CN110682380A - Bamboo toothpick processing method - Google Patents
Bamboo toothpick processing method Download PDFInfo
- Publication number
- CN110682380A CN110682380A CN201910938148.2A CN201910938148A CN110682380A CN 110682380 A CN110682380 A CN 110682380A CN 201910938148 A CN201910938148 A CN 201910938148A CN 110682380 A CN110682380 A CN 110682380A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- filaments
- soaking
- toothpick
- machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bamboo toothpick processing method, which belongs to the technical field of toothpicks and comprises the following steps: taking materials, airing, sawing bamboo, breaking bamboo, slicing, drawing wire, sawing wire, polishing, soaking, drying, sterilizing and forming; the processed bamboo and wood raw materials are placed into the soaking solution for soaking, the soaking solution adopts environment-friendly raw materials, the effect on a human body is avoided, the traditional mode of formaldehyde is abandoned for carrying out antiseptic treatment on the toothpick, and the soaking solution has certain temperature, so that the bamboo filaments are softened, the soaking effect of the soaking solution is improved, the antiseptic property of the manufactured bamboo toothpick is further improved, meanwhile, the processed bamboo filaments need to be subjected to a sterilization process through a sterilizer, and the properties of the manufactured bamboo toothpick, such as corrosion resistance, insect prevention, mildew prevention, moisture prevention and the like, are improved.
Description
Technical Field
The invention belongs to the technical field of toothpicks, and particularly relates to a bamboo toothpick processing method.
Background
The toothpick is usually a small thin stick with one or two tips, and also has a hook-shaped front end, the toothpick with one tip can be broken off and put on the toothpick head, and the toothpick is generally made of bamboo, wood or metal, can be used for cleaning oral cavity, removing tartar and foreign matters or food residues stuck in the gaps of teeth, and is an important oral hygiene tool.
At present, toothpicks which circulate in the market are produced by taking wood and bamboo as raw materials, most of the toothpicks are processed by the bleaching action of formaldehyde, and although the toothpicks have a certain anticorrosion effect by utilizing the formaldehyde, the frequent use of the toothpicks containing the formaldehyde can easily cause a large amount of formaldehyde to be accumulated in the human body, thereby forming a great threat to the health of people.
Disclosure of Invention
The invention aims to provide a method for processing a bamboo toothpick, which aims to solve the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme:
a bamboo toothpick processing method comprises the following steps:
s1, taking materials, and selecting proper materials of Taizhu, zhaolvzhu, green tangerine orange peel bamboo or mao bamboo by technicians as raw materials of the bamboo toothpick;
s2, airing, namely placing the bamboo and wood raw materials selected in the step S1 in the sun for exposure, and removing redundant moisture in the bamboo and wood raw materials;
s3, sawing bamboo, namely placing the bamboo and wood raw materials exposed in the step S2 on a bamboo sawing machine for cutting, sawing the bamboo and wood raw bamboo into required specification length, and removing the head and tail of the bamboo and wood raw materials;
s4, breaking bamboo, namely putting the bamboo and wood cut in the step S3 into a bamboo breaking machine for breaking bamboo, wherein the number of the broken pieces is determined according to the required width of the bamboo pieces;
s5, splitting, namely putting the bamboo and wood raw material subjected to bamboo breaking treatment in the step S4 into a splitting machine for processing and cutting off convex sections on the outer edge of the bamboo and wood raw material;
s6, performing wire drawing treatment, namely putting the bamboo chips subjected to bamboo breaking in the step S5 into a wire drawing forming machine for wire drawing treatment;
s7, sawing, namely putting the bamboo filaments pulled in the step S6 into a sawing machine and cutting the bamboo filaments into required lengths;
s8, polishing, namely putting the bamboo filaments cut in the step S7 into a polishing machine for surface polishing treatment to remove burrs on the bamboo filaments;
s9, soaking, namely soaking the bamboo filaments polished in the step S8 in a soaking box;
s10, drying, namely taking out the bamboo filaments soaked in the step S9 and putting the bamboo filaments into a dryer for quick drying;
s11, sterilizing, namely putting the dried bamboo filaments in the step S10 into a sterilizer for sterilization;
and S12, forming, namely putting the bamboo filaments processed in the step S11 into a sharpening machine to prepare the finished toothpick.
