CN1108988A - Dry process for manufacture of non-adhesive hardboard - Google Patents
Dry process for manufacture of non-adhesive hardboard Download PDFInfo
- Publication number
- CN1108988A CN1108988A CN 94102560 CN94102560A CN1108988A CN 1108988 A CN1108988 A CN 1108988A CN 94102560 CN94102560 CN 94102560 CN 94102560 A CN94102560 A CN 94102560A CN 1108988 A CN1108988 A CN 1108988A
- Authority
- CN
- China
- Prior art keywords
- dry
- manufacture method
- hardboard
- glue
- well
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The method for manufacturing artificial board without adhesive includes such technical steps as separating of raw plant materials, drying, shaping without syuthetic resin, and hot pressing. The obtained hard fibrd board features better water resistance, and good physical mechanical performance.
Description
The present invention is the manufacture method that a kind of dry method does not have the glue hardboard, belongs to the B27N class in International Classification of Patents.This method be with plant material through fiber separation, drying, do not applying the method that the condition compacted under of synthetic resin gum, hot pressing get a kind of artificial board, the alternative timber of its product is used for furniture, fields such as interior decoration, building, the vehicles, packing.
U.S.'s dry-process fiberboard that begins one's study the forties begins suitability for industrialized production the fifties.Aborning,, generally all to add a spot of synthetic resin gum for improving the intensity and the water proofing property of plate, however one of principal element that resin glue but is a board cost to rise.For without glue, and can guarantee the performance of sheet material, all carry out the research of non-glue fibre board in recent years both at home and abroad.35 volume (1985) 2 phases of U.S.'s forestry products magazine, published the research report of American scholar about " two kinds of different fibrous raw materials are made non-glue fibre board ", the raw material (wood chip) that wherein a kind of method is a fiber, will boiling 2 '-2 ' 30 ' under the 1.3MPa vapour pressure ', the acquisition average moisture content is 60% wet fiber behind defibrination, under 104 ℃ of temperature, be dried to constant weight (over dry state) then, the weak point of this method is: 1. increase energy consumption, also be difficult to reach over dry because of safety factor in actual production; 2. the sheet material water absorption rate of making is 60%, substantially exceeds standard-required.The no glue making sheet technology that Canada Shen Guo town doctor invents (Chinese patent application number 85105958.9 specifications P.1-5,9-10), a projecting point is that plant fiber material need carry out in good time high-pressure water vapor processing, make the hemicellulose degraded in the raw material components and be hydrolyzed into water-soluble substances, its hot water extract is approximately about 10-30%, the method is used for common dry-process fiberboard production line, also the high steam pre-processing device must be before defibrination, acquired, the requirement of no glue glued adhesion could be satisfied.China Zhongnan Forestry Inst. journal 10 volume (nineteen ninety) 1 phases have been delivered the test report about " no glue dry horminess fibreboard heat pressing process discussion " such as Jiang Yuanzhou, common dry horminess fibreboard two sections pressurizations commonly used are adopted in this test, drawing hot pressing temperature by orthogonal test is remarkable influence factor, with 220 ℃ be best hot pressing temperature parameter, its weak point is: 1. hot pressing temperature height; 2. the sheet material water absorption rate is also higher, mostly surpasses 30%; 3. significantly the panel compacting is difficult, just as described herein, and being used for suitability for industrialized production also needs further research.
The objective of the invention is to avoid above-mentioned weak point of the prior art, but the production method that provides a kind of dry method of suitability for industrialized production not have the glue hardboard, and the quality of product can reach the hardboard request of national standard; Two of purpose of the present invention provides a kind of dry method that is directly used on the existing dry horminess fibreboard production line does not have glue hardboard production technology; Three of purpose of the present invention be for the process and technology innovation of wet pressed hardboard seek a kind of economy, feasible, do not have a method of contaminated wastewater again.
Except that not having " applying glue " operation, all the other are identical with existing dry horminess fibreboard production process, and device therefor is also identical.
The used plant material of the present invention mixes the fiber of seeds etc. for meaning poplar, birch, weedtree and factory, after washing under the 0.4-1.2MPa vapour pressure boiling and defibrination 1 '-15 ', the paraffin that applies 0-2% simultaneously is as waterproofing agent.But fiber separation vapour steps down to 0.4-0.7MPa, when the time, weak point was 1 '-6 ', then can improve the fiber yield, reduces the hot water extract, helps improving plate face quality and resistance to water, and table 1 is the hot water extract and the pH value of two kinds of fibers.
Table 1 hot water extract and pH value
| Seeds | Hot water extract % | PH value |
| The meaning poplar | 3.46 | 5.31 |
| Birch | 4.62 | 4.66 |
The tabular hot water extract is far below the requirement of aforementioned Shen Guo town patent of invention.The present invention can not apply paraffin, but applies the paraffin of 0.5-1.5%, then can obviously reduce the water absorption rate of sheet material, thereby make sheet material have excellent water tolerance.After the fiber discharging, be that to be dried to moisture content under the 170-190 ℃ of condition be 4-12% in the drying medium temperature, with the moisture content during for 5-8% for well, both can shorten pressing cycle, can obtain plate property preferably again.Dried fiber carries out hot pressing after shop blank molding, precompressed, the saw limit gets product.Adopt three sections pressurizations when characteristics of the present invention are hot pressing, its heat pressing process condition is:
Pressure: high pressure 3.4-6.4MPa(has the wet pressed hardboard press now, and general pressure is 5-5.4MPa)
Low pressure 0.5-2.0MPa
Temperature: 180-210 ℃
Time: t
1(high-pressure closing) 10 ' '-90 ' '
t
2(steam discharge) 30 ' '-240 ' '
t
3(mould and close) 30 ' '-240 ' '
Heat pressing process is that dry method does not have the key that the glue hardboard is made, and adopts process conditions of the present invention, does not apply any synthetic resin gum, and the dry method that makes does not have the desired value of the physical and mechanical property of glue hardboard above hardboard national standard seconds.
