CN110485168A - A kind of cool feeling, the production method of fragrance, plastic-spraying Fashion - Google Patents
A kind of cool feeling, the production method of fragrance, plastic-spraying Fashion Download PDFInfo
- Publication number
- CN110485168A CN110485168A CN201910764878.5A CN201910764878A CN110485168A CN 110485168 A CN110485168 A CN 110485168A CN 201910764878 A CN201910764878 A CN 201910764878A CN 110485168 A CN110485168 A CN 110485168A
- Authority
- CN
- China
- Prior art keywords
- fabric
- spraying
- plastic
- cool feeling
- cool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cool feelings, the production method of fragrance, plastic-spraying Fashion, include the following steps: fabric → fabric desizing → washing, sour neutralization → stoving process → plastic-spraying → cool feeling test.The present invention produces satin weave fabric using ultra-high molecular weight polyethylene long filament on loom, wherein warp and weft is all made of 50D ultra-high molecular weight polyethylene long filament, after desizing drying, crow-style spraying decoration is applied using the plastic-spraying that silica gel plus pigment add perfumed finishing agent to carry out unique art creation, fabric is made to have fashion, the vision of art simultaneously but also with the functions such as fragrance, nice and cool.Fabric uses 100% ultra-high molecular weight polyethylene long filament simultaneously, and thermally conductive, rapid heat dissipation, thermal resistance is small, and 4-5 DEG C lower than common fabric temperature when wearing, cool feeling Q-max value is up to 0.81 after tested, nice and cool as summer clothes fabric not only fashion.
Description
Technical field
The invention belongs to textile industry fabric fields, and in particular to a kind of cool feeling, fragrance, plastic-spraying Fashion producer
Method.
Background technique
Ultra-high molecular weight polyethylene (UHMWPE) fiber is the high-performance fiber for realizing industrialized production the 1980s,
Also known as high-strength and high-modulus weight northylen (PE) fiber, good heat conductivity, radiating rate are used as the cool feeling fabric in summer fastly, but should
Fiber can not dye be current civil use industry bottleneck.
Point molding technology is the characteristic that using thermoplastic macromolecule material there is state can be changed, i.e., has under certain condition glutinous
Fluidity, and can restore solid characteristic under room temperature, and use method appropriate and special tool ink-jet sticks stream mode at it
Under fashion into the form of design as required, then curing molding at normal temperature.The surface point of textile fabric has white or colored point
Glue ornaments, are products as a kind of PVC silica type, the modeling of PVC point can also be made a modeling shoes, insole, support sole, sofa backrest,
The series of products such as handrail, dinner cloth, mahjong tablecloth, automobile interior trim.
Summary of the invention
Goal of the invention: in order to solve the deficiencies in the prior art, the present invention provides a kind of cool feeling, fragrance, plastic-spraying fashion faces
The production method of material.
Technical solution: a kind of cool feeling, the production method of fragrance, plastic-spraying Fashion include the following steps: fabric → fabric
Desizing → washing, sour neutralization → stoving process → plastic-spraying → cool feeling test；
The fabric desizing: technology preparation and condition are as follows:
The washing, acid neutralize: process flow is as follows: and high temperature washing → cold water washes → and acid neutralizes；
The washing of a high temperature: temperature is 80-90 DEG C；Time is 2-3min；
B cold water is washed: temperature is 30-40 DEG C；Time is 2-3min；
C acid neutralizes formula: glacial acetic acid 1-2g/L；PH value is 6-8.
The plastic-spraying: spray gun, the modeling of creative and artistic spraying various shape, size, color on fabric are used
Point, the characteristic that using thermoplastic macromolecule material there is state can be changed have glutinous fluidity under certain condition, and can under room temperature
Restore solid characteristic, and use method appropriate and special tool plastic-spraying, fashions into and set as required in the case where it sticks stream mode
The form of meter, then curing molding at normal temperature；
A formula is as follows:
B slurrying: the various substances in the above formula are prepared in proportion, the mixing time in high speed centrifugation stirring material bucket
For 8-10min.