Preferably, in the step S2, the airing time of the bamboo wood raw material is 1 to 3 days.
Preferably, in S6, the step of processing is performed. The diameter of the bamboo filament after being processed by the wire drawing forming machine is 1.8-2.2 mm.
Preferably, in the step S7, the length of the bamboo filament processed by the filament sawing machine is specifically 6-7 cm.
Preferably, in S9, a soaking solution is placed in the soaking tank, and the soaking solution is specifically prepared from the following raw materials in parts by weight: 7.7-7.9 parts of fresh perilla leaves, 5.6-5.8 parts of fresh mint leaves, 8.1-8.3 parts of fresh camphor leaves, 11.3-11.5 parts of fresh orange peels, 6.4-6.6 parts of fresh violet petals, 0.44-0.46 part of calcium nitrate and 136-138 parts of water.
In S11, the temperature of the immersion liquid in the immersion tank in S9 is preferably 70 ° to 80 °.
Preferably, in S9, the pH of the immersion liquid in the immersion tank is 5 to 6.
Preferably, in S10, the drying temperature of the dryer is 120 ° to 130 °, and the drying time is 1h to 1.5 h.
Preferably, in S11, the bamboo filaments are sterilized by an ozone generator in a sterilizer for 5 to 7 hours.
Preferably, in S12, the sharpening machine is a double-pointed single-pointed toothpick grinding machine, and grinds the two tips into one tip or two tips.
Compared with the prior art, the invention has the beneficial effects that: the scheme is that the bamboo and wood raw materials after being processed are placed into the soak solution for soaking, because the soak solution adopts all is the raw and other materials of environmental protection, no influence is caused to the human body, the mode of abandoning traditional formaldehyde carries out anticorrosive treatment to the toothpick, and the soak solution has certain temperature, thereby make the bamboo filament soften, improve the immersion effect of soak solution, and then improve the corrosion resisting property of bamboo toothpick after making, the bamboo filament after the while processing need carry out the sterilization process through the sterilizer, the performances such as anticorrosive, protection against insects, mildew and dampproofing of bamboo toothpick after having improved and having made are improved.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example one
The invention provides a technical scheme that: a bamboo toothpick processing method comprises the following steps:
s1, taking materials, and selecting proper materials of Taizhu, zhaolvzhu, green tangerine orange peel bamboo or mao bamboo by technicians as raw materials of the bamboo toothpick;
s2, airing, namely placing the bamboo and wood raw material selected in the step S1 in the sun for exposure to the sun, and removing redundant moisture in the bamboo and wood raw material, wherein the airing time of the bamboo and wood raw material is 1-3 days;
s3, sawing bamboo, namely placing the bamboo and wood raw materials exposed in the step S2 on a bamboo sawing machine for cutting, sawing the bamboo and wood raw bamboo into required specification length, and removing the head and tail of the bamboo and wood raw materials;
s4, breaking bamboo, namely putting the bamboo and wood cut in the step S3 into a bamboo breaking machine for breaking bamboo, wherein the number of the broken pieces is determined according to the required width of the bamboo pieces;
s5, splitting, namely putting the bamboo and wood raw material subjected to bamboo breaking treatment in the step S4 into a splitting machine for processing and cutting off convex sections on the outer edge of the bamboo and wood raw material;
s6, performing wire drawing treatment, namely putting the bamboo chips subjected to bamboo breaking in the step S5 into a wire drawing forming machine for wire drawing treatment, wherein the diameter of the bamboo filaments subjected to the wire drawing forming machine treatment is 1.8-2.2 mm;
s7, processing the bamboo filaments, namely putting the bamboo filaments pulled in the step S6 into a filament sawing machine and cutting the bamboo filaments into required lengths, wherein the lengths of the bamboo filaments processed by the filament sawing machine are 6-7 cm;
s8, polishing, namely putting the bamboo filaments cut in the step S7 into a polishing machine for surface polishing treatment to remove burrs on the bamboo filaments;
