CN110603648A - 晶硅太阳能电池正面导电浆料及其制备方法和太阳能电池 - Google Patents

晶硅太阳能电池正面导电浆料及其制备方法和太阳能电池 Download PDF

Info

Publication number
CN110603648A
CN110603648A CN201880000359.5A CN201880000359A CN110603648A CN 110603648 A CN110603648 A CN 110603648A CN 201880000359 A CN201880000359 A CN 201880000359A CN 110603648 A CN110603648 A CN 110603648A
Authority
CN
China
Prior art keywords
solar cell
crystalline silicon
silicon solar
oxide
oxide etchant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201880000359.5A
Other languages
English (en)
Other versions
CN110603648B (zh
Inventor
刘小丽
孙丰振
李宇
黄玉平
李德林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Soltrium Technology Ltd
Original Assignee
Soltrium Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Soltrium Technology Ltd filed Critical Soltrium Technology Ltd
Publication of CN110603648A publication Critical patent/CN110603648A/zh
Application granted granted Critical
Publication of CN110603648B publication Critical patent/CN110603648B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种晶硅太阳能电池正面导电浆料，按照重量份计，所述晶硅太阳能电池正面导电浆料包括以下原料组分：金属粉80.0～93.0份；有机载体6.0～15.0份；氧化物刻蚀剂1.0～5.0份；其中，以所述氧化物刻蚀剂摩尔量为100％计，所述氧化物刻蚀剂包括以下组分：PbO 15～30％；TeO225～40％；Li2O 8.0～15.0％；SiO29.0～20.0％；Bi2O35.0～15.0％；MgO 0.1～10.0％；ZnO 0.5～10.0％；CaO 0.1～10.0％；添加元素的氧化物0～5.0％。该正面导电浆料在烧结过程中可以使得金属粉与硅形成良好的欧姆接触，极大的降低电阻，最终获得接触电阻低，导电性能好，附着力强的正面电极。

Description

PCT国内申请，说明书已公开。

Claims (1)

  1. PCT国内申请，权利要求书已公开。
CN201880000359.5A 2018-03-30 2018-03-30 晶硅太阳能电池正面导电浆料及其制备方法和太阳能电池 Active CN110603648B (zh)