CN110666310A - Flat butt joint MIG welding method for aluminum-magnesium alloy sheet - Google Patents

Flat butt joint MIG welding method for aluminum-magnesium alloy sheet Download PDF

Info

Publication number
CN110666310A
CN110666310A CN201911025919.5A CN201911025919A CN110666310A CN 110666310 A CN110666310 A CN 110666310A CN 201911025919 A CN201911025919 A CN 201911025919A CN 110666310 A CN110666310 A CN 110666310A
Authority
CN
China
Prior art keywords
welding
percent
less
equal
magnesium alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201911025919.5A
Other languages
Chinese (zh)
Other versions
CN110666310B (en
Inventor
兰玲
王高飞
朱若凡
阎璐
宋金英
朱国斌
周鸿翔
任闻杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Shipbuilding Technology Research Institute
Original Assignee
Shanghai Institute Of Shipbuilding Technology (11th Institute Of China Shipbuilding Industry Group Corporation)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Institute Of Shipbuilding Technology (11th Institute Of China Shipbuilding Industry Group Corporation) filed Critical Shanghai Institute Of Shipbuilding Technology (11th Institute Of China Shipbuilding Industry Group Corporation)
Priority to CN201911025919.5A priority Critical patent/CN110666310B/en
Publication of CN110666310A publication Critical patent/CN110666310A/en
Application granted granted Critical
Publication of CN110666310B publication Critical patent/CN110666310B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a flat butt MIG welding method of an aluminum magnesium alloy sheet, which is characterized by comprising the following steps of: carrying out MIG welding on 2 aluminum-magnesium alloy sheets at a flat position, and welding a groove by adopting a symmetrical V-shaped groove, wherein the angle of the groove is 15-20 degrees at a single side, and the gap is 0-2 mm; the welding voltage is 17-19.5V, the welding current is 90-105A, and the protective gas flow is 20-25L/min. The welding method can ensure that the tensile strength of the welding joint is more than 333MPa, no crack or other defects of more than 3mm appear on the surface of the welding joint after the welding joint is bent forwards and backwards for 180 degrees, and the welding seam has excellent corrosion resistance.

