CN110857241A - Ceramic glaze formula - Google Patents
Ceramic glaze formula Download PDFInfo
- Publication number
- CN110857241A CN110857241A CN201810960631.6A CN201810960631A CN110857241A CN 110857241 A CN110857241 A CN 110857241A CN 201810960631 A CN201810960631 A CN 201810960631A CN 110857241 A CN110857241 A CN 110857241A
- Authority
- CN
- China
- Prior art keywords
- ceramic glaze
- ceramic
- glaze formula
- clay
- purity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A ceramic glaze formula belongs to the technical field of ceramic manufacturing and aims to achieve the purpose of improving the surface hardness of ceramic. The technical scheme adopted by the invention mainly comprises 55% of clay, 25% of silicon dioxide, 5% of zirconium oxide and the balance of water by mass percent. The ceramic glaze formula provided by the invention can form ceramic glaze with hard texture and can obtain good effect.
Description
Technical Field
The invention belongs to the technical field of ceramic manufacturing, and particularly relates to a ceramic glaze formula.
Background
Ceramics are various products made by kneading, shaping, and calcining clay or a mixture containing clay. Ranging from the coarsest earthenware to the finest fine ceramics and porcelain. In order to improve the hardness and the smoothness of the ceramic surface and expand the use value and the artistic value of the ceramic surface, a layer of ceramic glaze is generally coated on the surface of a product, and then the product is obtained by high-temperature sintering.
Disclosure of Invention
The technical problem to be solved by the invention is to provide a ceramic glaze formula so as to achieve the purpose of improving the surface hardness of ceramics.
In order to solve the technical problems, the technical scheme adopted by the invention is as follows: a ceramic glaze formula mainly comprises clay, and is characterized in that the ceramic glaze formula comprises 55% of clay, 25% of silicon dioxide, 5% of zirconia and the balance of water by mass percent;
the purity of the clay is 87%;
the purity of the silicon dioxide is 99%;
the preparation method of the ceramic glaze formula comprises the following steps,
1) crushing, namely crushing the raw materials;
2) mixing, adding water into the crushed materials, and uniformly mixing at a high speed;
3) filtering, and filtering the mixture with a 400-mesh sieve to remove impurities;
through the steps, the ceramic glaze formula with excellent performance can be obtained.
According to the ceramic glaze formula obtained in the process, after the ceramic glaze formula is coated on a product, the ceramic glaze with hard texture can be formed through sintering, and a good effect can be obtained.
Detailed Description
Example 1:
a ceramic glaze formula mainly comprises 55% of clay, 25% of silicon dioxide, 5% of zirconia and the balance of water by mass percent;
the purity of the clay is 87%;
the purity of the silicon dioxide is 99%;
the preparation method of the ceramic glaze formula comprises the following steps,
1) crushing, namely crushing the raw materials;
2) mixing, adding water into the crushed materials, and uniformly mixing at a high speed;
3) filtering, and filtering the mixture with a 400-mesh sieve to remove impurities;
through the steps, the ceramic glaze formula with excellent performance can be obtained.
The ceramic glaze formula obtained by the process is coated on a product and then sintered to form the ceramic glaze with hard texture, so that a good effect can be obtained.
Claims (4)
1. A ceramic glaze formula mainly comprises clay, and is characterized in that: 55% of clay, 25% of silicon dioxide, 5% of zirconium oxide and the balance of water according to mass percentage.
2. A ceramic glaze formulation according to claim 1, wherein: the purity of the clay was 87%.
3. A ceramic glaze formulation according to claim 1, wherein: the purity of the silica was 99%.
4. A method for preparing a ceramic glaze formulation according to claims 1 to 3, characterized in that: comprises the following steps of (a) carrying out,
crushing, namely crushing the raw materials;
mixing, adding water into the crushed materials, and uniformly mixing at a high speed;
filtering, and filtering the mixture with a 400-mesh sieve to remove impurities;
through the steps, the ceramic glaze formula with excellent performance can be obtained.