CN105884348A - High-strength ceramic tile capable of removing peculiar smells and preparation method of high-strength ceramic tile - Google Patents
High-strength ceramic tile capable of removing peculiar smells and preparation method of high-strength ceramic tile Download PDFInfo
- Publication number
- CN105884348A CN105884348A CN201610222102.7A CN201610222102A CN105884348A CN 105884348 A CN105884348 A CN 105884348A CN 201610222102 A CN201610222102 A CN 201610222102A CN 105884348 A CN105884348 A CN 105884348A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- kaolin
- raw material
- strength ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength ceramic tile capable of removing peculiar smells. The high-strength ceramic tile comprises a green body and glaze, wherein the green body is prepared from raw materials in parts by weight as follows: 55-65 parts of zircon sand, 23-28 parts of radiobarite, 34-40 parts of coal cinder, 18-24 parts of sandstone, 10-15 parts of bentonite, 20-24 parts of potassium feldspar, 12-17 parts of corundum, 9-13 parts of kaolin, 3-5 parts of sodium tripolyphosphate, 7-10 parts of calcium titanate, 6-8 parts of a magnesium oxide and 8-12 parts of tempered glass; the glaze is prepared from raw materials in parts by weight as follows: 18-23 parts of kaolin, 25-30 parts of calcite, 25-30 parts of potassium feldspar, 6-9 parts of an aluminum oxide, 28-32 parts of fire rock clay, 16-19 parts of sepiolite, 12-15 parts of zirconium silicate, 13-15 parts of magnetic wave stone, 8-10 parts of diatomite and 2-5 parts of samarium oxide. The invention further provides a preparation method of the high-strength ceramic tile capable of removing peculiar smells. The prepared ceramic tile is prepared in a reasonable proportion, the mechanical performance of the ceramic tile can be improved by 20%, the peculiar smells can be removed, harmful substances are adsorbed, and purification of air is facilitated.
Description
Technical field
The present invention relates to building material field, a kind of can the high-strength ceramic brick and preparation method thereof of dispelling abnormal flavor.
Background technology
Modern society, the moulding of building is the most various, function is the most perfect, high-tech is increasingly being applied to building field, each product is all with research and development point that meeting the market requirement is self product, ornamental decorative effect from early days the most increasingly tends to nature, elegance, tool personality elements, and the market demand needing durable, environmental protection, growing with each passing hour.Ceramic is high, various in style with its strong adaptability, consistency, pattern enriches, good decorating effect, easily maintain, when it is applied to suitable environment, due to reaching its maturity of production technology, it is true to nature that the pattern of product also becomes closer to nature, thus favored by consumers.Along with developing rapidly of China's Building Ceramics Industry, China is more and more vigorous for the demand of building ceramics, especially Ceramic Tiles field.Existing Ceramic Tiles of a great variety, quality is uneven, and general strength is relatively low, and existing Ceramic Tiles only has single decoration functions, it is impossible to meet the demand that people improve day by day.
Summary of the invention
It is an object of the invention to provide a kind of can the high-strength ceramic brick and preparation method thereof of dispelling abnormal flavor, with the problem solving to propose in above-mentioned background technology.
For achieving the above object, the present invention provides following technical scheme:
A kind of can the high-strength ceramic brick of dispelling abnormal flavor, including base substrate and glaze, described base substrate is made up of according to the raw material of weight portion following: zircon sand 55-65 part, hokutolite 23-28 part, cinder 34-40 part, white sand rock 18-24 part, bentonite 10-15 part, potassium feldspar 20-24 part, corundum 12-17 part, Kaolin 9-13 part, sodium tripolyphosphate 3-5 part, calcium titanate 7-10 part, magnesium oxide 6-8 part, safety glass 8-12 part；Described glaze is made up of according to the raw material of weight portion following: Kaolin 18-23 part, calcite 25-30 part, potassium feldspar 25-30 part, aluminium oxide 6-9 part, fire rock mud 28-32 part, meerschaum 16-19 part, Zirconium orthosilicate. 12-15 part, magnetic wave stone 13-15 part, kieselguhr 8-10 part, Disamarium trioxide 2-5 part.
