtex, length 38mm, returning
Damp rate 1.63%.
5. the production method of close SEILE textile strand according to claim 1, which is characterized in that the needle cloth in carding step
Model are as follows: flat-clothing MCH32, Bearded-needle knitted cloth AC2030*01550, doffer's needle cloth AD4030*01890, taker-in roller wire
AT5610*06311。
6. the production method of close SEILE textile strand according to claim 1, which is characterized in that pass through one of Yu Bing tri-
And and, double six fibers of polyamide fibre are pre- and 7 and close, and 6 and close together, and close and be assigned as 3 combed long staple cotton items, 3 polyamide fibres are double
Six ribbons.
7. the production method of close SEILE textile strand according to claim 3, which is characterized in that rings used in spinning process
For PG1-4254, wire loop is W321 36#.
8. the production method of close SEILE textile strand according to claim 3, which is characterized in that the equipment that production line uses
It include: A002C type automatic plucker, A036B porcupine opener, A092A type tandem feeder, A076C type lapper, A186
Carding machine, SXF1338 lap former, SXF1348 ribbon lap machine, FA266 combing machine, FA305 drawing frame, A454 fly frame, FA502 are thin
Yarn machine, 21C~S bobbin-winding machine, TSB-36C doubling winder and TDN-128B chopped fiber two-for-one twisting machine.
9. a kind of close SEILE textile strand, which is characterized in that be made by the described in any item production methods of claim 1 to 8.
10. a kind of SEILE textile strand as claimed in claim 9 close for make to wearability, tear resistance require compared with
The purposes of high army's training clothes.