CN110510624A - 一种耐高温云母粉制造工艺 - Google Patents

一种耐高温云母粉制造工艺 Download PDF

Info

Publication number
CN110510624A
CN110510624A CN201910814852.7A CN201910814852A CN110510624A CN 110510624 A CN110510624 A CN 110510624A CN 201910814852 A CN201910814852 A CN 201910814852A CN 110510624 A CN110510624 A CN 110510624A
Authority
CN
China
Prior art keywords
mica powder
mica
high temperature
temperature resistant
manufacturing process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910814852.7A
Other languages
English (en)
Inventor
王峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XUZHOU JINYA POWDER CO Ltd
Original Assignee
XUZHOU JINYA POWDER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XUZHOU JINYA POWDER CO Ltd filed Critical XUZHOU JINYA POWDER CO Ltd
Priority to CN201910814852.7A priority Critical patent/CN110510624A/zh
Publication of CN110510624A publication Critical patent/CN110510624A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐高温云母粉制造工艺，该工艺的生产步骤为：(1)称重、(2)冲洗、(3)破碎、(4)湿磨、(5)磁吸附、(6)除杂、(7)旋流分级、(8)烘干和(9)打散。本发明的一种耐高温云母粉制造工艺，以白云母、绢云母为原料，以金云母为原料和耐热添加剂，以湿磨代替常规研磨，基本杜绝了扬尘，保护了操作工人的健康，且生产出的云母粉具有耐高温的特性。

Description

一种耐高温云母粉制造工艺
技术领域
本发明涉及化工建材领域，具体是一种耐高温云母粉制造工艺。
背景技术
云母粉是一种非金属矿物，具有良好的弹性和韧性，还具有较高的绝缘性、耐酸碱、耐腐蚀性，是一种优良的添加剂。它广泛地应用于电器、电焊条、橡胶、塑料、造纸、油漆、涂料、颜料、陶瓷、化妆品、新型建材等行业，用途极其广泛。现有技术中制造的云母粉不能用于较高温的工作环境，且制造过程中，研磨设备会使云母粉弥散在空气中，使生产工人吸入肺中，危害健康。
发明内容
针对上述现有技术存在的问题，本发明的目的是提供一种耐高温云母粉制造工艺，使用该工艺制造云母粉，可以杜绝研磨过程中的扬尘，且生产出的云母粉具有耐高温的特性。
为实现上述目的，本发明采用的技术方案是：一种耐高温云母粉制造工艺，包括以下步骤:
(1)称重：按重量份称取配料白云母36份、绢云母31份、金云母15-26份；
(2)冲洗：将称取的物料放入冲洗池中清洗干净；
(3)破碎：将清洗后的物料放入破碎机破碎成云母颗粒；
(4)湿磨：将云母颗粒放入湿法研磨机进行研磨；
(5)磁吸附：将研磨后的云母粉浆放入磁分选机进行磁吸附；
(6)除杂：向磁吸附后的云母粉浆中投加除杂剂进行纯化和除杂；
(7)旋流分级：将除杂后的云母粉浆倒入分级旋流器，将不同粒径的云母粉颗粒进行分级；
(8)烘干：将不同粒径的云母粉分别进行烘干；
(9)打散：将烘干后的云母粉块打散后，进行包装，即完成耐高温云母粉的制作。
优选地，所述步骤(6)的除杂剂为重量份为2-5的碳酸氢钠。
本发明的一种耐高温云母粉制造工艺，以白云母、绢云母为原料，以金云母为原料和耐热添加剂，以湿磨代替常规研磨，基本杜绝了扬尘，保护了操作工人的健康，且生产出的云母粉具有耐高温的特性。
具体实施方式
下面结合实施例对本发明作进一步详细说明。
实施例1
一种耐高温云母粉制造工艺，包括以下步骤:
(1)称重：按重量份称取配料白云母36份、绢云母31份、金云母15份；
(2)冲洗：将称取的物料放入冲洗池中清洗干净；
(3)破碎：将清洗后的物料放入破碎机破碎成云母颗粒；
(4)湿磨：将云母颗粒放入湿法研磨机进行研磨；
(5)磁吸附：将研磨后的云母粉浆放入磁分选机进行磁吸附；
(6)除杂：向磁吸附后的云母粉浆中投加除杂剂进行纯化和除杂；
(7)旋流分级：将除杂后的云母粉浆倒入分级旋流器，将不同粒径的云母粉颗粒进行分级；
(8)烘干：将不同粒径的云母粉分别进行烘干；
(9)打散：将烘干后的云母粉块打散后，进行包装，即完成耐高温云母粉的制作。
作为进一步地优选方案，所述步骤(6)的除杂剂为重量份为2的碳酸氢钠。
经此步骤制成的耐高温云母粉产品，具有较好的耐高温性能，白度为83。
实施例2
一种耐高温云母粉制造工艺，包括以下步骤:
(1)称重：按重量份称取配料白云母36份、绢云母31份、金云母26份；
(2)冲洗：将称取的物料放入冲洗池中清洗干净；
(3)破碎：将清洗后的物料放入破碎机破碎成云母颗粒；
(4)湿磨：将云母颗粒放入湿法研磨机进行研磨；
(5)磁吸附：将研磨后的云母粉浆放入磁分选机进行磁吸附；
(6)除杂：向磁吸附后的云母粉浆中投加除杂剂进行纯化和除杂；
(7)旋流分级：将除杂后的云母粉浆倒入分级旋流器，将不同粒径的云母粉颗粒进行分级；
(8)烘干：将不同粒径的云母粉分别进行烘干；
(9)打散：将烘干后的云母粉块打散后，进行包装，即完成耐高温云母粉的制作。
作为进一步地优选方案，所述步骤(6)的除杂剂为重量份为5的碳酸氢钠。
经此步骤制成的耐高温云母粉产品，具有极佳的耐高温性能，白度为82。

Claims (2)

1.一种耐高温云母粉制造工艺，其特征在于，包括以下步骤:
(1)称重：按重量份称取配料白云母36份、绢云母31份、金云母15-26份；
(2)冲洗：将称取的物料放入冲洗池中清洗干净；
(3)破碎：将清洗后的物料放入破碎机破碎成云母颗粒；
(4)湿磨：将云母颗粒放入湿法研磨机进行研磨；
(5)磁吸附：将研磨后的云母粉浆放入磁分选机进行磁吸附；
(6)除杂：向磁吸附后的云母粉浆中投加除杂剂进行纯化和除杂；
(7)旋流分级：将除杂后的云母粉浆倒入分级旋流器，将不同粒径的云母粉颗粒进行分级；
(8)烘干：将不同粒径的云母粉分别进行烘干；
(9)打散：将烘干后的云母粉块打散后，进行包装，即完成耐高温云母粉的制作。
2.根据权利要求1所述的一种耐高温云母粉制造工艺，其特征在于，所述步骤(6)的除杂剂为重量份为2-5的碳酸氢钠。
CN201910814852.7A 2019-08-30 2019-08-30 一种耐高温云母粉制造工艺 Pending CN110510624A (zh)