As the further scheme of the present invention: described base substrate is made up of according to the raw material of weight portion following: zircon sand 57-63 part, hokutolite 24-27 part, cinder 35-38 part, white sand rock 19-23 part, bentonite 11-14 part, potassium feldspar 21-23 part, corundum 13-16 part, Kaolin 10-12 part, sodium tripolyphosphate 4-5 part, calcium titanate 8-9 part, magnesium oxide 6-7 part, safety glass 9-11 part；Described glaze is made up of according to the raw material of weight portion following: Kaolin 19-22 part, calcite 26-28 part, potassium feldspar 26-29 part, aluminium oxide 7-8 part, fire rock mud 29-31 part, meerschaum 17-18 part, Zirconium orthosilicate. 13-14 part, magnetic wave stone 14-15 part, kieselguhr 9-10 part, Disamarium trioxide 3-4 part.
As the present invention further scheme: described base substrate is made up of according to the raw material of weight portion following: zircon sand 61 parts, hokutolite 25 parts, cinder 36 parts, 22 parts of white sand rock, bentonite 12 parts, potassium feldspar 23 parts, 14 parts of corundum, Kaolin 11 parts, sodium tripolyphosphate 5 parts, calcium titanate 8 parts, magnesium oxide 6 parts, safety glass 10 parts；Described glaze is made up of according to the raw material of weight portion following: Kaolin 21 parts, 27 parts of calcite, potassium feldspar 28 parts, aluminium oxide 8 parts, fire 30 parts of rock mud, meerschaum 17 parts, Zirconium orthosilicate. 13 parts, 14 parts of magnetic wave stone, 9 parts of kieselguhr, Disamarium trioxide 4 parts.
Described can the preparation method of high-strength ceramic brick of dispelling abnormal flavor, step is as follows:
1) weighing blank stock, in addition to sodium tripolyphosphate and calcium titanate, other blank stock are all put in ball mill, use ethanol as ball-milling medium, ball milling mixing 5-8h, are subsequently adding sodium tripolyphosphate and calcium titanate, continue ball milling mixing 1-2h, it is thus achieved that slurry；
2) sieving slurry, after drying, under 100-120Mpa, isostatic pressed is compressing, after at room temperature ageing 1-2 days, it is thus achieved that green compact；
3) by green compact presintering 50-60min at 850-860 DEG C, it is thus achieved that presintering green compact；
4) glaze raw material is weighed, after Kaolin, calcite, potassium feldspar, aluminium oxide, fire rock mud and meerschaum mix homogeneously, it is warming up to 950-1000 DEG C, insulation 3-4h, then it is cooled to 550-580 DEG C, is incubated 1-2h, pulverizes after water quenching cooling to room temperature, and cross 100-150 mesh sieve, it is thus achieved that the first mixing glaze；
5) Zirconium orthosilicate. in glaze raw material, magnetic wave stone, kieselguhr and Disamarium trioxide are put in ball mill, use ethanol as ball-milling medium, ball milling mixing 4-5h, be subsequently adding the first mixing glaze, continue ball milling mixing 1-2h, it is thus achieved that glaze；
6) glaze is sprayed at presintering green surface, be then sintered at 1250-1280 DEG C, it is thus achieved that can the high-strength ceramic brick of dispelling abnormal flavor.
Above-mentioned Ceramic Tiles can purify the air of a room.
Compared with prior art, the invention has the beneficial effects as follows:
Ceramic Tiles prepared by the present invention is by rational proportioning, it is possible to make mechanical performance and the mechanical property raising 20% of Ceramic Tiles, additionally, Ceramic Tiles prepared by the present invention can go to eliminate the unusual smell, absorption harmful substance, is conducive to purifying air, meets the environmental requirement that people improve day by day.
Detailed description of the invention
Below in conjunction with detailed description of the invention, technical scheme is described in more detail.
Embodiment 1
A kind of can the high-strength ceramic brick of dispelling abnormal flavor, including base substrate and glaze, described base substrate is made up of according to the raw material of weight portion following: zircon sand 55 parts, hokutolite 23 parts, cinder 34 parts, 18 parts of white sand rock, bentonite 10 parts, potassium feldspar 20 parts, 12 parts of corundum, Kaolin 9 parts, sodium tripolyphosphate 3 parts, calcium titanate 7 parts, magnesium oxide 6 parts, safety glass 8 parts；Described glaze is made up of according to the raw material of weight portion following: Kaolin 18 parts, 25 parts of calcite, potassium feldspar 25 parts, aluminium oxide 6 parts, fire 28 parts of rock mud, meerschaum 16 parts, Zirconium orthosilicate. 12 parts, 13 parts of magnetic wave stone, 8 parts of kieselguhr, Disamarium trioxide 2 parts.
