CN110437768B - Adhesive for apron adhesive tape of hovercraft and preparation method thereof - Google Patents
Adhesive for apron adhesive tape of hovercraft and preparation method thereof Download PDFInfo
- Publication number
- CN110437768B CN110437768B CN201910684127.2A CN201910684127A CN110437768B CN 110437768 B CN110437768 B CN 110437768B CN 201910684127 A CN201910684127 A CN 201910684127A CN 110437768 B CN110437768 B CN 110437768B
- Authority
- CN
- China
- Prior art keywords
- adhesive
- chloroprene rubber
- hovercraft
- rubber compound
- apron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to an adhesive for an apron adhesive tape of a hovercraft and a preparation method thereof, belonging to the technical field of rubber. The adhesive comprises a raw material A and a raw material B, wherein the raw material A comprises a chloroprene rubber compound and xylene, the component B comprises kemullock, and the mass ratio of the chloroprene rubber compound to the xylene to the kemullock is 1: 1-6: 0.1-5. The method comprises the steps of firstly preparing neoprene rubber compound, then dissolving the neoprene rubber compound in dimethylbenzene, and finally adding Kellock to obtain the neoprene rubber compound. The invention adopts an open mill to prepare the neoprene rubber compound serving as the adhesive, thereby effectively preventing scorching and gel generation. The adhesive containing the kelvin can be subjected to crosslinking reaction with an RFL treating agent for dipping the surface of the framework material and can also be subjected to crosslinking reaction with chloroprene rubber compound containing sulfur, so that the adhesive strength of the chloroprene rubber layer and the framework material is improved.
Description
Technical Field
The invention relates to an adhesive for an apron adhesive tape of a hovercraft and a preparation method thereof, in particular to an adhesive for bonding a framework material and a rubber coating layer in the apron adhesive tape of the hovercraft, belonging to the technical field of rubber.
Background
The apron of the hovercraft is made of rubberized fabric, and the rubberized fabric consists of framework materials (comprising nylon, polyester and the like) and a rubber-coated layer (rubber) on the surface. The apron is subjected to corrosion under severe conditions of deflection, abrasion, seawater, wind wave, aging and the like all year round under a dynamic environment, and abrasion, cracking and even delamination phenomena occur, so that the apron product fails. Therefore, the adhesive strength is one of the key factors affecting the performance of the blanket. In order to improve the adhesive strength, the surface treatment of the frame material is required to improve the adhesive strength between the rubber layer and the frame material.
Generally, a framework material woven by white gray cloth has low surface activity, and a commercial framework material is subjected to surface treatment by resorcinol-formaldehyde-latex (RFL) impregnation liquid to obtain an impregnated framework material which can be used. If the diene rubber material mainly comprising natural rubber is adopted, the bonding strength with the impregnated framework material is higher. However, natural rubber has poor aging resistance, and chloroprene rubber is adopted to improve the aging resistance of the rubber layer, but the chloroprene rubber has poor bonding strength with the impregnated framework material, so that the application of the chloroprene rubber is limited. The conventional neoprene adhesive is adopted to carry out secondary gluing treatment on the impregnated framework material, and the requirement of high bonding strength cannot be met.
Disclosure of Invention
Aiming at the defects in the prior art, the invention aims to provide an adhesive for apron adhesive tapes of a hovercraft and a preparation method thereof.
In order to achieve the purpose of the invention, the following technical scheme is provided.
The adhesive for the apron adhesive tape of the hovercraft is characterized by comprising a component A and a component B, wherein the component A comprises chloroprene mixed rubber and xylene, the component B comprises cimex 402, and the mass ratio of the chloroprene mixed rubber to the xylene to the cimex 402 is 1: 1-6: 0.1-5. The chloroprene rubber compound comprises the following raw materials in parts by weight:
composition of matter | Parts by mass |
Chloroprene rubber CR244 | 100.0 |
MgO | 2.0~4.0 |
ZnO | 4.0~10.0 |
Stearic acid | 0.5~2.0 |
Carbon Black N330 | 1.0~5.0 |
White carbon black | 3.0~8.0 |
Sulfur | 0.5~2.0 |
Anti-aging agent A | 0.5~2.0 |
Adhesive RC | 4.0~10.0 |
Wherein the antioxidant A is N-phenyl-alpha naphthylamine. The adhesive RC is a commercial compound-type m-whiting adhesive system. Kelvin 402 is a commercially available isocyanate-based adhesive.
