CN110877961A - Preparation method of anti-dazzle glass - Google Patents
Preparation method of anti-dazzle glass Download PDFInfo
- Publication number
- CN110877961A CN110877961A CN201811036480.1A CN201811036480A CN110877961A CN 110877961 A CN110877961 A CN 110877961A CN 201811036480 A CN201811036480 A CN 201811036480A CN 110877961 A CN110877961 A CN 110877961A
- Authority
- CN
- China
- Prior art keywords
- glass
- dazzle
- glass sheet
- placing
- processor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of anti-dazzle glass, which comprises the following steps of 1: cutting the glass sheet according to the requirement, washing the cut glass sheet with clear water, performing corrosion-resistant ink silk-screen printing (special screen printing machine), taking out the glass sheet, drying in an oven, and cooling in the step 2: placing the dried glass sheet into a processor, placing the glass into special formula bath liquid for anti-dazzle treatment for 12 hours, then pumping cleaning liquid into the processor by a pump, and discharging the cleaning liquid after cleaning is finished; and step 3: then the glass is fished out from the solution and then is washed clean by clear water, and the glass is subjected to deep processing treatment, so that the anti-dazzle effect is achieved.
Description
Technical Field
The invention relates to glass components, in particular to a preparation method of anti-dazzle glass.
Background
Anti-glare glass is also called antireflection glass or non-reflection glass. Is glass with the surface specially treated. The principle is that the single side or double sides of high-quality glass are processed. Compared with common glass, the glass has lower reflectance, and the light reflectivity is reduced to below 1%, so that the interference of ambient light is reduced, the definition and the energy of pictures are improved, the screen reflection is reduced, and the images are clearer and more vivid. The viewer can enjoy better visual effect.
SUMMARY OF THE PATENT FOR INVENTION
The invention aims to provide a preparation method of anti-dazzle glass.
The technical scheme for realizing the purpose is as follows: a preparation method of anti-dazzle glass comprises the following steps: step 1: cutting the glass sheet according to the requirement, washing the cut glass sheet with clear water, performing corrosion-resistant ink silk-screen printing (special screen printing machine), taking out the glass sheet, drying in an oven, and cooling in the step 2: placing the dried glass sheet into a processor, placing the glass into special formula bath liquid for anti-dazzle treatment for 12 hours, then pumping cleaning liquid into the processor by a pump, and discharging the cleaning liquid after cleaning is finished; and step 3: then the glass is fished out from the solution and then is washed clean by clear water, and the glass is subjected to deep processing treatment, so that the anti-dazzle effect is achieved.
The invention has the beneficial effects that: compared with common glass, the glass has lower reflectance, so that the light reflectivity is reduced to below 1 percent, the interference of ambient light is reduced, the definition of a picture is improved, the reflection of light on a screen is reduced, the image is clearer and more vivid, and a viewer can enjoy better visual effect. The anti-dazzle glass reduces the reflectivity of the glass surface to be less than or equal to 2 percent, the light transmittance to be more than or equal to 80 percent and the glossiness to be more than or equal to 60 percent.
Detailed Description
The embodiment is a preparation method of anti-dazzle glass, which comprises the following steps:
step 1: cutting the glass sheet according to the requirement, washing the cut glass sheet with clear water, performing corrosion-resistant ink silk-screen printing (special screen printing machine), taking out the glass sheet, drying in an oven, and cooling
Step 2: placing the dried glass sheet into a processor, placing the glass into special formula bath liquid for anti-dazzle treatment for 12 hours, then pumping cleaning liquid into the processor by a pump, and discharging the cleaning liquid after cleaning is finished;
and step 3: then the glass is fished out from the solution and then is washed clean by clear water, and the glass is subjected to deep processing treatment, so that the anti-dazzle effect is achieved.
The above description is only for the purpose of illustrating the preferred embodiments of the present invention and is not to be construed as limiting the present invention, and any modifications, equivalents, improvements and the like made within the spirit and principle of the present invention shall be included in the scope of the present invention.
Claims (1)
1. A preparation method of anti-dazzle glass is characterized in that: the method comprises the following steps:
step 1: cutting the glass sheet according to the requirement, washing the cut glass sheet with clear water, performing corrosion-resistant ink silk-screen printing (special screen printing machine), taking out the glass sheet, drying in an oven, and cooling
Step 2: placing the dried glass sheet into a processor, placing the glass into special formula bath liquid for anti-dazzle treatment for 12 hours, then pumping cleaning liquid into the processor by a pump, and discharging the cleaning liquid after cleaning is finished;
and step 3: then the glass is fished out from the solution and then is washed clean by clear water, and the glass is subjected to deep processing treatment, so that the anti-dazzle effect is achieved.