Described in the present embodiment can the preparation method of high-strength ceramic brick of dispelling abnormal flavor, step is as follows:
1) weighing blank stock, in addition to sodium tripolyphosphate and calcium titanate, other blank stock are all put in ball mill, use ethanol as ball-milling medium, ball milling mixing 5h, are subsequently adding sodium tripolyphosphate and calcium titanate, continue ball milling mixing 1h, it is thus achieved that slurry；
2) sieving slurry, after drying, under 100Mpa, isostatic pressed is compressing, after at room temperature ageing 1 day, it is thus achieved that green compact；
3) by green compact presintering 50min at 850 DEG C, it is thus achieved that presintering green compact；
4) weigh glaze raw material, after Kaolin, calcite, potassium feldspar, aluminium oxide, fire rock mud and meerschaum mix homogeneously, be warming up to 950 DEG C, insulation 3h, is then cooled to 550 DEG C, is incubated 1h, water quenching cooling is pulverized to room temperature, and crosses 100 mesh sieves, it is thus achieved that the first mixing glaze；
5) Zirconium orthosilicate. in glaze raw material, magnetic wave stone, kieselguhr and Disamarium trioxide are put in ball mill, use ethanol as ball-milling medium, ball milling mixing 4h, be subsequently adding the first mixing glaze, continue ball milling mixing 1h, it is thus achieved that glaze；
6) glaze is sprayed at presintering green surface, be then sintered at 1250 DEG C, it is thus achieved that can the high-strength ceramic brick of dispelling abnormal flavor.
Embodiment 2
A kind of can the high-strength ceramic brick of dispelling abnormal flavor, including base substrate and glaze, described base substrate is made up of according to the raw material of weight portion following: zircon sand 65 parts, hokutolite 28 parts, cinder 40 parts, 24 parts of white sand rock, bentonite 15 parts, potassium feldspar 24 parts, 17 parts of corundum, Kaolin 13 parts, sodium tripolyphosphate 5 parts, calcium titanate 10 parts, magnesium oxide 8 parts, safety glass 12 parts；Described glaze is made up of according to the raw material of weight portion following: Kaolin 23 parts, 30 parts of calcite, potassium feldspar 30 parts, aluminium oxide 9 parts, fire 32 parts of rock mud, meerschaum 19 parts, Zirconium orthosilicate. 15 parts, 15 parts of magnetic wave stone, 10 parts of kieselguhr, Disamarium trioxide 5 parts.
Described in the present embodiment can the preparation method of high-strength ceramic brick of dispelling abnormal flavor, step is as follows:
1) weighing blank stock, in addition to sodium tripolyphosphate and calcium titanate, other blank stock are all put in ball mill, use ethanol as ball-milling medium, ball milling mixing 8h, are subsequently adding sodium tripolyphosphate and calcium titanate, continue ball milling mixing 2h, it is thus achieved that slurry；
2) sieving slurry, after drying, under 120Mpa, isostatic pressed is compressing, after at room temperature ageing 2 days, it is thus achieved that green compact；
3) by green compact presintering 60min at 860 DEG C, it is thus achieved that presintering green compact；
4) weigh glaze raw material, after Kaolin, calcite, potassium feldspar, aluminium oxide, fire rock mud and meerschaum mix homogeneously, be warming up to 1000 DEG C, insulation 4h, is then cooled to 580 DEG C, is incubated 2h, water quenching cooling is pulverized to room temperature, and crosses 150 mesh sieves, it is thus achieved that the first mixing glaze；
5) Zirconium orthosilicate. in glaze raw material, magnetic wave stone, kieselguhr and Disamarium trioxide are put in ball mill, use ethanol as ball-milling medium, ball milling mixing 5h, be subsequently adding the first mixing glaze, continue ball milling mixing 2h, it is thus achieved that glaze；
6) glaze is sprayed at presintering green surface, be then sintered at 1280 DEG C, it is thus achieved that can the high-strength ceramic brick of dispelling abnormal flavor.