C plastic-spraying: the slurry being stirred is packed into spray gun, spray tip diameter 1-3mm, the mill base of different colours is packed into different
Spray gun, according to the intention of design teacher adjust jet size and nozzle residence time and color collocation, spray it is various
Pattern.
D solidification: room temperature open width standing time is 30-50min, can batching packaging after being crosslinked silica gel solidification, adhesive.
As further optimization: the fabric specification: warp and weft is all made of 50D ultra-high molecular weight polyethylene long filament,
Breadth is 145-155cm, grammes per square metre 110-120g/m2, using forging line tissue.
As further optimization: the stoving process: forming machine drying temperature is 100-105 DEG C, time 3-
5min, door width are 145-155cm.
As further optimization: the cool feeling test: fabric cool feeling index Q-max value is up to 0.81.
The utility model has the advantages that specific advantage of the invention is as follows:
1, fabric of the invention forges line weave using 100%50D ultra-high molecular weight polyethylene long filament, and fabric has well
Thermal conductivity, thermal resistance is small, and surface gloss is high, soft and smooth nice and cool, is mainly used as summer clothes fabric.
2, due to ultra-high molecular weight polyethylene non-refractory, it is unable to high temperature pre-setting, dyeing print can not be carried out using dyestuff
Flower, therefore crow-style spraying decoration is applied using the plastic-spraying that silica gel adds pigment that perfumed finishing agent is added to carry out unique art creation, make fabric sometimes
Still, artistic vision is simultaneously but also with the functions such as fragrance, nice and cool.
3, silica gel is a kind of high activity adsorbent material, not soluble in water and any solvent, non-toxic and tasteless, environment-friendly degradable, sense of touch
Softer, suppleness is better than plastic cement, there is higher mechanical strength, and temperature resistant range can reach (- 40~230 DEG C).Absorption property
Height, thermal stability is good, chemical property is stable, has higher mechanical strength, can be securely bonded to the face PE under adhesive effect
On material.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, so that the technology of this field
Personnel can better understand advantages and features of the invention, to make apparent boundary to protection scope of the present invention
It is fixed.Embodiment described in the invention is only a part of the embodiment of the present invention, instead of all the embodiments, based on the present invention
In embodiment, those of ordinary skill in the art's every other implementation obtained without making creative work
Example, shall fall within the protection scope of the present invention.
Embodiment
The present invention produces satin weave fabric using ultra-high molecular weight polyethylene long filament on loom, and wherein warp and weft is adopted
With 50D ultra-high molecular weight polyethylene long filament, after desizing drying, adds perfumed finishing agent to carry out unique art using silica gel plus pigment and create
The plastic-spraying of meaning applies crow-style stamp, and fabric is made to have fashion, the vision of art simultaneously but also with the functions such as fragrance, nice and cool.Fabric simultaneously
Using 100% ultra-high molecular weight polyethylene long filament, thermally conductive, rapid heat dissipation, thermal resistance is small, 4-5 DEG C lower than common fabric temperature when wearing,
Cool feeling Q-max value is up to 0.81 after tested, nice and cool as summer clothes fabric not only fashion.
Specific embodiment 1
Process flow of the invention is substantially as follows: fabric → fabric desizing → washing, sour neutralization → stoving process → plastic-spraying
The test of → cool feeling.
1, fabric specification: warp and weft is all made of 50D ultra-high molecular weight polyethylene long filament, breadth 145-155cm, and grammes per square metre is
110-120g/m2, using forging line tissue.
2, fabric desizing: technology preparation and condition are as follows:
3, washing, acid neutralize: process flow is as follows: high temperature washing → cold water washes → acid neutralization；
The washing of a high temperature: temperature is 80 DEG C；Time is 2min；
B cold water is washed: temperature is 30 DEG C；Time is 2min；
C acid neutralizes formula: glacial acetic acid 1g/L；PH value is 6.
4, stoving process: forming machine drying temperature is 100 DEG C, time 3min, and door width is 145cm.
