CN110498641A - A kind of environmental and ecological plate - Google Patents
A kind of environmental and ecological plate Download PDFInfo
- Publication number
- CN110498641A CN110498641A CN201910823655.1A CN201910823655A CN110498641A CN 110498641 A CN110498641 A CN 110498641A CN 201910823655 A CN201910823655 A CN 201910823655A CN 110498641 A CN110498641 A CN 110498641A
- Authority
- CN
- China
- Prior art keywords
- environmental
- ecological
- ecological plate
- coupling agent
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmental and ecological plates, including following each component: tobermorite, wood pulp cellulose, extruding vermiculite, is hydrated negative ion powder, silane coupling agent, stabilizer, additive;Environmental and ecological plate of the invention achievees the effect that environmental protection compared with prior art, using no asbestos, the natural nonpollution material without formaldehyde;A certain amount of surface treating agent is added, improves the mechanical property of ecological board;A certain amount of negative ion powder is added, human body synthesis and vitamin storage can be facilitated, there is highly important effect to the vital movement of human body and other biological, in addition, environmental and ecological plate thermal coefficient provided by the invention can be down to 0.2 hereinafter, excellent thermal insulation performance, meets the industrial policy of national energy-saving heat preservation, advantage is had more at two aspects of energy conservation and environmental protection, application prospect is very wide.
Description
Technical field
The present invention relates to calcium silicate board technical field, specially a kind of environmental and ecological plate.
Background technique
Calcium silicate board is as new green environment protection building materials, other than having the function of conventional gypsum plate, with more superior
The advantages of fire protecting performance and moisture resistance, service life overlength, it is widely used in the suspended ceiling and partition wall of industry and commerce engineering construction, family
The siding of the indoor engineerings such as front yard finishing, the liner plate of furniture, the refractory slab in warehouse, net floor and tunnel.
Due to using a large amount of raw ore substance and lignocellulose raw material in the preparation process of these existing calcium silicate boards, no
Conducive to the protection of the natural resources such as raw ore and timber, meanwhile, the existing calcium silicate board problem bad there is also mechanical property, because
This, also needs to conduct further research it.
Summary of the invention
Technical assignment of the invention be in view of the deficiencies of the prior art, provide it is a kind of it is environmentally protective, insulated fire effect is good
Environmental and ecological plate, meanwhile, a certain amount of surface treating agent silane coupling agent is added can weaken calcium silicate board internal stress and answer
Become, improves mechanical property.
The technical solution adopted by the present invention to solve the technical problems is:
A kind of environmental and ecological plate is each composition by following mass percent:
Tobermorite 50 ~ 55%
Wood pulp cellulose 8 ~ 12%
Extruding vermiculite 1 ~ 3%
It is hydrated negative ion powder 1 ~ 2%
Silane coupling agent 3 ~ 5%
Stabilizer 10 ~ 15%
Additive 10 ~ 20%
The preparation method comprises the following steps: a kind of preparation method of the ecological board of heat preservation environment protection, comprising the following steps:
(1) by formula weigh composition insulated fire environmental and ecological plate each raw material, mix uniformly, and be crushed to 100 mesh ~
200 mesh, obtain mixture;
(2) mixture is put into beater, water is added to be beaten, obtain mixed slurry, wherein the mass parts of mixture and water ratio is
1:60~70。
(3) by mixed slurry starching, platemaking machine plate-making, cutting machine cutting plate, still kettle be steam-cured, drying machine drying, edge polisher
Edging, abrasive finishing machine abrasive finishing, both the environmental and ecological plate.
The beneficial effects of the present invention are: the environmental and ecological plate that (1) is of the invention, raw material sources are abundant, low in cost, preparation
Method is simple, combined strength bination is high, water absorption rate is low, environmentally protective, heat preservation and soundproof effect is good, light weight durable;(2) ring of the invention
Ecological board is protected, fire protecting performance is good, and using the calcium silicate board of secure and non-combustible as major ingredient, fire endurance is greater than 2 hours, reaches A1 rank
Fire-protection standard can satisfy the fire prevention demand of any building.
Specific embodiment
With reference to embodiment, the embodiment of the present invention is furthur described in detail.Following embodiment is used for
Illustrate the present invention, but is not intended to limit the scope of the invention.
