CN110564370A - 一种具有光催化的抑尘剂及其制备方法 - Google Patents
一种具有光催化的抑尘剂及其制备方法 Download PDFInfo
- Publication number
- CN110564370A CN110564370A CN201910890467.0A CN201910890467A CN110564370A CN 110564370 A CN110564370 A CN 110564370A CN 201910890467 A CN201910890467 A CN 201910890467A CN 110564370 A CN110564370 A CN 110564370A
- Authority
- CN
- China
- Prior art keywords
- water
- dust
- dust suppressant
- soluble high
- molecular polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种具有光催化的抑尘剂及其制备方法,属于抑尘剂加工技术领域。本抑尘剂包括如下重量百分比的原料配置而成:水溶性高分子聚合物1~5%,双亲结构表面活性剂10~20%,复合光催化剂0.5~2%,余量为水。本发明通过同时具有亲油亲水功能的双亲结构表面活性剂可以使得疏水性粉尘快速被水润湿,水溶性高分子聚合物可以使得被润湿后的粉尘加速团聚而降落,达到快速有效除尘的效果;同时,配方中的复合光催化剂的催化效率高,可以在光照作用下有效降解粉尘上沾染的有机污染物,达到净化空气的效果。
Description
技术领域
本发明属于抑尘剂加工技术领域,具体涉及一种具有光催化的抑尘剂及其制备方法。
背景技术
在目前所有的降尘技术中,洒水降尘不仅工艺简单,而且降尘效果相对较好。但是,通过相关研究我们知道,粉尘分为亲水性粉尘和疏水性粉尘,疏水性粉尘由于其所具有的疏水性质,加之水的表面张力较大,使得粉尘在遇到水雾或水幕时,并不能快速地被水润湿和团聚,而洒水降尘只是通过碰撞、拦截等作用,促使粉尘降落,导致降尘效果受到限制。另外,环境中的粉尘多沾染有很多有机污染物,如果不对这些有机污染物进行一定程度的降解处理,人体吸入后会有损自身健康。
发明内容
本发明的目的在于提供一种可快速润湿和团聚疏水性粉尘且能通过光催化降解粉尘上有机污染物的抑尘剂。
为了达到上述目的,本发明的技术方案是:一种具有光催化的抑尘剂,包括如下重量百分比的原料配置而成:
水溶性高分子聚合物 1~5%;
双亲结构表面活性剂 10~20%;
复合光催化剂 0.5~2%;
余量为水。
进一步地,所述水溶性高分子聚合物为可溶性淀粉衍生物。
进一步地,所述双亲结构表面活性剂为胆酸盐类表面活性剂。
进一步地,所述复合光催化剂为金红石型纳米二氧化钛与石墨烯的水热合成物。
本发明的另一目的在于提供一种上述具有光催化抑尘剂的制备方法,包括如下步骤:
S1、首先将水溶性高分子聚合物加入水中在70~90℃下进行搅拌,直至完全溶解,而后静置冷却至室温;
S2、然后向上述S1步骤得到的溶液中加入双亲结构表面活性剂,进行充分搅拌,静置10~30min;
S3、最后向上述S2步骤得到的混合液中缓慢均匀加入复合光催化剂,进行充分搅拌,静置10~30min后封装,即制得成品抑尘剂。
相较于现有技术,本发明的有益效果在于:
本发明通过同时具有亲油亲水功能的双亲结构表面活性剂可以使得疏水性粉尘快速被水润湿,水溶性高分子聚合物可以使得被润湿后的粉尘加速团聚而降落,达到快速有效除尘的效果;同时,配方中的复合光催化剂的催化效率高,可以在光照作用下有效降解粉尘上沾染的有机污染物,达到净化空气的效果。
具体实施方式
以下是本发明的具体实施例,对本发明的技术方案作进一步的描述,但本发明并不限于这些实施例。
实施例1
