CN110845895A - Multifunctional anion interior wall putty - Google Patents
Multifunctional anion interior wall putty Download PDFInfo
- Publication number
- CN110845895A CN110845895A CN201911264130.5A CN201911264130A CN110845895A CN 110845895 A CN110845895 A CN 110845895A CN 201911264130 A CN201911264130 A CN 201911264130A CN 110845895 A CN110845895 A CN 110845895A
- Authority
- CN
- China
- Prior art keywords
- parts
- negative ion
- interior wall
- powder
- wall putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses multifunctional negative ion interior wall putty, and relates to the technical field of decorative materials. The material comprises the following components in parts by weight: 25-35 parts of Portland cement; 0.1-0.3 part of water reducing agent; 7-15 parts of limestone powder; 5-10 parts of nano tourmaline powder; 20-30 parts of shell powder; 1-3 parts of nano zinc oxide; 0.5-1 part of wood fiber; 0.3-0.5 part of polyethylene cellulose; 1-3 parts of HJS-OP silicone-acrylic redispersible rubber powder; 1-3 parts of acrylic waterproof rubber powder. The multifunctional negative ion putty for interior walls, provided by the invention, is added with nano tourmaline as an activation catalyst, and nano titanium and nano zinc oxide are catalyzed to generate strong oxidation free radical OH+And active O2‑The shell powder contains rich pore structures, and can adsorb harmful gas, degrade harmful organic substances such as formaldehyde, benzene, ammonia substances, TOVC and other toxic and harmful gases and generate harmless H by matching with other components2O and CO2And a large amount of negative ions are generated, so that the effects of sterilizing, purifying air and removing peculiar smell are achieved.
Description
Technical Field
The invention relates to the technical field of decorative coatings, in particular to multifunctional negative ion interior wall putty.
Background
With the development of economy, the requirements of people on physical life are improved, people pay attention to health, and people also have new knowledge and pursuit on indoor and decorative materials. The existing decorative materials are changed greatly from inner wall putty brush, inner wall latex paint and wall paper to diatom ooze paint in form, or from aesthetic appearance, environmental protection, moisture resistance, negative ion release and the like in functional requirements. However, the existing decorating materials also face the same problems: poor water resistance, easy delamination and peeling, complex construction and the like (high construction cost).
Disclosure of Invention
The invention aims to solve the technical problem of providing the interior wall putty which is convenient to construct, low in manufacturing cost, capable of being made into any shape and has multiple functions.
In order to solve the above problems, the present invention proposes the following technical solutions:
the multifunctional negative ion interior wall putty comprises the following components in parts by weight:
25 parts of Portland cement;
0.1-0.3 part of water reducing agent;
7-15 parts of limestone powder;
5-10 parts of nano tourmaline powder;
20-30 parts of shell powder;
1-3 parts of nano zinc oxide;
0.5-1 part of wood fiber;
0.3-0.5 part of polyethylene cellulose;
1-3 parts of HJS-OP silicone-acrylic redispersible rubber powder;
1-3 parts of acrylic waterproof rubber powder.
Further, the water reducing agent is poly-amino acid.
Further, the particle size of the limestone powder is 800-1000 meshes.
Further, the particle size of the nano tourmaline powder is 800-1000 meshes.
Further, the particle size of the shell powder is 200-300 meshes.
Furthermore, the particle size of the nano zinc oxide is 10-30 meshes.
Further, the particle size of the wood fiber is 50-100 meshes.
Further, the viscosity of the polyethyl cellulose is 10 ten thousand mpa.s.
Further, the portland cement is 325-mesh white portland cement.