5, plastic-spraying: use spray gun, on fabric creative and artistic spraying various shape, size, color modeling point.Spray
Molding technology is the characteristic that using thermoplastic macromolecule material there is state can be changed, i.e., has glutinous fluidity under certain condition, and normal
Temperature is lower can to restore solid characteristic again, and uses method appropriate and special tool plastic-spraying, as required in the case where it sticks stream mode
The form of design is fashioned into, then curing molding at normal temperature.
A formula is as follows:
B slurrying: the various substances in the above formula are prepared in proportion, the mixing time in high speed centrifugation stirring material bucket
For 8min.
C plastic-spraying: the slurry being stirred is packed into spray gun, spray tip diameter 1mm, the mill base of different colours is packed into different
Spray gun adjusts the collocation of jet size and nozzle residence time and color according to the intention of design teacher, sprays various figures
Case.
D solidification: room temperature open width standing time is 30min, can batching packaging after being crosslinked silica gel solidification, adhesive.
6, cool feeling is tested: fabric cool feeling index Q-max value is up to 0.81.
Specific embodiment 2
Process flow of the invention is substantially as follows: fabric → fabric desizing → washing, sour neutralization → stoving process → plastic-spraying
The test of → cool feeling.
1, fabric specification: warp and weft is all made of 50D ultra-high molecular weight polyethylene long filament, breadth 145-155cm, and grammes per square metre is
120g/m2, using forging line tissue.
2, fabric desizing: technology preparation and condition are as follows:
3, washing, acid neutralize: process flow is as follows: high temperature washing → cold water washes → acid neutralization；
The washing of a high temperature: temperature is 90 DEG C；Time is 3min；
B cold water is washed: temperature is 40 DEG C；Time is 3min；
C acid neutralizes formula: glacial acetic acid 2g/L；PH value is 8.
4, stoving process: forming machine drying temperature is 105 DEG C, time 5min, and door width is 155cm.
5, plastic-spraying: use spray gun, on fabric creative and artistic spraying various shape, size, color modeling point.Spray
Molding technology is the characteristic that using thermoplastic macromolecule material there is state can be changed, i.e., has glutinous fluidity under certain condition, and normal
Temperature is lower can to restore solid characteristic again, and uses method appropriate and special tool plastic-spraying, as required in the case where it sticks stream mode
The form of design is fashioned into, then curing molding at normal temperature.
A formula is as follows:
B slurrying: the various substances in the above formula are prepared in proportion, the mixing time in high speed centrifugation stirring material bucket
For 10min.
C plastic-spraying: the slurry being stirred is packed into spray gun, spray tip diameter 3mm, the mill base of different colours is packed into different
Spray gun adjusts the collocation of jet size and nozzle residence time and color according to the intention of design teacher, sprays various figures
Case.
D solidification: room temperature open width standing time is 50min, can batching packaging after being crosslinked silica gel solidification, adhesive.
6, cool feeling is tested: fabric cool feeling index Q-max value is up to 0.81.
Specific embodiment 3
Process flow of the invention is substantially as follows: fabric → fabric desizing → washing, sour neutralization → stoving process → plastic-spraying
The test of → cool feeling.
1, fabric specification: warp and weft is all made of 50D ultra-high molecular weight polyethylene long filament, breadth 149cm, and grammes per square metre is
113g/m2, using forging line tissue.
2, fabric desizing: technology preparation and condition are as follows:
3, washing, acid neutralize: process flow is as follows: high temperature washing → cold water washes → acid neutralization；
The washing of a high temperature: temperature is 83 DEG C；Time is 2.5min；
B cold water is washed: temperature is 36 DEG C；Time is 2.4min；
C acid neutralizes formula: glacial acetic acid 1.3g/L；PH value is 7.
4, stoving process: forming machine drying temperature is 104 DEG C, time 4min, and door width is 149cm.
5, plastic-spraying: use spray gun, on fabric creative and artistic spraying various shape, size, color modeling point.Spray
Molding technology is the characteristic that using thermoplastic macromolecule material there is state can be changed, i.e., has glutinous fluidity under certain condition, and normal
Temperature is lower can to restore solid characteristic again, and uses method appropriate and special tool plastic-spraying, as required in the case where it sticks stream mode
The form of design is fashioned into, then curing molding at normal temperature.
