CN110585467A - 空气净化凝胶组合物及其制备方法 - Google Patents
空气净化凝胶组合物及其制备方法 Download PDFInfo
- Publication number
- CN110585467A CN110585467A CN201910912780.XA CN201910912780A CN110585467A CN 110585467 A CN110585467 A CN 110585467A CN 201910912780 A CN201910912780 A CN 201910912780A CN 110585467 A CN110585467 A CN 110585467A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- gel composition
- air purification
- gel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了空气净化凝胶组合物及其制备方法，包括二氧化氯溶液、二氧化钛、活性炭粉、凝胶剂、热活化剂、表面活性剂、缓释剂、高效消臭剂、PH调节剂、非挥发性防冻剂、防腐剂和消泡剂，各原料重量份数的组份为：二氧化氯溶液10‑20份、二氧化钛30‑40份、活性炭粉10‑20份、凝胶剂4‑6份、热活化剂4‑6份、表面活性剂4‑6份、缓释剂3‑5份、高效消臭剂3‑5份、PH调节剂3‑5份、非挥发性防冻剂3‑5份、防腐剂3‑5份和消泡剂3‑5份，所述凝胶剂选自羧甲基纤维素醚和壳聚糖的混合物，且混合比例为3:1，所述热活化剂选自微细铁粉为粒度10‑44μm的细粉。该空气净化凝胶组合物及其制备方法，能够从多种角度对有害物质进行处理，提升车内的空气质量。
Description
技术领域
本发明属于空气净化技术领域，具体涉及空气净化凝胶组合物，还涉及空气净化凝胶组合物的制备方法。
背景技术
近年来，随着人们生活水平的提高和人们对环境健康的关注度日益提升，人们对室内空气质量的改善日益关注。在封闭环境如车内、办公室、卧室、客厅等空气不流通的环境中，油漆、皮革制品、树脂、塑料等所制成的内饰、配件都会或多或少释放出甲醛、苯及其同系物等具有不愉快气味及有害的气体。空气清新剂、空气净化剂、空气净化凝胶成为了不可或缺的日化产品。现有的空气净化凝胶中对一些汽车尾气中的有害气体并净化作用不强。
因此针对这一现状，迫切需要设计和生产空气净化凝胶组合物及其制备方法，能够很好的净化汽车尾气以及其他有害气体。
发明内容
本发明的目的在于提供空气净化凝胶组合物及其制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：空气净化凝胶组合物，包括二氧化氯溶液、二氧化钛、活性炭粉、凝胶剂、热活化剂、表面活性剂、缓释剂、高效消臭剂、PH调节剂、非挥发性防冻剂、防腐剂和消泡剂，各原料重量份数的组份为：二氧化氯溶液10-20份、二氧化钛30-40份、活性炭粉10-20份、凝胶剂4-6份、热活化剂4-6份、表面活性剂4-6份、缓释剂3-5份、高效消臭剂3-5份、PH调节剂3-5份、非挥发性防冻剂3-5份、防腐剂3-5份和消泡剂3-5份。
优选的，所述凝胶剂选自羧甲基纤维素醚和壳聚糖的混合物，且混合比例为3:1，所述热活化剂选自微细铁粉为粒度10-44μm的细粉。