Description

Flat butt joint MIG welding method for aluminum-magnesium alloy sheet
Technical Field
The invention belongs to the technical field of aluminum alloy material welding, and particularly relates to a flat butt MIG welding method of an aluminum-magnesium alloy sheet.
Background
The aluminum alloy has the characteristics of small specific gravity, good corrosion resistance, easy processing and the like, is widely applied to ships, and is mainly a 5083 plate and a 6082 section in China at present. With the improvement of the requirements of ships on navigational speed, loading capacity and structural weight, the demand for high-strength corrosion-resistant aluminum alloy is more urgent.
At present, high-strength corrosion-resistant aluminum-magnesium alloy materials are developed in China, the magnesium content of the high-strength corrosion-resistant aluminum-magnesium alloy materials is 5.5% -6.5%, and the strength of the high-strength corrosion-resistant aluminum-magnesium alloy materials can reach 400 Mpa. The magnesium content of the aluminum-magnesium alloy material is greatly improved, so that the aluminum-magnesium alloy material is seriously burnt in the welding process, has high air hole and crack sensitivity, and the welded joint is seriously softened. In the ship construction process, the welding occupation ratio of the flat position of the high-strength corrosion-resistant aluminum-magnesium alloy is large, and no welding process suitable for the vertical position of the high-strength corrosion-resistant aluminum-magnesium alloy exists at present.
Disclosure of Invention
The invention aims to provide a flat butt joint semi-automatic MIG welding method suitable for a high-strength corrosion-resistant aluminum-magnesium alloy sheet, so as to overcome the defect that no suitable welding method for the domestic high-strength corrosion-resistant aluminum-magnesium alloy sheet in the prior art is available.
In order to achieve the purpose, the technical scheme of the invention is as follows:
the invention discloses a flat butt MIG welding method of an aluminum magnesium alloy sheet, which is characterized by comprising the following steps of: carrying out MIG welding on 2 aluminum-magnesium alloy sheets at a flat position, and welding a groove by adopting a symmetrical V-shaped groove, wherein the angle of the groove is 15-20 degrees at a single side, and the gap is 0-2 mm; the welding voltage is 17-19.5V, the welding current is 90-105A, and the protective gas flow is 20-25L/min;
the aluminum magnesium alloy comprises the following components in percentage by mass: si: less than or equal to 0.4 percent, Fe: less than or equal to 0.4 percent, Cu: less than or equal to 0.1 percent, Mn: 0.7% -1.3%, Mg: 5.5% -6.5%, Zn: less than or equal to 0.2 percent, Zr: 0.02% -0.12%, Er:0.10 to 0.25 percent, and the balance of Al and inevitable impurities;
the welding wire adopted by the welding comprises the following components in percentage by mass: si: less than or equal to 0.4 percent, Fe: less than or equal to 0.4 percent, Cu: less than or equal to 0.05 percent, Mn: 0.8% -1.1%, Mg: 5.5% -6.5%, Zn: less than or equal to 0.2 percent, Zr: 0.02-0.12 percent of Er, 0.10-0.25 percent of Er, and the balance of Al and inevitable impurities; the diameter of the welding wire is 1.0mm or 1.2 mm.
Further, the welding is double-sided welding; the aluminum magnesium alloy sheet is 3-5 mm in thickness.
Further, the welding shielding gas is argon, and the purity of the argon is more than or equal to 99.995%; the preferred guard gas flow rate is 22L/min.
Furthermore, the flat butt MIG welding method of the aluminum-magnesium alloy sheet is used for welding under the conditions that the ambient temperature is not less than 0 ℃ and the relative humidity is not higher than 85%, and preheating is not needed during welding.
According to the flat butt MIG welding method for the aluminum-magnesium alloy, the welding position is a flat position, the tensile strength of a welding joint can be guaranteed to be higher than 333Mpa, the length of cracks or other defects appearing on the surface of the welding joint after the surface is bent or back-bent for 180 degrees is not more than 3mm, the appearance inspection of the welding seam of the welding joint meets the quality requirement, no obvious surface defect exists, the X-ray flaw detection rating of the internal quality of the welding seam is not lower than grade I, the spalling corrosion and the intergranular corrosion meet the requirement, and the welding process can complete the flat butt welding of the high-strength corrosion-resistant aluminum-magnesium alloy.
Drawings
FIG. 1 is a schematic view of a flat butt MIG welding groove of the present invention;
the reference numbers of the various drawings indicate the following: 1-magnesium aluminum alloy plate and 2-flat position groove.
Detailed Description
It should be understood by those skilled in the art that the present embodiment is only for illustrating the present invention and is not to be used as a limitation of the present invention, and changes and modifications of the embodiment can be made within the scope of the claims of the present invention.
Example 1
(1) Welding material
Base material: the high-strength aluminum-magnesium alloy plate in the O/H112 state comprises the following components in percentage by mass: si: less than or equal to 0.4 percent, Fe: less than or equal to 0.4 percent, Cu: less than or equal to 0.1 percent, Mn: 0.7% -1.3%, Mg: 5.5% -6.5%, Zn: less than or equal to 0.2 percent, Zr: 0.02% -0.12%, Er:0.10 to 0.25 percent, and the balance of Al and inevitable impurities. The thickness of the plate is 4 mm.
Welding wires: si: less than or equal to 0.4 percent, Fe: less than or equal to 0.4 percent, Cu: less than or equal to 0.05 percent, Mn: 0.8% -1.1%, Mg: 5.5% -6.5%, Zn: less than or equal to 0.2 percent, Zr: 0.02% -0.12%, Er:0.10 to 0.25 percent, and the balance of Al and inevitable impurities, and the diameter of the welding wire is 1.2 mm.
Protective gas: the selected protective gas is argon, and the purity of the argon is more than or equal to 99.995 percent.
(2) Welding method
Adopting an MIG double-sided welding method, wherein the welding position is a flat position, the groove of the aluminum plate butt joint adopts a symmetrical single V-shaped groove, the angle of the groove is single-side 18 degrees, and the gap width at the bottom of the V-shaped groove is 2 mm; the welding voltage is 19V, the welding current is 90A, and the protective gas flow is 22L/min.
Welding at normal temperature with the ambient temperature not less than 0 ℃ and the relative humidity not higher than 85%, wherein the welding process parameters are shown in table 1.
Examples 2 to 3
The welding materials (base metal and welding wire) were the same as in example 1, wherein the plate thickness and the diameter of the welding wire are shown in Table 1.
(1) The MIG double-sided welding method is adopted, the welding position is a vertical position, the groove of the aluminum plate butt joint adopts a symmetrical single V-shaped groove, the welding is carried out at the normal temperature of which the ambient temperature is not less than 0 ℃ and the relative humidity is not higher than 85 percent, and the rest welding process parameters are shown in the table 1.
TABLE 1 examples 1-3 welding Process parameters
Figure BDA0002248620950000041
(3) Test results
And (4) carrying out welding test piece inspection on the welding joint according to GB/T2651-2008 and GB/T2653-2008, and finishing the detection of tensile and bending performances (the joint adopts a bending core with the diameter of 22mm and the surface bending or back bending of 180 degrees). The test results are shown in table 2, and meet the standard requirements.
TABLE 2 examples 1-3 weld joint Properties
The X-ray inspection rating of the welded aluminum alloy joint in the embodiment 1 meets the I-grade standard requirement in CB 3929; in a peeling corrosion test of the welded joint, the corrosion morphology of the welded joint meets the N grade in ASTM G66; an indicator of intergranular corrosion rate of the welded joint was 4.34mg/cm2Satisfying ASTM G67 of not more than 15mg/cm2The index requirements of (1).
In the embodiment 2, the X-ray inspection rating of the welded aluminum alloy joint meets the I-grade standard requirement in CB 3929; in a peeling corrosion test of the welded joint, the corrosion morphology of the welded joint meets the PA grade in ASTM G66; the intergranular corrosion rate of the welded joint is indicated by 5.12mg/cm2Satisfying ASTM G67 of not more than 15mg/cm2The index requirements of (1).
Example 3 the X-ray inspection rating of the welded aluminum alloy joint after welding meets the requirement of class i standard in CB 3929; in a peeling corrosion test of the welded joint, the corrosion morphology of the welded joint meets the N grade in ASTM G66; the intergranular corrosion rate of the welded joint is indicated to be 4.86mg/cm2Satisfying ASTM G67 of not more than 15mg/cm2The index requirements of (1).
The foregoing is a more detailed description of the present invention in connection with specific preferred embodiments thereof, and it is not intended that the invention be limited to the specific details set forth herein. For those skilled in the art to which the invention pertains, several simple deductions or substitutions can be made without departing from the spirit of the invention, and all shall be considered as belonging to the protection scope of the invention.

