CN110467405A - The mortar for adhering heat insulating plate and technique prepared with brick mixed building garbage regeneration powder - Google Patents
The mortar for adhering heat insulating plate and technique prepared with brick mixed building garbage regeneration powder Download PDFInfo
- Publication number
- CN110467405A CN110467405A CN201910878136.5A CN201910878136A CN110467405A CN 110467405 A CN110467405 A CN 110467405A CN 201910878136 A CN201910878136 A CN 201910878136A CN 110467405 A CN110467405 A CN 110467405A
- Authority
- CN
- China
- Prior art keywords
- powder
- mortar
- brick
- parts
- heat insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of mortar for adhering heat insulating plate and technique with the preparation of brick mixed building garbage regeneration powder, take full advantage of construction refuse regenerated micro mist, resource is saved, simultaneously in the micro mist that also plays the characteristics of common brick micro mist and performance, it is good adhesive property has been made, it is light-weight, the area that paves is big, the small mortar for adhering heat insulating plate of thermal coefficient.
Description
Technical field
The present invention relates to the technical field of mortar for building more particularly to a kind of brick mixed building garbage regeneration powder preparations
Mortar for adhering heat insulating plate and technique.
Background technique
Regenerative powder belongs to building waste partial size obtained in crushing and screening production recycled aggregate process and is less than 0.15mm
A kind of byproduct.The alternative part of cement of regenerative powder, for regeneration concrete, regeneration ordinary mortar and regeneration brick product
In, but its volume needs strict control, as substitution rate be more than it is a certain amount of, will cause regeneration concrete and mortar construct substantially reduce,
The adverse effects such as intensity decline.Wherein, the regenerative powder after brick mixed building refuse breaking is being found after largely studying, then
Fecula material has certain activity, when in for extraordinary mortar, can significantly improve product later strength.Currently, country encourages
Develop the insulation novel wall material of energy-conserving profit waste, it was reported that the EPS insulating layer of more ground external thermal insulation system is completing
Occur the more serious quality problems such as crack, fall off in 5 years, basic reason is the adhesive mortar durability of insulating layer
It can not be up to standard caused.The invention proposes a kind of preparation methods of novel mortar for adhering heat insulating plate, are remarkably improved binding sand
The performance of slurry.Belong to solid wastes recycling utilization simultaneously, the cost of raw material is cheap, excellent product performance.
Summary of the invention
To solve the above-mentioned problems, the present invention proposes a kind of adhering heat insulating plate prepared with brick mixed building garbage regeneration powder
Mortar and technique.
The technical scheme is that a kind of mortar for adhering heat insulating plate prepared with brick mixed building garbage regeneration powder is matched
Side, raw material includes following component in parts by weight:
350-400 parts of ordinary portland cement,
180-420 parts of natural river sand,
180-450 parts of regenerative powder,
12-16 parts of redispersible latex powder,
2-3 parts of hydroxypropyl methyl cellulose ether,
0.2-0.3 parts of starch ether;
24-25 parts of water.
Preferably;The ordinary portland cement of the model PO42.5 of the cement;
The ratio of powder containing common brick about 50%-55% in the regenerative powder, the about 45%- of ratio containing concrete powder
50%, partial size 0-0.3mm, moisture content is less than 0.6%;
The natural river sand fineness modulus is 2.4-2.5.
A kind of mortar for adhering heat insulating plate production technology prepared with brick mixed building garbage regeneration powder, includes the following steps:
A. the recycling and screening of the building waste of common brick
Transport the building waste containing common brick cleared of classification to treating construction waste field, using mobile impact crusher and
Screening plant processes building waste, removes the building rubbish containing common brick by sundries sorting and magnetic sorting in screening process
Wood materials, organic material and ferrous material in rubbish, it is containing red that screening, which obtains the building waste containing common brick that partial size is 0-5 millimeters,
The recycled fine aggregate of brick, 5 millimeters the above are the regenerated coarse aggregates containing common brick;
B. it dries
The recycled fine aggregate for being 0-5 millimeters to partial size obtained in step a is dried;In order to sieve;
C. dusting cover point
The recycled fine aggregate for being 0-5 millimeters by the partial size after drying, obtains 0-0.3 millimeters of brick mixed building garbage regeneration powder
Material;
D. it is spare (drying temperature is 90-120 degrees Celsius) that room temperature is down to after natural river sand being dried, moisture content 0-
0.5%;
E. redispersible latex powder, hydroxypropyl methyl cellulose ether, starch ether amalgamation are played into investment blender and stirs 3 points
Clock, until full and uniform;
F. cement, river sand, regenerative powder is added to be mixed 5 minutes, until full and uniform;
G. adding water and stirring the time need to control at 5 minutes, so that regenerative powder sufficiently absorbs water.
