CN110923885A - 一种基于生物提取的功能性中药保健包芯纱的制备方法 - Google Patents
一种基于生物提取的功能性中药保健包芯纱的制备方法 Download PDFInfo
- Publication number
- CN110923885A CN110923885A CN201911200177.5A CN201911200177A CN110923885A CN 110923885 A CN110923885 A CN 110923885A CN 201911200177 A CN201911200177 A CN 201911200177A CN 110923885 A CN110923885 A CN 110923885A
- Authority
- CN
- China
- Prior art keywords
- extract
- cotton fibers
- cotton
- traditional chinese
- chinese medicine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种基于生物提取的功能性中药保健包芯纱的制备方法，依次通过松散除杂‑预处理‑整理‑纤维混合‑纺纱制得功能性中药保健针织高支纱，在制备方法填充了传统中草药保健的作用方式，最终得到高品质生物提取的功能性中药保健针织高支纱，使其获得了提高免疫力、疾病预防等等生态保健功能性，通过纱线整理的方法将中草药提取物吸附固着在棉纤维上，得到不同功能性的棉，然后根据所需功能进行多种功能纤维的混拼，最终得到高品质生物提取的功能性中药保健针织高支纱，使其获得了提高免疫力、疾病预防等等生态保健功能性，适合于体质比较差的特殊人群的高端针织服装，突出了服装的特殊风格。
Description
技术领域
本发明涉及设计一种基于生物提取的功能性中药保健包芯纱的制备方法，应用于功能性纯棉面料织造，以达到生态、环保、保健等功能性。
背景技术
随着人们生活水平的提高, 对纺织品的质量要求也越来越高, 回归大自然 的呼声日益强烈, 衣着追求舒适、自然和保健, 因此提高纺织品的附加值, 使产品多样化、功能化和高档化是纺织品整理和纺织品制备的发展方向。
中国是中医中药的故乡, 我国植物资源丰富, 古人开发利用药用植物资源更是历史悠久, 用现代 科学技术挖掘和整理这笔宝贵遗产, 可以继续造福人类。中草药不仅能对纺织品染色而且具有医疗保健功效, 开发具有多功能的中草药保健纺织品, 起到滋润皮肤、抗菌防臭、抗紫外线等保健作用, 有利于人的身心健康和延年益寿, 既满足了生态环保的生产需求, 又符合健康、功能化的服用要求, 适合于体质比较差的特殊人群的高端针织服装，突出了服装的特殊风格。
发明内容
发明目的：本发明的目的是针对目前市场上对高端纺织品的需求，解决传统口服中草药汤剂和丸药，通过纱线整理的方法将中草药提取物吸附固着在棉纤维上，得到不同功能性的棉，然后根据所需功能进行多种功能纤维的混拼，最终得到高品质生物提取的功能性中药保健针织高支纱，使其获得了提高免疫力、疾病预防等等生态保健功能性，适合于体质比较差的特殊人群的高端针织服装，突出了服装的特殊风格。
为了达到上述目的，本发明提供了一种基于生物提取的功能性中药保健包芯纱的制备方法，填充了传统中草药保健的作用方式，最终得到高品质生物提取的功能性中药保健针织高支纱，使其获得了提高免疫力、疾病预防等等生态保健功能性。
本发明的技术原理是：设计生物提取的功能性中药保健纺针织高支纱制备工艺流程及各个步骤的工艺条件。包括：除杂、松解、开松、预处理、中草药整理、棉混拼、梳理、精梳、牵伸、加捻、卷绕，最后得到各种功能的高品质生物提取的功能性中药保健针织高支纱。
技术方案：为实现上述目的，本发明提供了一种基于生物提取的功能性中药保健包芯纱的制备方法，所述方法的具体步骤如下：
步骤1、松散除杂：将原棉进行除杂、松解、开松，制备成松散的棉纤维；
步骤2、预处理:对步骤1中的棉纤维进行预处理，预处理采用超声波碱氧一浴预处理，其中碱氧一浴工艺处方：碱液浓度4.0-6.0g/L，双氧水浓度4.0-6.0g/L；
步骤3、整理：棉纤维中草药提取物整理工艺，得到功能性棉纤维，所述中草药提取物至少包含当归提取物、党参提取物及黄芪提取物中的其中两种，将步骤2处理后的棉纤维分别进行吸附中草药提取物，进行整理工艺，得到对应的中草药棉纤维；
步骤4、纤维混合：将步骤3中制得的至少两种不同的中草药棉纤维作为原料，放入纤维混合机中进行充分混合，得到混合棉纤维；