Compared with the prior art, the invention can achieve the following technical effects:
the multifunctional negative ion putty for interior walls provided by the invention is added with nano tourmalineAs an activating catalyst, the nano titanium and the nano zinc oxide are catalyzed to generate strong oxidation free radical OH+And active O2-The shell powder contains rich pore structures, and can adsorb harmful gas, degrade harmful organic substances such as formaldehyde, benzene, ammonia substances, TOVC and other toxic and harmful gases and generate harmless H by matching with other components2O and CO2And a large amount of negative ions are generated, so that the effects of sterilizing, purifying air and removing peculiar smell are achieved.
Detailed Description
The technical solutions in the examples will be clearly and completely described below. It is apparent that the embodiments to be described below are only a part of the embodiments of the present invention, and not all of them. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Embodiment 1, this embodiment provides a multifunctional negative ion interior wall putty, including the following components in parts by weight:
25 parts of 325-mesh white Portland cement;
0.3 part of a polyamino acid water reducing agent;
7 parts of 800-mesh limestone powder;
5 parts of 1000-mesh nano tourmaline powder;
30 parts of 200-mesh shell powder;
1 part of 10-mesh nano zinc oxide;
1 part of 50-mesh wood fiber;
0.3 part of polyethylene cellulose with the viscosity of 10 ten thousand mpa.s;
1 part of HJS-OP silicone acrylic redispersible rubber powder;
1 part of acrylic waterproof glue powder.
Embodiment 2, this embodiment provides a multifunctional negative ion interior wall putty, which comprises the following components in parts by weight:
35 parts of 325-mesh white Portland cement;
0.1 part of a polyamino acid water reducing agent;
9 parts of limestone powder with the granularity of 900 meshes;
8 parts of 900-mesh nano tourmaline powder;
20 parts of 250-mesh shell powder;
3 parts of 30-mesh nano zinc oxide;
0.8 part of 100-mesh wood fiber;
0.5 part of polyethylene cellulose with the viscosity of 10 ten thousand mpa.s;
3 parts of HJS-OP silicone acrylic redispersible rubber powder;
3 parts of acrylic waterproof rubber powder.
Embodiment 3, this example provides a multifunctional negative ion interior wall putty, including the following components in parts by weight:
30 parts of 325-mesh white Portland cement;
0.2 part of a polyamino acid water reducing agent;
15 parts of 1000-mesh limestone powder;
10 parts of 800-mesh nano tourmaline powder;
25 parts of 300-mesh shell powder;
2 parts of 20-mesh nano zinc oxide;
0.5 part of 80-mesh wood fiber;
0.4 part of polyethylene cellulose with the viscosity of 10 ten thousand mpa.s;
2 parts of HJS-OP silicone acrylic redispersible rubber powder;
2 parts of acrylic waterproof rubber powder.
Embodiment 4, this example provides a multifunctional negative ion interior wall putty, including the following components in parts by weight:
33 parts of 325-mesh white Portland cement;
0.25 part of a polyamino acid water reducing agent;
12 parts of 850-mesh limestone powder;
7 parts of 950-mesh nano tourmaline powder;
28 parts of 220-mesh shell powder;
2.5 parts of 16-mesh nano zinc oxide;
0.9 part of wood fiber with 70 meshes;
0.45 part of polyethylene cellulose with the viscosity of 10 ten thousand mpa.s;
2.4 parts of HJS-OP silicone-acrylic redispersible rubber powder;
1.8 parts of acrylic waterproof rubber powder.
Comparison of Performance
The results of comparing the use, construction and performance of the commercially available interior wall putty with the multifunctional negative ion interior wall putty provided in example 1 of the present invention are shown in table 1.
Table 1 shows the comparison of the commercially available interior wall putty and example 1
The comparison results in table 1 show that the multifunctional negative ion interior wall putty provided by the embodiment of the invention has a lasting degradation effect on toxic and harmful substances such as indoor formaldehyde, benzene, ammonia substances, TOVC and the like; can replace a putty leveling layer; the multifunctional negative ion putty has high adhesive force and strong water resistance, can be peeled off after being soaked in water for 36 hours by an ordinary indoor putty through an actual test, and does not have delamination and peeling after being soaked in water for 3 months (equivalent to 2160 hours).
