CN110643245A - 一种水包水多彩涂料 - Google Patents
一种水包水多彩涂料 Download PDFInfo
- Publication number
- CN110643245A CN110643245A CN201910982071.9A CN201910982071A CN110643245A CN 110643245 A CN110643245 A CN 110643245A CN 201910982071 A CN201910982071 A CN 201910982071A CN 110643245 A CN110643245 A CN 110643245A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- agent
- emulsion
- multicolor paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及装饰涂料技术领域，尤其是一种水包水多彩涂料，包括分散相、保护胶溶液、连续相和助剂，所述分散相与保护胶溶液的质量比为1.5‑3:1:1‑2；所述分散相的质量份组成如下：水200‑300份、聚乙烯醇10‑20份、乳液50‑100份、有机颜料6‑12份、交联剂10‑20份、凝胶剂30‑60份、成膜助剂2‑3份、增韧剂1‑2份、防霉杀菌剂0.2‑0.8份、润湿剂1‑3份、消泡剂0.2‑1份；本发明中通过采用有机改性丙烯酸酯乳液作为乳液，该乳液是含有丙烯酰氧基的有机硅单体，在常温下乳液成膜过程中发生自交联，不仅可以提高涂抹的致密度、耐水性、附着力、光泽，而且在抗回粘方面发挥优异的性能，水包水多彩涂料中采用该乳液后，不仅可以提高涂膜的耐水白性，而且涂料中不会出现增稠现象，贮存稳定性好。
Description
技术领域
本发明涉及装饰涂料技术领域，尤其是一种水包水多彩涂料。
背景技术
水包水多彩是由液态的水性树脂提炼包裹成胶状的水性彩色颗粒，并均匀地悬浮在特定的水性乳液中，最终形成了多姿多彩的、颗粒大小随意的高分子液态胶状的共聚物，是一种纯水性、无公害、富有花岗纹理、高分子元素结构的产品。经喷涂过的建筑成品突显古朴秀美典雅华贵，花岗纹理自然流畅浑然交融，表面光洁、柔和、手感滑爽不毛糙，涂膜坚韧，高附着，不龟裂，高耐候抗温变，高耐污易清洗，自洁功能强。该技术既源于建筑涂料的合成理念，但又超越了建筑涂料技术和工艺的认知概念，是对建筑涂料制造技术的一项重大突破。
现有的水包水多彩涂料存在初期耐水白性差、耐候性该有待提高的不足，长时间雨水冲刷后，漆膜表面会泛白，漆膜易剥落，影响建筑物外墙的美观性。
发明内容
本发明的目的是：克服现有技术中不足，提供一种耐水白性强、漆膜剥离强度高、体系稳定性强的水包水多彩涂料。
为解决上述技术问题，本发明采用的技术方案如下：
一种水包水多彩涂料，包括分散相、保护胶溶液、连续相和助剂，所述分散相与保护胶溶液的质量比为1.5-3:1:1-2；所述分散相的质量份组成如下：水200-300份、聚乙烯醇10-20份、乳液50-100份、有机颜料6-12份、交联剂10-20份、凝胶剂30-60份、成膜助剂2-3份、增韧剂1-2份、防霉杀菌剂0.2-0.8份、润湿剂1-3份、消泡剂0.2-1份；
所述保护胶溶液的质量份组成如下：去离子水80-100份、保护胶5-16份；
所述连续相的质量份组成如下：去离子水50-80份、消泡剂0.1-0.3份、成膜助剂2.1-3.2份、填料2.8-3.6份、乳液60-100份、防霉杀菌剂0.2-0.5份。
进一步的，所述乳液选用有机改性丙烯酸酯乳液。
进一步的，所述凝胶剂选用丙烯酰胺-淀粉接枝共聚物、含有单一-CH2COO-基的羧甲基交联淀粉、聚阴离子离子纤维素醚、聚丙烯酸钠、聚乙烯醇、黏土中的一种或几种。
进一步的，所述胶凝剂选用含有单一-CH2COO-基的羧甲基交联淀粉和黏土的混合物，其质量比为1:1-5。
