CN111482165A - 一种改性光触媒溶液的制备方法 - Google Patents
一种改性光触媒溶液的制备方法 Download PDFInfo
- Publication number
- CN111482165A CN111482165A CN202010288245.4A CN202010288245A CN111482165A CN 111482165 A CN111482165 A CN 111482165A CN 202010288245 A CN202010288245 A CN 202010288245A CN 111482165 A CN111482165 A CN 111482165A
- Authority
- CN
- China
- Prior art keywords
- solution
- steps
- modified
- photocatalyst
- following
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的一种改性光触媒溶液的制备方法，属于光触媒技术领域，溶液的基础组份分别是：二氧化钛10％～15％、无水乙醇1％～5％、去离子水60％～90％、分散剂5％～8％、改性液4％～7％和氧化铝溶液2％～5％，采用该制备方法制备的光触媒溶液，性能较传统光触媒溶液有较大的提升，消除异味和有害气体能力强，效率高，稳定性高，能长期保存。
Description
技术领域
本发明属于光触媒技术领域，更具体来说，涉及一种改性光触媒溶液的制备方法。
背景技术
光触媒是一种以纳米级二氧化钛为代表的具有光催化功能的光半导体材料的总称，它涂布于基材表面，在紫外光及可见光的作用下，产生强烈催化降解功能：能有效地降解空气中有毒有害气体；能有效杀灭多种细菌，并能将细菌或真菌释放出的毒素分解及无害化处理；同时还具备除甲醛、除臭、抗污、净化空气等功能。
现实中常常制作光触媒溶液来喷涂物体表面或者空气中来消除异味或者有害气体。
发明内容
1.发明要解决的技术问题
本发明的目的在于解决现有技术中对异味难消除的困扰，提供一种改性光触媒溶液的制备方法，采用该制备方法制备的光触媒溶液，性能较传统光触媒溶液有较大的提升，消除异味和有害气体能力强，效率高，稳定性高，能长期保存。
2.技术方案
为达到上述目的，本发明提供的技术方案为：
本发明的一种改性光触媒溶液的制备方法，溶液的基础组份分别是：二氧化钛10％～15％、无水乙醇1％～5％、去离子水60％～90％、分散剂5％～8％、改性液4％～7％和氧化铝溶液2％～5％。
优选的，改性液包含聚乙二醇和聚丙烯酰胺。
优选的，改性液的加工方法为首先将聚乙二醇液态溶液进行加热搅拌，加热到一定温度后添加无水乙醇进行溶解，待全部溶于乙醇后添加聚丙烯酰胺进行改性。
优选的，聚乙二醇选用平均分子量为200-500的白色透明的聚乙二醇。
优选的，光触媒溶液的制备方法的步骤为：
S100、将二氧化钛和去离子水加入氧化铝溶液内，得到初液；
S200、添加改性液进行改性，在常温下充分搅拌得到混合液；
S300、在混合液中加入无水乙醇进行溶解析出的结晶，得到饱和液；
S400、在饱和液中加入分散剂并进行加热加压制备，最后冷却得到光触媒溶液。
优选的，步骤S400中加热的温度不低于50℃，加热时间不低于30min。
3.有益效果
采用本发明提供的技术方案，与现有技术相比，具有如下有益效果：
(1)本发明的一种改性光触媒溶液的制备方法，溶液的基础组份分别是：二氧化钛10％～15％、无水乙醇1％～5％、去离子水60％～90％、分散剂5％～8％、改性液4％～7％和氧化铝溶液2％～5％，采用此配方比制备的光触媒溶液，能够有效的去除有害气体和异味，稳定性高容易保存。
(2)本发明的一种改性光触媒溶液的制备方法，改性液包含聚乙二醇和聚丙烯酰胺，此配方的改性液，能够提高光触媒溶液的润滑性、保湿性和分散性，能够提高去除异味的效率。
附图说明
图1为本发明的一种改性光触媒溶液的制备方法的实施例对比图；
图2为本发明的一种改性光触媒溶液的XRD图。
具体实施方式
为了便于理解本发明，下面将参照相关附图对本发明进行更全面的描述，附图中给出了本发明的若干实施例，但是，本发明可以以许多不同的形式来实现，并不限于本文所描述的实施例，相反地，提供这些实施例的目的是使对本发明的公开内容更加透彻全面。