步骤5、纺纱：将步骤4中混合棉纤维进行纺纱处理，所述纺纱处理依次包括梳理、精梳、牵伸、加捻、卷绕，经纺纱处理后制得高品质生物提取的功能性中药保健针织高支纱。
进一步的，所述步骤2超声波碱氧一浴预处理中工艺条件：超声波作用时间45-70min，作用温度40-60℃。
进一步的，所述将步骤3中原棉纤维与中草药提取物进行整理工艺分别为当归提取物整理工艺、党参提取物整理工艺及黄芪提取物整理工艺，具体如下：
当归提取物整理工艺：吸附时间为40-60min、当归提取物用量为3-10%(omf)、pH值为5-7、吸附温度为30-50℃、浴比为1:10-1:40；党参提取物整理工艺：吸附时间为40-60min、党参提取物用量为3-10%(omf)、pH值为6-7、吸附温度为30-60℃、浴比为1:15-1:30；黄芪提取物整理工艺：吸附时间为30-50min、纤维提取物用量为4-8%(omf)、pH值为5-7、吸附温度为30-70℃、浴比为1:10-1:40。
优选的，所述步骤3将当归棉、党参棉纤维为原料进行混合，其中将当归棉纤维、党参棉纤维以1:1比例进行混合。
优选的，所述步骤3将当归棉纤维、黄芪棉纤维为原料进行混合，其中将当归棉纤维、黄芪棉纤维以2:1比例进行混合。
优选的，所述步骤3将当归棉纤维、党参棉纤维、黄芪棉纤维为原料进行混合，其中将当当归棉纤维、党参、黄芪棉纤维、棉纤维以2:1:1比例进行混合。
有益效果：本发明制备一种基于生物提取的功能性中药保健包芯纱的制备方法，通过本发明对散棉进行超声波碱氧一浴预处理，然后进行不同功能的天然中草药提取物整理，得到不同功能的散棉，然后根据所需功能进行多种纤维的混纤混拼，最终得到高品质生物提取的功能性中药保健针织高支纱，使其获得了提高免疫力、疾病预防等等生态保健功能性，适合于体质比较差的特殊人群的高端针织服装，突出了服装的特殊风格。
具体实施方式
实施例1
一种基于生物提取的功能性中药保健包芯纱的制备方法，所述方法的具体步骤如下：
步骤1、松散除杂：将原棉进行除杂、松解、开松，制备成松散的棉纤维；
步骤2、预处理：对步骤1中的棉纤维进行预处理，预处理步骤采用超声波碱氧一浴预处理，其中，碱氧一浴工艺处方：碱液浓度4.0/L，双氧水浓度4.0/L，工艺条件：超声波作用时间45min，作用温度40℃；
步骤3、整理：棉纤维中草药提取物整理工艺，得到功能性棉纤维，将步骤2处理后的棉纤维分别进行吸附中草药提取物，所述中草药提取物分别为当归提取物和党参提取物，进行整理工艺，得到对应的当归棉纤维和党参棉纤维；具体如下：
棉纤维吸附当归提取物：当归提取物整理工艺处方：吸附时间为40min、提取物用量为3%(omf)、pH值为5、吸附温度为30℃、浴比为1:40；
棉纤维吸附党参提取物：党参提取物整理工艺处方：吸附时间为40min、提取物用量为3%(omf)、pH值为6、吸附温度为30℃、浴比为1:30；
步骤4、纤维混合：将步骤3中制得的当归棉纤维、党参棉纤维为原料，放入纤维混合机中进行充分混合，其中当归棉纤维、党参棉纤维以1:1比例进行混合，得到混合棉纤维；
步骤5、将步骤4制得的混合棉纤维按照纺纱原理进行梳理、精梳、牵伸、加捻、卷绕，制得不同功能的中药保健针织高支纱。
实施例2
一种基于生物提取的功能性中药保健包芯纱的制备方法，所述方法的具体步骤如下：
步骤1、松散除杂：将原棉进行除杂、松解、开松，制备成松散的棉纤维；
步骤2、预处理：对步骤1中的棉纤维进行预处理，预处理步骤采用超声波碱氧一浴预处理，其中，碱氧一浴工艺处方：碱液浓度5.0g/L，双氧水浓度5.0g/L，工艺条件：超声波作用时间50min，作用温度50℃；
步骤3、整理：棉纤维中草药提取物整理工艺，得到功能性棉纤维，将步骤2处理后的棉纤维分别进行吸附中草药提取物，所述中草药提取物分别为当归提取物和黄芪提取物，进行整理工艺，得到对应的当归棉纤维和黄芪棉纤维；具体如下：
棉纤维吸附当归提取物：当归提取物整理工艺处方：吸附时间为50min、提取物用量为4%(omf)、pH值为5、吸附温度为50℃、浴比为1:30；
棉纤维吸附黄芪提取物：黄芪提取物整理工艺处方：吸附时间为40min、提取物用量为4%(omf)、pH值为6、吸附温度为40℃、浴比为1:30；
步骤4、纤维混合：将步骤3中制得的当归棉纤维、黄芪棉纤维为原料，放入纤维混合机中进行充分混合，其中当归棉纤维、黄芪棉纤维以2:1比例进行混合，得到混合棉纤维；
步骤5、将步骤4制得的混合棉纤维按照纺纱原理进行梳理、精梳、牵伸、加捻、卷绕，制得不同功能的中药保健针织高支纱。
实施例3