A preparation method of an adhesive for apron adhesive tapes of a hovercraft comprises the following steps:
(1) preparation of chloroprene rubber compound: preparing materials: the neoprene gross rubber raw material composition and the mass portion requirement are proportioned; plasticating: thinly passing chloroprene rubber CR244 on an open mill for 10-20 times; open mixing: on a two-roller open mill, at the temperature of 40-60 ℃, after chloroprene rubber CR244, stearic acid, an anti-aging agent A, MgO, carbon black N330 and white carbon black are sequentially added, ZnO, an adhesive RC and sulfur are added; obtaining the chloroprene rubber compound after sheet discharge;
(2) cutting the chloroprene rubber compound into small pieces with the size of less than or equal to 100mm multiplied by 100mm, adding the small pieces into dimethylbenzene for swelling, wherein the swelling time is more than or equal to 10 hours; then stirring for 3-9 hours in an explosion-proof state to ensure that the components are completely dissolved and have no flocculent gel on the appearance, thus obtaining a component A;
(3) adding the component B into the component A, and stirring for 10-30min to obtain the adhesive for bonding the skeleton material and the rubber in the hovercraft apron.
Preferably, the roll spacing of the open mill is 1-5mm during plastication, and the roll temperature is 40-60 ℃.
Preferably, the thickness of the chloroprene rubber compound is 0.5 to 5 mm.
Preferably, the effective service time of the adhesive is not more than 8 hours.
Preferably, the adhesive is used for bonding the framework material and the adhesive coating layer in the apron adhesive tape of the hovercraft.
Advantageous effects
(1) The invention adopts an open mill to prepare the neoprene rubber compound serving as the adhesive, instead of banburying at the rubber discharge temperature of more than 100 ℃, so that the temperature of the rubber material is controlled between 40 and 60 ℃, and scorching and gel generation are effectively prevented. When the apron adhesive tape adopts chloroprene rubber as the adhesive layer, the requirement of the adhesive performance index of the framework material and the adhesive layer can be met.
(2) The sulfur can react with RFL butyl pyridine glue on the surface of the impregnated framework material to promote the binding force of the chloroprene rubber and the butyl pyridine, thereby improving the binding strength of the chloroprene rubber and the framework material.
(3) The adhesive is prepared just before use, the effective use time is not more than 8 hours, and the improvement of the adhesive performance is facilitated. The adhesive containing the kelvin can be subjected to crosslinking reaction with an RFL treating agent for dipping the surface of the framework material and can also be subjected to crosslinking reaction with chloroprene rubber compound containing sulfur, so that the adhesive strength of the chloroprene rubber layer and the framework material is improved.
Detailed Description
The following is a detailed description of preferred embodiments of the invention.
Example 1
An adhesive for bonding a skeleton material and rubber in a hovercraft apron comprises the following raw materials in percentage by mass:
the chloroprene rubber compound comprises the following raw materials in parts by weight:
serial number | Name of Material | Parts by mass |
1 | Chloroprene rubber CR244 | 100.0 |
2 | MgO | 2.0 |
3 | ZnO | 4.0 |
4 | Stearic acid | 0.5 |
5 | Carbon Black N330 | 1.0 |
6 | White carbon black | 3.0 |
7 | Sulfur | 0.5 |
8 | Anti-aging agent A | 0.5 |
9 | Adhesive RC | 4.0 |
A preparation method of an adhesive for bonding a framework material and rubber in an apron of a hovercraft comprises the following steps:
(1) preparation of chloroprene rubber compound: preparing materials: the neoprene gross rubber raw material composition and the mass portion requirement are proportioned; plasticating: thinly passing chloroprene rubber CR244 on an open mill for 10 times, wherein the roller spacing is 1mm, and the roller temperature is 40 ℃; open mixing: on a two-roller open mill, at 40 ℃, after plasticated chloroprene rubber CR244, stearic acid, an anti-aging agent A, MgO, carbon black N330 and white carbon black are sequentially added, ZnO, an adhesive RC and sulfur are added; and (5) obtaining the chloroprene rubber compound after sheet discharge, wherein the thickness of the chloroprene rubber compound is 0.5 mm.
