CN110548501A - 一种脱硝脱汞催化剂及其制备方法 - Google Patents
一种脱硝脱汞催化剂及其制备方法 Download PDFInfo
- Publication number
- CN110548501A CN110548501A CN201910680203.2A CN201910680203A CN110548501A CN 110548501 A CN110548501 A CN 110548501A CN 201910680203 A CN201910680203 A CN 201910680203A CN 110548501 A CN110548501 A CN 110548501A
- Authority
- CN
- China
- Prior art keywords
- denitration
- demercuration catalyst
- parts
- polyoxyethylene ether
- demercuration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种脱硝脱汞催化剂及其制备方法，其特征在于，按重量由以下组分组成：载体70‑85份；玻璃纤维6‑8份；生物质基炭材料150‑200份；硝酸钼40‑80份；添加剂2‑4份；结构助剂2‑10份；润滑粘结剂2‑8份；聚氧乙烯醚3‑6份；丝瓜络15‑18份；玉米秸秆4‑5份。本发明提供的脱汞吸附剂对木炭和粉煤灰进行了改性，增加了木炭和粉煤灰表面的孔洞，进而增大了木炭和粉煤灰的吸附能力，使用效果较好。
Description
技术领域
本发明涉及脱硝脱汞技术领域，尤其涉及一种脱硝脱汞催化剂及其制备方法。
背景技术
随着我国经济的发展，我国煤能源消耗量以及机动车的数量大幅度增加，造成空气中各种污染物的含量也在迅速上升；经过几十年的努力，我国在控制粉尘以及二氧化硫污染方面已经取得了一定的成功，但是汞和氮氧化物的污染尚未得到控制；传统的催化剂只能对汞或氮氧化物进行单向滤除，导致过滤混合烟气时，所需设备构造复杂，增加了生产成本，滤除效果不好。
发明内容
本发明正是针对以上技术问题，提供一种脱硝脱汞催化剂及其制备方法。
本发明为实现上述目的，采用以下技术方案：一种脱硝脱汞催化剂，其特征在于，按重量由以下组分组成：
所述载体成份构成为TiO2和Al2O3，且TiO2和Al2O3的质量添加比为4:1。
所述添加剂按重量百分比由以下组分组成：白泥27-28.5％、二氧化铈0.3-0.6％、硫酸锰0.3-0.6％、草酸0.9-1.8％、其余为水。
所述结构助剂包括铁、镁、钙、锌元素中的至少一种。
所述润滑粘结剂包括膨润土和甲基硅油，且膨润土和甲基硅油的质量比为2:1。
所述聚氧乙烯醚为蓖麻油聚氧乙烯醚、脂肪醇聚氧乙烯醚、异构醇聚氧乙烯醚中的一种或两种以上的组合。
本发明还提供一种制备上述脱硝脱汞催化剂的方法，其特征在于，包括以下步骤：(1)按照上述比例称取上述各原料，并将各原料溶解在去离子水中，室温下搅拌均匀，得到混合溶液；(2)将氨水倒入上述混合溶液中，并调整混合溶液的pH达到10，形成沉淀，搅拌5-10min后静置，多次倒去上层清液并添加新的去离子水，直至溶液的pH值达到7；(3)将沉淀过滤，烘干后移至马弗炉煅烧，即得到产品。
本发明的有益效果是：本发明提供的催化剂具有较高的比表面积，能够有效的提高催化剂的催化性能，使用效果较好。
具体实施方式
下面结合实施例对本发明作进一步说明：
一种脱硝脱汞催化剂，其特征在于，按重量由以下组分组成：
所述载体成份构成为TiO2和Al2O3，且TiO2和Al2O3的质量添加比为4:1。
所述添加剂按重量百分比由以下组分组成：白泥27-28.5％、二氧化铈0.3-0.6％、硫酸锰0.3-0.6％、草酸0.9-1.8％、其余为水。
所述结构助剂包括铁、镁、钙、锌元素中的至少一种。
所述润滑粘结剂包括膨润土和甲基硅油，且膨润土和甲基硅油的质量比为2:1。
所述聚氧乙烯醚为蓖麻油聚氧乙烯醚、脂肪醇聚氧乙烯醚、异构醇聚氧乙烯醚中的一种或两种以上的组合。