本实施例提供的一种具有光催化的抑尘剂,包括如下重量百分比的原料配置而成:水溶性高分子聚合物1%,双亲结构表面活性剂10%,复合光催化剂0.5%,余量为水。
其中,水溶性高分子聚合物为可溶性淀粉衍生物,双亲结构表面活性剂为胆酸盐类表面活性剂,复合光催化剂为金红石型纳米二氧化钛与石墨烯的水热合成物。
该抑尘剂的制备方法,包括如下步骤:
S1、首先将水溶性高分子聚合物加入水中在70℃下进行搅拌,直至完全溶解,而后静置冷却至室温;
S2、然后向上述S1步骤得到的溶液中加入双亲结构表面活性剂,进行充分搅拌,静置10min;
S3、最后向上述S2步骤得到的混合液中缓慢均匀加入复合光催化剂,进行充分搅拌,静置10min后封装,即制得成品抑尘剂。
实施例2
本实施例提供的一种具有光催化的抑尘剂,包括如下重量百分比的原料配置而成:水溶性高分子聚合物3%,双亲结构表面活性剂15%,复合光催化剂1.3%,余量为水。
其中,水溶性高分子聚合物为可溶性淀粉衍生物,双亲结构表面活性剂为胆酸盐类表面活性剂,复合光催化剂为金红石型纳米二氧化钛与石墨烯的水热合成物。
该抑尘剂的制备方法,包括如下步骤:
S1、首先将水溶性高分子聚合物加入水中在80℃下进行搅拌,直至完全溶解,而后静置冷却至室温;
S2、然后向上述S1步骤得到的溶液中加入双亲结构表面活性剂,进行充分搅拌,静置20min;
S3、最后向上述S2步骤得到的混合液中缓慢均匀加入复合光催化剂,进行充分搅拌,静置20min后封装,即制得成品抑尘剂。
实施例3
本实施例提供的一种具有光催化的抑尘剂,包括如下重量百分比的原料配置而成:水溶性高分子聚合物5%,双亲结构表面活性剂20%,复合光催化剂2%,余量为水。
其中,水溶性高分子聚合物为可溶性淀粉衍生物,双亲结构表面活性剂为胆酸盐类表面活性剂,复合光催化剂为金红石型纳米二氧化钛与石墨烯的水热合成物。
该抑尘剂的制备方法,包括如下步骤:
S1、首先将水溶性高分子聚合物加入水中在90℃下进行搅拌,直至完全溶解,而后静置冷却至室温;
S2、然后向上述S1步骤得到的溶液中加入双亲结构表面活性剂,进行充分搅拌,静置30min;
S3、最后向上述S2步骤得到的混合液中缓慢均匀加入复合光催化剂,进行充分搅拌,静置30min后封装,即制得成品抑尘剂。
将实施例1、实施例2和实施例3所示的抑尘剂添加在清水中对环境进行喷洒除尘与仅采用清水对环境进行喷洒除尘情况下的环境粉尘浓度进行对比,如下表1所示:
表1
从表1数据可以看出,应用实施例1、实施例2和实施例3所述的抑尘剂进行喷洒后,相较于清水喷洒可以使环境达到快速降尘的效果。
本文中所描述的具体实施例仅仅是对本发明精神作举例说明。本发明所属技术领域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代,但并不会偏离本发明的精神或者超越所附权利要求书所定义的范围。
Claims (5)
1.一种具有光催化的抑尘剂,包括如下重量百分比的原料配置而成:
水溶性高分子聚合物 1~5%;
双亲结构表面活性剂 10~20%;
复合光催化剂 0.5~2%;
余量为水。
2.根据权利要求1所述的具有光催化的抑尘剂,其特征在于,所述水溶性高分子聚合物为可溶性淀粉衍生物。
3.根据权利要求1所述的具有光催化的抑尘剂,其特征在于,所述双亲结构表面活性剂为胆酸盐类表面活性剂。
4.根据权利要求1所述的具有光催化的抑尘剂,其特征在于,所述复合光催化剂为金红石型纳米二氧化钛与石墨烯的水热合成物。
5.一种上述具有光催化的抑尘剂的制备方法,包括如下步骤:
S1、首先将水溶性高分子聚合物加入水中在70~90℃下进行搅拌,直至完全溶解,而后静置冷却至室温;
S2、然后向上述S1步骤得到的溶液中加入双亲结构表面活性剂,进行充分搅拌,静置10~30min;
S3、最后向上述S2步骤得到的混合液中缓慢均匀加入复合光催化剂,进行充分搅拌,静置10~30min后封装,即制得成品抑尘剂。