CN110776841A - 一种dbtx非沥青基高分子自粘防水卷材 - Google Patents

一种dbtx非沥青基高分子自粘防水卷材 Download PDF

Info

Publication number
CN110776841A
CN110776841A CN201911124069.4A CN201911124069A CN110776841A CN 110776841 A CN110776841 A CN 110776841A CN 201911124069 A CN201911124069 A CN 201911124069A CN 110776841 A CN110776841 A CN 110776841A
Authority
CN
China
Prior art keywords
asphalt
dbtx
polymer self
adhesive waterproof
based polymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911124069.4A
Other languages
English (en)
Inventor
施新伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
World Leak Free Shanghai Technology Co Ltd
Original Assignee
World Leak Free Shanghai Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by World Leak Free Shanghai Technology Co Ltd filed Critical World Leak Free Shanghai Technology Co Ltd
Priority to CN201911124069.4A priority Critical patent/CN110776841A/zh
Publication of CN110776841A publication Critical patent/CN110776841A/zh
Pending legal-status Critical Current

Abstract

本发明提供的一种DBTX非沥青基高分子自粘防水卷材，包括隔离膜、胶料、加强筋层、交叉膜，DBTX非沥青基高分子自粘防水卷材由下至上依次为隔离膜、胶料、加强筋层、交叉膜，所述DBTX非沥青基高分子自粘防水材料总厚度为0.8‑3mm。本发明提高了防水卷材的性能，避免了沥青对环境的污染，减少了防水材料对人体健康的危害。具有很高的粘结力，施工时可以与基面满粘，不会出现空鼓现象。

Description

一种DBTX非沥青基高分子自粘防水卷材
技术领域
本发明涉及防水卷材技术领域，特别涉及一种DBTX非沥青基高分子自粘防水卷材。
背景技术
传统的防水卷材一般使用沥青作为主体材料。沥青防水卷材具有良好的憎水性、黏结性和延展性，能耐酸、碱、盐的腐蚀，抗冲击性能较好，价格便宜，因此得到广泛的使用。但沥青防水卷材的缺点是大气稳定性和温度稳定性差，冬天易龟裂，夏天易流淌，强度偏低。沥青所含组分及含量随产地和提炼工艺的不同而差异很大，所以其性能不稳定，只能用作对性能要求不高的低档材料。另外，沥青中常含有萘、蒽、吡啶、苯酚等有毒物质，使用过程中有较大气味，污染环境，对皮肤黏膜有刺激性，有光毒作用和致癌作用。我国已经逐渐限制沥青类防水卷材的使用范围。防水涂料在使用时需要涂敷在基层上，不能作为单独的防水层独立使用；聚氨酯冷库板产品鱼龙混杂，产品质量规范不统一，因此生产的聚氨酯冷库板产品的质量难以保证；弹性体改性沥青防水卷材在使用时需要加热，因此会挥发出对环境有一定污染的气体，在较密闭的环境中使用这种材料存在安全隐患，并且，现有的弹性体改性沥青防水卷材的自身重量较重，立墙施工时会出现滑动的情况；另外，由于使用时，这些材料多处于低温环境下，温度过低时，这些材料会出现开裂、发硬、延伸率下降等的问题，无法满足低温环境下使用的需求。
特别是申请号为201510471982.7，非沥青基高分子压敏型自粘卷材，缺少必要的拉筋也就是延展防护层，从结构及材料组成会材料会出现开裂、发硬、延伸率下降等的问题。
针对现有技术中存在的上述缺陷，本发明提出了一种非沥青基高分子防水自粘卷材料。
发明内容
本发明的目的在于提供一种DBTX非沥青基高分子自粘防水卷材，以解决上述背景技术中提出的问题。
本发明的目的是通过下述技术方案予以实现：一种DBTX非沥青基高分子自粘防水卷材，包括隔离膜、胶料、加强筋层、交叉膜，DBTX非沥青基高分子自粘防水卷材由下至上依次为隔离膜、胶料、加强筋层、交叉膜，所述DBTX非沥青基高分子自粘防水材料总厚度为0.8-3mm。
进一步地，其特征在于：所述胶料为高分子混合胶料，所述胶料为丁苯橡胶与丁基橡胶的混合物。
进一步地，其特征在于：所述丁苯橡胶与丁基橡胶混合比例为2:1。
进一步地，其特征在于：所述加强筋层由聚氨酯纤维与碳纤维、木质纤维混合组成。
进一步地，所述加强筋层厚度为0.1-0.7mm，所述聚氨酯纤维与碳纤维、木质纤维混合比例为1:0.5:0.5。
进一步地，所述加强筋层3克重控制在65-80之间，优选65-70克重。
与现有技术相比，本发明的有益效果是：本发明提供的非沥青基高分子自粘防水自粘卷材，对水泥基建筑具有良好的粘结效果，有很好的低温柔韧性和高温稳定性，无刺激气味，安全无毒，是一种较为环保的新型防水卷材。
附图说明
图1是本发明整体结构示意图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例，基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
由图1所示，一种DBTX非沥青基高分子自粘防水卷材，包括隔离膜1、胶料2、加强筋层3、交叉膜4，DBTX非沥青基高分子自粘防水卷材由下至上依次为隔离膜1、胶料2、加强筋层3、交叉膜4，所述DBTX非沥青基高分子自粘防水材料总厚度为0.8-3mm。
在本实施中，其特征在于：所述胶料2为高分子混合胶料，所述胶料2为丁苯橡胶与丁基橡胶的混合物。
在本实施中，其特征在于：所述丁苯橡胶与丁基橡胶混合比例为2:1。
在本实施中，其特征在于：所述加强筋层3由聚氨酯纤维与碳纤维、木质纤维混合组成。
在本实施中，所述加强筋层3厚度为0.1-0.7mm，所述聚氨酯纤维与碳纤维、木质纤维混合比例为1:0.5:0.5。
所述加强筋层3通过交叉膜4与所述胶料2高强度结合，增强其双向耐撕裂，具有高强度、高延展性、耐老化、环保等优点。
所述加强筋层3采用不同成分得纤维组合而成，所述加强筋层3克重控制在65-80之间，优选65-70克重。
所述交叉膜4为聚乙烯高强度粘结剂，胶料2、加强筋层3、交叉膜4三者混合后在覆着隔离膜,所述隔离膜合成树脂混合物，至少两种树脂混合，混合比例为1:1，所述合成树脂以涤纶树脂为主要成分。
该发明在原有专利基础上增加加强筋层，以此来保证卷材的高强度及延展性。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。