A formula is as follows:
B slurrying: the various substances in the above formula are prepared in proportion, the mixing time in high speed centrifugation stirring material bucket
For 9min.
C plastic-spraying: the slurry being stirred is packed into spray gun, spray tip diameter 2mm, the mill base of different colours is packed into different
Spray gun adjusts the collocation of jet size and nozzle residence time and color according to the intention of design teacher, sprays various figures
Case.
D solidification: room temperature open width standing time is 40min, can batching packaging after being crosslinked silica gel solidification, adhesive.
6, cool feeling is tested: fabric cool feeling index Q-max value is up to 0.81.
Fabric of the invention forges line weave using 100%50D ultra-high molecular weight polyethylene long filament, and fabric has good
Thermal conductivity, thermal resistance is small, and surface gloss is high, soft and smooth nice and cool, is mainly used as summer clothes fabric.Due to ultra-high molecular weight polyethylene
Non-refractory is unable to high temperature pre-setting, dyeing and printing can not be carried out using dyestuff, therefore add pigment to add spice finish using silica gel
The plastic-spraying that agent carries out unique art creation applies crow-style stamp, and fabric is made to have fashion, the vision of art simultaneously but also with fragrance, nice and cool
Etc. functions.Silica gel is a kind of high activity adsorbent material, and not soluble in water and any solvent, non-toxic and tasteless, environment-friendly degradable, sense of touch compares
Softness, suppleness is better than plastic cement, there is higher mechanical strength, and temperature resistant range can reach (- 40~230 DEG C).Absorption property is high, warm
Stability is good, chemical property is stable, has higher mechanical strength, can be securely bonded on PE fabric under adhesive effect.
Claims (4)
1. the production method of a kind of cool feeling, fragrance, plastic-spraying Fashion, characterized by the following steps: fabric → fabric
Desizing → washing, sour neutralization → stoving process → plastic-spraying → cool feeling test；
The fabric desizing: technology preparation and condition are as follows:
The washing, acid neutralize: process flow is as follows: and high temperature washing → cold water washes → and acid neutralizes；
The washing of a high temperature: temperature is 80-90 DEG C；Time is 2-3min；
B cold water is washed: temperature is 30-40 DEG C；Time is 2-3min；
C acid neutralizes formula: glacial acetic acid 1-2g/L；PH value is 6-8.
The plastic-spraying: using spray gun, on fabric creative and artistic spraying various shape, size, color modeling point, it is sharp
The characteristic that with thermoplastic macromolecule material there is state can be changed has glutinous fluidity under certain condition, and can restore under room temperature
Solid characteristic, and method appropriate and special tool plastic-spraying are used, design is fashioned into as required in the case where it sticks stream mode
Form, then curing molding at normal temperature；
A formula is as follows:
B slurrying: the various substances in the above formula are prepared in proportion, and mixing time is 8- in high speed centrifugation stirring material bucket
10min。
C plastic-spraying: the slurry being stirred is packed into spray gun, spray tip diameter 1-3mm, the mill base of different colours is packed into different sprays
Rifle adjusts the collocation of jet size and nozzle residence time and color according to the intention of design teacher, sprays various figures
Case.
D solidification: room temperature open width standing time is 30-50min, can batching packaging after being crosslinked silica gel solidification, adhesive.
2. the production method of cool feeling according to claim 1, fragrance, plastic-spraying Fashion, it is characterised in that: the base
Cloth specification: warp and weft is all made of 50D ultra-high molecular weight polyethylene long filament, breadth 145-155cm, grammes per square metre 110-120g/m2,
Using forging line tissue.
3. the production method of cool feeling according to claim 1, fragrance, plastic-spraying Fashion, it is characterised in that: the baking
Dry technique: forming machine drying temperature is 100-105 DEG C, time 3-5min, and door width is 145-155cm.
4. the production method of cool feeling according to claim 1, fragrance, plastic-spraying Fashion, it is characterised in that: described is cool
Sensing examination: fabric cool feeling index Q-max value is up to 0.81.