(2) Cutting the chloroprene rubber compound into small pieces with the size of less than or equal to 100mm multiplied by 100mm, adding the small pieces into dimethylbenzene for swelling, and swelling for 10 hours; then stirring for 3 hours in an explosion-proof state to ensure that the components are completely dissolved and have no flocculent gel on the appearance, thus obtaining a component A;
(3) and adding the component B into the component A, and stirring for 10min to obtain the adhesive for bonding the skeleton material and the rubber in the apron of the hovercraft. The effective service time of the adhesive is not more than 8 h.
Example 2
An adhesive for bonding a skeleton material and rubber in a hovercraft apron comprises the following raw materials in percentage by mass:
the chloroprene rubber compound comprises the following raw materials in parts by weight:
serial number | Name of Material | Mass portion of |
1 | Chloroprene rubber CR244 | 100.0 |
2 | MgO | 3.0 |
3 | ZnO | 6.0 |
4 | Stearic acid | 1.0 |
5 | Carbon Black N330 | 3.0 |
6 | White carbon black | 5.0 |
7 | Sulfur | 1.0 |
8 | Anti-aging agent A | 1.0 |
9 | Adhesive RC | 6.0 |
A preparation method of an adhesive for bonding a framework material and rubber in an apron of a hovercraft comprises the following steps:
(1) preparation of chloroprene rubber compound: preparing materials: the neoprene gross rubber raw material composition and the mass portion requirement are proportioned; plasticating: thinly passing chloroprene rubber CR244 on an open mill for 15 times, wherein the roller spacing is 3mm, and the roller temperature is 50 ℃; open mixing: on a two-roller open mill, at 50 ℃, after chloroprene rubber CR244 after plastication, stearic acid, an anti-aging agent A, MgO, carbon black N330 and white carbon black are sequentially added, ZnO, an adhesive RC and sulfur are added; and (5) obtaining the chloroprene rubber compound after sheet discharge, wherein the thickness of the chloroprene rubber compound is 3 mm.
(2) Cutting the chloroprene rubber compound into small pieces with the size of less than or equal to 100mm multiplied by 100mm, adding the small pieces into dimethylbenzene for swelling, and swelling for 12 hours; then stirring for 6 hours in an explosion-proof state to ensure that the components are completely dissolved and have no flocculent gel on the appearance, thus obtaining a component A;
(3) and adding the component B into the component A, and stirring for 20min to obtain the adhesive for bonding the skeleton material and the rubber in the apron of the hovercraft. The effective service time of the adhesive is not more than 8 h.
Example 3
An adhesive for bonding a skeleton material and rubber in a hovercraft apron comprises the following raw materials in percentage by mass:
the chloroprene rubber compound comprises the following raw materials in parts by weight:
serial number | Name of Material | Mass portion of |
1 | Chloroprene rubber CR244 | 100.0 |
2 | MgO | 4.0 |
3 | ZnO | 10.0 |
4 | Stearic acid | 2.0 |
5 | Carbon Black N330 | 5.0 |
6 | White carbon black | 8.0 |
7 | Sulfur | 2.0 |
8 | Anti-aging agent A | 2.0 |
9 | Adhesive RC | 10.0 |
A preparation method of an adhesive for bonding a framework material and rubber in an apron of a hovercraft comprises the following steps:
(1) preparation of chloroprene rubber compound: preparing materials: the neoprene gross rubber raw material composition and the mass portion requirement are proportioned; plasticating: thinly passing chloroprene rubber CR244 on an open mill for 20 times, wherein the roller spacing is 5mm, and the roller temperature is 60 ℃; open mixing: on a two-roller open mill, at 60 ℃, after plasticated chloroprene rubber CR244, stearic acid, an anti-aging agent A, MgO, carbon black N330 and white carbon black are sequentially added, ZnO, an adhesive RC and sulfur are added; and (5) obtaining the chloroprene rubber compound after sheet discharge, wherein the thickness of the chloroprene rubber compound is 5 mm.