Embodiment 3
A kind of can the high-strength ceramic brick of dispelling abnormal flavor, including base substrate and glaze, described base substrate is made up of according to the raw material of weight portion following: zircon sand 61 parts, hokutolite 25 parts, cinder 36 parts, 22 parts of white sand rock, bentonite 12 parts, potassium feldspar 23 parts, 14 parts of corundum, Kaolin 11 parts, sodium tripolyphosphate 5 parts, calcium titanate 8 parts, magnesium oxide 6 parts, safety glass 10 parts；Described glaze is made up of according to the raw material of weight portion following: Kaolin 21 parts, 27 parts of calcite, potassium feldspar 28 parts, aluminium oxide 8 parts, fire 30 parts of rock mud, meerschaum 17 parts, Zirconium orthosilicate. 13 parts, 14 parts of magnetic wave stone, 9 parts of kieselguhr, Disamarium trioxide 4 parts.
Described in the present embodiment can the preparation method of high-strength ceramic brick of dispelling abnormal flavor, step is as follows:
1) weighing blank stock, in addition to sodium tripolyphosphate and calcium titanate, other blank stock are all put in ball mill, use ethanol as ball-milling medium, ball milling mixing 6h, are subsequently adding sodium tripolyphosphate and calcium titanate, continue ball milling mixing 1.5h, it is thus achieved that slurry；
2) sieving slurry, after drying, under 110Mpa, isostatic pressed is compressing, after at room temperature ageing 1.5 days, it is thus achieved that green compact；
3) by green compact presintering 55min at 855 DEG C, it is thus achieved that presintering green compact；
4) weigh glaze raw material, after Kaolin, calcite, potassium feldspar, aluminium oxide, fire rock mud and meerschaum mix homogeneously, be warming up to 980 DEG C, insulation 3.5h, is then cooled to 560 DEG C, is incubated 1.5h, water quenching cooling is pulverized to room temperature, and crosses 130 mesh sieves, it is thus achieved that the first mixing glaze；
5) Zirconium orthosilicate. in glaze raw material, magnetic wave stone, kieselguhr and Disamarium trioxide are put in ball mill, use ethanol as ball-milling medium, ball milling mixing 4.5h, be subsequently adding the first mixing glaze, continue ball milling mixing 1.5h, it is thus achieved that glaze；
6) glaze is sprayed at presintering green surface, be then sintered at 1260 DEG C, it is thus achieved that can the high-strength ceramic brick of dispelling abnormal flavor.
Embodiment 4
A kind of can the high-strength ceramic brick of dispelling abnormal flavor, including base substrate and glaze, described base substrate is made up of according to the raw material of weight portion following: zircon sand 55 parts, hokutolite 28 parts, cinder 35 parts, 24 parts of white sand rock, bentonite 12 parts, potassium feldspar 24 parts, 17 parts of corundum, Kaolin 11 parts, sodium tripolyphosphate 5 parts, calcium titanate 8 parts, magnesium oxide 6 parts, safety glass 8 parts；Described glaze is made up of according to the raw material of weight portion following: Kaolin 23 parts, 26 parts of calcite, potassium feldspar 30 parts, aluminium oxide 8 parts, fire 32 parts of rock mud, meerschaum 16 parts, Zirconium orthosilicate. 14 parts, 15 parts of magnetic wave stone, 8 parts of kieselguhr, Disamarium trioxide 3 parts.
