CN110885585A - Production process of interior wall putty powder capable of purifying formaldehyde - Google Patents
Production process of interior wall putty powder capable of purifying formaldehyde Download PDFInfo
- Publication number
- CN110885585A CN110885585A CN201911195421.3A CN201911195421A CN110885585A CN 110885585 A CN110885585 A CN 110885585A CN 201911195421 A CN201911195421 A CN 201911195421A CN 110885585 A CN110885585 A CN 110885585A
- Authority
- CN
- China
- Prior art keywords
- putty powder
- formaldehyde
- interior wall
- powder
- production process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A production process of interior wall putty powder capable of purifying formaldehyde relates to the technical field of decoration and building materials. The invention provides a production process of interior wall putty powder capable of purifying formaldehyde for solving the problem of formaldehyde release of interior wall putty powder, and the invention discovers that German Ryansun is added®After the biological aldehyde-cleaning factor is adopted, the formaldehyde release amount of the putty powder can be greatly reduced, and meanwhile, formaldehyde in other materials can be adsorbed, so that an obvious aldehyde-cleaning effect is achieved.
Description
Technical Field
The invention relates to the technical field of decoration and building materials, in particular to a production process of interior wall putty powder capable of purifying formaldehyde.
Background
The putty powder is a base material for repairing and leveling the surface of a wall, is used for filling gaps of a construction surface and correcting curve deviation of the construction surface, and lays a good foundation for the decoration of paint, wallpaper and the like in the next step. The adhesive used in the production process of the putty powder contains a certain amount of formaldehyde, and the formaldehyde released by paint, wallpaper and the like are mutually overlapped, so that the formaldehyde in the indoor environment is easily overproof, and meanwhile, the formaldehyde release period of the materials is long, so that the health and safety of consumers are seriously influenced. Therefore, the environment-friendly interior wall putty powder is the key direction of future development.
Disclosure of Invention
In order to solve the problem of formaldehyde release of interior wall putty powder, the invention provides a production process of interior wall putty powder capable of purifying formaldehyde, which has an aldehyde-purifying function, can adsorb free formaldehyde, ensures that the formaldehyde release amount of the putty powder is far lower than the national standard, and can adsorb formaldehyde in other materials to play a role in purifying formaldehyde.
The invention provides the following technical scheme:
the formula proportion is as follows: 0.4-0.45% of NSJF-6A rubber powder, 50-60% of heavy calcium carbonate powder, 15-20% of sierozem powder, 15-20% of white cement (425 #), and 10-15% of aldehyde cleaning agent for putty powder, wherein the sum of the weight of the components is 100%.
Preferably, the putty powder is usedThe aldehyde-cleaning agent consists of 10 parts of German ryan Ryansunun®Biological aldehyde-removing factor, 70 parts of diatomite, 20 parts of activated clay, 5 parts of fumed silica and 2.5 parts of nano titanium dioxide;
the preparation method of the interior wall putty powder comprises the following steps:
1) mixing German ryan Ryansunun®Uniformly spraying biological aldehyde-cleaning factors on diatomite under high pressure, drying at 180 ℃, adding activated clay, gas-phase white carbon black and nano titanium dioxide, and uniformly stirring to prepare an aldehyde-cleaning agent for putty powder;
2) the NSJF-6A rubber powder, the calcium carbonate powder, the white cement and the putty powder are uniformly mixed and stirred for 20 minutes by using an aldehyde cleaning agent to obtain the interior wall putty powder capable of purifying formaldehyde.
The invention discovers that German Ryansun is added®After the biological aldehyde-cleaning factor is adopted, the formaldehyde release amount of the putty powder can be greatly reduced, and meanwhile, formaldehyde in other materials can be adsorbed, so that an obvious aldehyde-cleaning effect is achieved.
Detailed description of the preferred embodiments
The putty powder is prepared from the following raw materials in parts by weight: ryansunun, Laien, Germany®Biological clean aldehyde factor 10KG, diatomite 70KG, active clay 20KG, gas phase white carbon black 5KG and nanometer titanium dioxide 2.5 KG;
the putty powder for the inner wall comprises 4KG of NSJF-6A rubber powder, 50KG of double flying powder, 15KG of sierozem powder, 15KG of white cement (425 #), and 10KG of aldehyde cleaning agent for the putty powder.
The concrete steps
1) Mixing German ryan Ryansunun®Uniformly spraying biological aldehyde-cleaning factors on diatomite under high pressure, drying at 180 ℃, adding activated clay, gas-phase white carbon black and nano titanium dioxide, and uniformly stirring to prepare an aldehyde-cleaning agent for putty powder;
2) the NSJF-6A rubber powder, the calcium carbonate powder, the white cement and the putty powder are uniformly mixed and stirred for 20 minutes by using an aldehyde cleaning agent to obtain the interior wall putty powder capable of purifying formaldehyde.
The interior wall putty powder prepared in this example was added with German Ryansun®Biological aldehyde-cleaning factor capable of effectively adsorbing in other materialsThe free formaldehyde greatly reduces the release amount of formaldehyde and ensures that the indoor air reaches the environmental protection standard.
Claims (3)
1. The production process of the interior wall putty powder capable of purifying formaldehyde is characterized by comprising the following steps: the formula proportion is as follows: 0.4-0.45% of NSJF-6A rubber powder, 50-60% of heavy calcium carbonate powder, 15-20% of sierozem powder, 15-20% of white cement (425 #), and 10-15% of aldehyde cleaning agent for putty powder, wherein the sum of the weight of the components is 100%.
2. The production process of the formaldehyde-purifying interior wall putty powder as claimed in claim 1, which is characterized in that: the aldehyde cleaning agent for the putty powder is prepared from 10 parts of German ryan Ryansunun biological aldehyde cleaning factors, 70 parts of diatomite, 20 parts of activated clay, 5 parts of gas phase process white carbon black and 2.5 parts of nano titanium dioxide.
3. The production process of the formaldehyde-purifying interior wall putty powder as claimed in claim 1, which is characterized in that: uniformly spraying German Ryansun biological formaldehyde cleaning factors on diatomite at high pressure, drying at 180 ℃, adding activated clay, gas phase white carbon black and nano titanium dioxide, and uniformly stirring to prepare the formaldehyde cleaning agent for putty powder.