CN110722093A - 一种动物胶改性制备的铸造型砂添加剂 - Google Patents
一种动物胶改性制备的铸造型砂添加剂 Download PDFInfo
- Publication number
- CN110722093A CN110722093A CN201910983377.6A CN201910983377A CN110722093A CN 110722093 A CN110722093 A CN 110722093A CN 201910983377 A CN201910983377 A CN 201910983377A CN 110722093 A CN110722093 A CN 110722093A
- Authority
- CN
- China
- Prior art keywords
- sand
- molding sand
- additive
- percent
- animal glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种动物胶改性制备的铸造型砂添加剂,涉及一种铸造砂型用添加剂,所述添加剂为动物胶改性铸造型砂添加剂,是一种复合型添加剂,其成分包括:氧化铁和纳米氧化铝;其纳米氧化铝重量百分比为60%‑85%、氧化铁重量百分比为20%‑40%;其制备过程如下:首先,将铸造型砂和型砂添加剂加入到混砂机中,型砂添加剂添加比例为1%‑5%,混砂时间为60‑150s,得到备用型砂;取适量备用型砂加入改性动物胶粘结剂,搅拌、混合均匀后放入模具中制得“8”字型试样,在100–300°C和10‑30min下烘干,得到样品。使用本发明的复合型添加剂能够提高铸件质量、改善环境污染、降低生产成。
Description
技术领域
本发明涉及一种铸造砂型用添加剂,本发明涉及一种动物胶改性制备的铸造型砂添加剂。
技术背景
目前,国家对环保工业生产越来越重视,传统的铸造工业已经不再满足当今工业发展的理念。传统的型砂及其添加剂存在有以下问题:
(1)生产环境差,对工人伤害大,对环境污染严重;
(2)型砂韧性差、强度低、水分高、取模困难。
发明内容
本发明的目的在于提供一种动物胶改性制备的铸造型砂添加剂,该动物胶改性铸造型砂添加剂能有效减少铸件的粘砂、夹砂、砂眼和气孔等缺陷;提高铸件表面光洁度和尺寸精度;同时型砂可循环使用、废砂排放量少,可大幅降低生产成本;型砂制备废砂排放过程中,改善生产环境,减少环境污染。
本发明的目的是通过以下技术方案实现的:
一种动物胶改性制备的铸造型砂添加剂,包括氧化铁和纳米氧化铝,其组分和含量(重量百分比)为:纳米氧化铝为60% - 85%、氧化铁为20% - 40%;
将所述的铸造型砂和型砂添加剂加入到混砂机中,型砂添加剂添加比例为1% - 5%,混砂时间为60 - 150 s,得到备用型砂;
取适量备用型砂加入改性动物胶粘结剂,搅拌、混合均匀后放入模具中制得“8”字型试样,在100 – 300 °C和10 - 30 min下烘干,得到样品。
本发明的优点与效果是:
本发明利用该添加剂制备的动物胶改性铸造型砂,能够效减少铸件的粘砂、夹砂、砂眼和气孔等缺陷;提高铸件表面光洁度和尺寸精度;同时型砂可循环使用、废砂排放量少,可大幅降低生产成本;型砂制备废砂排放过程中,改善生产环境,减少环境污染。
本发明在动物胶改性铸造型砂中加入添加剂能够显著提高型砂的性能指标,开发出一种白色无污染的铸造型砂。该铸造型砂,具有较高的流动性、透气性、湿强度、表面强度和韧性,基本满足高紧实率造型线的要求。同时铸件无粘砂、夹砂、砂眼和气孔等缺陷,表面粗糙度和尺寸公差等级均较低。
附图说明
图1 为本发明实施例中的型砂试样;
图2 为本发明实施例中的铸件试样。
具体实施方式
为进一步了解本发明的内容,结合实施例对本发明作详细描述:
实施例1:
一种动物胶改性铸造型砂添加剂,包括氧化铁和纳米氧化铝,其组分和含量(重量百分比)为:纳米氧化铝为85%、氧化铁为15%。将所述的铸造型砂和型砂添加剂加入到混砂机中,型砂添加剂添加比例为3%,混砂时间为80 s,得到备用型砂;随后加入改性动物胶粘结剂,搅拌、混合均匀后放入模具中制得“8”字型试样,在150 °C和20 min下烘干,得到样品,样品如图1所示。型砂样品性能为:紧实率35~40%,透气性80~100,平均细度51,含泥量0.51%,烧减量0.24%,初强度1.86 MPa,溃散强度(500 °C) 0.37 MPa。铸件无粘砂、夹砂、砂眼和气孔等缺陷,表面光洁度达到3.2和尺寸公差等级达到CT7,如图2所示。
实施例2:
一种动物胶改性铸造型砂添加剂,包括氧化铁和纳米氧化铝,其组分和含量(重量百分比)为:纳米氧化铝为78%、氧化铁为22%。将所述的铸造型砂和型砂添加剂加入到混砂机中,型砂添加剂添加比例为4%,混砂时间为120 s,得到备用型砂;随后加入改性动物胶粘结剂,搅拌、混合均匀后放入模具中制得“8”字型试样,将砂型在220 °C和15 min下烘干,得到样品,样品如图1所示。型砂样品性能为:紧实率35~40%,透气性80~100,平均细度51,含泥量0.51%,烧减量0.24%,初强度1.86 MPa,溃散强度(500 °C) 0.37 MPa。铸件无粘砂、夹砂、砂眼和气孔等缺陷,表面光洁度达到3.2和尺寸公差等级达到CT7,如图2所示。
Claims (1)
1.一种动物胶改性制备的铸造型砂添加剂,其特征在于,所述添加剂为动物胶改性铸造型砂添加剂,是一种复合型添加剂,其成分包括:氧化铁和纳米氧化铝;其纳米氧化铝重量百分比为60% - 85%、氧化铁重量百分比为20% - 40%;
其制备过程如下:
首先,将铸造型砂和型砂添加剂加入到混砂机中,型砂添加剂添加比例为1% - 5%,混砂时间为60 - 150 s,得到备用型砂;取适量备用型砂加入改性动物胶粘结剂,搅拌、混合均匀后放入模具中制得“8”字型试样,在100 – 300 °C和10 - 30 min下烘干,得到样品。