Preferably, it is characterized in that: drying in the step b is to be carried out in drying equipment using 90-120 degrees Celsius
Drying, being dried to moisture content is 0-0.5%.
Preferably, the dusting cover point uses aperture to be sorted for 0.3 millimeter of sieve.
Preferably, the recycled fine aggregate after regenerated coarse aggregate and step c dusting cover obtained in the step a point again into
Row drying blows away the powder of the attachment on its surface by pressure-air wind after then spreading out, and the sky of powder will be carried after wind
Gas collection imported into deduster, carries out the separation of air and powder, and the powder after separation is added to the powder after step c dusting cover point
In.
The method have the benefit that:
1. raw material is simple, save the cost.
Mortar for adhering heat insulating plate of the invention is mainly that raw material are brick mixed building rubbish after broken, drying, screening
Obtained regenerative powder, at low cost, production is simple, and technique has expanded the application range of construction refuse resource, environmental protection and energy saving,
Dual value with economic environmental protection.
2. adhesive property is good.
Mortar for adhering heat insulating plate of the invention, as cementitious material, mixes redispersible cream using ordinary portland cement outside
Rubber powder, hydroxypropyl methyl cellulose ether, starch ether improve the adhesion strength of cementitious material, while regenerative powder is active, In
Under the collective effect of these types of raw material, the adhesion strength of cementitious material is significantly improved.Common brick powder content reaches in regenerative micro powder
50%-55%, have light weight, the high feature of water retention, by adhering heat insulating plate on wall after, the moisture kept in mortar,
Slow release is equivalent to the maintenance action carried out to mortar itself, and the adhesion strength of such mortar is just elevated, to make
Adhesive mortar and insulation board, base course wall are sufficiently bonded together, and avoid the problem that falls off in later period.
3. light-weight, the area that paves is big, thermal coefficient is small.
Mortar for adhering heat insulating plate main raw material(s) brick mixed building garbage regeneration powder of the invention, common brick powder content is high, red
Be full of tiny hole inside brick powder, there is lesser bulk density, the regenerative powder mortar for adhering heat insulating plate of same weight compared with
The mortar of other materials with the bigger area that paves when construction, while having smaller thermal coefficient, to building masonry wall again
Heat preservation have humidification.
4. due to being full of tiny hole inside red brick powder, after mortar is completely dry, mortar itself is in similar micropore sea
Continuous shape has preferable flexibility, freeze thawing resistance;Cracking resistance, good weatherability, freedom from cracking, it is not easily to fall off, ensure that and protect outside entire exterior wall
The tightness of warm system significantly improves the durability and quality of its whole building exterior wall.
5, environmentally protective.
Mortar for adhering heat insulating plate of the invention is using brick mixed building garbage regeneration powder as primary raw material.To raising building waste
Utilization rate and the city ecological environment protection be of great significance.
6, mortar for adhering heat insulating plate of the invention has selected redispersible latex powder in the addition of additive, tool
Have that more prominent waterproof performance, adhesion strength are high, flexibility is good, increases the cohesive force of mortar, improves workability, improves
Mobile performance, can be very good to be distributed in entire mortar enhancing water-retaining property, give full play to its superior function.