Claims (6)

1.一种DBTX非沥青基高分子自粘防水卷材，其特征在于：包括隔离膜(1)、胶料(2)、加强筋层(3)、交叉膜(4)，DBTX非沥青基高分子自粘防水卷材由下至上依次为隔离膜(1)、胶料(2)、加强筋层(3)、交叉膜(4)，所述DBTX非沥青基高分子自粘防水材料总厚度为0.8-3mm。
2.根据权利要求1所述的一种DBTX非沥青基高分子自粘防水卷材，其特征在于：所述胶料(2)为高分子混合胶料，所述胶料(2)为丁苯橡胶与丁基橡胶的混合物。
3.根据权利要求1所述的一种DBTX非沥青基高分子自粘防水卷材，其特征在于：所述丁苯橡胶与丁基橡胶混合比例为2:1。
4.根据权利要求1所述的一种DBTX非沥青基高分子自粘防水卷材，其特征在于：所述加强筋层(3)由聚氨酯纤维与碳纤维、木质纤维混合组成。
5.根据权利要求1所述的一种DBTX非沥青基高分子自粘防水卷材，其特征在于：所述加强筋层(3)厚度为0.1-0.7mm，所述聚氨酯纤维与碳纤维、木质纤维混合比例为1:0.5:0.5。
6.根据权利要求1所述的一种DBTX非沥青基高分子自粘防水卷材，所述加强筋层3克重控制在65-80之间，优选65-70克重。
CN201911124069.4A 2019-11-18 2019-11-18 一种dbtx非沥青基高分子自粘防水卷材 Pending CN110776841A (zh)