CN106278088A - A kind of environmental protection is non-burning brick and preparation method thereof - Google Patents
A kind of environmental protection is non-burning brick and preparation method thereof Download PDFInfo
- Publication number
- CN106278088A CN106278088A CN201610618195.5A CN201610618195A CN106278088A CN 106278088 A CN106278088 A CN 106278088A CN 201610618195 A CN201610618195 A CN 201610618195A CN 106278088 A CN106278088 A CN 106278088A
- Authority
- CN
- China
- Prior art keywords
- parts
- burning brick
- environmental protection
- building waste
- ardealite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmental protection non-burning brick and preparation method thereof, it is non-burning brick is included by the weight portion of raw material: the domestic sludge of moisture content 80% 20 40 parts, building waste 15 18 parts, ardealite 5 10 parts, 20 30 parts of flyash, cinder 35 parts, 26 parts of slag, lime paste 0.2 1 parts, 47 parts of glue, prodan 0.01 0.2 parts, antifreezing agent 0.2 1 parts, water reducer 0.2 1.5 parts, air entraining agent 0.1 1 parts.The invention provides a kind of environmental protection non-burning brick and preparation method thereof, method is simple, with low cost, have employed the theory being directed to existing environmental protection, use multiple different waste resource to carry out non-burning brick manufacture, effectively while cost-effective, the most indirectly serve the effect of environmental protection, making it for environmental protection, a certain degree of assosting effect is played in ecological construction.
Description
Technical field
The present invention relates to technical field of buildings, particularly relate to a kind of environmental protection non-burning brick and preparation method thereof.
Background technology
Existing contamination class mainly has four aspects, be respectively atmospheric pollution, water pollute, noxious waste pollution and making an uproar
Sound pollution, and water pollutes main pollution source, from industrial wastewater (industrial water pollution essentially from paper-making industry, metallurgical industry,
Chemical industry and mining industry etc.) and city domestic sewage, and city domestic sewage is (although the discharge capacity of industrial wastewater is in mistake
Decline year by year between the decade gone, and the total amount of sanitary sewage increasing), and solid waste pollutes mainly industrial solid
Garbage, building waste and domestic waste.
Utilize (the one of above raw material such as flyash, cinder, gangue, mine tailings, residue of chemical industry or natural sand, tidal land mud
Plant or several) as primary raw material, a kind of novel wall material manufactured without high-temperature calcination is the most non-burning brick.This product
Meet the development building materials general policy of China's " protect the fields, save the energy, treatment in accordance with local conditions, gather materials on the spot ", meet State Council and once turned
Send out " strict limit ruin field bake bricks actively promote the suggestion of wall reform ", meet what the State Tax Administration of National Ministry of Finance once issued
(1996) No. 20 files of property tax word are " about continuing to lead to the implementation value-added tax preferential policies such as part resource comprehensive utilization product
Know ", this product is belonging to entirely exempt from the building material of value-added tax.
But, itself not utilizing most main pollution garbage, the meaning played for environmental protection is not
It is the hugest, is unfavorable for environmental protection, can not utilize efficiently for the main waste resource polluted.
Summary of the invention
The technical problem existed based on background technology, the present invention proposes that a kind of environmental protection is non-burning brick and preparation side
Method, has environmental protection, the waste gas utilization of resources, the advantage of low cost, and solving existing waste resource can not utilize, and causes environment
The problem polluted.
The present invention provides following technical scheme: a kind of environmental protection is non-burning brick, and it is non-burning brick is included by the weight portion of raw material:
Domestic sludge 20-40 part of moisture content 80%, building waste 15-18 part, ardealite 5-10 part, flyash 20-30 part, cinder 3-
5 parts, slag 2-6 part, lime paste 0.2-1 part, glue 4-7 part, prodan 0.01-0.2 part, antifreezing agent 0.2-1 part, water reducer
0.2-1.5 part, air entraining agent 0.1-1 part.