优选的，所述表面活性剂为十二烷基二甲基氧化铵和十八醇聚氧乙烯醚的混合物，所述缓释剂为羧甲基纤维素钠、羟丙基纤维素、黄原胶中的一种。
优选的，所述高效消臭剂为稳定性二氧化氯、固体二氧化氯、高锰酸钾、过氧化钙、茶多酚、高铁酸盐中的一种，所述pH值调节剂选自柠檬酸、酒石酸、磷酸、盐酸和硝酸中的多种混合物。
优选的，所述非挥发性防冻剂选自乙二醇、丙二醇、丙三醇中的一种或多种混合，所述防腐剂选自是甲基异噻唑啉酮、苯甲醇、苯氧乙醇、聚六亚甲基双胍中的一种或多种混合。
优选的，所述消泡剂选自植物油、矿物油、硅油的多种混合物。
权利要求1-6任一项所述的空气净化凝胶组合物的制备方法，包括以下步骤：
S1、搅拌：将凝胶剂、热活化剂、表面活性剂、缓释剂、高效消臭剂、PH调节剂，非挥发性防冻剂、防腐剂和消泡剂置于玻璃器皿中进行均匀搅拌，搅拌8-10分钟后，加入二氧化氯溶液，得到凝胶状物；
S2、混匀：将凝胶状物、二氧化钛和活性炭粉置于三维混合机中混合均匀；
S3、包装：检测合格后，批量包装。
优选的，所述搅拌中的加热温度设置为50-60度，所述三维混合机的型号设置为常州市彬达干燥制粒设备有限公司的SYH-200的三维混合机，混合温度设置为40-60度。
本发明的技术效果和优点：该空气净化凝胶组合物及其制备方法，二氧化钛配合光照，从而实现甲醛的催化分解，表面活性剂和热活化剂的配合，能够提升活性炭的吸附作用，对各种有毒气体均有处理作用，包括汽车尾气；二氧化氯具有一定的消毒的作用，配合防腐剂和缓释剂，能够提升凝胶的使用寿命，也能起到一定的除菌效果；高效除臭剂能够降低异味的传播；该空气净化凝胶组合物及其制备方法，能够从多种角度对有害物质进行处理，提升车内的空气质量。
具体实施方式
下面将结合本发明的内容，对本发明内容中的技术方案进行清楚、完整地描述，显然，所描述的内容仅仅是本发明一部分内容，而不是全部的内容。基于本发明中的内容，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他内容，都属于本发明保护的范围。
实施例1
本发明提供了空气净化凝胶组合物，包括二氧化氯溶液、二氧化钛、活性炭粉、凝胶剂、热活化剂、表面活性剂、缓释剂、高效消臭剂、PH调节剂、非挥发性防冻剂、防腐剂和消泡剂，各原料重量份数的组份为：二氧化氯溶液10份、二氧化钛30份、活性炭粉10份、凝胶剂4份、热活化剂4份、表面活性剂4份、缓释剂3份、高效消臭剂3份、PH调节剂3份、非挥发性防冻剂3份、防腐剂3份和消泡剂3份。
具体的，所述凝胶剂选自羧甲基纤维素醚和壳聚糖的混合物，且混合比例为3:1，所述热活化剂选自微细铁粉为粒度10-44μm的细粉。
具体的，所述表面活性剂为十二烷基二甲基氧化铵和十八醇聚氧乙烯醚的混合物，所述缓释剂为羧甲基纤维素钠、羟丙基纤维素、黄原胶中的一种。
具体的，所述高效消臭剂为稳定性二氧化氯、固体二氧化氯、高锰酸钾、过氧化钙、茶多酚、高铁酸盐中的一种，所述pH值调节剂选自柠檬酸、酒石酸、磷酸、盐酸和硝酸中的多种混合物。
具体的，所述非挥发性防冻剂选自乙二醇、丙二醇、丙三醇中的一种或多种混合，所述防腐剂选自是甲基异噻唑啉酮、苯甲醇、苯氧乙醇、聚六亚甲基双胍中的一种或多种混合。
具体的，所述消泡剂选自植物油、矿物油、硅油的多种混合物。
权利要求1-6任一项所述的空气净化凝胶组合物的制备方法，包括以下步骤：