Claims (5)

1. A flat butt-joint MIG welding method of an aluminum magnesium alloy sheet is characterized by comprising the following steps: carrying out MIG welding on 2 aluminum-magnesium alloy sheets at a flat position, and welding a groove by adopting a symmetrical V-shaped groove, wherein the angle of the groove is 15-20 degrees at a single side, and the gap is 0-2 mm; the welding voltage is 17-19.5V, the welding current is 90-105A, and the protective gas flow is 20-25L/min.
2. The flat butt MIG welding process of claim 1 wherein the aluminum magnesium alloy has the following composition in weight percent: si: less than or equal to 0.4 percent, Fe: less than or equal to 0.4 percent, Cu: less than or equal to 0.1 percent, Mn: 0.7% -1.3%, Mg: 5.5% -6.5%, Zn: less than or equal to 0.2 percent, Zr: 0.02% -0.12%, Er:0.10 to 0.25 percent, and the balance of Al and inevitable impurities;
the welding wire adopted by the welding comprises the following components in percentage by mass: si: less than or equal to 0.4 percent, Fe: less than or equal to 0.4 percent, Cu: less than or equal to 0.05 percent, Mn: 0.8% -1.1%, Mg: 5.5% -6.5%, Zn: less than or equal to 0.2 percent, Zr: 0.02-0.12 percent of Er, 0.10-0.25 percent of Er, and the balance of Al and inevitable impurities; the diameter of the welding wire is 1.0mm or 1.2 mm.
3. A flat butt MIG welding process as claimed in claim 1 wherein said welding is double sided welding; the aluminum magnesium alloy sheet is 3-5 mm in thickness.
4. The butt MIG welding process of claim 1 wherein the shielding gas for the welding is argon with an argon purity of 99.995% or more; the protective gas flow is 22L/min.
5. The welding method according to any one of claims 1 to 4, wherein the welding is performed at an ambient temperature of not less than 0 ℃ and a relative humidity of not more than 85%, and preheating is not required at the time of welding.
CN201911025919.5A 2019-10-25 2019-10-25 Flat butt joint MIG welding method for aluminum-magnesium alloy sheet Active CN110666310B (en)