Preferably, described a kind of environmental protection is non-burning brick, and it is non-burning brick is included by the weight portion of raw material: moisture content 80%
Domestic sludge 20 parts, building waste 15 parts, ardealite 5 parts, 20 parts of flyash, cinder 3 parts, 2 parts of slag, lime paste 0.2 part,
4 parts of glue, prodan 0.01 part, antifreezing agent 0.2 part, water reducer 0.2 part, air entraining agent 0.1 part.
Preferably, described a kind of environmental protection is non-burning brick, and it is non-burning brick is included by the weight portion of raw material: moisture content 80%
Domestic sludge 40 parts, building waste 18 parts, ardealite 10 parts, 30 parts of flyash, cinder 5 parts, 6 parts of slag, lime paste 1 part,
7 parts of glue, prodan 0.2 part, antifreezing agent 1 part, water reducer 1.5 parts, air entraining agent 1 part.
Preferably, described a kind of environmental protection is non-burning brick, and it is non-burning brick is included by the weight portion of raw material: moisture content 80%
Domestic sludge 30 parts, building waste 17 parts, ardealite 8 parts, 25 parts of flyash, cinder 4 parts, 4 parts of slag, lime paste 0.45
Part, 5 parts of glue, prodan 0.01 part, antifreezing agent 0.8 part, water reducer 0.5 part, air entraining agent 0.7 part.
Preferably, described building waste mainly comprises composition is dregs, concrete block, crushed stone, brick and tile fragment, antiquated sand
Slurry, mud, asphalt blocks, waste plastics, old metal, useless bamboo wood etc..
Preferably, the preparation method that described a kind of environmental protection is non-burning brick, comprise the steps:
S1, first building waste is carried out coarse crushing, then by magnetic separation, carry out the primary filter of building waste, then
Again by magnetic separation, carry out the secondary filter of building waste, then by selecting crude drugs with winnower, carry out three filtrations of building waste, at general
The building waste managed is collected standby；
S2, ardealite, cinder, slag carry out magnetic separation and coarse crushing, obtain ardealite, cinder and the slag handled well, storage
Deposit collection standby；
S3, again by the domestic sludge of moisture content 80%, building waste, ardealite, flyash, cinder, slag, Calx
Cream, glue, prodan, antifreezing agent, water reducer, air entraining agent uniform stirring in proportion mixes, then carries out pulverization process, prepares mixed
Close granule, and a diameter of 2mm of granule；
S4, then pour the material that S3 handles well into non-baking brick machine in be shaped process, prepare molding adobe；
S5, then the adobe of S4 molding is dried 10-12 hour in the environment of 80-90 DEG C or natural curing 28 is (natural
After maintenance 8-12 hour, sprinkling water, every maintenance in 3-5 hour once, maintenance is placed after 7-10 hour naturally), i.e. make green
Color environment-friendly baking-free bricks.
The invention provides a kind of environmental protection non-burning brick and preparation method thereof, method is simple, with low cost, have employed pin
For the theory of existing environmental protection, use multiple different waste resource to carry out non-burning brick manufacture, effectively saving
While cost, the most indirectly serve the effect of environmental protection so that it is for environmental protection, ecological construction is played a certain degree of
Assosting effect.
