CN110564190A - Inorganic fireproof coating with good air permeability - Google Patents
Inorganic fireproof coating with good air permeability Download PDFInfo
- Publication number
- CN110564190A CN110564190A CN201910942211.XA CN201910942211A CN110564190A CN 110564190 A CN110564190 A CN 110564190A CN 201910942211 A CN201910942211 A CN 201910942211A CN 110564190 A CN110564190 A CN 110564190A
- Authority
- CN
- China
- Prior art keywords
- parts
- air permeability
- inorganic fireproof
- good air
- fireproof coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an inorganic fireproof coating with good air permeability, belongs to the technical field of coatings, and aims to provide an inorganic fireproof coating with good air permeability and solve the problems of poor air permeability and insufficient environmental protection of the existing coatings. The composition comprises the following raw materials in parts by weight: 30-50 parts of silicate, 25-50 parts of calcium carbonate, 4-8 parts of colored soil, 5-9 parts of natural mineral gel and 6-13 parts of tourmaline. The invention is suitable for inorganic fireproof paint.
Description
Technical Field
The invention belongs to the technical field of coatings, and particularly relates to an inorganic fireproof coating with good air permeability.
Background
Coatings are a generic term for liquid or solid materials that can be applied to the surface of an object to form a solid film having protective, decorative or special properties (e.g., insulating, corrosion-resistant, fire-resistant, etc.). In the eighties of the last century, latex paint has entered the market to replace the more original lime water, almost occupied the whole inner wall coating market at a time, entered the Chinese coating market at large overseas brands and overseas capital, and rapidly consolidated a unique situation of latex paint in the wall coating field.
However, the events of leukemia in children, frequent lung cancer of painters and the like caused by decoration are often seen in media, and the health consciousness of a large number of consumers is rapidly aroused, so that the environmental protection problem of the latex paint is firstly brought to historical questioning tables in a rush in a large number of decoration materials, and people know the terms of formaldehyde and hackers from a repeated report. The emulsion paint is one of the water paint, which is the water paint put into use at the earliest time, and is prepared by using synthetic resin emulsion as a base material, using water as a dispersion medium, adding pigment, filler and an auxiliary agent and performing a certain technological process. The latex paint is generally prepared from chemical polyester, various combustion improvers and organic chemical adhesive, and has the advantages of formaldehyde, VOC, benzene series, heavy metal and other pollutants discharged, poor air permeability, easy cracking and bubbling of wall surfaces and poor antibacterial and mildewproof effects.
Therefore, the method solves the problems of poor air permeability and insufficient environmental protection of the existing coating and has important research significance.
Disclosure of Invention
The invention aims to: provides an inorganic fireproof coating with good air permeability, and solves the problems of poor air permeability and insufficient environmental protection of the existing coating.
The technical scheme adopted by the invention is as follows:
an inorganic fireproof coating with good air permeability is composed of the following raw materials in parts by weight: 30-50 parts of silicate, 25-50 parts of calcium carbonate, 4-8 parts of colored soil, 5-9 parts of natural mineral gel and 6-13 parts of tourmaline.
Preferably, the feed additive comprises the following raw materials in parts by weight: 30-45 parts of silicate, 25-40 parts of calcium carbonate, 5-7 parts of colored soil, 5-7 parts of natural mineral gel and 6-12 parts of tourmaline.
More preferably, the composition comprises the following raw materials in parts by weight: 42 parts of silicate, 35 parts of calcium carbonate, 6 parts of colored soil, 7 parts of natural mineral gel and 10 parts of tourmaline.
Further, the coating material is formed into a film by a physical film formation method.
In summary, due to the adoption of the technical scheme, the invention has the beneficial effects that:
1. The paint is prepared from silicate, calcium, colored soil, natural minerals and gel, the main base materials of the paint are inorganic materials, the prepared paint is different from the chemical film forming of the traditional paint, a novel physical film forming mode is adopted, the air environment can be adjusted, the paint is environment-friendly, high in fire protection level and high in air permeability, free evaporation of water in a building is facilitated, and cracking and bubbling of a wall surface are prevented. And the coating is alkaline, has excellent antibacterial and mildewproof effects, and solves the problems of poor air permeability and environmental pollution of the existing coating.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention is further described in detail with reference to the following embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
An inorganic fireproof coating with good air permeability is composed of the following raw materials in parts by weight: 30-50 parts of silicate, 25-50 parts of calcium carbonate, 4-8 parts of colored soil, 5-9 parts of natural mineral gel and 6-13 parts of tourmaline.
Preferably, the feed additive comprises the following raw materials in parts by weight: 30-45 parts of silicate, 25-40 parts of calcium carbonate, 5-7 parts of colored soil, 5-7 parts of natural mineral gel and 6-12 parts of tourmaline.
More preferably, the composition comprises the following raw materials in parts by weight: 42 parts of silicate, 35 parts of calcium carbonate, 6 parts of colored soil, 7 parts of natural mineral gel and 10 parts of tourmaline.
further, the coating material is formed into a film by a physical film formation method.
In the implementation process of the invention, before construction, the door and the window must be closed to reject air circulation; scraping waterproof putty and leveling the wall surface, and if the wall surface quality is poor, brushing the wall surface by using an interface agent; the first time, the wall surface is primed by applying a roller coating/spraying process; painting the wall surface for the second time under the condition of priming half-dry (no water on the wall surface); and after the second time of wall painting is finished, a scraper is used for polishing (note that polishing is not needed in the spraying process, and after the wall surface is completely dried, the protection is removed.
Example 1
An inorganic fireproof coating with good air permeability is composed of the following raw materials in parts by weight: 50 parts of silicate, 25 parts of calcium carbonate, 6 parts of colored soil, 8 parts of natural mineral gel and 11 parts of tourmaline.
Further, the coating material is formed into a film by a physical film formation method.
Example 2
An inorganic fireproof coating with good air permeability is composed of the following raw materials in parts by weight: 42 parts of silicate, 35 parts of calcium carbonate, 6 parts of colored soil, 7 parts of natural mineral gel and 10 parts of tourmaline.
Further, the coating material is formed into a film by a physical film formation method.
Example 3
An inorganic fireproof coating with good air permeability is composed of the following raw materials in parts by weight: 35 parts of silicate, 50 parts of calcium carbonate, 5 parts of colored soil, 7 parts of natural mineral gel and 8 parts of tourmaline.
Further, the coating material is formed into a film by a physical film formation method.
The above description is only for the purpose of illustrating the preferred embodiments of the present invention and is not to be construed as limiting the invention, and any modifications, equivalents and improvements made within the spirit and principle of the present invention are intended to be included within the scope of the present invention.
Claims (4)
1. The inorganic fireproof coating with good air permeability is characterized by comprising the following raw materials in parts by weight: 30-50 parts of silicate, 25-50 parts of calcium carbonate, 4-8 parts of colored soil, 5-9 parts of natural mineral gel and 6-13 parts of tourmaline.
2. The inorganic fireproof coating with good air permeability as claimed in claim 1, which is characterized by comprising the following raw materials in parts by weight: 30-45 parts of silicate, 25-40 parts of calcium carbonate, 5-7 parts of colored soil, 5-7 parts of natural mineral gel and 6-12 parts of tourmaline.
3. The inorganic fireproof coating with good air permeability as claimed in claim 2, which is characterized by comprising the following raw materials in parts by weight: 42 parts of silicate, 35 parts of calcium carbonate, 6 parts of colored soil, 7 parts of natural mineral gel and 10 parts of tourmaline.
4. The inorganic fireproof coating material with good air permeability of claim 1, wherein the coating material is physically formed into a film.