Effect of the experiment
The commercial universal putty of the comparative example 1 and the multifunctional negative ion putty provided by the embodiment 1 of the invention are respectively prepared into a sample of 200cm x 300cm x 3cm, the sample is placed in a transparent closed box of 500cm x 500cm, and the radiation value, the number of released negative ions and the water resistance of the sample of the comparative example 1 and the embodiment 1 are detected. The results are shown in Table 2.
Table 2 shows the results of testing the samples of comparative example 1 and example 1
Item | Comparative example 1 | Example 1 | Detection instrument |
Radiation value | 0.047 (qualified) | 0.059 (qualified) | Dnspeceor radiation tester |
Number of anions released | 0-500 pieces | 4000- | XDB-5800 anion tester |
Water resistance (immersion) | Peeling off for 10-15h | No peeling after 500-900h |
The putty product is one of the most widely applied materials in architectural decoration, and the putty sold in the market at present has poor quality and single function, and the product without technical content is inevitably eliminated. The multifunctional negative ion putty provided by the invention is wider in application and application range and saves more working procedures. For example:
in one embodiment, in the construction of wood panels or smooth surfaces, if commercial putties are used, an interface treatment is necessary or delamination can occur; the multifunctional negative ion putty provided by the embodiment of the invention only needs one-time construction without additional working procedures, thereby saving the labor cost and the material cost of the intermediate working procedures.
In another embodiment, the commercial putty can only be scraped and ground in batches, which is impossible to realize in terms of art processes such as spraying points, drawing lines, napping, embossing and the like; the multifunctional negative ion putty provided by the embodiment of the invention can be used for scraping, polishing, spraying dots, drawing lines, napping and embossing, and can be manufactured by various artistic processes.
Through comprehensive analysis, the multifunctional negative ion putty provided by the invention has wide application prospect and good market value.
In the above embodiments, the descriptions of the respective embodiments have respective emphasis, and for parts that are not described in detail in a certain embodiment, reference may be made to related descriptions of other embodiments.
While the invention has been described with reference to specific embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims. Therefore, the protection scope of the present invention shall be subject to the protection scope of the claims.
Claims (9)
1. The multifunctional negative ion interior wall putty is characterized by comprising the following components in parts by weight:
25-35 parts of Portland cement;
0.1-0.3 part of water reducing agent;
7-15 parts of limestone powder;
5-10 parts of nano tourmaline powder;
20-30 parts of shell powder;
1-3 parts of nano zinc oxide;
0.5-1 part of wood fiber;
0.3-0.5 part of polyethylene cellulose;
1-3 parts of HJS-OP silicone-acrylic redispersible rubber powder;
1-3 parts of acrylic waterproof rubber powder.
2. The multifunctional negative ion interior wall putty as set forth in claim 1, characterized in that said water reducing agent is a polyamino acid.
3. The multifunctional negative ion interior wall putty as set forth in claim 1, characterized in that the particle size of the limestone powder is 800-1000 meshes.
4. The multifunctional negative ion interior wall putty as claimed in claim 1, characterized in that the particle size of the nano tourmaline powder is 800-1000 meshes.
5. The multifunctional negative ion interior wall putty as claimed in claim 1, characterized in that the grain size of the shell powder is 200-300 meshes.
6. The multifunctional negative ion interior wall putty as claimed in claim 1, characterized in that the particle size of the nano zinc oxide is 10-30 meshes.
7. The multifunctional negative ion interior wall putty according to claim 1 characterised in that the particle size of the wood fibre is 50-100 mesh.
8. The multifunctional negative ion interior wall putty according to claim 1 characterised in that the viscosity of the polyethyl cellulose is 10 ten thousand mpa.s.
9. The multifunctional negative ion interior wall putty as claimed in claim 1, characterized in that the portland cement is 325 mesh white portland cement.