Embodiment 1:
A kind of environmental and ecological plate proposed by the present invention, is each composition by following mass percent:
Tobermorite 50%
Wood pulp cellulose 12%
Extruding vermiculite 1%
It is hydrated negative ion powder 2%
Silane coupling agent 3%
Stabilizer 15%
Additive 17%
(1) by formula weigh composition insulated fire environmental and ecological plate each raw material, mix uniformly, and be crushed to 100 mesh ~
200 mesh, obtain mixture;
(2) mixture is put into beater, water is added to be beaten, obtain mixed slurry, wherein the mass parts of mixture and water ratio is
1:60。
(3) by mixed slurry starching, platemaking machine plate-making, cutting machine cutting plate, still kettle be steam-cured, drying machine drying, edge polisher
Edging, abrasive finishing machine abrasive finishing, both the environmental and ecological plate.
Embodiment 2:
A kind of environmental and ecological plate proposed by the present invention, is each composition by following mass percent:
Tobermorite 55%
Wood pulp cellulose 8%
Extruding vermiculite 3%
It is hydrated negative ion powder 1%
Silane coupling agent 5%
Stabilizer 10%
Additive 18%
(1) by formula weigh composition insulated fire environmental and ecological plate each raw material, mix uniformly, and be crushed to 100 mesh ~
200 mesh, obtain mixture;
(2) mixture is put into beater, water is added to be beaten, obtain mixed slurry, wherein the mass parts of mixture and water ratio is
1:70。
(3) by mixed slurry starching, platemaking machine plate-making, cutting machine cutting plate, still kettle be steam-cured, drying machine drying, edge polisher
Edging, abrasive finishing machine abrasive finishing, both the environmental and ecological plate.
Embodiment 3:
A kind of environmental and ecological plate proposed by the present invention, is each composition by following mass percent:
Tobermorite 53%
Wood pulp cellulose 10%
Extruding vermiculite 2%
It is hydrated negative ion powder 2%
Silane coupling agent 4%
Stabilizer 13%
Additive 16%
(1) by formula weigh composition insulated fire environmental and ecological plate each raw material, mix uniformly, and be crushed to 100 mesh ~
200 mesh, obtain mixture;
(2) mixture is put into beater, water is added to be beaten, obtain mixed slurry, wherein the mass parts of mixture and water ratio is
1:65。
(3) by mixed slurry starching, platemaking machine plate-making, cutting machine cutting plate, still kettle be steam-cured, drying machine drying, edge polisher
Edging, abrasive finishing machine abrasive finishing, both the environmental and ecological plate.
The above is only the preferred embodiment of the present invention, however it is not limited to the present invention, it is noted that for this science and technology
For the technical staff in field, without departing from the technical principles of the invention, several improvement and optimization can also be made, this
A little improvement and optimization also should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of environmental and ecological plate, it is characterised in that: each component including following mass percent:
Tobermorite 50 ~ 55%
Wood pulp cellulose 8 ~ 12%
Extruding vermiculite 1 ~ 3%
It is hydrated negative ion powder 1 ~ 2%
Silane coupling agent 3 ~ 5%
Stabilizer 10 ~ 15%
Additive 10 ~ 20%.
2. environmental and ecological plate according to claim 1, it is characterised in that: consist of the following mass percentage components: snow
Silicoglaserite 52%;Wood pulp cellulose 10%;Extruding vermiculite 2%;It is hydrated negative ion powder 2%;Silane coupling agent 3%;Stabilizer 13%;
Additive 18%.
3. environmental and ecological plate according to claim 1, it is characterised in that: silane coupling agent described in step (2) is silane
Any one in coupling agent KH550, silane coupling agent KH560 or silane coupling agent KH570.
4. environmental and ecological plate described in any one according to claim 1 ~ 2, which is characterized in that comprise the steps of:
(1) each raw material that the composition environmental and ecological plate of insulated fire is weighed by formula, is uniformly mixed, and be crushed to 100 mesh ~ 200
Mesh obtains mixture；(2) mixture is put into beater, water is added to be beaten, obtain mixed slurry, wherein mixture and water
Mass parts ratio is 1:60 ~ 70；(3) by mixed slurry starching, platemaking machine plate-making, cutting machine cutting plate, still kettle be steam-cured, dryer
Drying, edge polisher edging, abrasive finishing machine abrasive finishing, both the environmental and ecological plate.
5. environmental and ecological plate according to claim 4, it is characterised in that: by the weighed environmental protection of formula in the step (1)
Each raw material of ecological board is uniformly mixed, and is crushed to 150 mesh, obtains mixture.
6. a kind of preparation method of environmental and ecological plate according to claim 4, which is characterized in that will in the step (2)
Mixture puts into beater, adds water to be beaten, obtains mixed slurry, wherein the mass parts of mixture and water ratio is 1:65.