The invention provides a kind of environmental protection non-burning brick and preparation method thereof, it uses the domestic sludge of moisture content 80%
With building waste as main material, both materials, pollute for water and the main pollution garbage of noxious waste pollution,
Its annual discharge capacity the most very huge, and the pollutant discharged can not effectively process, may result in environment deteriorates further,
It is unfavorable for the protection of environment, and the domestic sludge of this kind of moisture content 80% and the use of building waste, further save money
Source, protects environment, coordinates the use of ardealite simultaneously, and ardealite is typically powdery, and outward appearance is the most greyish white, sallow, light green
Isochrome, possibly together with organophosphor, sulfur fluoride compound, unit weight 0.733-0.88g/cm3, particle diameter is generally 5～15um, and it is main
Wanting composition is calcium sulphate dihydrate, and its content typically can reach 70～about 90%, and submember contained therein produces with rock phosphate in powder
Ground is different and different, the most all contains rock composition Ca, the phosphate of Mg and silicate.Ardealite discharges about the most every year in China
20000000 tons, accumulative discharge capacity nearly hundred million tons, is the one that in gypsum offscum, discharge capacity is maximum, and the phosphogypsum slag of discharge takies a large amount of soil
Ground, forms slag mountain, serious environment pollution, uses ardealite, in the case of improve environmental protection, also improve non-burning brick
Stability, uses flyash, cinder, slag, lime paste, glue, prodan, antifreezing agent, water reducer, the cooperation of air entraining agent simultaneously
Making non-burning brick, it is with low cost, environmental protection and energy saving, compression-resistant fire, thermal resistance thermal insulation, shock resistance are strong, has good economic benefit,
It is suitable for promoting the use of.
Detailed description of the invention
Below, by specific embodiment, technical scheme is described in detail.
Embodiment 1
The preparation method that a kind of environmental protection is non-burning brick, comprises the steps:
S1, first building waste 15 parts is carried out coarse crushing, then by magnetic separation, carries out the primary filter of building waste,
Then again by magnetic separation, carry out the secondary filter of building waste, then by selecting crude drugs with winnower, carry out three filtrations of building waste,
By standby for the building waste 15 parts collection handled well；
S2, ardealite 5 parts, cinder 3 parts, 2 parts of slag carry out magnetic separation and coarse crushing, obtain ardealite 5 parts, the coal handled well
Slag 3 parts and 2 parts of slag, store collected is standby；
S3, again by the domestic sludge 20 parts of moisture content 80%, building waste 15 parts, ardealite 5 parts, 20 parts of flyash,
Cinder 3 parts, 2 parts of slag, lime paste 0.2 part, 4 parts of glue, prodan 0.01 part, antifreezing agent 0.2 part, water reducer 0.2 part, bleed
0.1 part of uniform stirring mixing of agent, then carries out pulverization process, prepares hybrid particles, and a diameter of 2mm of granule；
S4, then pour the material that S3 handles well into non-baking brick machine in be shaped process, prepare molding adobe；
S5, then the adobe of S4 molding is dried 10-12 hour in the environment of 80-90 DEG C or natural curing 28 is (natural
After maintenance 8-12 hour, sprinkling water, every maintenance in 3-5 hour once, maintenance is placed after 7-10 hour naturally), i.e. make green
Color environment-friendly baking-free bricks.
Embodiment 2
The preparation method that a kind of environmental protection is non-burning brick, comprises the steps:
S1, first building waste 18 parts is carried out coarse crushing, then by magnetic separation, carries out the primary filter of building waste,
Then again by magnetic separation, carry out the secondary filter of building waste, then by selecting crude drugs with winnower, carry out three filtrations of building waste,
By standby for the building waste 18 parts collection handled well；
S2, ardealite 10 parts, cinder 5 parts, 6 parts of slag carry out magnetic separation and coarse crushing, the ardealite 10 parts that obtains handling well,
Cinder 5 parts and 6 parts of slag, store collected is standby；
S3, again by the domestic sludge 40 parts of moisture content 80%, building waste 18 parts, ardealite 10 parts, 30 parts of flyash,
Cinder 5 parts, 6 parts of slag, lime paste 1 part, 7 parts of glue, prodan 0.2 part, antifreezing agent 1 part, water reducer 1.5 parts, air entraining agent 1 part
Uniform stirring mixes, and then carries out pulverization process, prepares hybrid particles, and a diameter of 2mm of granule；
S4, then pour the material that S3 handles well into non-baking brick machine in be shaped process, prepare molding adobe；
S5, then the adobe of S4 molding is dried 10-12 hour in the environment of 80-90 DEG C or natural curing 28 is (natural
After maintenance 8-12 hour, sprinkling water, every maintenance in 3-5 hour once, maintenance is placed after 7-10 hour naturally), i.e. make green
Color environment-friendly baking-free bricks.