s9, soaking, namely soaking the bamboo filaments polished in the step S8 in a soaking box, wherein a soaking solution is placed in the soaking box and is prepared from the following raw materials in parts by weight: 7.7-7.9 parts of fresh perilla leaves, 5.6-5.8 parts of fresh mint leaves, 8.1-8.3 parts of fresh camphor leaves, 11.3-11.5 parts of fresh orange peels, 6.4-6.6 parts of fresh violet petals, 0.44-0.46 part of calcium nitrate and 136-138 parts of water, wherein the temperature of a soaking solution in the soaking tank is 70 degrees, and the pH value of the soaking solution in the soaking tank is 5;
s10, drying, namely taking out the bamboo filaments soaked in the step S9, and putting the bamboo filaments into a dryer for quick drying, wherein the drying temperature of the dryer is 120 degrees, and the drying time is 1 hour;
s11, sterilizing, namely putting the dried bamboo filaments in the step S10 into a sterilizer for sterilization, and sterilizing the bamboo filaments in the sterilizer for 5 hours by an ozone generator;
and S12, forming, namely putting the bamboo filaments processed in the step S11 into a sharpening machine to prepare a finished toothpick, wherein the sharpening machine is a double-tip single-tip grinding machine for the toothpick and grinds the bamboo filaments into one tip or two tips.
Example two
S1, taking materials, and selecting proper materials of Taizhu, zhaolvzhu, green tangerine orange peel bamboo or mao bamboo by technicians as raw materials of the bamboo toothpick;
s2, airing, namely placing the bamboo and wood raw material selected in the step S1 in the sun for exposure to the sun, and removing redundant moisture in the bamboo and wood raw material, wherein the airing time of the bamboo and wood raw material is 1-3 days;
s3, sawing bamboo, namely placing the bamboo and wood raw materials exposed in the step S2 on a bamboo sawing machine for cutting, sawing the bamboo and wood raw bamboo into required specification length, and removing the head and tail of the bamboo and wood raw materials;
s4, breaking bamboo, namely putting the bamboo and wood cut in the step S3 into a bamboo breaking machine for breaking bamboo, wherein the number of the broken pieces is determined according to the required width of the bamboo pieces;
s5, splitting, namely putting the bamboo and wood raw material subjected to bamboo breaking treatment in the step S4 into a splitting machine for processing and cutting off convex sections on the outer edge of the bamboo and wood raw material;
s6, performing wire drawing treatment, namely putting the bamboo chips subjected to bamboo breaking in the step S5 into a wire drawing forming machine for wire drawing treatment, wherein the diameter of the bamboo filaments subjected to the wire drawing forming machine treatment is 1.8-2.2 mm;
s7, processing the bamboo filaments, namely putting the bamboo filaments pulled in the step S6 into a filament sawing machine and cutting the bamboo filaments into required lengths, wherein the lengths of the bamboo filaments processed by the filament sawing machine are 6-7 cm;
s8, polishing, namely putting the bamboo filaments cut in the step S7 into a polishing machine for surface polishing treatment to remove burrs on the bamboo filaments;
s9, soaking, namely soaking the bamboo filaments polished in the step S8 in a soaking box, wherein a soaking solution is placed in the soaking box and is prepared from the following raw materials in parts by weight: 7.7-7.9 parts of fresh perilla leaves, 5.6-5.8 parts of fresh mint leaves, 8.1-8.3 parts of fresh camphor leaves, 11.3-11.5 parts of fresh orange peels, 6.4-6.6 parts of fresh violet petals, 0.44-0.46 part of calcium nitrate and 136-138 parts of water, wherein the temperature of a soaking solution in the soaking tank is 75 degrees, and the pH value of the soaking solution in the soaking tank is 5.5;
s10, drying, namely taking out the bamboo filaments soaked in the step S9, and putting the bamboo filaments into a dryer for quick drying, wherein the drying temperature of the dryer is 125 degrees, and the drying time is 1.25 hours;
s11, sterilizing, namely putting the dried bamboo filaments in the step S10 into a sterilizer for sterilization, and sterilizing the bamboo filaments in the sterilizer for 6 hours by an ozone generator;
and S12, forming, namely putting the bamboo filaments processed in the step S11 into a sharpening machine to prepare a finished toothpick, wherein the sharpening machine is a double-tip single-tip grinding machine for the toothpick and grinds the bamboo filaments into one tip or two tips.