7, for present invention process process by first drying, the mode of rear wind adheres to again the surface of coarse aggregate and fine aggregate
Fecula material has carried out comprehensive clearing and retrieving, the rate of recovery of regenerative powder is on the one hand improved, on the other hand also by recycled aggregate
Removing surface is clean, make the surface micropore of common brick particle in regenerated coarse aggregate and fine aggregate as early as possible may more than expose, avoid
It is wrapped up and is covered by powder, when being able to ascend regenerated coarse aggregate and fine aggregate production regeneration concrete in this way, aggregate is micro- by its
Being able to ascend for the bond strength of hole and cement slurry, kills two birds with one stone.
8, the experimental results showed that, the apparent density of mortar for adhering heat insulating plate of the present invention is 1800 kilograms per cubic meter, is stretched viscous
Knotting strength can reach standard requirements, and operable time 2.0-3.0 hours, freeze thawing is good, durability is good.Physical properties index
Meet the requirements.
9, the raw material sources of mortar for adhering heat insulating plate of the present invention are extensive, at low cost, simple production process, easily operated, energy
Enough meet the needs of different construction materials, there is good social and economic benefit.
Specific embodiment
Embodiment one: a kind of mortar for adhering heat insulating plate formula prepared with brick mixed building garbage regeneration powder, raw material include
Following component in parts by weight: 350 parts of cement, 400 parts of regenerative powder, 230 parts of natural river sand, redispersible latex powder
17 parts, 2.8 parts of hydroxypropyl methyl cellulose ether, 0.2 part of starch ether, 24-25 parts of water.
The ordinary portland cement of the model PO42.5 of the cement;
The ratio of powder containing common brick about 50%-55% in the regenerative powder, the about 45%- of ratio containing concrete powder
50%, partial size 0-0.3mm, moisture content is less than 0.6%;
Its production technology, includes the following steps:
A. the recycling and screening of the building waste of common brick
Transport the building waste containing common brick cleared of classification to treating construction waste field, using mobile impact crusher and
Screening plant processes building waste, removes the building rubbish containing common brick by sundries sorting and magnetic sorting in screening process
Wood materials, organic material and ferrous material in rubbish, it is containing red that screening, which obtains the building waste containing common brick that partial size is 0-5 millimeters,
The recycled fine aggregate of brick, 5 millimeters the above are the regenerated coarse aggregates containing common brick;
B. it dries
The recycled fine aggregate for being 0-5 millimeters to partial size obtained in step a is dried;In order to sieve;
C. dusting cover point
The recycled fine aggregate for being 0-5 millimeters by the partial size after drying, obtains 0-0.3 millimeters of brick mixed building garbage regeneration powder
Material;
D. it is spare (drying temperature is 90-120 degrees Celsius) that room temperature is down to after natural river sand being dried, moisture content 0-
0.5%;
E. redispersible latex powder, hydroxypropyl methyl cellulose ether, starch ether amalgamation are played into investment blender and stirs 3 points
Clock, until full and uniform;
F. cement, river sand, regenerative powder is added to be mixed 5 minutes, until full and uniform;
G. adding water and stirring the time need to control at 5 minutes, so that regenerative powder sufficiently absorbs water.
Drying is to be dried in drying equipment using 90-120 degrees Celsius in the step b, is dried to moisture content
For 0-0.5%.
The dusting cover point uses aperture to be sorted for 0.3 millimeter of sieve.
Regenerated coarse aggregate obtained in the step a and the recycled fine aggregate after step c dusting cover point are dried again,
Then by pressure-air wind after spreading out, the powder of the attachment on its surface is blown away, the air trapping of powder will be carried after wind
It is imported into deduster, carries out the separation of air and powder, the powder after separation is added in the powder after step c dusting cover divides.
Embodiment two: embodiment two is basically the same as the first embodiment, and the same thing is not repeated, and difference is embodiment two
In 300 parts of cement, 400 parts of regenerative powder, 280 parts of natural river sand, 17 parts of redispersible latex powder, hydroxypropyl methyl is fine
Plain 2.8 parts of the ether of dimension, 0.2 part of starch ether, 24-25 parts of water.
Embodiment three: embodiment three is basically the same as the first embodiment, and the same thing is not repeated, and difference is embodiment three
In 400 parts of cement, 285 parts of regenerative powder, 300 parts of natural river sand, 12 parts of redispersible latex powder, hydroxypropyl methyl is fine
Plain 2.8 parts of the ether of dimension, 0.2 part of starch ether, 24-25 parts of water.