Embodiment 3
The preparation method that a kind of environmental protection is non-burning brick, comprises the steps:
S1, first building waste 17 parts is carried out coarse crushing, then by magnetic separation, carries out the primary filter of building waste,
Then again by magnetic separation, carry out the secondary filter of building waste, then by selecting crude drugs with winnower, carry out three filtrations of building waste,
By standby for the building waste 17 parts collection handled well；
S2, ardealite 8 parts, cinder 4 parts, 4 parts of slag carry out magnetic separation and coarse crushing, obtain ardealite 8 parts, the coal handled well
Slag 4 parts and 4 parts of slag, store collected is standby；
S3, again by the domestic sludge 30 parts of moisture content 80%, building waste 17 parts, ardealite 8 parts, 25 parts of flyash,
Cinder 4 parts, 4 parts of slag, lime paste 0.45 part, 5 parts of glue, prodan 0.01 part, antifreezing agent 0.8 part, water reducer 0.5 part, draws
0.7 part of uniform stirring mixing of gas agent, then carries out pulverization process, prepares hybrid particles, and a diameter of 2mm of granule；
S4, then pour the material that S3 handles well into non-baking brick machine in be shaped process, prepare molding adobe；
S5, then the adobe of S4 molding is dried 10-12 hour in the environment of 80-90 DEG C or natural curing 28 is (natural
After maintenance 8-12 hour, sprinkling water, every maintenance in 3-5 hour once, maintenance is placed after 7-10 hour naturally), i.e. make green
Color environment-friendly baking-free bricks.
Non-burning brick the carrying out of a kind of environmental protection described in embodiment 1-3 is used to manufacture and test (according to standard GB/T/T
The method that 2542-2012 specifies):
1 comprcssive strength:
Meansigma methods 15.3Mpa, monolithic minima 12.5Mpa, individual event evaluation: qualified
2 rupture strengths
Meansigma methods 2.5Mpa, monolithic minima 2.6Mpa, individual event evaluation: qualified
3 freeze proof degree
Freezing rear average strength 13Mpa, mass loss monolithic value 0.4%, individual event is evaluated: qualified
The non-burning brick intensity that specific embodiment 2 and embodiment 3 manufacture is higher, according to JC this product of 239-2001 standard monitoring
The requirement of product performance indications, its strength grade is MU10.
The invention provides a kind of environmental protection non-burning brick and preparation method thereof, method is simple, with low cost, have employed pin
For the theory of existing environmental protection, use multiple different waste resource to carry out non-burning brick manufacture, effectively saving
While cost, the most indirectly serve the effect of environmental protection so that it is for environmental protection, ecological construction is played a certain degree of
Assosting effect.
The invention provides a kind of environmental protection non-burning brick and preparation method thereof, it uses the domestic sludge of moisture content 80%
With building waste as main material, both materials, pollute for water and the main pollution garbage of noxious waste pollution,
Its annual discharge capacity the most very huge, and the pollutant discharged can not effectively process, may result in environment deteriorates further,
It is unfavorable for the protection of environment, and the domestic sludge of this kind of moisture content 80% and the use of building waste, further save money
Source, protects environment, coordinates the use of ardealite simultaneously, and ardealite is typically powdery, and outward appearance is the most greyish white, sallow, light green
Isochrome, possibly together with organophosphor, sulfur fluoride compound, unit weight 0.733-0.88g/cm3, particle diameter is generally 5～15um, and it is main
Wanting composition is calcium sulphate dihydrate, and its content typically can reach 70～about 90%, and submember contained therein produces with rock phosphate in powder
Ground is different and different, the most all contains rock composition Ca, the phosphate of Mg and silicate.Ardealite discharges about the most every year in China
20000000 tons, accumulative discharge capacity nearly hundred million tons, is the one that in gypsum offscum, discharge capacity is maximum, and the phosphogypsum slag of discharge takies a large amount of soil
Ground, forms slag mountain, serious environment pollution, uses ardealite, in the case of improve environmental protection, also improve non-burning brick
Stability, uses flyash, cinder, slag, lime paste, glue, prodan, antifreezing agent, water reducer, the cooperation of air entraining agent simultaneously
Making non-burning brick, it is with low cost, environmental protection and energy saving, compression-resistant fire, thermal resistance thermal insulation, shock resistance are strong, has good economic benefit,
It is suitable for promoting the use of.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto,
Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and
Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.