Described in the present embodiment can the preparation method of high-strength ceramic brick of dispelling abnormal flavor, step is as follows:
1) weighing blank stock, in addition to sodium tripolyphosphate and calcium titanate, other blank stock are all put in ball mill, use ethanol as ball-milling medium, ball milling mixing 6h, are subsequently adding sodium tripolyphosphate and calcium titanate, continue ball milling mixing 2h, it is thus achieved that slurry；
2) sieving slurry, after drying, under 120Mpa, isostatic pressed is compressing, after at room temperature ageing 1 day, it is thus achieved that green compact；
3) by green compact presintering 50min at 855 DEG C, it is thus achieved that presintering green compact；
4) weigh glaze raw material, after Kaolin, calcite, potassium feldspar, aluminium oxide, fire rock mud and meerschaum mix homogeneously, be warming up to 990 DEG C, insulation 4h, is then cooled to 550 DEG C, is incubated 1.5h, water quenching cooling is pulverized to room temperature, and crosses 150 mesh sieves, it is thus achieved that the first mixing glaze；
5) Zirconium orthosilicate. in glaze raw material, magnetic wave stone, kieselguhr and Disamarium trioxide are put in ball mill, use ethanol as ball-milling medium, ball milling mixing 4h, be subsequently adding the first mixing glaze, continue ball milling mixing 2h, it is thus achieved that glaze；
6) glaze is sprayed at presintering green surface, be then sintered at 1255 DEG C, it is thus achieved that can the high-strength ceramic brick of dispelling abnormal flavor.
Embodiment 5
A kind of can the high-strength ceramic brick of dispelling abnormal flavor, including base substrate and glaze, described base substrate is made up of according to the raw material of weight portion following: zircon sand 58 parts, hokutolite 28 parts, cinder 36 parts, 24 parts of white sand rock, bentonite 11 parts, potassium feldspar 24 parts, 15 parts of corundum, Kaolin 9 parts, sodium tripolyphosphate 5 parts, calcium titanate 10 parts, magnesium oxide 6 parts, safety glass 9 parts；Described glaze is made up of according to the raw material of weight portion following: Kaolin 23 parts, 25 parts of calcite, potassium feldspar 28 parts, aluminium oxide 7 parts, fire 32 parts of rock mud, meerschaum 18 parts, Zirconium orthosilicate. 15 parts, 14 parts of magnetic wave stone, 9 parts of kieselguhr, Disamarium trioxide 5 parts.
Described in the present embodiment can the preparation method of high-strength ceramic brick of dispelling abnormal flavor, step is as follows:
1) weighing blank stock, in addition to sodium tripolyphosphate and calcium titanate, other blank stock are all put in ball mill, use ethanol as ball-milling medium, ball milling mixing 7h, are subsequently adding sodium tripolyphosphate and calcium titanate, continue ball milling mixing 2h, it is thus achieved that slurry；
2) sieving slurry, after drying, under 100Mpa, isostatic pressed is compressing, after at room temperature ageing 2 days, it is thus achieved that green compact；
3) by green compact presintering 55min at 860 DEG C, it is thus achieved that presintering green compact；
4) weigh glaze raw material, after Kaolin, calcite, potassium feldspar, aluminium oxide, fire rock mud and meerschaum mix homogeneously, be warming up to 960 DEG C, insulation 3h, is then cooled to 580 DEG C, is incubated 2h, water quenching cooling is pulverized to room temperature, and crosses 100 mesh sieves, it is thus achieved that the first mixing glaze；
5) Zirconium orthosilicate. in glaze raw material, magnetic wave stone, kieselguhr and Disamarium trioxide are put in ball mill, use ethanol as ball-milling medium, ball milling mixing 4h, be subsequently adding the first mixing glaze, continue ball milling mixing 1h, it is thus achieved that glaze；
6) glaze is sprayed at presintering green surface, be then sintered at 1280 DEG C, it is thus achieved that can the high-strength ceramic brick of dispelling abnormal flavor.
Ceramic Tiles prepared by the present invention is by rational proportioning, it is possible to make mechanical performance and the mechanical property raising 20% of Ceramic Tiles, additionally, Ceramic Tiles prepared by the present invention can go to eliminate the unusual smell, absorption harmful substance, is conducive to purifying air, meets the environmental requirement that people improve day by day.
Above the better embodiment of the present invention is explained in detail, but the present invention is not limited to above-mentioned embodiment, in the ken that one skilled in the relevant art is possessed, it is also possible to various changes can be made on the premise of without departing from present inventive concept.