Table 1 is one test result of embodiment
The heat insulation cementing mortar tensile bond strength experimental data table of 1 brick mixed building garbage regeneration powder of table preparation
The heat insulation cementing mortar tensile bond strength experimental data table of 1 brick mixed building garbage regeneration powder of table preparation
Table 2 is two test result of embodiment
The heat insulation cementing mortar tensile bond strength experimental data table of 2 brick mixed building garbage regeneration powder of table preparation
Table 3 is three test result of embodiment
The heat insulation cementing mortar tensile bond strength experimental data table of 3 brick mixed building garbage regeneration powder of table preparation.
Claims (6)
1. a kind of mortar for adhering heat insulating plate formula prepared with brick mixed building garbage regeneration powder, raw material includes in parts by weight
Following component:
350-400 parts of ordinary portland cement,
180-420 parts of natural river sand,
180-450 parts of regenerative powder,
12-16 parts of redispersible latex powder,
2-3 parts of hydroxypropyl methyl cellulose ether,
0.2-0.3 parts of starch ether;
24-25 parts of water.
2. the mortar for adhering heat insulating plate formula according to claim 1 prepared with brick mixed building garbage regeneration powder, special
Sign is:
The ordinary portland cement of the model PO42.5 of the cement;
The ratio of powder containing common brick about 50%-55% in the regenerative powder, the about 45%-50% of ratio containing concrete powder, grain
Diameter is 0-0.3mm, and moisture content is less than 0.6%;
The natural river sand fineness modulus is 2.4-2.5.
3. the insulation board prepared with brick mixed building garbage regeneration powder that raw material according to claim 1 or 2 carry out is viscous
Mortar production technology is tied, is included the following steps:
A. the recycling and screening of the building waste of common brick
It transports the building waste containing common brick that classification is cleared to treating construction waste field, utilizes mobile impact crusher and screening
Equipment processes building waste, is removed in the building waste containing common brick in screening process by sundries sorting and magnetic sorting
Wood materials, organic material and ferrous material, screening obtains building waste containing common brick that partial size is 0-5 millimeter as containing common brick
Recycled fine aggregate, 5 millimeters the above are the regenerated coarse aggregates containing common brick;
B. it dries
The recycled fine aggregate for being 0-5 millimeters to partial size obtained in step a is dried;In order to sieve;
C. dusting cover point
The recycled fine aggregate for being 0-5 millimeters by the partial size after drying, obtains 0-0.3 millimeters of brick mixed building garbage regeneration powder;
D. it is spare (drying temperature is 90-120 degrees Celsius) that room temperature is down to after natural river sand being dried, moisture content 0-0.5%;
E. redispersible latex powder, hydroxypropyl methyl cellulose ether, starch ether amalgamation are played investment blender and stirred 3 minutes,
It is extremely full and uniform;
F. cement, river sand, regenerative powder is added to be mixed 5 minutes, until full and uniform;
G. adding water and stirring the time need to control at 5 minutes, so that regenerative powder sufficiently absorbs water.
4. the mortar for adhering heat insulating plate production technology according to claim 3 prepared with brick mixed building garbage regeneration powder,
It is characterized in that:
Drying is to be dried in drying equipment using 90-120 degrees Celsius in the step b, and being dried to moisture content is 0-
0.5%.
5. the mortar for adhering heat insulating plate production technology according to claim 3 prepared with brick mixed building garbage regeneration powder,
It is characterized in that: the dusting cover point uses aperture to be sorted for 0.3 millimeter of sieve.
6. the mortar for adhering heat insulating plate production technology according to claim 5 prepared with brick mixed building garbage regeneration powder,
It is characterized in that: regenerated coarse aggregate obtained in the step a and the recycled fine aggregate after step c dusting cover point are dried again
It is dry, by pressure-air wind after then spreading out, the powder of the attachment on its surface is blown away, the air that powder is carried after wind is received
Collection imported into deduster, carries out the separation of air and powder, and the powder after separation is added in the powder after step c dusting cover divides.