Claims (6)
1. an environmental protection is non-burning brick, it is characterised in that it is non-burning brick is included by the weight portion of raw material: the life of moisture content 80%
Mud 20-40 part alive, building waste 15-18 part, ardealite 5-10 part, flyash 20-30 part, cinder 3-5 part, slag 2-6 part,
Lime paste 0.2-1 part, glue 4-7 part, prodan 0.01-0.2 part, antifreezing agent 0.2-1 part, water reducer 0.2-1.5 part, air entraining agent
0.1-1 part.
A kind of environmental protection the most according to claim 1 is non-burning brick, it is characterised in that it is non-burning brick by the weight portion of raw material
Including: the domestic sludge of moisture content 80% 20 parts, building waste 15 parts, ardealite 5 parts, 20 parts of flyash, cinder 3 parts, slag 2
Part, lime paste 0.2 part, 4 parts of glue, prodan 0.01 part, antifreezing agent 0.2 part, water reducer 0.2 part, air entraining agent 0.1 part.
A kind of environmental protection the most according to claim 1 is non-burning brick, it is characterised in that it is non-burning brick by the weight portion of raw material
Including: the domestic sludge of moisture content 80% 40 parts, building waste 18 parts, ardealite 10 parts, 30 parts of flyash, cinder 5 parts, slag
6 parts, lime paste 1 part, 7 parts of glue, prodan 0.2 part, antifreezing agent 1 part, water reducer 1.5 parts, air entraining agent 1 part.
A kind of environmental protection the most according to claim 1 is non-burning brick, it is characterised in that it is non-burning brick by the weight portion of raw material
Including: the domestic sludge of moisture content 80% 30 parts, building waste 17 parts, ardealite 8 parts, 25 parts of flyash, cinder 4 parts, slag 4
Part, lime paste 0.45 part, 5 parts of glue, prodan 0.01 part, antifreezing agent 0.8 part, water reducer 0.5 part, air entraining agent 0.7 part.
5. non-burning brick according to a kind of environmental protection described in claim 1-4 any one, it is characterised in that: described building waste
Mainly comprise composition be dregs, concrete block, crushed stone, brick and tile fragment, waste mortar, mud, asphalt blocks, waste plastics, old metal,
Useless bamboo wood etc..
6. according to the preparation method that a kind of environmental protection described in claim 1-4 any one is non-burning brick, it is characterised in that bag
Include following steps:
S1, first building waste is carried out coarse crushing, then by magnetic separation, carry out the primary filter of building waste, the most again
By magnetic separation, carry out the secondary filter of building waste, then by selecting crude drugs with winnower, carry out three filtrations of building waste, will handle well
Building waste collect standby；
S2, ardealite, cinder, slag carry out magnetic separation and coarse crushing, obtain ardealite, cinder and the slag handled well, store and receive
Collect standby；
S3, again by the domestic sludge of moisture content 80%, building waste, ardealite, flyash, cinder, slag, lime paste, glue,
Prodan, antifreezing agent, water reducer, air entraining agent uniform stirring in proportion mixes, then carries out pulverization process, prepares mixing
Grain, and a diameter of 2mm of granule；
S4, then pour the material that S3 handles well into non-baking brick machine in be shaped process, prepare molding adobe；
S5, then by the adobe of S4 molding in the environment of 80-90 DEG C be dried 10-12 hour or natural curing 28 (natural curing
After 8-12 hour, sprinkling water, every maintenance in 3-5 hour once, maintenance is placed after 7-10 hour naturally), i.e. make green ring
Protect non-burning brick.