一种基于生物提取的功能性中药保健包芯纱的制备方法，所述方法的具体步骤如下：
步骤1、松散除杂：将原棉进行除杂、松解、开松，制备成松散的棉纤维；
步骤2、预处理：对步骤1中的棉纤维进行预处理，预处理步骤采用超声波碱氧一浴预处理，其中，碱氧一浴工艺处方：碱液浓度6.0/L，双氧水浓度6.0/L；工艺条件：超声波作用时间70min，作用温度60℃；
步骤3、整理：棉纤维中草药提取物整理工艺，得到功能性棉纤维，将步骤2处理后的棉纤维分别进行吸附中草药提取物，所述中草药提取物分别为当归提取物、党参提取物及黄芪提取物，进行整理工艺，得到对应的当归棉纤维、党参棉纤维、黄芪棉纤维；具体如下：
散棉吸附当归提取物：当归提取物整理工艺处方：吸附时间为60min、提取物用量为10%(omf)、pH值为7、吸附温度为50℃、浴比为1:10；
散棉吸附党参提取物：党参提取物整理工艺处方：吸附时间为60min、提取物用量为10%(omf)、pH值为7、吸附温度为60℃、浴比为1:15；
散棉吸附黄芪提取物：黄芪提取物整理工艺处方：吸附时间为50min、提取物用量为8%(omf)、pH值为7、吸附温度为70℃、浴比为1:10；
步骤4、纤维混合：将步骤3中制得的当归棉纤维、党参棉纤维、黄芪棉纤维为原料，放入纤维混合机中进行充分混合，其中当当归棉纤维、党参棉纤维、黄芪棉纤维以2:1:1比例进行混合，得到混合棉纤维；步骤5、将步骤2中制得的混合棉纤维按照纺纱原理进行梳理、精梳、牵伸、加捻、卷绕，制得不同功能的中药保健针织高支纱。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内，当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案的内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。
Claims (6)
1.一种基于生物提取的功能性中药保健包芯纱的制备方法，其特征在于：所述方法的具体步骤如下：
步骤1、松散除杂：将原棉进行除杂、松解、开松，制备成松散的棉纤维；
步骤2、预处理:对步骤1中的棉纤维进行预处理，预处理采用超声波碱氧一浴预处理，其中碱氧一浴工艺处方：碱液浓度4.0-6.0g/L，双氧水浓度4.0-6.0g/L；
步骤3、整理：棉纤维中草药提取物整理工艺，得到功能性棉纤维，所述中草药提取物至少包含当归提取物、党参提取物及黄芪提取物中的其中两种，将步骤2处理后的棉纤维分别进行吸附中草药提取物，进行整理工艺，得到对应的中草药棉纤维；
步骤4、纤维混合：将步骤3中制得的至少两种不同的中草药棉纤维作为原料，放入纤维混合机中进行充分混合，得到混合棉纤维；
步骤5、纺纱：将步骤4中混合棉纤维进行纺纱处理，所述纺纱处理依次包括梳理、精梳、牵伸、加捻、卷绕，经纺纱处理后制得高品质生物提取的功能性中药保健针织高支纱。
2.根据权利要求1所述的一种基于生物提取的功能性中药保健包芯纱的制备方法，其特征在于：所述步骤2超声波碱氧一浴预处理中工艺条件：超声波作用时间45-70min，作用温度40-60℃。
3.根据权利要求1所述的一种基于生物提取的功能性中药保健包芯纱的制备方法，其特征在于：所述将步骤3中原棉纤维与中草药提取物进行整理工艺分别为当归提取物整理工艺、党参提取物整理工艺及黄芪提取物整理工艺，具体如下：
当归提取物整理工艺：吸附时间为40-60min、当归提取物用量为3-10%(omf)、pH值为5-7、吸附温度为30-50℃、浴比为1:10-1:40；党参提取物整理工艺：吸附时间为40-60min、党参提取物用量为3-10%(omf)、pH值为6-7、吸附温度为30-60℃、浴比为1:15-1:30；黄芪提取物整理工艺：吸附时间为30-50min、纤维提取物用量为4-8%(omf)、pH值为5-7、吸附温度为30-70℃、浴比为1:10-1:40。
4.根据权利要求1所述的一种基于生物提取的功能性中药保健包芯纱的制备方法，其特征在于：所述步骤3将当归棉、党参棉纤维为原料进行混合，其中将当归棉纤维、党参棉纤维以1:1比例进行混合。
5.根据权利要求1所述的一种基于生物提取的功能性中药保健包芯纱的制备方法，其特征在于：所述步骤3将当归棉纤维、黄芪棉纤维为原料进行混合，其中将当归棉纤维、黄芪棉纤维以2:1比例进行混合。
6.根据权利要求1所述的一种基于生物提取的功能性中药保健包芯纱的制备方法，其特征在于：所述步骤3将当归棉纤维、党参棉纤维、黄芪棉纤维为原料进行混合，其中将当当归棉纤维、党参、黄芪棉纤维、棉纤维以2:1:1比例进行混合。