进一步的，所述交联剂选用乳酸钛氨、柠檬多价金属盐和二戊醛的混合物，其质量比为1-2:1:1.2-1.8。
进一步的，所述颜料选用有机颜料选用酞菁颜料。
进一步的，所述填料选用有机改性蒙脱石粉、改性二氧化硅、改性碳酸钙、重钙粉中的一种或几种。
进一步的，所述增韧剂选用端羟基液体丁腈橡胶、端硫醇基丁腈橡胶、聚氯酯橡胶和羟甲基尼龙中的一种或几种。
进一步的，所述保护胶选用AP525、GTS、S-482A中的一种。
进一步的，所述防霉杀菌剂选用JF-90、聚2-甲基-4-异噻唑啉-3-酮化合物和聚5-氯-2-甲基-4-异噻唑啉-3-酮化合物中的一种。
采用本发明的技术方案的有益效果是：
本发明中通过采用有机改性丙烯酸酯乳液作为乳液，该乳液是含有丙烯酰氧基的有机硅单体，在常温下乳液成膜过程中发生自交联，不仅可以提高涂抹的致密度、耐水性、附着力、光泽，而且在抗回粘方面发挥优异的性能，水包水多彩涂料中采用该乳液后，不仅可以提高涂膜的耐水白性，而且涂料中不会出现增稠现象，贮存稳定性好。
本发明中的保护胶溶液采用去离子水和保护胶的混合物，保护胶溶液包覆多彩涂料后，可以对多彩涂料起到有效的物理隔离作用，本发明中的保护胶选用AP525、GTS、S-482A中的一种，上述几种保护胶具有优异的剪切变稀性能，在多彩涂料的搅拌和喷涂过程中可以起到润滑剂的作用，从而有效阻止不同颜色的色漆混合在一起，同时也提高了水包水多彩涂料的储存稳定性和应用稳定性。
具体实施方式
为使本发明的上述目的、特征和优点能够更加明显易懂，下面结合具体实施方式对本发明作进一步详细的说明。
一种水包水多彩涂料，包括分散相、保护胶溶液、连续相和助剂，所述分散相与保护胶溶液的质量比为1.5-3:1:1-2；所述分散相的质量份组成如下：水200-300份、聚乙烯醇10-20份、乳液50-100份、有机颜料6-12份、交联剂10-20份、凝胶剂30-60份、成膜助剂2-3份、增韧剂1-2份、防霉杀菌剂0.2-0.8份、润湿剂1-3份、消泡剂0.2-1份；交联剂和凝胶剂反应生成凝胶使分散相形成不溶于水的彩色凝胶粒子，凝胶剂将颜料包覆形成凝胶彩色粒子均匀分布于分散相，从而使得水性多彩涂料能够稳定的储存。
所述保护胶溶液的质量份组成如下：去离子水80-100份、保护胶5-16份；
所述连续相的质量份组成如下：去离子水50-80份、消泡剂0.1-0.3份、成膜助剂2.1-3.2份、填料2.8-3.6份、乳液60-100份、防霉杀菌剂0.2-0.5份。
作为一个优选实施方式，本实施例中的乳液选用有机改性丙烯酸酯乳液。
作为一个优选实施方式，本实施例中的凝胶剂选用丙烯酰胺-淀粉接枝共聚物、含有单一-CH2COO-基的羧甲基交联淀粉、聚阴离子离子纤维素醚、聚丙烯酸钠、聚乙烯醇、黏土中的一种或几种。
作为一个优选实施方式，本实施例中的胶凝剂选用含有单一-CH2COO-基的羧甲基交联淀粉和黏土的混合物，其质量比为1:1-5。
作为一个优选实施方式，本实施例中的交联剂选用乳酸钛氨、柠檬多价金属盐和二戊醛的混合物，其质量比为1-2:1:1.2-1.8。
作为一个优选实施方式，本实施例中的颜料选用有机颜料选用酞菁颜料。
作为一个优选实施方式，本实施例中的填料选用有机改性蒙脱石粉、改性二氧化硅、改性碳酸钙、重钙粉中的一种或几种。
作为一个优选实施方式，本实施例中的增韧剂选用端羟基液体丁腈橡胶、端硫醇基丁腈橡胶、聚氯酯橡胶和羟甲基尼龙中的一种或几种。
作为一个优选实施方式，本实施例中的保护胶选用AP525、GTS、S-482A中的一种。本发明中的保护胶溶液采用去离子水和保护胶的混合物，保护胶溶液包覆多彩涂料后，可以对多彩涂料起到有效的物理隔离作用，本发明中的保护胶选用AP525、GTS、S-482A中的一种，上述几种保护胶具有优异的剪切变稀性能，在多彩涂料的搅拌和喷涂过程中可以起到润滑剂的作用，从而有效阻止不同颜色的色漆混合在一起，同时也提高了水包水多彩涂料的储存稳定性和应用稳定性。
作为一个优选实施方式，本实施例中的防霉杀菌剂选用JF-90、聚2-甲基-4-异噻唑啉-3-酮化合物和聚5-氯-2-甲基-4-异噻唑啉-3-酮化合物中的一种。