Claims (5)
1. one kind can the high-strength ceramic brick of dispelling abnormal flavor, it is characterized in that, including base substrate and glaze, described base substrate is made up of according to the raw material of weight portion following: zircon sand 55-65 part, hokutolite 23-28 part, cinder 34-40 part, white sand rock 18-24 part, bentonite 10-15 part, potassium feldspar 20-24 part, corundum 12-17 part, Kaolin 9-13 part, sodium tripolyphosphate 3-5 part, calcium titanate 7-10 part, magnesium oxide 6-8 part, safety glass 8-12 part；Described glaze is made up of according to the raw material of weight portion following: Kaolin 18-23 part, calcite 25-30 part, potassium feldspar 25-30 part, aluminium oxide 6-9 part, fire rock mud 28-32 part, meerschaum 16-19 part, Zirconium orthosilicate. 12-15 part, magnetic wave stone 13-15 part, kieselguhr 8-10 part, Disamarium trioxide 2-5 part.
The most according to claim 1 can the high-strength ceramic brick of dispelling abnormal flavor, it is characterized in that, described base substrate is made up of according to the raw material of weight portion following: zircon sand 57-63 part, hokutolite 24-27 part, cinder 35-38 part, white sand rock 19-23 part, bentonite 11-14 part, potassium feldspar 21-23 part, corundum 13-16 part, Kaolin 10-12 part, sodium tripolyphosphate 4-5 part, calcium titanate 8-9 part, magnesium oxide 6-7 part, safety glass 9-11 part；Described glaze is made up of according to the raw material of weight portion following: Kaolin 19-22 part, calcite 26-28 part, potassium feldspar 26-29 part, aluminium oxide 7-8 part, fire rock mud 29-31 part, meerschaum 17-18 part, Zirconium orthosilicate. 13-14 part, magnetic wave stone 14-15 part, kieselguhr 9-10 part, Disamarium trioxide 3-4 part.
The most according to claim 2 can the high-strength ceramic brick of dispelling abnormal flavor, it is characterized in that, described base substrate is made up of according to the raw material of weight portion following: zircon sand 61 parts, hokutolite 25 parts, cinder 36 parts, 22 parts of white sand rock, bentonite 12 parts, potassium feldspar 23 parts, 14 parts of corundum, Kaolin 11 parts, sodium tripolyphosphate 5 parts, calcium titanate 8 parts, magnesium oxide 6 parts, safety glass 10 parts；Described glaze is made up of according to the raw material of weight portion following: Kaolin 21 parts, 27 parts of calcite, potassium feldspar 28 parts, aluminium oxide 8 parts, fire 30 parts of rock mud, meerschaum 17 parts, Zirconium orthosilicate. 13 parts, 14 parts of magnetic wave stone, 9 parts of kieselguhr, Disamarium trioxide 4 parts.
4. one kind as described in claim 1-3 is arbitrary can the preparation method of high-strength ceramic brick of dispelling abnormal flavor, it is characterised in that step is as follows:
1) weighing blank stock, in addition to sodium tripolyphosphate and calcium titanate, other blank stock are all put in ball mill, use ethanol as ball-milling medium, ball milling mixing 5-8h, are subsequently adding sodium tripolyphosphate and calcium titanate, continue ball milling mixing 1-2h, it is thus achieved that slurry；
2) sieving slurry, after drying, under 100-120Mpa, isostatic pressed is compressing, after at room temperature ageing 1-2 days, it is thus achieved that green compact；
3) by green compact presintering 50-60min at 850-860 DEG C, it is thus achieved that presintering green compact；
4) glaze raw material is weighed, after Kaolin, calcite, potassium feldspar, aluminium oxide, fire rock mud and meerschaum mix homogeneously, it is warming up to 950-1000 DEG C, insulation 3-4h, then it is cooled to 550-580 DEG C, is incubated 1-2h, pulverizes after water quenching cooling to room temperature, and cross 100-150 mesh sieve, it is thus achieved that the first mixing glaze；
5) Zirconium orthosilicate. in glaze raw material, magnetic wave stone, kieselguhr and Disamarium trioxide are put in ball mill, use ethanol as ball-milling medium, ball milling mixing 4-5h, be subsequently adding the first mixing glaze, continue ball milling mixing 1-2h, it is thus achieved that glaze；
6) glaze is sprayed at presintering green surface, be then sintered at 1250-1280 DEG C, it is thus achieved that can the high-strength ceramic brick of dispelling abnormal flavor.
5. the purposes in air cleaning of the Ceramic Tiles as described in claim 1-3 is arbitrary.