CN1105348A - 砌筑保温砂浆粉及其生产方法 - Google Patents
砌筑保温砂浆粉及其生产方法 Download PDFInfo
- Publication number
- CN1105348A CN1105348A CN94100097A CN94100097A CN1105348A CN 1105348 A CN1105348 A CN 1105348A CN 94100097 A CN94100097 A CN 94100097A CN 94100097 A CN94100097 A CN 94100097A CN 1105348 A CN1105348 A CN 1105348A
- Authority
- CN
- China
- Prior art keywords
- powder
- flyash
- insulating mortar
- mortar powder
- pearlstone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是一种砌筑保温砂浆粉及其生产方法,为
粉状组合物,其组合物为粉煤灰50~75%,膨胀珍珠
岩3~8%,石灰粉10~20%,石膏粉3~8%。生产
方法为将上述原材料按配比混合均匀,装袋即成。该
产品具有体轻,保温性能好,和易性好,使用方便等优
点,适用于作建筑物的砌筑砂浆和墙体抹面,屋顶保
温等。
Description
本发明是一种砌筑保温砂浆粉及其生产方法,属于建材技术领域,适用于框架建筑的墙体砌筑及隔墙砌筑,也适用于墙体抹面。
目前,砌筑砂浆大多是水泥加砂子,比例为1∶5~1∶1。其缺点是密度大,一般为2000kg/m3,保温性差,一般导热泵数是1W/m·k。尤其在用加气块和粉煤灰砖砌筑墙的情况下,由于水泥砂浆是非节能材料,砌筑主体材料与砂浆不配套,会产生大量热桥现象,严重影响节能效果。
本发明的目的在于克服上述背景技术中的不足之处,而提供一种具有保温性能好,体轻抗压强度达到建筑要求的砌筑保温砂浆粉及其生产方法。
本发明的目的是这样实现的:其形态为粉状组合物,组合物及其配比为(重量比):粉煤灰50~70%,膨胀珍珠岩3~8%,石灰粉10~20%,石膏粉3~8%,生产方法是将上述的粉煤灰、膨胀珍珠岩、石灰粉、石膏粉,去杂后按配比混合均匀,装袋即成。
本发明的目的还可以通过以下措施来达到:
其组合物的最佳配比(重量比)为:粉煤灰75%,膨胀珍珠岩5%,石灰粉15%,石膏粉5%。
石灰粉的细度在150目左右。
在使用时,将砌筑保温砂浆粉加一倍左右的水即可应用。在养护过程中,石灰和石膏能击发粉煤灰的活性,增加强度与粘结力。膨胀珍珠岩和粉煤灰体轻,空心可提高保温绝热性能。
本发明与背景技术相比,具有如下效果:
1、体轻:干燥密度为580~600kg/m3
2、保温性能好,导热系数为0.1~0.14W/m·k。
3、其主要原料是粉煤灰,为废物利用,可减少对环境的污染。
4、由于该产品加水就可应用,因此使用方便,可实现文明施工。
5、成本低,生产工艺科学,方法简单。
下面结合实施例,对本发明作进一步详述:
实施例:取粉煤灰75公斤,膨胀珍珠岩5公斤,石灰粉15公斤,石膏粉5公斤,去杂混拌均匀装袋即成。袋要密封袋,以免在贮存时受潮。该产品不但是砌筑保温砂浆,也可做房屋的墙面抹面砂浆。
Claims (3)
1、一种砌筑保温砂浆粉,其特征在于:其形态为粉状组合物,组合物为(重量比)粉煤灰50~75%,膨胀珍珠岩3~8%,石灰粉10~20%,石膏粉3~8%。
2、根据权利要求1所述的砌筑保温砂浆粉,其特征在于:其组合物的最佳配比为(重量比):粉煤灰75%,膨胀珍珠岩5%,石灰粉15%,石膏粉5%。
3、如权利要求1所述的砌筑保温砂浆粉的生产方法,其特征在于:将粉煤灰、膨胀珍珠岩,石灰粉,石膏粉去杂,按配比要求混拌均匀,装袋即为成品。