实施例1
一种水包水多彩涂料，包括分散相、保护胶溶液、连续相和助剂，所述分散相与保护胶溶液的质量比为1.5:1:1；所述分散相的质量份组成如下：水200份、聚乙烯醇10份、乳液50份、有机颜料6份、交联剂10份、凝胶剂30份、成膜助剂2份、增韧剂1份、防霉杀菌剂0.2份、润湿剂1份、消泡剂0.2份；
所述保护胶溶液的质量份组成如下：去离子水80份、保护胶5份；
所述连续相的质量份组成如下：去离子水50份、消泡剂0.1份、成膜助剂2.1份、填料2.8份、乳液60份、防霉杀菌剂0.2份。
其中，乳液选用有机改性丙烯酸酯乳液。
其中，凝胶剂选用丙烯酰胺-淀粉接枝共聚物。
其中，交联剂选用乳酸钛氨、柠檬多价金属盐和二戊醛的混合物，其质量比为1:1:1.2。
其中，颜料选用有机颜料选用酞菁颜料。
其中，填料选用有机改性蒙脱石粉。
其中，增韧剂选用端羟基液体丁腈橡胶。
其中，保护胶选用AP525。
其中，防霉杀菌剂选用JF-90。
实施例2
一种水包水多彩涂料，包括分散相、保护胶溶液、连续相和助剂，所述分散相与保护胶溶液的质量比为1.8:1:1.2；所述分散相的质量份组成如下：水220份、聚乙烯醇12份、乳液60份、有机颜料8份、交联剂12份、凝胶剂40份、成膜助剂2.1份、增韧剂1.2份、防霉杀菌剂0.3份、润湿剂1.5份、消泡剂0.3份；
所述保护胶溶液的质量份组成如下：去离子水85份、保护胶6份；
所述连续相的质量份组成如下：去离子水60份、消泡剂0.2份、成膜助剂2.5份、填料3份、乳液70份、防霉杀菌剂0.3份。
其中，乳液选用有机改性丙烯酸酯乳液。
其中，胶凝剂选用含有单一-CH2COO-基的羧甲基交联淀粉和黏土的混合物，其质量比为1:1。
其中，交联剂选用乳酸钛氨、柠檬多价金属盐和二戊醛的混合物，其质量比为1.2:1:1.2。
其中，颜料选用有机颜料选用酞菁颜料。
其中，填料选用有改性二氧化硅。
其中，增韧剂选用端硫醇基丁腈橡胶。
其中，保护胶选用AP525。
其中，防霉杀菌剂选用JF-90。
实施例3
一种水包水多彩涂料，包括分散相、保护胶溶液、连续相和助剂，所述分散相与保护胶溶液的质量比为2:1:1.5；所述分散相的质量份组成如下：水200-300份、聚乙烯醇15份、乳液80份、有机颜料9份、交联剂15份、凝胶剂45份、成膜助剂2.5份、增韧剂1.5份、防霉杀菌剂0.5份、润湿剂2份、消泡剂0.6份；
所述保护胶溶液的质量份组成如下：去离子水90份、保护胶10份；
所述连续相的质量份组成如下：去离子水70份、消泡剂0.2份、成膜助剂2.8份、填料3.2份、乳液80份、防霉杀菌剂0.3份。
其中，乳液选用有机改性丙烯酸酯乳液。
其中，胶凝剂选用含有单一-CH2COO-基的羧甲基交联淀粉和黏土的混合物，其质量比为1:2。
其中，交联剂选用乳酸钛氨、柠檬多价金属盐和二戊醛的混合物，其质量比为1.5:1:1.5。
其中，颜料选用有机颜料选用酞菁颜料。
其中，填料选用有机改性蒙脱石粉和改性碳酸钙的混合物，其质量比为1:1。
其中，增韧剂选用端硫醇基丁腈橡胶。
其中，保护胶选用GTS。
其中，防霉杀菌剂选用聚2-甲基-4-异噻唑啉-3-酮化合物。
实施例4
一种水包水多彩涂料，包括分散相、保护胶溶液、连续相和助剂，所述分散相与保护胶溶液的质量比为2.5:1:1.8；所述分散相的质量份组成如下：水280份、聚乙烯醇18份、乳液90份、有机颜料10份、交联剂18份、凝胶剂50份、成膜助剂2.8份、增韧剂1.8份、防霉杀菌剂0.6份、润湿剂2.5份、消泡剂0.8份；
所述保护胶溶液的质量份组成如下：去离子水90份、保护胶15份；
所述连续相的质量份组成如下：去离子水70份、消泡剂0.2份、成膜助剂3份、填料3.2份、乳液90份、防霉杀菌剂0.4份。
其中，乳液选用有机改性丙烯酸酯乳液。
其中，胶凝剂选用含有单一-CH2COO-基的羧甲基交联淀粉和黏土的混合物，其质量比为1:4。
其中，交联剂选用乳酸钛氨、柠檬多价金属盐和二戊醛的混合物，其质量比为1.8:1:1.6。