需要说明的是，当元件被称为“固设于”另一个元件，它可以直接在另一个元件上或者也可以存在居中的元件；当一个元件被认为是“连接”另一个元件，它可以是直接连接到另一个元件或者可能同时存在居中元件；本文所使用的术语“垂直的”、“水平的”、“左”、“右”以及类似的表述只是为了说明的目的。
除非另有定义，本文所使用的所有的技术和科学术语与属于本发明的技术领域的技术人员通常理解的含义相同；本文中在本发明的说明书中所使用的术语只是为了描述具体的实施例的目的，不是旨在于限制本发明；本文所使用的术语“及/或”包括一个或多个相关的所列项目的任意的和所有的组合。
一种改性光触媒溶液的制备方法，溶液的基础组份分别是：二氧化钛10％～15％、无水乙醇1％～5％、去离子水60％～90％、分散剂5％～8％、改性液4％～7％和氧化铝溶液2％～5％。
上述的改性液包含聚乙二醇和聚丙烯酰胺。
上述的改性液的加工方法为首先将聚乙二醇液态溶液进行加热搅拌，加热到一定温度后添加无水乙醇进行溶解，待全部溶于乙醇后添加聚丙烯酰胺进行改性。
上述的聚乙二醇选用平均分子量为200-500的白色透明的聚乙二醇。
上述的光触媒溶液的制备方法的步骤为：
S100、将二氧化钛和去离子水加入氧化铝溶液内，得到初液；
S200、添加改性液进行改性，在常温下充分搅拌得到混合液；
S300、在混合液中加入无水乙醇进行溶解析出的结晶，得到饱和液；
S400、在饱和液中加入分散剂并进行加热加压制备，最后冷却得到光触媒溶液。
上述的步骤S400中加热的温度不低于50℃，加热时间不低于30min。
采用上述方法制备的光触媒溶液具有较高的分散性、稳定性、润滑和保湿性，能够高效全面的去除异味等有害气体。
参照附图1-图2所示各实施例的具体情况描述如下：
实施例1
本实施例的一种改性光触媒溶液的制备方法，溶液的基础组份分别是：二氧化钛10％、无水乙醇1％、去离子水75％、分散剂5％、改性液4％和氧化铝溶液5％。
测得采用上述配比制备的光触媒溶液降解单位体积内95％以上有害气体的时间为45min。
实施例2
本实施例的一种改性光触媒溶液的制备方法，溶液的基础组份分别是：二氧化钛15％、无水乙醇5％、去离子水65％、分散剂5％、改性液5％和氧化铝溶液5％。
测得采用上述配比制备的光触媒溶液降解单位体积内95％以上有害气体的时间为30min。
实施例3
本实施例的一种改性光触媒溶液的制备方法，溶液的基础组份分别是：二氧化钛15％、无水乙醇5％、去离子水65％、分散剂5％、改性液7％和氧化铝溶液3％。
测得采用上述配比制备的光触媒溶液降解单位体积内95％以上有害气体的时间为20min。
以上所述实施例仅表达了本发明的某种实施方式，其描述较为具体和详细，但并不能因此而理解为对本发明专利范围的限制；应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围；因此，本发明专利的保护范围应以所附权利要求为准。
Claims (6)
1.一种改性光触媒溶液的制备方法，其特征在于：所述溶液的基础组份分别是：二氧化钛10％～15％、无水乙醇1％～5％、去离子水60％～90％、分散剂5％～8％、改性液4％～7％和氧化铝溶液2％～5％。
2.根据权利要求1所述的一种改性光触媒溶液的制备方法，其特征在于：所述改性液包含聚乙二醇和聚丙烯酰胺。
3.根据权利要求1或2所述的一种改性光触媒溶液的制备方法，其特征在于：所述改性液的加工方法为首先将聚乙二醇液态溶液进行加热搅拌，加热到一定温度后添加无水乙醇进行溶解，待全部溶于乙醇后添加聚丙烯酰胺进行改性。
4.根据权利要求1或2所述的一种改性光触媒溶液的制备方法，其特征在于：所述聚乙二醇选用平均分子量为200-500的白色透明的聚乙二醇。
5.根据权利要求1所述的一种改性光触媒溶液的制备方法，其特征在于：所述光触媒溶液的制备方法的步骤为：
S100、将二氧化钛和去离子水加入氧化铝溶液内，得到初液；
S200、添加改性液进行改性，在常温下充分搅拌得到混合液；
S300、在混合液中加入无水乙醇进行溶解析出的结晶，得到饱和液；
S400、在饱和液中加入分散剂并进行加热加压制备，最后冷却得到光触媒溶液。
6.根据权利要求1所述的一种改性光触媒溶液的制备方法，其特征在于：所述步骤S400中加热的温度不低于50℃，加热时间不低于30min。