EXAMPLE III
S1, taking materials, and selecting proper materials of Taizhu, zhaolvzhu, green tangerine orange peel bamboo or mao bamboo by technicians as raw materials of the bamboo toothpick;
s2, airing, namely placing the bamboo and wood raw material selected in the step S1 in the sun for exposure to the sun, and removing redundant moisture in the bamboo and wood raw material, wherein the airing time of the bamboo and wood raw material is 1-3 days;
s3, sawing bamboo, namely placing the bamboo and wood raw materials exposed in the step S2 on a bamboo sawing machine for cutting, sawing the bamboo and wood raw bamboo into required specification length, and removing the head and tail of the bamboo and wood raw materials;
s4, breaking bamboo, namely putting the bamboo and wood cut in the step S3 into a bamboo breaking machine for breaking bamboo, wherein the number of the broken pieces is determined according to the required width of the bamboo pieces;
s5, splitting, namely putting the bamboo and wood raw material subjected to bamboo breaking treatment in the step S4 into a splitting machine for processing and cutting off convex sections on the outer edge of the bamboo and wood raw material;
s6, performing wire drawing treatment, namely putting the bamboo chips subjected to bamboo breaking in the step S5 into a wire drawing forming machine for wire drawing treatment, wherein the diameter of the bamboo filaments subjected to the wire drawing forming machine treatment is 1.8-2.2 mm;
s7, processing the bamboo filaments, namely putting the bamboo filaments pulled in the step S6 into a filament sawing machine and cutting the bamboo filaments into required lengths, wherein the lengths of the bamboo filaments processed by the filament sawing machine are 6-7 cm;
s8, polishing, namely putting the bamboo filaments cut in the step S7 into a polishing machine for surface polishing treatment to remove burrs on the bamboo filaments;
s9, soaking, namely soaking the bamboo filaments polished in the step S8 in a soaking box, wherein a soaking solution is placed in the soaking box and is prepared from the following raw materials in parts by weight: 7.7-7.9 parts of fresh perilla leaves, 5.6-5.8 parts of fresh mint leaves, 8.1-8.3 parts of fresh camphor leaves, 11.3-11.5 parts of fresh orange peels, 6.4-6.6 parts of fresh violet petals, 0.44-0.46 part of calcium nitrate and 136-138 parts of water, wherein the temperature of a soaking solution in the soaking tank is 80 degrees, and the pH value of the soaking solution in the soaking tank is 6;
s10, drying, namely taking out the bamboo filaments soaked in the step S9, and putting the bamboo filaments into a dryer for quick drying, wherein the drying temperature of the dryer is 130 degrees, and the drying time is 1.5 hours;
s11, sterilizing, namely putting the dried bamboo filaments in the step S10 into a sterilizer for sterilization, and sterilizing the bamboo filaments in the sterilizer for 7 hours by an ozone generator;
and S12, forming, namely putting the bamboo filaments processed in the step S11 into a sharpening machine to prepare a finished toothpick, wherein the sharpening machine is a double-tip single-tip grinding machine for the toothpick and grinds the bamboo filaments into one tip or two tips.