S1、搅拌：将凝胶剂、热活化剂、表面活性剂、缓释剂、高效消臭剂、PH调节剂，非挥发性防冻剂、防腐剂和消泡剂置于玻璃器皿中进行均匀搅拌，搅拌8-10分钟后，加入二氧化氯溶液，得到凝胶状物；
S2、混匀：将凝胶状物、二氧化钛和活性炭粉置于三维混合机中混合均匀；
S3、包装：检测合格后，批量包装。
具体的，所述搅拌中的加热温度设置为50-60度，所述三维混合机的型号设置为常州市彬达干燥制粒设备有限公司的SYH-200的三维混合机，混合温度设置为40-60度。
实施例2
本发明提供了空气净化凝胶组合物，包括二氧化氯溶液、二氧化钛、活性炭粉、凝胶剂、热活化剂、表面活性剂、缓释剂、高效消臭剂、PH调节剂、非挥发性防冻剂、防腐剂和消泡剂，各原料重量份数的组份为：二氧化氯溶液20份、二氧化钛40份、活性炭粉20份、凝胶剂6份、热活化剂6份、表面活性剂6份、缓释剂5份、高效消臭剂5份、PH调节剂5份、非挥发性防冻剂5份、防腐剂5份和消泡剂5份。
具体的，所述凝胶剂选自羧甲基纤维素醚和壳聚糖的混合物，且混合比例为3:1，所述热活化剂选自微细铁粉为粒度10-44μm的细粉。
具体的，所述表面活性剂为十二烷基二甲基氧化铵和十八醇聚氧乙烯醚的混合物，所述缓释剂为羧甲基纤维素钠、羟丙基纤维素、黄原胶中的一种。
具体的，所述高效消臭剂为稳定性二氧化氯、固体二氧化氯、高锰酸钾、过氧化钙、茶多酚、高铁酸盐中的一种，所述pH值调节剂选自柠檬酸、酒石酸、磷酸、盐酸和硝酸中的多种混合物。
具体的，所述非挥发性防冻剂选自乙二醇、丙二醇、丙三醇中的一种或多种混合，所述防腐剂选自是甲基异噻唑啉酮、苯甲醇、苯氧乙醇、聚六亚甲基双胍中的一种或多种混合。
具体的，所述消泡剂选自植物油、矿物油、硅油的多种混合物。
权利要求1-6任一项所述的空气净化凝胶组合物的制备方法，包括以下步骤：
S1、搅拌：将凝胶剂、热活化剂、表面活性剂、缓释剂、高效消臭剂、PH调节剂，非挥发性防冻剂、防腐剂和消泡剂置于玻璃器皿中进行均匀搅拌，搅拌8-10分钟后，加入二氧化氯溶液，得到凝胶状物；
S2、混匀：将凝胶状物、二氧化钛和活性炭粉置于三维混合机中混合均匀；
S3、包装：检测合格后，批量包装。
具体的，所述搅拌中的加热温度设置为50-60度，所述三维混合机的型号设置为常州市彬达干燥制粒设备有限公司的SYH-200的三维混合机，混合温度设置为40-60度。
实施例3
本发明提供了空气净化凝胶组合物，包括二氧化氯溶液、二氧化钛、活性炭粉、凝胶剂、热活化剂、表面活性剂、缓释剂、高效消臭剂、PH调节剂、非挥发性防冻剂、防腐剂和消泡剂，各原料重量份数的组份为：二氧化氯溶液15份、二氧化钛35份、活性炭粉15份、凝胶剂5份、热活化剂5份、表面活性剂5份、缓释剂4份、高效消臭剂4份、PH调节剂4份、非挥发性防冻剂4份、防腐剂4份和消泡剂4份。
具体的，所述凝胶剂选自羧甲基纤维素醚和壳聚糖的混合物，且混合比例为3:1，所述热活化剂选自微细铁粉为粒度10-44μm的细粉。
具体的，所述表面活性剂为十二烷基二甲基氧化铵和十八醇聚氧乙烯醚的混合物，所述缓释剂为羧甲基纤维素钠、羟丙基纤维素、黄原胶中的一种。
具体的，所述高效消臭剂为稳定性二氧化氯、固体二氧化氯、高锰酸钾、过氧化钙、茶多酚、高铁酸盐中的一种，所述pH值调节剂选自柠檬酸、酒石酸、磷酸、盐酸和硝酸中的多种混合物。
具体的，所述非挥发性防冻剂选自乙二醇、丙二醇、丙三醇中的一种或多种混合，所述防腐剂选自是甲基异噻唑啉酮、苯甲醇、苯氧乙醇、聚六亚甲基双胍中的一种或多种混合。