Adopt low temperature boiling technology and the hot pressing pressure that is lower than common dry horminess fibreboard, to make slurrying and leading portion equipment thereof in the existing wet pressed hardboard production line, loader and back segment equipment thereof, do not have and all can utilize when the glue hardboard is produced changing dry method into, reduced the input of technical cost.
The present invention does further narration in conjunction with the embodiments
Embodiment 1:
It is raw material that the present invention adopts meaning poplar, birch and different factories string, and aforementioned process conditions have been carried out multiple authentication, will verify that now the situation example is in table 2:
Embodiment 2:
The present invention has carried out the pilot production of an order of classes or grades at school on the dry-process fiberboard production line of timber company fibre-board plant, Zhuzhou City, pressing plate is 277 altogether, and specification is 2440 * 1220 * (3-8) mm.Production technology behind fiber drying, add after applying wax, the precompressed transversal, other processes are identical with the aforementioned technical process of the present invention.Raw material is a kind of to be meaning poplar, a kind of compound that adds a small amount of masson pine for the meaning poplar.The back wood chip moisture content of chipping is 50%, is 58% after the washing.With the continuous steamer boiling wood chip of total length 5m, vapour pressure is 0.6-0.65MPa, time 2 '.Because not applying glue, moisture participates in the no sizing material, so drying process is different with general dry method, and generally the medium inlet temperature of dry horminess fibreboard is 170-175 ℃, need the two-stage drying just can reach required moisture content.The medium inlet temperature is 120-125 ℃ during the dry meaning of the present invention poplar fiber, and the whole moisture content of one-level dried fibres reaches 5-6%, when dry meaning, loose compound, and 154 ℃ of medium inlet temperatures, the whole moisture content of one-level dried fibres reaches 6.8%.Applying wax amount 1.5%.The press number of plies is 10 layers, and during hot pressing temperature 195-203 ℃, it is that 5.4MPa(is consistent with existing wet method press pressure that maximum pressure has 39 cars), 1 car is the common dry method pressure of 6.3MPa(6.9-7.8MPa); Hot pressing time: meaning poplar plate 3 ' 30 ' '-6 ', poplar, deals 2 ' 30 ' '-3 ' 45 ' ', shorten time 1/2-1/3 than wet production.
In 277 plates of whole 40 car meters, randomly draw 16 cars totally 18 plates, carry out the physical and mechanical property test, meet the last 83% that account for of hardboard national standard spy, I and II plate index, concrete heat pressing process condition and performance exemplify as table 3
Table 3 pilot production hot pressing condition and product physical and mechanical property
Embodiment 3
The present invention has also carried out not adding the test of paraffin, and its main technique condition and sheet material physical and mechanical property see Table 4
Process conditions when table 4. does not add paraffin and sheet material physical and mechanical property
Add paraffin by finding out in the table that the sheet material water absorption rate that do not add paraffin will be higher than, but still meet the seconds requirement of hardboard national Specification.
The present invention compared with prior art has the following advantages:
1, the glue-free hardboard of dry method of producing with the present invention has good resistance to water, and its water absorption rate is starkly lower than general hardboard.
2, because not applying glue, adopt the one-level drying can reach required fiber moisture requirement, but therefore energy savings, and simplify drying device.
3, can make the manufacture of the glue-free hardboard of dry method.
4, existing dry horminess fibreboard production line adopts the present invention without any transformation, just can the glue-free hardboard of directly production dry method.
5, provide foundation for the wet pressed hardboard technological transformation, in existing wet-process fiber board is produced, only need to increase drying, moulding, pre-press equipment, can transform dry method non-glue fibre board production line as, thereby produce the product of pleasing both parties that the back side does not have wire mark, and can shorten pressing cycle than wet production, raise labour productivity, particularly but saving water resource is eliminated the contaminated wastewater in the wet production, makes the production of wet pressed hardboard obtain newborn.
6, one ton of dry horminess fibreboard, the applied amount of phenolic resin glue is about 3%, with no gluing method of the present invention, can reduce production costs about 1/3, and by present price, plate per ton can be saved about 300 yuan of sizing material expenses.
Claims (6)
1, a kind of manufacture method of dry method non-glue fibre board, main processes is:
Raw material → wood chip → washing →
→ moulding → precompressed → transversal → hot pressing → saw limit
It is characterized in that three sections pressurizations of the fashionable employing of slab hot compression molding, the heat pressing process condition is: high pressure 3.4-6.4MPa, low pressure 0.5-2.0MPa; Hot pressing temperature 180-210 ℃; Hot pressing time: t
1(high-pressure closing) 10 " 90 ", t
2(steam discharge) 30 " 240 ", t
3(mould and close) 30 " 240 ".
2, manufacture method according to claim 1, the defibrator process vapour pressure during its fiber separation is 0.4-1.2MPa, with 0.4-0.7MPa for well; Time is 1 '-15 ', with 1 '-6 ' for well.
3, manufacture method according to claim 1, the moisture content of dry back fiber is 4-12%, with 5-8% for well.
4, manufacture method according to claim 1 can apply paraffin in defibrator process or when dry, and the applying wax amount is 0-2%, with 0.5-1.5% for well.
5, manufacture method according to claim 1, the preferred value of its heat pressing process condition is: high pressure 5-5.4MPa, low pressure 1.3-1.7MPa, temperature 195-205 ℃.
6, manufacture method according to claim 1 is applicable to that the dry method of each plant fiber raw material do not have the manufacturing of glue hardboard.