Examples 1-3 of the present invention provide corrosion performance tests with the results as follows:
although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (10)
1. A method for processing bamboo toothpicks is characterized in that: the method comprises the following steps:
s1, taking materials, and selecting proper materials of Taizhu, zhaolvzhu, green tangerine orange peel bamboo or mao bamboo by technicians as raw materials of the bamboo toothpick;
s2, airing, namely placing the bamboo and wood raw materials selected in the step S1 in the sun for exposure, and removing redundant moisture in the bamboo and wood raw materials;
s3, sawing bamboo, namely placing the bamboo and wood raw materials exposed in the step S2 on a bamboo sawing machine for cutting, sawing the bamboo and wood raw bamboo into required specification length, and removing the head and tail of the bamboo and wood raw materials;
s4, breaking bamboo, namely putting the bamboo and wood cut in the step S3 into a bamboo breaking machine for breaking bamboo, wherein the number of the broken pieces is determined according to the required width of the bamboo pieces;
s5, splitting, namely putting the bamboo and wood raw material subjected to bamboo breaking treatment in the step S4 into a splitting machine for processing and cutting off convex sections on the outer edge of the bamboo and wood raw material;
s6, performing wire drawing treatment, namely putting the bamboo chips subjected to bamboo breaking in the step S5 into a wire drawing forming machine for wire drawing treatment;
s7, sawing, namely putting the bamboo filaments pulled in the step S6 into a sawing machine and cutting the bamboo filaments into required lengths;
s8, polishing, namely putting the bamboo filaments cut in the step S7 into a polishing machine for surface polishing treatment to remove burrs on the bamboo filaments;
s9, soaking, namely soaking the bamboo filaments polished in the step S8 in a soaking box;
s10, drying, namely taking out the bamboo filaments soaked in the step S9 and putting the bamboo filaments into a dryer for quick drying;
s11, sterilizing, namely putting the dried bamboo filaments in the step S10 into a sterilizer for sterilization;
and S12, forming, namely putting the bamboo filaments processed in the step S11 into a sharpening machine to prepare the finished toothpick.
2. The method for processing the bamboo toothpick according to claim 1, wherein: in the S2, the airing time of the bamboo and wood raw materials is specifically 1-3 days.
3. The method for processing the bamboo toothpick according to claim 1, wherein: in the S6, the diameter of the bamboo filament processed by the wire drawing forming machine is 1.8-2.2 mm.
4. The method for processing the bamboo toothpick according to claim 1, wherein: in S7, the length of the bamboo filament processed by the filament sawing machine is specifically 6-7 cm.
5. The method for processing the bamboo toothpick according to claim 1, wherein: in the step S9, a soaking solution is placed in the soaking box, and the soaking solution is prepared from the following raw materials in parts by weight: 7.7-7.9 parts of fresh perilla leaves, 5.6-5.8 parts of fresh mint leaves, 8.1-8.3 parts of fresh camphor leaves, 11.3-11.5 parts of fresh orange peels, 6.4-6.6 parts of fresh violet petals, 0.44-0.46 part of calcium nitrate and 136-138 parts of water.
6. A method of processing a bamboo toothpick according to claim 3, wherein: in the step S9, the temperature of the soak solution in the soaking box is 70-80 degrees.
7. A method of processing a bamboo toothpick according to claim 3, wherein: and in the step S9, the pH value of the soaking solution in the soaking box is 5-6.
8. The method for processing the bamboo toothpick according to claim 1, wherein: in the S10, the drying temperature of the dryer is 120-130 degrees, and the drying time is 1-1.5 hours.
9. The method for processing the bamboo toothpick according to claim 1, wherein: and in the S11, the bamboo filaments are sterilized in the sterilizer by an ozone generator for 5-7 h.
10. The method for processing the bamboo toothpick according to claim 1, wherein: in the step S12, the sharpening machine is specifically a double-tip single-tip grinding machine for toothpicks, and is ground into one tip or two tips.