(2) Cutting the chloroprene rubber compound into small pieces with the size of less than or equal to 100mm multiplied by 100mm, adding the small pieces into dimethylbenzene for swelling, wherein the swelling time is not less than 12 h; then stirring for 9 hours in an explosion-proof state to ensure that the components are completely dissolved and have no flocculent gel on the appearance, thus obtaining a component A;
(3) and adding the component B into the component A, and stirring for 30min to obtain the adhesive for bonding the skeleton material and the rubber in the apron of the hovercraft. The effective service time of the adhesive is not more than 8 h.
The properties of the adhesives prepared in examples 1-3 are shown in the table below.
Test items | Example 1 | Example 2 | Example 3 | Test standard |
hardness/Shore A | 50 | 52 | 54 | GB/T 531.1-2008 |
Tensile strength MPa | 18.4 | 18.1 | 18.6 | GB/T 528-2009 |
Elongation/percent | 508 | 511 | 525 | GB/T 528-2009 |
Adhesive strength kN/m | 21.9 | 18.7 | 19.8 | GB/T 532-2008 |
Note: the adhesive strength refers to the adhesive strength between the chloroprene rubber coating layer and the framework material after the framework material is treated by the adhesive.
In summary, the invention includes but is not limited to the above embodiments, and any equivalent replacement or local modification made under the spirit and principle of the invention should be considered as being within the protection scope of the invention.
Claims (5)
1. The adhesive for the apron adhesive tape of the hovercraft is characterized in that: the adhesive comprises a raw material A and a raw material B, wherein the raw material A comprises a chloroprene rubber compound and xylene, the component B is a cimex 402, and the mass ratio of the chloroprene rubber compound to the xylene to the cimex 402 is 1: 1-6: 0.1-5; the chloroprene rubber compound comprises the following raw materials in parts by weight:
Wherein the antioxidant A is N-phenyl-alpha naphthylamine;
adding the component B into the component A, and stirring for 10-30min to obtain an adhesive for the apron adhesive tape of the hovercraft; the adhesive is used for bonding a framework material in the apron adhesive tape of the hovercraft and a chloroprene rubber adhesive-coated layer.
2. A method for preparing the adhesive for the apron adhesive tape of the hovercraft as claimed in claim 1, which is characterized in that: the method comprises the following steps:
(1) preparation of chloroprene rubber compound: preparing materials: the neoprene gross rubber raw material composition and the mass portion requirement are proportioned; plasticating: thinly passing chloroprene rubber CR244 on an open mill for 10-20 times; open mixing: on a two-roller open mill, at the temperature of 40-60 ℃, after chloroprene rubber CR244, stearic acid, an anti-aging agent A, MgO, carbon black N330 and white carbon black are sequentially added, ZnO, an adhesive RC and sulfur are added; obtaining the chloroprene rubber compound after sheet discharge;
(2) cutting the chloroprene rubber compound into small pieces with the size of less than or equal to 100mm multiplied by 100mm, adding the small pieces into dimethylbenzene for swelling, wherein the swelling time is more than or equal to 10 hours; then stirring for 3-9 hours in an explosion-proof state to ensure that the components are completely dissolved and have no flocculent gel on the appearance, thus obtaining a component A;
(3) adding the component B into the component A, and stirring for 10-30min to obtain the adhesive for the apron adhesive tape of the hovercraft.
3. The preparation method of the adhesive for the apron adhesive tape of the hovercraft as claimed in claim 2, wherein the adhesive comprises the following steps: during plastication, the roller spacing of the open mill is 1-5mm, and the roller temperature is 40-60 ℃.
4. The preparation method of the adhesive for the apron adhesive tape of the hovercraft as claimed in claim 2, wherein the adhesive comprises the following steps: the thickness of the neoprene rubber compound is 0.5-5 mm.
5. The preparation method of the adhesive for the apron adhesive tape of the hovercraft as claimed in claim 2, wherein the adhesive comprises the following steps: the effective service time of the adhesive is not more than 8 h.