具体的，所述消泡剂选自植物油、矿物油、硅油的多种混合物。
权利要求1-6任一项所述的空气净化凝胶组合物的制备方法，包括以下步骤：
S1、搅拌：将凝胶剂、热活化剂、表面活性剂、缓释剂、高效消臭剂、PH调节剂，非挥发性防冻剂、防腐剂和消泡剂置于玻璃器皿中进行均匀搅拌，搅拌8-10分钟后，加入二氧化氯溶液，得到凝胶状物；
S2、混匀：将凝胶状物、二氧化钛和活性炭粉置于三维混合机中混合均匀；
S3、包装：检测合格后，批量包装。
具体的，所述搅拌中的加热温度设置为50-60度，所述三维混合机的型号设置为常州市彬达干燥制粒设备有限公司的SYH-200的三维混合机，混合温度设置为40-60度。
最后应说明的是：以上所述仅为本发明的优选内容而已，并不用于限制本发明，尽管参照前述内容对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各内容所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换,凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.空气净化凝胶组合物，其特征在于：包括二氧化氯溶液、二氧化钛、活性炭粉、凝胶剂、热活化剂、表面活性剂、缓释剂、高效消臭剂、PH调节剂、非挥发性防冻剂、防腐剂和消泡剂，各原料重量份数的组份为：二氧化氯溶液10-20份、二氧化钛30-40份、活性炭粉10-20份、凝胶剂4-6份、热活化剂4-6份、表面活性剂4-6份、缓释剂3-5份、高效消臭剂3-5份、PH调节剂3-5份、非挥发性防冻剂3-5份、防腐剂3-5份和消泡剂3-5份。
2.根据权利要求1所述的空气净化凝胶组合物，其特征在于：所述凝胶剂选自羧甲基纤维素醚和壳聚糖的混合物，且混合比例为3:1，所述热活化剂选自微细铁粉为粒度10-44μm的细粉。
3.根据权利要求1所述的空气净化凝胶组合物，其特征在于：所述表面活性剂为十二烷基二甲基氧化铵和十八醇聚氧乙烯醚的混合物，所述缓释剂为羧甲基纤维素钠、羟丙基纤维素、黄原胶中的一种。
4.根据权利要求1所述的空气净化凝胶组合物，其特征在于：所述高效消臭剂为稳定性二氧化氯、固体二氧化氯、高锰酸钾、过氧化钙、茶多酚、高铁酸盐中的一种，所述pH值调节剂选自柠檬酸、酒石酸、磷酸、盐酸和硝酸中的多种混合物。
5.根据权利要求1所述的空气净化凝胶组合物，其特征在于：所述非挥发性防冻剂选自乙二醇、丙二醇、丙三醇中的一种或多种混合，所述防腐剂选自是甲基异噻唑啉酮、苯甲醇、苯氧乙醇、聚六亚甲基双胍中的一种或多种混合。
6.根据权利要求1所述的空气净化凝胶组合物，其特征在于：所述消泡剂选自植物油、矿物油、硅油的多种混合物。
7.权利要求1-6任一项所述的空气净化凝胶组合物的制备方法，其特征在于，包括以下步骤：
S1、搅拌：将凝胶剂、热活化剂、表面活性剂、缓释剂、高效消臭剂、PH调节剂，非挥发性防冻剂、防腐剂和消泡剂置于玻璃器皿中进行均匀搅拌，搅拌8-10分钟后，加入二氧化氯溶液，得到凝胶状物；
S2、混匀：将凝胶状物、二氧化钛和活性炭粉置于三维混合机中混合均匀；
S3、包装：检测合格后，批量包装。
8.根据权利要求7所述的空气净化凝胶组合物的制备方法，其特征在于：所述搅拌中的加热温度设置为50-60度，所述三维混合机的型号设置为常州市彬达干燥制粒设备有限公司的SYH-200的三维混合机，混合温度设置为40-60度。