本发明还提供一种制备上述脱硝脱汞催化剂的方法，其特征在于，包括以下步骤：(1)按照上述比例称取上述各原料，并将各原料溶解在去离子水中，室温下搅拌均匀，得到混合溶液；(2)将氨水倒入上述混合溶液中，并调整混合溶液的pH达到10，形成沉淀，搅拌5-10min后静置，多次倒去上层清液并添加新的去离子水，直至溶液的pH值达到7；(3)将沉淀过滤，烘干后移至马弗炉煅烧，即得到产品。
实施例1一种脱硝脱汞催化剂，按重量由以下组分组成：
所述载体成份构成为TiO2和Al2O3，且TiO2和Al2O3的质量添加比为4:1。
所述添加剂按重量百分比由以下组分组成：白泥27％、二氧化铈0.3％、硫酸锰0.3％、草酸0.9％、水71.5％。
所述结构助剂包括铁、镁、钙、锌元素中的至少一种。
所述润滑粘结剂包括膨润土和甲基硅油，且膨润土和甲基硅油的质量比为2:1。
所述聚氧乙烯醚为蓖麻油聚氧乙烯醚、脂肪醇聚氧乙烯醚、异构醇聚氧乙烯醚中的一种或两种以上的组合。
上述脱硝脱汞催化剂的制备方法：首先按照上述比例称取70kg载体、6kg玻璃纤维、150kg生物质基炭材料、40kg硝酸钼、2kg添加剂、2kg结构助剂、2kg润滑粘结剂、3kg聚氧乙烯醚、15kg丝瓜络和4kg玉米秸秆溶解在去离子水中，室温下搅拌均匀，得到混合溶液；(2)将氨水倒入上述混合溶液中，并调整混合溶液的pH达到10，形成沉淀，搅拌5min后静置，多次倒去上层清液并添加新的去离子水，直至溶液的pH值达到7；(3)将沉淀过滤，烘干后移至马弗炉煅烧，即得到产品。
实施例2一种脱硝脱汞催化剂，按重量由以下组分组成：
所述载体成份构成为TiO2和Al2O3，且TiO2和Al2O3的质量添加比为4:1。
所述添加剂按重量百分比由以下组分组成：白泥28.5％、二氧化铈0.6％、硫酸锰0.6％、草酸1.8％、水68.5％。
所述结构助剂包括铁、镁、钙、锌元素中的至少一种。
所述润滑粘结剂包括膨润土和甲基硅油，且膨润土和甲基硅油的质量比为2:1。
所述聚氧乙烯醚为蓖麻油聚氧乙烯醚、脂肪醇聚氧乙烯醚、异构醇聚氧乙烯醚中的一种或两种以上的组合。
上述脱硝脱汞催化剂的制备方法：(1)首先按照上述比例称取85kg载体、8kg玻璃纤维、200kg生物质基炭材料、80kg硝酸钼、4kg添加剂、10kg结构助剂、8kg润滑粘结剂、6kg聚氧乙烯醚、18kg丝瓜络和5kg玉米秸秆溶解在去离子水中，室温下搅拌均匀，得到混合溶液；(2)将氨水倒入上述混合溶液中，并调整混合溶液的pH达到10，形成沉淀，搅拌5-10min后静置，多次倒去上层清液并添加新的去离子水，直至溶液的pH值达到7；(3)将沉淀过滤，烘干后移至马弗炉煅烧，即得到产品。
上面对本发明进行了示例性描述，显然本发明具体实现并不受上述方式的限制，只要采用了本发明的方法构思和技术方案进行的各种改进，或未经改进直接应用于其它场合的，均在本发明的保护范围之内。
Claims (7)
1.一种脱硝脱汞催化剂，其特征在于，按重量由以下组分组成：
2.根据权利要求1所述的一种脱硝脱汞催化剂，其特征在于，所述载体成份构成为TiO2和Al2O3，且TiO2和Al2O3的质量添加比为4:1。
3.根据权利要求2所述的一种脱硝脱汞催化剂，其特征在于，所述添加剂按重量百分比由以下组分组成：白泥27-28.5％、二氧化铈0.3-0.6％、硫酸锰0.3-0.6％、草酸0.9-1.8％、其余为水。
4.根据权利要求1所述的一种脱硝脱汞催化剂，其特征在于，所述结构助剂包括铁、镁、钙、锌元素中的至少一种。
5.根据权利要求1所述的一种脱硝脱汞催化剂，其特征在于，所述润滑粘结剂包括膨润土和甲基硅油，且膨润土和甲基硅油的质量比为2:1。
6.根据权利要求1所述的一种脱硝脱汞催化剂，其特征在于，所述聚氧乙烯醚为蓖麻油聚氧乙烯醚、脂肪醇聚氧乙烯醚、异构醇聚氧乙烯醚中的一种或两种以上的组合。
7.一种制备权利要求1所述的脱硝脱汞催化剂的方法，其特征在于，包括以下步骤：(1)按照上述比例称取上述各原料，并将各原料溶解在去离子水中，室温下搅拌均匀，得到混合溶液；(2)将氨水倒入上述混合溶液中，并调整混合溶液的pH达到10，形成沉淀，搅拌5-10min后静置，多次倒去上层清液并添加新的去离子水，直至溶液的pH值达到7；(3)将沉淀过滤，烘干后移至马弗炉煅烧，即得到产品。