其中，颜料选用有机颜料选用酞菁颜料。
其中，填料选用有机改性蒙脱石粉、改性二氧化硅和重钙粉的混合物，其质量比为1:2:1。
其中，增韧剂选用端羟基液体丁腈橡胶和聚氯酯橡胶的混合物，其质量比为1:2。
其中，保护胶选用GTS。
其中，防霉杀菌剂选用聚2-甲基-4-异噻唑啉-3-酮化合物。
实施例5
一种水包水多彩涂料，包括分散相、保护胶溶液、连续相和助剂，所述分散相与保护胶溶液的质量比为3:1: 2；所述分散相的质量份组成如下：水300份、聚乙烯醇20份、乳液100份、有机颜料12份、交联剂20份、凝胶剂60份、成膜助剂3份、增韧剂2份、防霉杀菌剂0.8份、润湿剂3份、消泡剂1份；
所述保护胶溶液的质量份组成如下：去离子水100份、保护胶16份；
所述连续相的质量份组成如下：去离子水80份、消泡剂0.3份、成膜助剂3.2份、填料3.6份、乳液100份、防霉杀菌剂0.5份。
其中，乳液选用有机改性丙烯酸酯乳液。
其中，胶凝剂选用含有单一-CH2COO-基的羧甲基交联淀粉和黏土的混合物，其质量比为1:5。
其中，交联剂选用乳酸钛氨、柠檬多价金属盐和二戊醛的混合物，其质量比为2:1:1.8。
其中，颜料选用有机颜料选用酞菁颜料。
其中，填料选用有机改性蒙脱石粉。
其中，增韧剂选用羟甲基尼龙。
其中，保护胶选用S-482A。
其中，防霉杀菌剂选用聚5-氯-2-甲基-4-异噻唑啉-3-酮化合物。
实施例1-5中的水包水多彩涂料的制备方法采用现有技术，本发明中不再赘述。
对实施例1-5中的水包水多彩涂料的涂料性能和涂层性能进行检测，检测结果见表1。
表1
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。
Claims (10)
1.一种水包水多彩涂料，其特征在于：包括分散相、保护胶溶液、连续相和助剂，所述分散相与保护胶溶液的质量比为1.5-3:1:1-2；所述分散相的质量份组成如下：水200-300份、聚乙烯醇10-20份、乳液50-100份、有机颜料6-12份、交联剂10-20份、凝胶剂30-60份、成膜助剂2-3份、增韧剂1-2份、防霉杀菌剂0.2-0.8份、润湿剂1-3份、消泡剂0.2-1份；
所述保护胶溶液的质量份组成如下：去离子水80-100份、保护胶5-16份；
所述连续相的质量份组成如下：去离子水50-80份、消泡剂0.1-0.3份、成膜助剂2.1-3.2份、填料2.8-3.6份、乳液60-100份、防霉杀菌剂0.2-0.5份。
2.根据权利要求1所述的一种水包水多彩涂料，其特征在于：所述乳液选用有机改性丙烯酸酯乳液。
3.根据权利要求1所述的一种水包水多彩涂料，其特征在于：所述凝胶剂选用丙烯酰胺-淀粉接枝共聚物、含有单一-CH2COO-基的羧甲基交联淀粉、聚阴离子离子纤维素醚、聚丙烯酸钠、聚乙烯醇、黏土中的一种或几种。
4.根据权利要求3所述的一种水包水多彩涂料，其特征在于：所述胶凝剂选用含有单一-CH2COO-基的羧甲基交联淀粉和黏土的混合物，其质量比为1:1-5。
5.根据权利要求1所述的一种水包水多彩涂料，其特征在于：所述交联剂选用乳酸钛氨、柠檬多价金属盐和二戊醛的混合物，其质量比为1-2:1:1.2-1.8。
6.根据权利要求1所述的一种水包水多彩涂料，其特征在于：所述颜料选用有机颜料选用酞菁颜料。
7.根据权利要求1所述的一种水包水多彩涂料，其特征在于：所述填料选用有机改性蒙脱石粉、改性二氧化硅、改性碳酸钙、重钙粉中的一种或几种。
8.根据权利要求1所述的一种水包水多彩涂料，其特征在于：所述增韧剂选用端羟基液体丁腈橡胶、端硫醇基丁腈橡胶、聚氯酯橡胶和羟甲基尼龙中的一种或几种。
9.根据权利要求1所述的一种水包水多彩涂料，其特征在于：所述保护胶选用AP525、GTS、S-482A中的一种。
10.根据权利要求1所述的一种水包水多彩涂料，其特征在于：所述防霉杀菌剂选用JF-90、聚2-甲基-4-异噻唑啉-3-酮化合物和聚5-氯-2-甲基-4-异噻唑啉-3-酮化合物中的一种。